Rashba Metamaterials and Metasurfaces with Zero Reflectivity and Effect of Surface States in Ultrathin Metal Films.

Metals, renowned for their high reflectivity, find extensive use in various technological applications, from mirrors to optical coatings in radars, telescopes, and mobile communications. However, their potential in antireflective coatings has remained largely untapped. In this study, we demonstrate that by applying an ultrathin metallic film onto an oxide layer, we can achieve a flawless optical surface with zero reflectivity. This phenomenon has been successfully observed across various metals, including Sn, Ag, Au, Pt, Bi, and Nb, showcasing its broad applicability. The underlying principle lies in the emergence of surface states, where the Rashba effect is strong, which give rise to the formation of Rashba metamaterial and metasurface (RMM) structures. Remarkably, these RMMs can be fine-tuned to act as high-resolution Veselago lenses. To illustrate, we achieved zero reflectivity with an RMM consisting of a 1 nm thick Sn metal film on a 1 nm Ge buffer, situated on a 60 nm Al2O3/Si substrate. Similar results were observed for other metals (Pt, Au, Ag, and Nb) and semimetals (Bi) by adjusting the film thickness to 2, 3, 5, 10, and 6 nm, respectively. The revelation of RMMs with zero reflectivity (R = 0) has tremendous potential to revolutionize optical device technologies, covering renewable energy, optoelectronics, and the telecommunications industry.

Highly Uniform Spherical MoO2-MoO3/Polypyrrole Core-Shell Nanocomposite as an Optoelectronic Photodetector in UV, Vis, and IR Domains.

A highly uniform spherical MoO2-MoO3/polypyrrole core-shell nanocomposite has been successfully synthesized as an optoelectronic photon sensing material, capable of detecting light in the UV, Vis, and IR domains. The nanocomposite is prepared through the oxidation of pyrrole using Na2MoO4, resulting in a uniform spherical morphology that has been confirmed by TEM, theoretical modeling, and SEM analyses. This morphology contributes to its promising optical behavior, characterized by a small bandgap of 1.36 eV. The optoelectronic photosensing capability of the nanocomposite has been evaluated across the UV, Vis, and IR spectra, demonstrating high efficiency. The photoresponsivity R values indicate the ability of the nanocomposite to generate hot electrons in response to incident photons. With an R value of 4.15 mA·W-1 at 440 nm, this optoelectronic device exhibits considerable promise for integration into an advanced technological apparatus. The detection (D) value of 9.30 × 108 Jones at 440 nm further confirms the high sensitivity in the Vis region. The excellent stability of the device can be attributed to the inherent MoO2-MoO3 oxide and Ppy polymer materials. This stability has been demonstrated through reproducibility studies and current-voltage measurements under various optical conditions. The combination of stability, efficiency, and sensitivity makes this optoelectronic device well suited for light sensing applications in both industrial and commercial settings. Its promising performance opens up opportunities for advancements in various fields requiring accurate and reliable light detection.

Photodetection Properties of CdS/Si Heterojunction Prepared by Pulsed Laser Ablation in DMSO Solution for Optoelectronic Application.

The high-quality n-type CdS on a p-type Si (111) photodetector device was prepared for the first time by a one-pot method based on an ns laser ablation method in a liquid medium. Cadmium target was ablated in DMSO solution, containing sulfur precursor, and stirred, assisting in 1D-growth, to create the sulfide structure as CdS nano-ropes form, followed by depositing on the Si-substrate by spin coating. The morphological, structural, and optical characteristics of the CdS structure were examined using X-ray diffraction, transmission, and scanning electron microscopy, photoluminescence, and UV-VIS spectroscopy. From X-ray diffraction analysis, the growing CdS spheres have a good crystal nature, with a high purity and desired c-axis orientation along the (002) plane, and the crystallinity was around 30 nm. According to optical characterization, high transparency was found in the visible-near-infrared areas of the electromagnetic spectrum, and the CdS spheres have a direct optical energy band gap of 3.2 eV. After that, the CdS/Si hetero-structured device was found to be improved remarkably after adding CdS. It showed that the forward current is constantly linear, while the dark current is around 4.5 µA. Up to a bias voltage of 4 V, there was no breakdown, and the reverse current of the heterojunctions somewhat increased with reverse bias voltage, while the photocurrent reached up to 580 and 690 µA for using 15 and 30 W/cm2 light power, respectively. Additionally, the ideal factors for CdS/Si heterojunction were 3.1 and 3.3 for 15 and 30 W/cm2 light power, respectively. These results exhibited high performance compared to the same heterojunction produced by other techniques. In addition, this opens the route for obtaining more enhancements of these values based on the changing use of sulfide structures in the heterojunction formation.

