Accuracy in Rietveld quantitative phase analysis: a comparative study of strictly monochromatic Mo and Cu radiations.

This study reports 78 Rietveld quantitative phase analyses using Cu Kα1, Mo Kα1 and synchrotron radiations. Synchrotron powder diffraction has been used to validate the most challenging analyses. From the results for three series with increasing contents of an analyte (an inorganic crystalline phase, an organic crystalline phase and a glass), it is inferred that Rietveld analyses from high-energy Mo Kα1 radiation have slightly better accuracies than those obtained from Cu Kα1 radiation. This behaviour has been established from the results of the calibration graphics obtained through the spiking method and also from Kullback-Leibler distance statistic studies. This outcome is explained, in spite of the lower diffraction power for Mo radiation when compared to Cu radiation, as arising because of the larger volume tested with Mo and also because higher energy allows one to record patterns with fewer systematic errors. The limit of detection (LoD) and limit of quantification (LoQ) have also been established for the studied series. For similar recording times, the LoDs in Cu patterns, ∼0.2 wt%, are slightly lower than those derived from Mo patterns, ∼0.3 wt%. The LoQ for a well crystallized inorganic phase using laboratory powder diffraction was established to be close to 0.10 wt% in stable fits with good precision. However, the accuracy of these analyses was poor with relative errors near to 100%. Only contents higher than 1.0 wt% yielded analyses with relative errors lower than 20%.

Exploring a novel preparation method of 1D metal organic frameworks based on supercritical CO2.

The preparation of copper(II) one-dimensional MOFs using an eco-efficient method is reported here. This method is based exclusively on using supercritical CO2 as a solvent, without the addition of any other additive or co-solvent. Neutral acetylacetonate copper complexes and two linear linkers, namely, the bidentate 4,4'-bipyridine and 4,4'-trimethylenedipyridine molecules, were reacted under compressed CO2 at 60 °C and 20 MPa for periods of 4 or 24 h. The success achieved in the synthesis of the different studied 1D-MOFs was related to the solubility of the reagents in supercritical CO2. The reaction yield of the synthesized coordination polymers via the supercritical route was close to 100% because both the reactants were almost completely depleted in the performed experiments.