Mechanical Properties of Macro Polypropylene Fibre-Reinforced Concrete.

Adding fibers to concrete helps enhance its tensile strength and ductility. Synthetic fibres are preferable to steel ones which suffer from corrosion that reduces their functionality with time. More consideration is given to synthetic fibres as they can be sourced from waste plastics and their incorporation in concrete is considered a new recycling pathway. Thus, this work investigates the potential engineering benefits of a pioneering application using extruded macro polyfibres in concrete. Two different fiber dosages, 4 kg/m3 and 6 kg/m3, were used to investigate their influence based on several physical, mechanical and microstructural tests, including workability, compressive strength, modulus of elasticity, splitting-tensile strength, flexural test, CMOD, pull-out test and porosity. The test results revealed a slight decrease in the workability of the fibre-reinforced concrete, while all the mechanical and microstructural properties were enhanced significantly. It was observed that the compressive, splitting tensile and bonding strength of the concrete with 6 kg/m3 fibre dosage increased by 19.4%, 41.9% and 17.8% compared to the plain concrete specimens, respectively. Although there was no impact of the fibres on the modulus of rupture, they significantly increased the toughness, resulting in a progressive type of failure instead of the sudden and brittle type. Moreover, the macroporosity was reduced by the fibre addition, thus increasing the concrete compressive strength. Finally, simplified empirical formulas were developed to predict the mechanical properties of the concrete with fibre addition. The outcome of this study will help to increase the implementation of the recycled plastic waste in concrete mix design and promote a circular economy in the waste industry.

Transversely isotropic elastic-plastic properties in thermal arc sprayed Al-Zn coating: a microporomechanics approach.

The transversely isotropic behaviour of thermal sprayed aluminium and zinc coating has been investigated based on a combination of nanoindentation experimental data and microporomechanics theory. A recently developed strength homogenisation approach comprises of the solid and porous medium is adopted to investigate the morphology properties of thermal sprayed aluminum and zinc coating. The finding of this paper demonstrates that the individual aluminum and zinc phases in the coating have a characteristic packing density close to the theoretical highest spherical packing ratio for face-centred cubic and hexagonal close packed. Also, the plasticity properties of solid particles in both aluminum and zinc are found to have a significant transversely isotropic condition, while the elasticity properties are close to isotropic. These findings led to the conclusion that the anisotropic condition of the coating is dominantly affected by the plasticity properties, in terms of cohesion and friction coefficient.

Cohesive-strength homogenisation model of porous and non-porous materials using linear comparison composites and application.

An estimation of the strength of composite materials with different strength behaviours of the matrix and inclusion is of great interest in science and engineering disciplines. Linear comparison composite (LCC) is an approach introduced for estimating the macroscopic strength of matrix-inclusion composites. The LCC approach has however not been expanded to model non-porous composites. Therefore, this paper is to fill this gap by developing a cohesive-strength method for modelling frictional composite materials, which can be porous and non-porous, using the LCC approach. The developed cohesive-strength homogenisation model represents the matrix and inclusion as a two-phase composite containing solids and pores. The model is then implemented in a multiscaling model in which porous cohesive-frictional solids intermix with each other at different scale levels classified as micro, meso and macro. The developed model satisfies an upscaling scheme and is suitable for investigating the effects of the microstructure, the composition, and the interface condition of the materials at micro scales on the macroscopic strength of the composites. To further demonstrate the application of the developed cohesive-strength homogenisation model, the cohesive-strength properties of very high strength concrete are determined using instrumented indentation, nonlinear limit analysis and second-order cone programming to obtain material properties at different scale levels.

Relationship of Stiffness-Based Indentation Properties Using Continuous-Stiffness-Measurement Method.

The determination of elastic modulus (E) and hardness (H) relies on the accuracy of the contact area under the indenter tip, but this parameter cannot be explicitly measured during the nanoindentation process. This work presents a new approach that can derive the elastic modulus (E) and contact depth (hc) based on measured experiment stiffness using the continuous-stiffness-measurement (CSM) method. To achieve this, an inverse algorithm is proposed by incorporating a set of stiffness-based relationship functions that are derived from combining the dimensional analysis approach and computational simulation. This proposed solution considers both the sink-in and pile-up contact profiles; therefore, it provides a more accurate solution when compared to a conventional method that only considers the sink-in contact profile. While the proposed solution is sensitive to Poisson's ratio (ν) and the equivalent indentation conical angle (θ), it is not affected by material plasticity, including yield strength (σy) and work hardening (n) for the investigated range of 0.001 < σy/E < 0.5. The proposed stiffness-based approach can be used to consistently derive elastic modulus and hardness by using stiffness and the load-and-unload curve measured by the continuous-stiffness-measurement (CSM) method.