Quantification of muscle involvement in familial amyloid polyneuropathy using MRI.

BACKGROUND AND PURPOSE: Transthyretin familial amyloid polyneuropathy (TTR-FAP) is a rare genetic disease with autosomal-dominant inheritance. In this study, we aimed to quantify fatty infiltration (fat fraction [FF]) and magnetization transfer ratio (MTR) in individual muscles of patients with symptomatic and asymptomatic TTR-FAP using magnetic resonance imaging. Secondarily, we aimed to assess correlations with clinical and electrophysiological variables. METHODS: A total of 39 patients with a confirmed mutation in the TTR gene (25 symptomatic and 14 asymptomatic) and 14 healthy volunteers were included. A total of 16 muscles were manually delineated in the nondominant lower limb from T1-weighted anatomical images. The corresponding masks were propagated on the MTR and FF maps. Detailed neurological and electrophysiological examinations were conducted in each group. RESULTS: The MTR was decreased (42.6 AU; p = 0.001) and FF was elevated (14%; p = 0.003) in the lower limbs of the symptomatic group, with preferential posterior and lateral involvement. In the asymptomatic group, elevated FF was quantified in the gastrocnemius lateralis muscle (11%; p = 0.021). FF was significantly correlated with disease duration (r = 0.49, p = 0.015), neuropathy impairment score for the lower limb (r = 0.42, p = 0.041), Overall Neuropathy Limitations Scale score (r = 0.49, p = 0.013), polyneuropathy disability score (r = 0.57, p = 0.03) and the sum of compound muscle action potential (r = 0.52, p = 0.009). MTR was strongly correlated to FF (r = 0.78, p < 0.0001), and a few muscles with an FF within the normal range had a reduced MTR. CONCLUSION: These observations suggest that FF and MTR could be interesting biomarkers in TTR-FAP. In asymptomatic patients, FF in the gastrocnemius lateralis muscle could be a good indicator of the transition from an asymptomatic to a symptomatic form of the disease. MTR could be an early biomarker of muscle alterations.

Comparative Study between First and Second Harmonics of a Nd:YAG Laser for Cleaning Manifestation Damages That Appeared in Pigments Used on Archaeological Cartonnage.

This study focused on identifying the effect of the laser wavelengths used in cleaning some manifestation damage appearing in pigments used on archaeological cartonnage preserved in the Egyptian Museum, Egypt. The manifestations of damage appear as mud, resin, color, dust and microbiological damage stains. Lasers were chosen as one of the modern applications that give good results when cleaning the pigment materials without making direct contact with the material. Accordingly, lasers with a wavelength of 532 and 1064 nm were tested to identify their effect on stains caused by pigments and to choose the best one for use in cases similar to those materials in the future. This study was conducted to identify the effect of the selected wavelengths and choose the best ones to apply to the archaeological model. The evaluations were conducted using several tests and analyses, such as digital microscopy, X-ray florescence, Fourier transform infrared spectroscopy, and Handy colorimetry to evaluate that effect of lasers with a wavelength of 532 and 1064 nm to remove stains. The experimental study demonstrated the good effect of the Nd:YAG laser with a wavelength of 1064 nm compared with that of the 532 nm laser. The results of using the Nd:YAG laser proved the good effect of removing all stains compared with the 532 nm laser, which caused big changes when used to clean the stains on the pigment's surfaces; it also did not help in removing or reducing some stains such as mud stains. According to these results, the good effect of the Nd:YAG laser (1064 nm) make it more suitable for cleaning than that of the Nd:YAG laser (532 nm), which is not recommended for use as it gave bad results when applied.

Effect of CuO Nanoparticles on the Optical, Structural, and Electrical Properties in the PMMA/PVDF Nanocomposite.

