Effect of low power Er:YAG laser irradiation of CAD-CAM resin-based composites on resin bonding.

PURPOSE: To investigate the effect of painless low-power Er:YAG laser irradiation of conventional and polymer-infiltrated ceramic network (PICN) type CAD-CAM resin-based composites (RBCs) on resin bonding. METHODS: An Er:YAG laser system, phosphoric acid etchant, universal adhesive, RBC, and two types of CAD-CAM RBC block were used. Microtensile bond strength, fracture mode, scanning electron microscopy (SEM) observations of bonding interfaces and CAD-CAM surfaces, and surface roughness of ground and pretreated surfaces were investigated. As pretreatment methods, low-power Er:YAG laser irradiation and air-abrasion with alumina particles were used. RESULTS: The effect of low-power Er:YAG laser irradiation of CAD-CAM RBCs on bonding to repair resin varied depending on the type of CAD-CAM RBCs. CLINICAL SIGNIFICANCE: The low-power Er:YAG laser irradiation of the conventional CAD-CAM RBCs was shown to be effective as a surface pretreatment for resin bonding, while the laser irradiation of PICN-type CAD-CAM RBCs was not effective.

Fracture resistance of chairside CAD-CAM lithium disilicate occlusal veneer with various designs after mechanical aging.

PURPOSE: This study evaluated the fracture resistance of chairside computer-aided design and computer-aided manufacturing (CAD-CAM) lithium disilicate crown, onlay, and non-anatomical occlusal veneer (A-OV) with and without margin fabricated. MATERIALS AND METHODS: Sixty-four CAD-CAM lithium disilicate restorations were designed as (1) complete coverage crown (CCC); (2) A-OV with margin; (3) non-A-OV with margin (NA-OV-M); and (4) non-A-OV without margin (NA-OV-NM), 16 of each. Restorations were crystallized and adhesively luted to resin dies using resin cement. Specimens were then subjected to 400,000 cycles of chewing in a mastication simulator. A universal testing machine was used to apply a compressive load at a crosshead speed of 1 mm/min to the long axis of the tooth with a stainless-steel sphere until fracture occurred. One-way ANOVA followed by post hoc tests were used to assess the impact of preparation design on the fracture load of CAD-CAM lithium disilicate restorations. RESULTS: The highest fracture load was recorded for CAD-CAM lithium disilicate indirect restorations for non-A-OVs preparation with margin (2549 ± 428 N) and onlay (2549 ± 293 N) and the lowest fracture load was recorded for CCCs (2389 ± 428 N); however, there was no significant (p = 0.640) between groups. CONCLUSIONS: CAD-CAM lithium disilicate restorations fabricated for anatomical and non-A-OV preparation display a fracture resistance similar to CCCs. Conservative partial coverage restorations may be considered an acceptable approach for posterior teeth.

Mechanical properties and degree of conversion of resin-based core build-up materials and short fiber-reinforced flowable resin-based composite.

To evaluate the degree of conversion (DC), surface hardness (SH), and flexural strength (FS) of resin-based core build-up materials. Core build-up materials used were: MultiCore Flow (MCF); Activa (ACT); Core-X Flow (CXF); and everX flow (EVX), and DC, SH and FS were measured. An increase of DC was identified for all materials post-cure, except for EVX. The DC change percentage ranged from 5%-33%, and EVX was displayed the greatest DC rate. All materials displayed an SH increase after 30 days and the greatest increase was observed in ACT. At 1 h, the SH of EVX and CXF was different from the other materials. At 30 days, MCF displayed the greatest SH. All materials displayed an increase in their FS after 30 days except for EVX, and ranging 3%-36% were noticed. Differences observed between materials, thus clinician should be acquainted mechanical properties of these materials to ensure the success of the restorations.

