RESUMO
In the current study, nanocrystalline CoY0.5xLa0.5xFe2-xO4 (where x = 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10) ferrites have been synthesized via a sol-gel auto combustion process. The synthesized powders were pressed into pellet forms and sintered at 900 °C for 4 h in the air. X-ray diffractometry (XRD) confirmed the single-phase cubic spinel structure of the synthesized samples having the mean crystallite domain sizes ranging from 122 and 54 nm. FTIR spectroscopic analyses revealed two strong bands within the range of 600 to 350 cm-1, further confirming the cubic inverse spinel structure of the prepared materials. The surface morphologies and composition were investigated by Field Emission Scanning Electron Microscopy (FE-SEM) and Energy Dispersive X-ray (EDX) Spectroscopy. The magnetic hysteresis curves recorded at room temperature exhibit ferrimagnetic behavior. The highest coercivity (Hcâ¼1276 Oe) was found at a high doping (x = 0.10) concentration of Y3+ and La3+ in cobalt ferrite. Dielectric constant increase with increased doping concentration whereas real-impedance and dielectric loss decrease with increased in doping concentration and applied frequency. The band gap energy increased from 1.48 to 1.53 eV with increasing Y3+ and La3+concentrations in the UV-Vis region. The elevated levels of magnetic and dielectric substances in the ferrite nanoparticles suggest that the material could be used for magnetic recording media and high-frequency devices.
RESUMO
In this report, we study the Yttrium-doped Barium Titanate (Y-BT) Ba1 - xYxTiO3 (with x = 0.00, 0.01, 0.03, 0.05, 0.07 mmol) perovskite ceramics synthesized by sol-gel method. The as-made powder samples were pressed into a pellet shape and subsequently sintered at 1300 °C for 5 h in air. The structural, morphological, electrical, and optical properties of the synthesized samples were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), impedance analyzer, and UV-Vis-NIR Spectroscopy respectively. The XRD study revealed the formations of single phase tetragonal structure of Barium Titanate (BT) with â¼23-33 nm mean crystallite size. The crystallite size increases initially with Y-doping, found at about 33 nm for x = 0.01, and reduces for increase in Y3+ concentration further. The microstructural study from FESEM depicts the uniform distribution of compact and well-faceted grain growth for Y-BT in contrast with undoped barium titanate. The average grain size (â¼0.29-0.78 µm) of the Y-BT decreases with increasing doping concentration. Frequency-dependent impedance analyses show enhanced dielectric properties like dielectric constant, quality factor, and conductivity with low dielectric loss in the presence of Yttrium. The optical bandgap energy (â¼2.63-3.72 eV) estimated from UV-Vis-NIR diffuse reflection data shows an increasing trend with a higher concentration of yttrium doping.