Development of an electroactive aerobic biocathode for microbial fuel cell applications.

Microbial biocathodes are gaining interest due to their low cost, environmental friendliness and sustainable nature. In this study, a microbial consortium was enriched from activated sludge obtained from a common textile effluent treatment plant in the absence of organic carbon source to produce an electroactive biofilm. Chronoamperometry method of enrichment was carried out for over 70 days to select for electroactive bacteria that could be used as a cathode catalyst in microbial fuel cells (MFC). The resultant biofilm produced an average peak current of -0.7 mA during the enrichment and produced a maximum power density of 64.6 ± 3.5 mW m-2 compared to platinum (72.7 ± 1.2 mW m-2 ) in a Shewanella-based MFC. Microbial community analysis of the initial sludge sample and enriched samples, based on 16S rRNA gene sequencing, revealed the selection of chemolithotrophs with the most dominant phylum being Bacteroidetes, Proteobacteria, Firmicutes, Actinobacteria and Acidobacteria in the enriched samples. A variety of CO2 fixing and nitrate-reducing bacteria was present in the resultant biofilm on the cathode. This study suggests that microbial consortia are capable of replacing expensive platinum as a cathode catalyst in MFCs.

Effect of neutral red incorporation on Al-doped ZnO thin films and its bio-electrochemical interaction with NAD+/NADP+ dependent enzymes.

A new approach to deposition of electroactive ZnO thin films have been carried out, by one-pot chemical bath deposition with Al dopant and incorporation of neutral red as organic mediator. The morphological, structural and functional characterization of the neutral red incorporated, Al-doped ZnO (NR-AZO) film was carried out using electron microscopy, FTIR, XRD and EIS respectively. The incorporated neutral red was found to induce strain in the crystal of AZO proportional to the concentration used in depositing solution which further affected the charge transfer resistance of the films in solution. One mM neutral red was found to be the optimum concentration for both conductivity and response to NADH/NADPH. The response of the films was further validated by immobilizing NAD+ dependent alcohol dehydrogenase (ADH) and NADP+ dependent glucose dehydrogenase (GDH) independently. The ADH/NR-AZO showed a sensitivity of 3.2 µA cm-2 mM-1 with a LoD of 1.7 µM of ethanol in the range 5.6 µM-7 mM, whereas GDH/NR-AZO showed a sensitivity of 4.33 µA cm-2 mM-1 with a LoD of 27 µM of glucose in the range 90 µM-4 mM. This method serves as a simple alternative to immobilize the organic redox dyes into the inorganic thin films in a single step making it electroactive towards specific biomolecules.

New approach to biosensing of co-enzyme nicotinamide adenine dinucleotide (NADH) by incorporation of neutral red in aluminum doped nanostructured ZnO thin films.

Biosensing of NADH on bare electrodes has drawbacks such as high over-potential and poisoning during the oxidation reaction. To overcome this challenge a different approach has been undertaken by incorporating neutral red (NR) in Al doped ZnO (AZO) thin films using one-pot chemical bath deposition (CBD). The surface morphology of the films was hexagonal nanorods along the c-axis, perpendicular to the substrate. The thickness of the thin films were ranging from 400 to 3000nm varying dependent on time of deposition (30 to 150min). The average diameter of the nanorods was larger in the presence of neutral red (NR-AZO) with ~300nm in contrast to its absence (AZO) with ~200nm. The density of the packing of nanorods was dependent on the citrate concentration used during deposition. Control over the dopant concentration in the films was achieved by varying the area of Al foil used in the deposition solution. The selected area diffraction (SAED) and X-ray diffraction (XRD) indicated 002 plane of orientation in the nanorods. FTIR and FT-Raman analysis revealed conserved structure of NR and AZO. Chronoamperometric (CA) analysis showed a sensitivity of 0.45µAcm-2mM-1 and LoD of 22µM within the range 0.075-4mM of NADH. The biological sensing of NADH was validated by physical adsorption of NAD+ dependent-lactate dehydrogenase (LDH) on NR-AZO. CA showed sensitivity of 0.56µAcm-2mM-1 and LoD for lactate was 27µM in the range of 0.1-1mM of lactate. Further validation with real-time serum sample shows that LDH/NR-AZO correlates with the clinical values. The distinction in this study is that the organic mediator like neutral red has been incorporated into the grain structure of the ZnO thin film whereas other study with the mediators have only attempted surface functionalization. This article is part of a Special Issue entitled "Recent Advances in Bionanomaterials" Guest Editor: Dr. Marie-Louise Saboungi and Dr. Samuel D. Bader.