Immediate implant placement with soft tissue grafting and an ultra-translucent zirconia crown. Replacement of a primary tooth in the esthetic zone

OBJECTIVES: The present case report describes the atraumatic extraction of a primary maxillary right canine followed by immediate implant placement with a customized zirconia abutment and monolithic ultra-translucent zirconia (5Y-PSZ) crown. CLINICAL CONSIDERATIONS: A 31-year-old patient presented to the clinic with the primary concern of mobility and gingival inflammation around the maxillary right canine. After clinical evaluation, the tooth was found to be a primary retained tooth that presented grade 3 mobility and gingival inflammation. Atraumatic tooth extraction was performed, followed by immediate implant placement of a screw-retained provisional restoration with the use of a surgical guide. The soft tissue was contoured until ideal architecture was obtained. The final restoration included a customized zirconia and titanium abutment and a characterized implant-supported monolithic 5Y-PSZ crown. CONCLUSIONS: Well-planned surgical and restorative procedures including atraumatic extraction, 3D implant planning for surgical guide fabrication, implant placement, and a customized zirconia abutment with a monolithic 5Y-PSZ crown can achieve high esthetic results in replacing a primary tooth in the esthetic zone.

Fracture Resistance of Chairside CAD/CAM Molar Crowns Fabricated with Different Lithium Disilicate Ceramic Materials

PURPOSE: To compare the fracture resistance of five different groups of chairside CAD/CAM molar crowns fabricated from various lithium disilicate ceramic materials (LDC): one conventional precrystallized CAD/CAM LDC, two novel precrystallized LDCs, and one fully crystallized LDC tested both with and without optional sintering. MATERIALS AND METHODS: A total of 60 chairside CAD/CAM lithium disilicate molar crowns (n = 12 per group) with 1.5-mm occlusal thickness and a 1.0-mm chamfer finish were designed and fabricated with a chairside CAD/CAM system (CEREC, Dentsply Sirona). The restorations were divided into five groups: (1) IPS e.max CAD; (2) Amber Mill; (3) Straumann n!ce; (4) Straumann n!ce with optional sintering; and (5) Supreme CAD. Restorations were cemented using conventional resin luting cement and primer system to 3D-printed resin dies. Bonded restorations were loaded for 100,000 cycles with 275-N force, and the load at break (LB) and peak load (PL) until fracture were measured. SEM images of fracture surfaces on the printed dies were obtained. RESULTS: Fracture resistance was significantly different depending on the material. Supreme CAD showed the highest fracture resistance (LB: 1,557.2 N; PL: 1,785.8 N), followed by Amber Mill (LB: 1,393.0 N; PL: 1,604.2 N) and IPS e.max CAD (LB: 1,315.7 N; PL: 1,461.9 N). Straumann n!ce without (LB: 862.4 N; PL: 942.9 N) and with the optional sintering (LB: 490.4 N; PL: 541.0 N) showed significantly lower fracture resistance than the others. CONCLUSION: The fracture resistance of chairside CAD/CAM lithium disilicate molar crowns varied depending on the material, and the novel materials did not perform as well as the conventional equivalents. Fully crystallized lithium disilicate ceramic block materials showed lower fracture resistance than precrystallized counterparts and should be used with caution in the clinic, especially with optional sintering.

Ceramic versus Composite Resin Polishing Systems on the Surface Roughness of Milled Leucite-Reinforced Ceramics.

Background and Objective: This study aimed to compare the surface finish of milled leucite-reinforced ceramics polished with ceramic and composite polishing systems based on the manufacturers' recommendations. Materials and Methods: Sixty subtractive computer-aided manufactured (s-CAM) leucite-reinforced glass-ceramic specimens (IPS-Empress-CAD) were assigned into six groups: no polishing, a ceramic polishing kit, and four composite kit groups. The roughness average (Ra) was evaluated in microns using a profilometer, and scanning electron micrographs were obtained for qualitative analysis. A Tukey HSD posthoc test (α = 0.05) was used to determine significant intergroup differences. Results: After surface evaluation of the ceramics, the Ra values of the polishing systems ranked OptraFine (0.41 ± 0.26) < Enhance (1.60 ± 0.54) < Shofu (2.14 ± 0.44) < Astropol (4.05 ± 0.72) < DiaComp (5.66 ± 0.62) < No Polishing (5.66 ± 0.74). Discussion: Composite polishing systems did not provide as smooth surfaces as the ceramic polishing kit for CAD-CAM leucite-reinforced ceramics. Thus, using ceramic polishing systems, polishing leucite ceramics is recommended, whereas composite polishing systems should not be considered as an alternative for use in minimally invasive dentistry.

