Magnetic properties and growth mechanism of ultrathin Co films on Si(111)-7 x 7 surface have been studied by using both surface magneto-optic Kerr effect (SMOKE) and scanning tunneling microscopy (STM), respectively. STM results show that the growth mechanism of ultrathin Co films on Si(111)-7 x 7 surface at room temperature belongs to Stranski-Krastanov (SK) growth mode. Due to formation of CoSi2 layer, no magnetic signal could be detected by SMOKE for 1-4 ML Co deposited on Si(111) surface. Because of rougher surface, both longitudinal and perpendicular magnetic anisotropy configuration appear for 4.2-10 ML Co/Si(111) films. When the Co thickness is increased to 10 ML, only longitudinal anisotropy configuration is found, resulting from the contribution to the volume anisotropy. Furthermore, in-plane coercivity increases with Co coverage because of enhancement of ferromagnetic coupling with Co thickness, out-of-plane coercivity increases with Co coverage due to the increment of demagnetized field, induced by the rougher Co surface and pinhole structures.