The in vitro remineralizing effect of CPP-ACP and CPP-ACPF after 6 and 12 weeks on initial caries lesion.

OBJECTIVE: The aim of this in vitro study was to determine the effects of remineralization promoting agents containing casein phosphopeptide-stabilized amorphous calcium phosphate (CPP-ACP), or CPP-ACP in combination with fluoride (CPP-ACPF) on artificial white spot lesions (WSLs) after 6 and 12 weeks. METHODOLOGY: White spot lesions were created on 123 sectioned premolars (246 specimens) with a demineralization solution during a 96 hours pH-cycling regime. Two experimental groups were created: a CPP-ACP group (Tooth Mousse™), and a CPP-ACPF group (Mi Paste Plus™). Additionally, two control groups were created, one using only a conventional toothpaste (1450 ppm fluoride) and another one without any working agents. All teeth were also daily brushed with the conventional toothpaste except the second control group. Tooth Mousse™ and Mi Paste Plus™ were applied for 180 seconds every day. The volume of demineralization was measured with transverse microradiography. Six lesion characteristics regarding the lesion depth and mineral content of WSLs were also determined. RESULTS: The application of CPP-ACP and CPP-ACPF had a significant regenerative effect on the WSLs. Compared to Control group 1 and 2 the volume of demineralization after 6 weeks decreased significantly for CPP-ACP (respectively p<0.001 and p<0.001) and CPP-ACPF (respectively p=0.001 and p=0.003). The same trend was observed after 12 weeks. For the CPP-ACPF group, WSL dimensions decreased significantly between 6 and 12 weeks follow-up (p=0.012). The lesion depth reduced significantly after application of CPP-ACP and CPP-ACPF but increased significantly in the Control groups. Mineral content increased for CPP-ACP and CPP-ACPF after an application period of 12 weeks, but this was only significant for CPP-ACP. CONCLUSIONS: Long-term use of CPP-ACP and CPP-ACPF in combination with a conventional tooth paste shows beneficial effects in the recovery of in vitro subsurface caries lesions.

The in vitro remineralizing effect of CPP-ACP and CPP-ACPF after 6 and 12 weeks on initial caries lesion

Abstract Objective: The aim of this in vitro study was to determine the effects of remineralization promoting agents containing casein phosphopeptide-stabilized amorphous calcium phosphate (CPP-ACP), or CPP-ACP in combination with fluoride (CPP-ACPF) on artificial white spot lesions (WSLs) after 6 and 12 weeks. Methodology: White spot lesions were created on 123 sectioned premolars (246 specimens) with a demineralization solution during a 96 hours pH-cycling regime. Two experimental groups were created: a CPP-ACP group (Tooth Mousse™), and a CPP-ACPF group (Mi Paste Plus™). Additionally, two control groups were created, one using only a conventional toothpaste (1450 ppm fluoride) and another one without any working agents. All teeth were also daily brushed with the conventional toothpaste except the second control group. Tooth Mousse™ and Mi Paste Plus™ were applied for 180 seconds every day. The volume of demineralization was measured with transverse microradiography. Six lesion characteristics regarding the lesion depth and mineral content of WSLs were also determined. Results: The application of CPP-ACP and CPP-ACPF had a significant regenerative effect on the WSLs. Compared to Control group 1 and 2 the volume of demineralization after 6 weeks decreased significantly for CPP-ACP (respectively p<0.001 and p<0.001) and CPP-ACPF (respectively p=0.001 and p=0.003). The same trend was observed after 12 weeks. For the CPP-ACPF group, WSL dimensions decreased significantly between 6 and 12 weeks follow-up (p=0.012). The lesion depth reduced significantly after application of CPP-ACP and CPP-ACPF but increased significantly in the Control groups. Mineral content increased for CPP-ACP and CPP-ACPF after an application period of 12 weeks, but this was only significant for CPP-ACP. Conclusions: Long-term use of CPP-ACP and CPP-ACPF in combination with a conventional tooth paste shows beneficial effects in the recovery of in vitro subsurface caries lesions.

Fracture resistance of endodontically restored, weakened incisors.

OBJECTIVES: To test the fracture strength of weakened bovine incisors endodontically treated with mineral trioxide aggregate (MTA), calcium phosphate bone cement (CPBC) or fibre reinforced composite (FRC) posts, and to evaluate the fracture mode. METHODS: Weakened bovine incisors (n = 75), standardized according to the dentinal wall thickness at the cervical area, were randomly assigned to one control group and three experimental groups. Unfilled teeth were assigned to group 1 (n = 20) and served as control group. Group 2 (n = 17) consisted of teeth filled with MTA. In group 3 (n = 18), the incisors were filled with CPBC and in group 4 (n = 20) with FRC posts. All specimens were subjected to load at a cross-head speed of 60 mm min(-1) until fracture occurred. The initial (IL) and final fracture (FL) loads (N) were recorded, and the failure mode among the different groups was evaluated. RESULTS: anova showed a statistically significant difference in fracture load among the groups. Tukey's test revealed a significant difference for the IL between the control group and the experimental groups with exception of the MTA group. The FL was not significantly different among the experimental groups. A high percentage of favourable fractures was seen in the FRC and CPBC groups. CONCLUSION: FRC posts and CPBC could be promising materials to strengthen non-vital structurally compromised teeth.