Study of Strain-Hardening Behaviour of Fibre-Reinforced Alkali-Activated Fly Ash Cement.

This paper presents a study of parameters affecting the fibre pull out capacity and strain-hardening behaviour of fibre-reinforced alkali-activated cement composite (AAC). Fly ash is a common aluminosilicate source in AAC and was used in this study to create fly ash based AAC. Based on a numerical study using Taguchi's design of experiment (DOE) approach, the effect of parameters on the fibre pull out capacity was identified. The fibre pull out force between the AAC matrix and the fibre depends greatly on the fibre diameter and embedded length. The fibre pull out test was conducted on alkali-activated cement with a capacity in a range of 0.8 to 1.0 MPa. The strain-hardening behaviour of alkali-activated cement was determined based on its compressive and flexural strengths. While achieving the strain-hardening behaviour of the AAC composite, the compressive strength decreases, and fine materials in the composite contribute to decreasing in the flexural strength and strain capacity. The composite critical energy release rate in AAC matrix was determined to be approximately 0.01 kJ/m 2 based on a nanoindentation approach. The results of the flexural performance indicate that the critical energy release rate of alkali-activated cement matrix should be less than 0.01 kJ/m 2 to achieve the strain-hardening behaviour.

An Investigation of Nanomechanical Properties of Materials using Nanoindentation and Artificial Neural Network.

Mechanical properties of materials can be derived from the force-displacement relationship through instrumented indentation tests. Complications arise when establishing the full elastic-plastic stress-strain relationship as the accuracy depends on how the material's and indenter's parameters are incorporated. For instance, the effect of the material work-hardening phenomenon such as the pile-up and sink-in effect cannot be accounted for with simplified analytical indentation solutions. Due to this limitation, this paper proposes a new inverse analysis approach based on dimensional functions analysis and artificial neural networks (ANNs). A database of the dimensional functions relating stress and strain parameters of materials has been developed. The database covers a wide range of engineering materials that have the yield strength-to-modulus ratio (σy/E) between 0.001 to 0.5, the work-hardening power (n) between 0-0.5, Poisson's ratio (v) between 0.15-0.45, and the indentation angle (θ) between 65-80 degrees. The proposed algorithm enables determining the nanomechanical stress-strain parameters using the indentation force-displacement relationship, and is applicable to any materials that the properties are within the database range. The obtained results are validated with the conventional test results of steel and aluminum samples. To further demonstrate the application of the proposed algorithm, the nanomechanical stress-strain parameters of ordinary Portland cement phases were determined.

Optimization of Micro and Nano Palm Oil Fuel Ash to Determine the Carbonation Resistance of the Concrete in Accelerated Condition.

The carbonation rate of reinforced concrete is influenced by three parameters, namely temperature, relative humidity, and concentration of carbon dioxide (CO2) in the surroundings. As knowledge of the service lifespan of reinforced concrete is crucial in terms of corrosion, the carbonation process is important to study, and high-performance durable reinforced concretes can be produced to prolong the effects of corrosion. To examine carbonation resistance, accelerated carbonation testing was conducted in accordance with the standards of BS 1881-210:2013. In this study, 10⁻30% of micro palm oil fuel ash (mPOFA) and 0.5⁻1.5% of nano-POFA (nPOFA) were incorporated into concrete mixtures to determine the optimum amount for achieving the highest carbonation resistance after 28 days water curing and accelerated CO2 conditions up to 70 days of exposure. The effect of carbonation on concrete specimens with the inclusion of mPOFA and nPOFA was investigated. The carbonation depth was identified by phenolphthalein solution. The highest carbonation resistance of concrete was found after the inclusion of 10% mPOFA and 0.5% nPOFA, while the lowest carbonation resistance was found after the inclusion of 30% mPOFA and 1.5% nPOFA.