A polymeric nanocomposite film, composed of PMMA/PVDF and different amounts of CuO NPs, was successfully prepared using the casting method to enhance its electrical conductivity. Various techniques were employed to investigate their physicochemical properties. The addition of CuO NPs causes a noticeable difference in the intensities and locations of vibrational peaks in all bands, confirming the incorporation of CuO NPs inside the PVDF/PMMA. In addition, the broadening of the peak at 2θ = 20.6° becomes more intense with increasing amounts of CuO NPs, confirming the increase in the amorphous characteristic of PMMA/PVDF incorporated with CuO NPs in comparison with PMMA/PVDF. Furthermore, the image of the polymeric structure exhibits a smoother shape and interconnection of pore structure associated with spherical particles that agglomerate and give rise to a web-like organization that becomes a matrix. Increasing surface roughness is responsible for an increasing surface area. Moreover, the addition of CuO NPs in the PMMA/PVDF leads to a decrease in the energy band gap, and further increasing the additional amounts of CuO NPs causes the generation of localized states between the valence and conduction bands. Furthermore, the dielectric investigation shows an increase in the dielectric constant, dielectric loss, and electric conductivity, which may be an indication of an increase in the degree of disorder that confines the movement of charge carriers and demonstrates the creation of an interconnected percolating chain, enhancing its conductivity values compared with that without the incorporation of a matrix.

Estimation of subvoxel fat infiltration in neurodegenerative muscle disorders using quantitative multi-T2 analysis.

MRI's T2 relaxation time is a valuable biomarker for neuromuscular disorders and muscle dystrophies. One of the hallmarks of these pathologies is the infiltration of adipose tissue and a loss of muscle volume. This leads to a mixture of two signal components, from fat and from water, to appear in each imaged voxel, each having a specific T2 relaxation time. In this proof-of-concept work, we present a technique that can separate the signals from water and from fat within each voxel, measure their separate T2 values, and calculate their relative fractions. The echo modulation curve (EMC) algorithm is a dictionary-based technique that offers accurate and reproducible mapping of T2 relaxation times. We present an extension of the EMC algorithm for estimating subvoxel fat and water fractions, alongside the T2 and proton-density values of each component. To facilitate data processing, calf and thigh anatomy were automatically segmented using a fully convolutional neural network and FSLeyes software. The preprocessing included creating two signal dictionaries, for water and for fat, using Bloch simulations of the prospective protocol. Postprocessing included voxelwise fitting for two components, by matching the experimental decay curve to a linear combination of the two simulated dictionaries. Subvoxel fat and water fractions and relaxation times were generated and used to calculate a new quantitative biomarker, termed viable muscle index, and reflecting disease severity. This biomarker indicates the fraction of remaining muscle out of the entire muscle region. The results were compared with those using the conventional Dixon technique, showing high agreement (R = 0.98, p < 0.001). It was concluded that the new extension of the EMC algorithm can be used to quantify abnormal fat infiltration as well as identify early inflammatory processes corresponding to elevation in the T2 value of the water (muscle) component. This new ability may improve the diagnostic accuracy of neuromuscular diseases, help stratification of patients according to disease severity, and offer an efficient tool for tracking disease progression.

Photodetection Enhancement via Graphene Oxide Deposition on Poly 3-Methyl Aniline.

A graphene oxide (GO)/poly 3-methyl aniline (P3MA) photodetector has been developed for light detection in a broad optical region: UV, Vis, and IR. The 3-methyl aniline was initially synthesized via radical polymerization using an acid medium, i.e., K2S2O8 oxidant. Consequently, the GO/P3MA composite was obtained through the adsorption of GO into the surface of P3MA. The chemical structure and optical properties of the prepared materials have been illustrated via XRD, FTIR, SEM, and TEM analysis. The absorbance measurements demonstrate good optical properties in the UV, Vis, and near-IR regions, although a decrease in the bandgap from 2.4 to 1.6 eV after the composite formation was located. The current density (Jph) varies between 0.29 and 0.68 mA·cm-2 (at 2.0 V) under dark and light, respectively. The photodetector has been tested using on/off chopped light at a low potential, in which the produced Jph values decrease from 0.14 to 0.04 µA·cm-2, respectively. The GO/P3MA photodetector exhibits excellent R (and D) values of 4 and 2.7 mA·W-1 (0.90 × 109 and 0.60 × 109 Jones) in the UV (340 nm) and IR (730 nm) regions, respectively. The R and D values obtained here make the prepared photodetector a promising candidate for future light detection instruments.

Fabrication and characterization of Ag nanoparticle-embedded κ-Carrageenan-Sodium alginate nanocomposite hydrogels with potential antibacterial and cytotoxic activities.