The use of artificial intelligence and game-based learning in removable partial denture design: A comparative study.

PURPOSE: The purpose of this study was to compare student performance in removable partial denture (RPD) design during a pre-clinical RPD course with and without using a recently developed computer software named AiDental. Additionally, student perceptions associated with the use of this software were assessed. METHODS: The AiDental software consists of a learning environment containing an RPD design system that automatically designs RPDs based on the user's input. The software also contains an RPD game component that compares the user's RPD Design to an automatically generated RPD ideal design. The study was conducted in two phases. In phase one, pre-clinical second-year dental students who participated in the study were randomly divided into two groups: The AiDental group with AiDental software access (n = 36), and the conventional group without software access (n = 37). Both groups received conventional RPD instruction and practice, however, the AiDental group had additional access to the AiDental software. After 2 weeks, both groups took a mock practical test, which was collected and graded by the principal investigator (PI). The PI was blinded from group assignment and no identifying information was used in the mock practical. In phase two, all students were granted access to the AiDental software for the remainder of the pre-clinical course duration. At the conclusion of the course, all students were given a survey to evaluate their perceptions of the AiDental software. Descriptive statistics were calculated and analyzed. Variables related to perceptions of both the AiDental designer and game were assessed using Spearman's rank correlation test, the chi-square test, Fisher's exact test, and the non-parametric Wilcoxon rank-sum test as appropriate. In addition, a thematic analysis of the responses to the optional comments section was conducted using the Braun and Clarke method. RESULTS: Phase one results showed that subjects in the AiDental group were more likely than subjects in the conventional group to receive a final grade of A or B. Phase two results showed generally favorable student perceptions towards the software, and additionally, the results showed that age was significantly negatively correlated with ease of use of the software, improving decision-making, and critical thinking relative to RPD design choices. However, no correlation between age and using the software as a reference were noted. CONCLUSIONS: The use of AiDental's automated feedback and gamification techniques in RPD education had a positive effect on student grades and it was well-liked by students. Thus, the results suggest that AiDental has the potential to be a useful adjunct to pre-clinical teaching.

Effects of over-the-counter at-home whitening products with LED light on surface roughness of partially- and fully crystalized CAD/CAM lithium disilicate ceramics.

The aim of this study is to evaluate the effect of over-the-counter (OTC) at-home whitening products with LED light on partially- and fully-crystalized CAD/CAM lithium disilicate ceramics. Two partially-crystalized CAD/CAM lithium disilicate ceramics, Amber Mill and IPS e.max CAD, and one fully-crystalized CAD/CAM lithium disilicate ceramic, n!ce Straumann, were used. The specimens were divided based on treatment with OTC whitening products: no treatment provided, Colgate Optic, Crest 3D and Walgreens Deluxe. The surface roughness of the specimens was evaluated with an optical profilometer and scanning electron microscopy. The three LED whitening products significantly increased the surface roughness and changed surface morphology of Amber Mill and IPS e.max CAD but no differences for n!ce Straumann. OTC at-home whitening products with LED light can significantly increase the surface roughness of restorations fabricated with these partially-crystalized CAD/CAM lithium disilicate ceramic restorations. However, these products do not increase the surface roughness of restorations fabricated with this fully-crystalized lithium disilicate ceramic.

Full-Mouth Rehabilitation of a Patient with Sjogren's Syndrome with Maxillary Titanium-Zirconia and Mandibular Monolithic Zirconia Implant Prostheses Fabricated with CAD/CAM Technology: A Clinical Report.

