RESUMO
Hematite is a classical photoanode material for photoelectrochemical water splitting due to its stability, performance, and low cost. However, the effect of particle size is still a question due to the charge transfer to the electrodes. In this work, we addressed this subject by the fabrication of a photoelectrode with hematite nanoparticles embedded in close contact with the electrode substrate. The nanoparticles were synthesized by a solvothermal method and colloidal stabilization with charged hydroxide molecules, and we were able to further use them to prepare electrodes for water photo-oxidation. Hematite nanoparticles were embedded within electrospun tin-doped indium oxide nanofibers. The fibrous layer acted as a current collector scaffold for the nanoparticles, supporting the effective transport of charge carriers. This method allows better contact of the nanoparticles with the substrate, and also, the fibrous scaffold increases the optical density of the photoelectrode. Electrodes based on nanofibers with embedded nanoparticles display significantly enhanced photoelectrochemical performance compared to their flat nanoparticle-based layer counterparts. This nanofiber architecture increases the photocurrent density and photon-to-current internal conversion efficiency by factors of 2 and 10, respectively.
RESUMO
An FeNi (oxy)hydroxide cocatalyst overlayer was photoelectrochemically deposited on a thin-film hematite (α-Fe2O3) photoanode, leading to a cathodic shift of â¼100 mV in the photocurrent onset potential. Operando X-ray absorption spectroscopy (XAS) at the Fe and Ni K-edges was used to study the changes in the overlayer with potential in the dark and under illumination conditions. Potential or illumination only had a minor effect on the Fe oxidation state, suggesting that Fe atoms do not accumulate significant amount of charge over the whole potential range. In contrast, the Ni K-edge spectra showed pronounced dependence on potential in the dark and under illumination. The effect of illumination is to shift the onset for the Ni oxidation because of the generated photovoltage and suggests that holes that are photogenerated in hematite are transferred mainly to the Ni atoms in the overlayer. The increase in the oxidation state of Ni proceeds at potentials corresponding to the redox wave of Ni, which occurs immediately prior to the onset of the oxygen evolution reaction (OER). Linear combination fitting analysis of the obtained spectra suggests that the overlayer does not have to be fully oxidized to promote oxygen evolution. Cathodic discharge measurements show that the photogenerated charge is stored almost exclusively in the Ni atoms within the volume of the overlayer.
RESUMO
H2O2 is a sacrificial reductant that is often used as a hole scavenger to gain insight into photoanode properties. Here we show a distinct mechanism of H2O2 photo-oxidation on haematite (α-Fe2O3) photoanodes. We found that the photocurrent voltammograms display non-monotonous behaviour upon varying the H2O2 concentration, which is not in accord with a linear surface reaction mechanism that involves a single reaction site as in Eley-Rideal reactions. We postulate a nonlinear kinetic mechanism that involves concerted interaction between adions induced by H2O2 deprotonation in the alkaline solution with adjacent intermediate species of the water photo-oxidation reaction, thereby involving two reaction sites as in Langmuir-Hinshelwood reactions. The devised kinetic model reproduces our main observations and predicts coexistence of two surface reaction paths (bi-stability) in a certain range of potentials and H2O2 concentrations. This prediction is confirmed experimentally by observing a hysteresis loop in the photocurrent voltammogram measured in the predicted coexistence range.