Hydrogel nanocomposites are attracting increasing attention in field of biology owing to their unique properties. The present work focuses on the fabrication and characterization of novel hydrogel nanocomposite systems in which silver nanoparticles (AgNPs) are embedded in a carrageenan (κ-CGN)-sodium alginate (SA) hydrogel. The performance of the prepared κ-CGN-SA hydrogel and κ-CGN-SA/AgNPs hydrogel nanocomposite was determined by UV-visible spectroscopy, FTIR, XRD, SEM, EDX spectrum, EDX mapping, and TEM analysis. Surface plasmon resonance at 428 nm confirmed the presence of AgNPs in the κ-CGN-SA hydrogel. The results indicate that AgNPs with an average diameter of 30 nm were uniformly dispersed in the κ-CGN-SA hydrogel matrix. The amount of Ag+ ion release kinetic from the κ-CGN-SA hydrogel matrix is very low, showing that AgNPs were well trapped within the κ-CGN-SA/AgNPs hydrogel nanocomposite. The high antibacterial activity of the κ-CGN-SA/AgNPs hydrogel nanocomposite was found to be 89.6 ± 1.4% and 91.4 ± 2.3% against the gram-positive S. aureus and the gram-negative E. coli, respectively. Moreover, the κ-CGN-SA/AgNPs hydrogel nanocomposite showed good biocompatibility by the MTT test. The novel κ-CGN-SA/AgNPs hydrogel nanocomposite low cytotoxicity and antibacterial efficacy is proposed as a potential candidate for biomedical applications.

Preparation and Characterization of Salsalate-Loaded Chitosan Nanoparticles: In Vitro Release and Antibacterial and Antibiofilm Activity.

The controlled-release characteristic of drug delivery systems is utilized to increase the residence time of therapeutic agents in the human body. This study aimed to formulate and characterize salsalate (SSL)-loaded chitosan nanoparticles (CSNPs) prepared using the ionic gelation method and to assess their in vitro release and antibacterial and antibiofilm activities. The optimized CSNPs and CSNP-SSL formulation were characterized for particle size (156.4 ± 12.7 nm and 132.8 ± 17.4 nm), polydispersity index (0.489 ± 0.011 and 0.236 ± 132 0.021), zeta potential (68 ± 16 mV and 37 ± 11 mV), and entrapment efficiency (68.9 ± 2.14%). Physicochemical features of these nanoparticles were characterized using UV-visible and Fourier transform infrared spectroscopy and X-ray diffraction pattern. Scanning electron microscopy studies indicated that CSNPs and CSNP-SSL were spherical in shape with a smooth surface and their particle size ranged between 200 and 500 nm. In vitro release profiles of the optimized formulations showed an initial burst followed by slow and sustained drug release after 18 h (64.2 ± 3.2%) and 48 h (84.6 ± 4.23%), respectively. Additionally, the CSNPs and CSNP-SSL nanoparticles showed a sustained antibacterial action against Staphylococcus aureus (15.7 ± 0.1 and 19.1 ± 1.2 mm) and Escherichia coli (17.5 ± 0.8 and 21.6 ± 1.7 243 mm). Interestingly, CSNP-SSL showed better capability (89.4 ± 1.2% and 95.8 ± 0.7%) than did CSNPs in inhibiting antibiofilm production by Enterobacter tabaci (E2) and Klebsiella quasipneumoniae (SC3). Therefore, CSNPs are a promising dosage form for sustained drug delivery and enhanced antibacterial and antibiofilm activity of SSL; these results could be translated into increased patient compliance.

Petal-like NiS-NiO/G-C3N4 Nanocomposite for High-Performance Symmetric Supercapacitor.

Graphitic carbon nitride (G-C3N4) and NiS-NiO/G-C3N4 nanocomposite have been synthesized via combustion and hydrothermal techniques, respectively. The chemical and morphological properties of these materials were confirmed using different analytical methods. SEM confirms the formation of G-C3N4 sheets containing additional petal-like shapes of NiS-NiO nanoparticles. The electrochemical testing of NiS-NiO/G-C3N4 symmetric supercapacitors is carried out from 0.6 M HCl electrolyte. Such testing includes charge/discharge, cyclic voltammetry, impedance, and supercapacitor stability. The charge/discharge time reaches 790 s at 0.3 A/g, while the cyclic voltammetry curve forms under a high surface area. The produced specific capacitance (CS) and energy density values are 766 F/g and 23.55 W.h.kg-1, correspondingly.

