To etch or not to etch, Part II: On the hydrophobic-rich content and fatigue strength of universal adhesives.

OBJECTIVE: To determine whether smear layer management, via conservative etching protocols, and the hydrophobic-rich content of hybrid layers would affect the fatigue strength of resin-dentin interfaces. METHODS: Bar-shaped dentin beams obtained from sound third molars were wet-polished for 30 s. Dentin was etched with 32 % ortho-phosphoric acid for 3 or 15 s, 10 % meta-phosphoric acid for 15 s or by a prime-and-rinse application using a mild universal adhesive (Scotchbond Universal, 3M ESPE). Self-etch application served as control. Coating was performed with a solvent-free bisGMA-based resin. Composite buildups were made with a nanofilled composite. Resin-dentin beams with twin-bonded interfaces were sectioned and stored in deionized water for 24 h at 37 â„ƒ before 4-point flexural quasi-static monotonic testing (n = 16). Stress-life fatigue behavior was evaluated under cyclic loading (n = 35) by the staircase method at 4 Hz. The tension side of cyclic-loaded unfractured beams were evaluated under SEM, along with the micro-morphology of etched dentin surfaces. Monotonic data was analyzed by two-way ANOVA followed by the Tukey Test and cyclic-loaded data by Kruskal-Wallis on Ranks (α = 0.05). RESULTS: Etching protocols and higher hydrophobic-rich content produced significantly higher fatigue life distributions (p < 0.05). Dentin demineralization was ranked as OPA 15 s > MPA 15 s > OPA 3 s > P + R > SE. Less aggressive etching and coating reduced crack formation at hybrid layers. SIGNIFICANCE: Current oversimplification trends in resin-dentin bonding constitute a trade-off between hybridization quality and easier adhesive handling. Controlled dentin etching and increasing the hydrophobic-rich content of hybrid layers may be necessary to extend the longevity of mild universal adhesives.

To etch or not to etch, Part I: On the fatigue strength and dentin bonding performance of universal adhesives.

OBJECTIVE: To characterize whether the bonding performance and fatigue strength of resin-dentin interfaces created by a universal adhesive would be affected by different H3PO4-application times to more accurately assess long-term durability. METHODS: Mid-coronal flat dentin surfaces with standardized smear-layers were produced on sound third molars, etched with 32% H3PO4 for 0, 3 and 15 s, bonded with a mild universal adhesive (3M-ESPE) and restored with a nanofilled composite. Bonded specimens (0.9 × 0.9 mm) were stored in deionized water for 24 h and sectioned into beams for microtensile testing (n = 10). Resin-dentin beams were tested under tension until failure (0.5 mm/min) after 24 h or 6 month storage in artificial saliva at 37 ̊C. Bar-shaped resin-dentin beams (0.9 × 0.9 × 12 mm) were tested under 4-point-flexure initially at quasi-static loads (n = 22) and then under cyclic loads (n > 50). The stress-life fatigue behavior was evaluated using the twin-bonded interface approach by the staircase method at 4 Hz. Fractured interfaces and the tension side of unfractured beams were evaluated under SEM, along with the micro-morphology of the etched dentin surfaces and hybrid layers. Data were analyzed by ANOVA and Tukey test and Wilcoxon Rank Sum Test (α = 0.05). RESULTS: Quasi-static loads were limited to discriminate the bonding performance of resin-dentin interfaces. Application modes significantly affected etching patterns, fatigue strength, endurance limits and hybrid layer morphology (p < 0.001). SIGNIFICANCE: Reductions in fatigue strength of self-etched bonded interfaces raise concerns about the true ability of universal adhesives to properly bond to dentin.