Dental implants have become a well-established treatment modality for the management of complete and partial edentulism. Recent advancements in dental implant systems and CAD/CAM technologies have revolutionized prosthodontic practice by allowing for the predictable, efficient, and faster management of complex dental scenarios. This clinical report describes the interdisciplinary management of a patient with Sjogren's syndrome and terminal dentition. The patient was rehabilitated using dental implants and zirconia-based prostheses in the maxillary and mandibular arches. These prostheses were fabricated using a combination of CAD/CAM and analog techniques. The successful outcomes for the patient demonstrate the importance of appropriate use of biomaterials and the implementation of interdisciplinary collaboration in treating complex dental cases.

Minimally Invasive Laminate Veneer Therapy for Maxillary Central Incisors.

Minimally invasive dentistry is a considered process that requires the clinician to be prepared with the ideal sequence and the tools needed. This report describes a well-planned ultraconservative approach using only two ceramic laminate veneers for the maxillary central incisors to significantly improve the patient's overall smile. A 30-year-old female presented with the chief complaints of having diastemas between the central and lateral incisors as well as incisal wear. Diagnostic wax-up and mock-up were performed, and the patient approved the minimally invasive treatment with veneers only for central incisors. A reduction guide aided the conservative tooth preparations, and hand-crafted feldspathic veneers were bonded under total isolation with a rubber dam. The two final conservative veneers significantly improved the smile and fulfilled the patient's expectations. Following proper planning and sequencing, predictable outcomes were obtained and fulfilled the patient's esthetic demands. Minimally invasive restorative dentistry with only two single veneers can impact the entire smile frame. Overtreatment in the esthetic zone is unnecessary to meet a patient's esthetic expectations.

The Effect of Sintering on Zirconia Manufactured via Suspension-Enclosing Projection Stereolithography for Dental Applications: An In Vitro Study.

BACKGROUND: Zirconia is a widely used material in the dental industry due to its excellent mechanical and aesthetic properties. Recently, a new 3D printing process called suspension-enclosing projection stereolithography (SEPS) was introduced to fabricate zirconia dental restorations. However, the effect of the sintering time and temperature on the properties of zirconia produced via SEPS has not been fully investigated. METHODS: Zirconia slurries were prepared with varying percentages of zirconia powders and 3D printing resins, and 5Y-TZP (5 mol% yttria-stabilized zirconia) (n = 40) and 3Y-TZP (3 mol% yttria-stabilized zirconia) (n = 40) bar specimens were fabricated via SEPS manufacturing. The specimens were sintered at different temperatures and dwell times, and their flexural strength, density, and phase composition were measured. The viscosity of the slurries was also measured. Statistical analysis was performed using Welch's ANOVA and Kruskal-Wallis tests to evaluate the impact of the sintering conditions. RESULTS: Significant differences in flexural strength (p < 0.01) were observed between the 5Y-TZP samples, with those sintered at 1530 °C for 120 min showing an average strength of 268.34 ± 44.66 MPa, compared to 174.16 ± 42.29 MPa for those sintered at 1450 °C for 120 min. In terms of density, significant differences (p < 0.01) were noted for the 3Y-TZP specimens, with an average density of 6.66 ± 0.49 g/cm3 for samples sintered at 1530 °C for 120 min, versus 5.75 ± 0.55 g/cm3 for those sintered at 1530 °C for 10 min. X-ray diffraction confirmed the presence of a predominantly tetragonal phase in both materials. CONCLUSIONS: Zirconia printed via SEPS manufacturing can be sintered at a higher temperature with shorter dwell times, thereby producing high density samples. Different sintering conditions can be used to fully sinter 3D-printed zirconia for potential dental applications.

Diagnostic Mock-Up as a Surgical Reduction Guide for Crown Lengthening: Technique Description and Case Report.