Flower-Shaped CoS-Co2O3/G-C3N4 Nanocomposite for Two-Symmetric-Electrodes Supercapacitor of High Capacitance Efficiency Examined in Basic and Acidic Mediums.

Graphitic carbon nitride (G-C3N4) was synthesized through the direct combustion of urea in the air. The CoS-Co2O3/G-C3N4 composite was synthesized via the hydrothermal method of G-C3N4 using cobalt salts. The morphological and chemical structures were determined through XRD, XPS, SEM, and TEM. XRD and XPS analyses confirmed the chemical structure, function groups, and elements percentage of the prepared nanocomposite. SEM measurements illustrated the formation of G-C3N4 sheets, as well as the flower shape of the CoS-Co2O3/G-C3N4 composite, evidenced through the formation of nano appendages over G-C3N4 sheets. TEM confirmed the 2D nanosheets of G-C3N4 with an average width and length of 80 nm and 170 nm, respectively. Two symmetric electrodes for the supercapacitor from the CoS-Co2O3/G-C3N4 composite. Electrochemical measurements were carried out to determine the charge/discharge, cyclic voltammetry, stability, and impedance of the prepared supercapacitor. The measurements were carried out under acid (0.5 M HCL) and basic (6.0 M NaOH) mediums. The charge and discharge lifetime values in the acid and base medium were 85 and 456 s, respectively. The cyclic voltammetry behavior was rectangular in a base medium for the pseudocapacitance feature. The supercapacitor had 100% stability retention up to 600 cycles; then, the stability decreased to 98.5% after 1000 cycles. The supercapacitor displayed a specific capacitance (CS) of 361 and 92 F/g, and an energy density equal to 28.7 and 30.2 W h kg-1 in the basic and acidic mediums, respectively. Our findings demonstrate the capabilities of supercapacitors to become an alternative solution to batteries, owing to their easy and low-cost manufacturing technique.

Mixed Ionic and Electronic Conduction in TeO2-ZnO-V2O5 Glasses towards Good Dielectric Features.

The melt-quenching technique was used to synthesize tellurite glasses of the chemical composition 80TeO2-(20-x) ZnO-xV2O5. X-ray diffraction (XRD) patterns indicate the amorphous nature of the prepared glasses. Raman and FTIR measurements demonstrate a progressive substitution of the Te-O-Te linkages by the Te-O-V bridges and the formation of VO4 and VO5 units by a change of the vanadium coordination due to the higher number of oxygens incorporated by further addition of V2O5. The AC conductivity was investigated in the frequency range of 40 Hz to 107 Hz between 473 K to 573 K. A good coherence of the AC conductivity was found using a model correlating the barrier hopping (CPH) and the dominant conduction process changes from ionic to polaronic with the addition of V2O5. The dielectric constant exhibits high values in the range of lower and medium frequencies. Both variations of the electric modulus and the dielectric loss parameters with frequency and temperature showed a relaxation character mainly assigned to the vanadate phases. The electric modulus displays a non-Debye dielectric dispersion and a relaxation process. The present results open the door to future zinc-tellurite glasses-doped vanadium exploitation as a potential electrolyte-based material for solid-state batteries.

Development of a Highly Efficient Optoelectronic Device Based on CuFeO2/CuO/Cu Composite Nanomaterials.

Herein, an optoelectronic device synthesized from a CuFeO2/CuO/Cu nanocomposite was obtained through the direct combustion of Cu foil coated with Fe2O3 nanomaterials. The chemical, morphological, and optical properties of the nanocomposite were examined via different techniques, such as XRD, XPS, TEM, SEM, and UV/Vis spectrophotometer. The optical reflectance demonstrated a great enhancement in the CuFeO2 optical properties compared to CuO nanomaterials. Such enhancements were clearly distinguished through the bandgap values, which varied between 1.35 and 1.38 eV, respectively. The XRD and XPS analyses confirmed the chemical structure of the prepared materials. The produced current density (Jph) was studied in dark and light conditions, thereby confirming the obtained optoelectronic properties. The Jph dependency to monochromatic wavelength was also investigated. The Jph value was equal to 0.033 mA·cm-2 at 390 nm, which decreased to 0.031 mA·cm-2 at 508 nm, and then increased to 0.0315 mA·cm-2 at 636 nm. The light intensity effects were similarly inspected. The Jph values rose when the light intensities were augmented from 25 to 100 mW·cm-2 to reach 0.031 and 0.05 mA·cm-2, respectively. The photoresponsivity (R) and detectivity (D) values were found at 0.33 mA·W-1 and 7.36 × 1010 Jones at 390 nm. The produced values confirm the high light sensitivity of the prepared optoelectronic device in a broad optical region covering UV, Vis, and near IR, with high efficiency. Further works are currently being designed to develop a prototype of such an optoelectronic device so that it can be applied in industry.