Background and Objectives: The report describes a technique using a diagnostic mock-up as a crown-lengthening surgical guide to improve the gingival architecture. Materials and Methods: The patient's primary concern was improving her smile due to her "gummy smile" and short clinical crowns. After clinical evaluation, surgical crown lengthening accompanied by maxillary central full-coverage single-unit prostheses and lateral incisor veneers was recommended. The diagnostic mock-up was placed in the patient's maxillary anterior region and used as a soft tissue reduction guide for the gingivectomy. Once the planned gingival architecture was achieved, a flap was reflected to proceed with ostectomy in order to obtain an appropriate alveolar bone crest level using the overlay. After six months, all-ceramic crowns and porcelain veneers were provided as permanent restorations. Results: A diagnostic mock-up fabricated with a putty guide directly from the diagnostic wax-up can be an adequate surgical guide for crown-lengthening procedures. The diagnostic wax-up was used to fabricate the diagnostic mock-up. These results suggested that it can be used as a crown-lengthening surgical guide to modify the gingival architecture. Several advantages of the overlay used in the aesthetic complex case include: (1) providing a preview of potential restorative outcomes, (2) allowing for the appropriate positioning of gingival margins and the desired alveolar bone crest level for the crown-lengthening procedure, and (3) serving as a provisional restoration after surgery. Conclusions: The use of a diagnostic mock-up, which was based on a diagnostic wax-up, as the surgical guide resulted in successful crown lengthening and provisional restorations. Thus, a diagnostic overlay can be a viable option as a surgical guide for crown lengthening.

Bond Durability of Two-Step HEMA-Free Universal Adhesive.

The purpose of this study is to compare bond durability, in terms of fatigue bond strength, of a two-step HEMA-free universal adhesive and representative adhesives in each systematic category. The adhesives used in this study were OptiBond FL, Prime&Bond NT, Clearfil SE Bond 2, G2-Bond Universal, and Scotchbond Universal Plus Adhesive. Fatigue bond strength testing and scanning electron microscopy analysis of adhesively bonded enamel and dentin interfaces were performed. For the adhesives in etch-and-rinse mode, the enamel fatigue bond strength of the G2-Bond Universal adhesive was significantly higher than those of other adhesives, and the dentin fatigue bond strength of Prime&Bond NT was significantly lower than the others. For adhesives in self-etch mode, the enamel fatigue bond strengths of Clearfil SE Bond 2 and G2-Bond Universal were significantly higher than that of the Scotchbond Universal Plus Adhesive, and the dentin fatigue bond strength of G2-Bond Universal was significantly higher than Clearfil SE Bond 2 and the Scotchbond Universal Plus Adhesive. The two-step HEMA-free universal adhesive showed higher enamel and higher or equal dentin fatigue bond strength than other selected representative adhesive systems in etch-and-rinse mode and higher or equal enamel and higher dentin fatigue bond strength than adhesive systems in self-etch mode.

Fracture Resistance of Chairside CAD/CAM Molar Crowns Fabricated with Different Lithium Disilicate Ceramic Materials.

PURPOSE: To compare the fracture resistance of five different groups of chairside CAD/CAM molar crowns fabricated from various lithium disilicate ceramic materials (LDC): one conventional precrystallized CAD/CAM LDC, two novel precrystallized LDCs, and one fully crystallized LDC tested both with and without optional sintering. MATERIALS AND METHODS: A total of 60 chairside CAD/CAM lithium disilicate molar crowns (n = 12 per group) with 1.5-mm occlusal thickness and a 1.0-mm chamfer finish were designed and fabricated with a chairside CAD/CAM system (CEREC, Dentsply Sirona). The restorations were divided into five groups: (1) IPS e.max CAD; (2) Amber Mill; (3) Straumann n!ce; (4) Straumann n!ce with optional sintering; and (5) Supreme CAD. Restorations were cemented using conventional resin luting cement and primer system to 3D-printed resin dies. Bonded restorations were loaded for 100,000 cycles with 275-N force, and the load at break (LB) and peak load (PL) until fracture were measured. SEM images of fracture surfaces on the printed dies were obtained. RESULTS: Fracture resistance was significantly different depending on the material. Supreme CAD showed the highest fracture resistance (LB: 1,557.2 N; PL: 1,785.8 N), followed by Amber Mill (LB: 1,393.0 N; PL: 1,604.2 N) and IPS e.max CAD (LB: 1,315.7 N; PL: 1,461.9 N). Straumann n!ce without (LB: 862.4 N; PL: 942.9 N) and with the optional sintering (LB: 490.4 N; PL: 541.0 N) showed significantly lower fracture resistance than the others. CONCLUSION: The fracture resistance of chairside CAD/CAM lithium disilicate molar crowns varied depending on the material, and the novel materials did not perform as well as the conventional equivalents. Fully crystallized lithium disilicate ceramic block materials showed lower fracture resistance than precrystallized counterparts and should be used with caution in the clinic, especially with optional sintering.

Fatigue bond strength of dental adhesive systems: Historical background of test methodology, clinical considerations and future perspectives.

Numerous laboratory evaluations have been conducted since Dr. Rafael Bowen introduced a method for determining the bond strengths of adhesive systems to dental substrates in 1965. Most of the past studies have been conducted using static bond strength tests, such as shear and tensile bond strength testing with either macro or micro sized specimens. These static bond strength tests are conducted using a monotonically increasing load in which stress is applied continuously until failure occurs. Although the type of stress that develops in static bond strength tests is not typically encountered in clinical situations, over the years clinicians have based their choice of adhesive systems for use in daily practice on the results of such tests. However, some well-known researchers have reported that the results obtained from static bond strength testing may have limited clinical relevance and should not be used only by themselves to make recommendations for clinical use. In clinical situations, restorations undergo cyclic stress during mastication at stress levels well below the breaking stress used in static bond strength tests. Thus, dynamic bond strength tests, using cyclic loading, should be more clinically relevant than static bond strength tests. Over 15 years, a testing method designed to assess fatigue bond strengths of dental adhesive systems has been developed through inter-collegial and international collaborative efforts. This review discusses the development of fatigue bond strength testing methodology, provides both a historical perspective and current information regarding available testing data for all categories of adhesive systems to enamel and dentin and perspectives on the future development of both adhesive systems and testing methods.

CAD/CAM lithium disilicate ceramic crowns: Effect of occlusal thickness on fracture resistance and fractographic analysis.

This study uses fracture tests and fractographical analysis to compare computer-aided design and computer-aided manufacturing (CAD/CAM) lithium disilicate molar crowns with the previous occlusal thickness recommendation of 1.5-mm, the new recommendation of 1.0-mm, and a less invasive thickness of 0.8-mm. After fatigue application, fracture tests and fractographic analysis were conducted. The fracture resistance of CAD/CAM lithium disilicate molar crowns was different depending on the occlusal thickness of the restoration, and decreased with lower the thickness. However, the fracture resistance of crowns of all three thicknesses exceeded the reported maximum bite force in the first molar region after the fatigue process, and can be considered acceptable for use in the clinic.

Short fiber-reinforced resin-based composites (SFRCs); Current status and future perspectives.

One technique for placing of resin-based composite for large posterior cavities is the use of short fiber-reinforced resin-based composite (SFRC) to replace dentin in a biomimetic approach. As endurance under mastication cycles is a significant consideration in the clinical success of resin-based composite posterior restorations, the use of SFRC as a base material may prevent restorative fracture due to the fibers' effectiveness in stopping cracks. This review article specifies the characteristics of SFRC and describes the major underlying mechanisms of short fiber reinforcement for resin-based composite. Insights are further taken from laboratory studies used to define the short fiber-related properties of resin-based composite and the performance of currently available materials, focusing on aspects that are relevant to the reinforcement of resin-based composite. Finally, future standpoints on the development of SFRCs with nano fibers and different resin monomers, and their role in digital dentistry, are discussed.

Soft Tissue Management on Pontic and Implant Sites Before Implants Insertion.