Vibrational Emission Study of the CN and C2 in Nylon and ZnO/Nylon Polymer Using Laser-Induced Breakdown Spectroscopy (LIBS).

The laser-induced breakdown spectroscopy (LIBS) technique was performed on polymers to study the neutral and ionic emission lines along with the CN violet system (B2Σ+ to X2Σ+) and the C2 Swan system (d3 Пg-a3 Пu). For the laser-based emission analyses, the plasma was produced by focusing the laser beam of a Q-switched Nd: YAG laser (2ω) at an optical wavelength of 532 nm, 5 ns pulse width, and a repetition frequency of 10 Hz. The integration time of the detection system was fixed at 1-10 ms while the target sample was positioned in air ambiance. Two organic polymers were investigated in this work: nylon and nylon doped with ZnO. The molecular optical emission study of nylon and doped nylon polymer sample reveals CN and C2 molecular structures present in the polymer. The vibrational emission analysis of CN and C2 bands gives information about the molecular structure of polymers and dynamics influencing the excitation structures of the molecules. Besides, it was further investigated that the intensity of the molecular optical emission structure strongly depends on the electron number density (cm-3), excitation temperature (eV), and laser irradiance (W/cm2). These results suggest that LIBS is a reliable diagnostic technique for the study of polymers regarding their molecular structure, identification, and compositional analysis.

SARS-CoV-2 main protease (3CLpro) interaction with acyclovir antiviral drug/methyl-ß-cyclodextrin complex: Physiochemical characterization and molecular docking.

During the current outbreak of the novel coronavirus disease 2019 (COVID-19), researchers have examined several antiviral drugs with the potential to inhibit the proliferation of the severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2). The antiviral drug acyclovir (AVR), which is used to treat COVID-19, in complex with methyl-ß-cyclodextrin (Mß-CD) was examined in the solution and solid phases. UV-visible and fluorescence spectroscopic analyses confirmed that the guest (AVR) was included inside the host (Mß-CD) cavity. A solid inclusion complex of AVR was prepared by co-precipitation, physical mixing, kneading, and bath sonication methods at a 1:1 ratio of Mß-CD:AVR. The prepared Mß-CD:AVR inclusion complex was characterized using Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and scanning electron microscopy (SEM) analysis. Phase solubility studies indicated the Mß-CD:AVR inclusion complex exhibited a higher stability constant and linear enhancement in AVR solubility with increasing Mß-CD concentrations. In silico analysis of the Mß-CD/AVR inclusion complex confirmed that AVR drugs show potential as inhibitors of SARS-CoV-2 3C-like protease (3CLpro) receptors. Results obtained using the PatchDock and FireDock servers indicated that the most favorable docking ligand was Mß-CD:AVR, which interacted with SARS-CoV-2 (3CLPro) protease inhibitors with high geometric shape complementarity scores (2522 and 5872) and atomic contact energy (-313.77 and -214.70 kcal mol-1). Our results suggest that the Mß-CD/AVR inclusion complex inhibits the main protease of SARS-CoV-2, although further wet-lab experiments are needed to verify these findings.

Photon Drag Currents and Terahertz Generation in α-Sn/Ge Quantum Wells.

We have fabricated α-Sn/Ge quantum well heterostructures by sandwiching nano-films of α-Sn between Ge nanolayers. The samples were grown via e-beam deposition and characterized by Raman spectroscopy, atomic force microscopy, temperature dependence of electrical resistivity and THz time-resolved spectroscopy. We have established the presence of α-Sn phase in the polycrystalline layers together with a high electron mobility µ = 2500 ± 100 cm2 V-1 s-1. Here, the temperature behavior of the resistivity in a magnetic field is distinct from the semiconducting films and three-dimensional Dirac semimetals, which is consistent with the presence of linear two-dimensional electronic dispersion arising from the mutually inverted band structure at the α-Sn/Ge interface. As a result, the α-Sn/Ge interfaces of the quantum wells have topologically non-trivial electronic states. From THz time-resolved spectroscopy, we have discovered unusual photocurrent and THz radiation generation. The mechanisms for this process are significantly different from ambipolar diffusion currents that are responsible for THz generation in semiconducting thin films, e.g., Ge. Moreover, the THz generation in α-Sn/Ge quantum wells is almost an order of magnitude greater than that found in Ge. The substantial strength of the THz radiation emission and its polarization dependence may be explained by the photon drag current. The large amplitude of this current is a clear signature of the formation of conducting channels with high electron mobility, which are topologically protected.