Complex implant therapy can include methods requiring several phases of treatment, and they are usually referred to as one-stage and two-stage approaches. The reasons for the staged approach include the extraction of non-restorable teeth. Such a treatment approach may offer a fixed provisional prosthesis during implant osseointegration that enables the patient to avoid removable prostheses. However, this case aims to demonstrate how to manage the soft tissue in the pontic region prior to immediate implant placement. A 45- years old female patient presented with non-restorable teeth from the maxillary right lateral incisor to the left lateral incisor were removed, followed by socket preservation and fixed provisional restoration from right maxillary canine to left canine. Soft tissue was contoured to achieve ovate shape by first with a tooth-supported provisional restoration from the maxillary left canine to the right canine and then by re-shaping with carbide and diamond burs; after the tissue obtained the desired architecture, implants were inserted on sites of the maxillary right lateral incisor and left central lateral incisor without immediate loading, but the same provisional fixed restoration maintained the previously contour tissue. Once implant osseointegration was achieved, screw-retained provisional restoration was placed, followed by the definitive fixed implant restoration. Because the soft tissue was previously contoured, the screw-retained implant provisional restorations maintained the tissue architecture. These initial contouring procedures provided a more predictable outcome for the final tissue contour after implants were inserted. The final re-shaping with the implant screw-retained provisional restorations was minimum, and prostheses followed the previously provided tissue architecture. Before the endosteal implants are inserted, soft-tissue contouring prior to implant placement may provide a more predictable outcome of the final tissue architecture for pontic and implant areas. The patient and clinician can evaluate the success and limitations of tissue contouring prior to implant placement. It may also shorten the time required for tissue contouring with provisional implant restorations.

Effect of mold enclosure and chisel design on fatigue bond strength of dental adhesive systems.

To examine the effect of mold enclosure and chisel design on macro shear fatigue bond strengths of dental adhesive systems. The fatigue bond strength testing was conducted with two commercially available dental adhesive systems, (1) OptiBond eXTRa and (2) Scotchbond Universal, for bonding a resin composite (Filtek Supreme Ultra) to both enamel and dentin using a mold enclosure and a non-mold enclosure with a knife-edge and two sized notched-edge chisel assemblies for loading. As a loading reference for the fatigue testing, macro shear bond strengths of the adhesive systems to enamel and dentin were conducted using a mold enclosure and a knife-edge chisel assembly. The shear bond strengths with the mold enclosure using knife-edge chisel assembly did not exhibit a significant difference between the adhesive systems for either enamel or dentin. The fatigue bond strengths of bonded specimens demonstrated significant differences when comparing the mold enclosure and non-mold enclosure, but not between knife-edge and notched-edge chisel assemblies. The fatigue bond strengths of dental adhesive systems demonstrated significantly higher values when using mold-enclosed bonded specimens than a non-mold enclosure, regardless of type of chisel assembly.

Color stability of fully- and pre-crystalized chair-side CAD-CAM lithium disilicate restorations after required and additional sintering processes.

PURPOSE: The aim of this study was to investigate shade changes in fully- and pre-crystalized CAD-CAM lithium disilicate crowns after the required and additional firing processes. MATERIALS AND METHODS: One hundred and five crowns of shade A1 with high translucency were milled out of CAD-CAM lithium disilicate blocks and categorized as follows (n = 15): (1) restorations fabricated from Straumann n!ce with no additional sintering process; (2) restorations fabricated from Straumann n!ce with one additional sintering process; (3) restorations fabricated from Straumann n!ce with two additional sintering processes; (4) restorations fabricated from Amber Mill with one sintering process; (5) restorations fabricated from Amber Mill with two sintering processes; (6) restorations fabricated from IPS e.max CAD with one sintering process; (7) restorations fabricated from IPS e.max CAD with two sintering processes. All restorations were evaluated with a color imaging spectrophotometer. RESULTS: All restorations presented some color alteration from the original shade both after a single and after two firing processes. CONCLUSION: The required and additional sintering processes for restorations fabricated with chairside CAD-CAM lithium disilicate blocks cause an alteration of the original shade selected. Shade A1 high translucency restorations tend to change to a more yellowish B1 shade after a sintering process.