Enhanced Room Temperature Ammonia Gas Sensing Properties of Fe-Doped MoO3 Thin Films Fabricated Using Nebulizer Spray Pyrolysis.

MoO3 thin films are fabricated using nebulizer spray pyrolysis technique, which is doped with Fe at various concentrations of 1, 2, 3, and 4% for ammonia gas sensors application at room temperature. X-ray diffraction (XRD) study confirms the growth of the crystal by Fe doping up to 3%, nano rods shape morphology of the thin film samples observed by field emission scanning electron microscope (FESEM), reduction in bandgap is evidenced via UV-VIS spectrophotometer. Gas sensing study is performed using gas analyzing chamber attached with Keithley source meter. Since 3% Fe doped MoO3 sample displayed nano rods over the film surface which exhibits highest sensitivity of 38,500%, in a short period of raise and decay time 54 and 6 s. Our findings confirms that the 3% Fe doped MoO3 films suitability for ammonia gas sensing application.

Energy Efficiency Enhancement of Inductively Coupled Plasma Torch: Computational Study.

In this research, we studied the performance analysis of inductively coupled radiofrequency plasma "RF-ICP" torch used in multi-material processing. A 2D numerical model built with COMSOL Multiphysics was used to study the discharge behavior and evaluate the overall efficiency transmitted into the plasma system. The temperature and velocity flow of the plasma were investigated. The numerical results are consistent with previous experimental studies. The temperature and velocity profiles are represented under a wide range of RF power and for different sheath gas flow rates. With increasing power, the radial peak temperature typically shifts towards the wall. The resistance of the torch rises whereas the inductance diminishes with increasing RF power. The overall dependency of the coupling efficiency to the RF power is also estimated. The stabilization of the plasma flow dependency to the sheath swirl flow was investigated. The incorporation of Helium (0.02%) into an Argon gas was established to minimize the energy lost in the sidewall. The number and spacing of induction coil numbers affects the temperature and flow field distribution. A valuable approach to designing and optimizing the induction plasma system is presented in the proposed study. The obtained results are fundamental to specify ICP torch design criteria needed for multi-material processing.

Quantification of Intra-Muscular Adipose Infiltration in Calf/Thigh MRI Using Fully and Weakly Supervised Semantic Segmentation.

Purpose: Infiltration of fat into lower limb muscles is one of the key markers for the severity of muscle pathologies. The level of fat infiltration varies in its severity across and within patients, and it is traditionally estimated using visual radiologic inspection. Precise quantification of the severity and spatial distribution of this pathological process requires accurate segmentation of lower limb anatomy into muscle and fat. Methods: Quantitative magnetic resonance imaging (qMRI) of the calf and thigh muscles is one of the most effective techniques for estimating pathological accumulation of intra-muscular adipose tissue (IMAT) in muscular dystrophies. In this work, we present a new deep learning (DL) network tool for automated and robust segmentation of lower limb anatomy that is based on the quantification of MRI's transverse (T2) relaxation time. The network was used to segment calf and thigh anatomies into viable muscle areas and IMAT using a weakly supervised learning process. A new disease biomarker was calculated, reflecting the level of abnormal fat infiltration and disease state. A biomarker was then applied on two patient populations suffering from dysferlinopathy and Charcot-Marie-Tooth (CMT) diseases. Results: Comparison of manual vs. automated segmentation of muscle anatomy, viable muscle areas, and intermuscular adipose tissue (IMAT) produced high Dice similarity coefficients (DSCs) of 96.4%, 91.7%, and 93.3%, respectively. Linear regression between the biomarker value calculated based on the ground truth segmentation and based on automatic segmentation produced high correlation coefficients of 97.7% and 95.9% for the dysferlinopathy and CMT patients, respectively. Conclusions: Using a combination of qMRI and DL-based segmentation, we present a new quantitative biomarker of disease severity. This biomarker is automatically calculated and, most importantly, provides a spatially global indication for the state of the disease across the entire thigh or calf.