Dyeing of bacterial cellulose films using plant-based natural dyes.

The aim of this work was to test the use of plant-based natural dyes on bacterial cellulose (BC) to add aesthetic value to dyed pellicles while maintaining the mechanical properties. Natural pigments from Clitoria ternatea L. and Hibiscus rosa-sinensis were tested. The commercial ARAQCEL RL 500 was also used for comparison purposes. The behavior of biocellulose regarding dye fixation, rehydration, tensile strength, and elasticity was evaluated in comparison to the dried biomaterial, showing that dyeing is a process that can be performed on hydrated BC. Dyeing the BC films through an innovative process maintained the crystallinity, thermal stability and mechanical strength of the BC and confirmed the compatibility of the membrane with the dyes tested, from the observed Scanning Electron Microscopy (SEM) morphology of nanofibers. Dyed biomaterial can be applied to various products, as confirmed by the results of the mechanical tests. As environmental awareness and public concern regarding pollution increase, the combination of natural dyes and BC pellicles can produce an attractive new material for the textile industry.

Production of Bacterial Cellulose by Gluconacetobacter hansenii Using Corn Steep Liquor As Nutrient Sources.

Cellulose is mainly produced by plants, although many bacteria, especially those belonging to the genus Gluconacetobacter, produce a very peculiar form of cellulose with mechanical and structural properties that can be exploited in numerous applications. However, the production cost of bacterial cellulose (BC) is very high to the use of expensive culture media, poor yields, downstream processing, and operating costs. Thus, the purpose of this work was to evaluate the use of industrial residues as nutrients for the production of BC by Gluconacetobacter hansenii UCP1619. BC pellicles were synthesized using the Hestrin-Schramm (HS) medium and alternative media formulated with different carbon (sugarcane molasses and acetylated glucose) and nitrogen sources [yeast extract, peptone, and corn steep liquor (CSL)]. A jeans laundry was also tested. None of the tested sources (beside CSL) worked as carbon and nutrient substitute. The alternative medium formulated with 1.5% glucose and 2.5% CSL led to the highest yield in terms of dry and hydrated mass. The BC mass produced in the alternative culture medium corresponded to 73% of that achieved with the HS culture medium. The BC pellicles demonstrated a high concentration of microfibrils and nanofibrils forming a homogenous, compact, and three-dimensional structure. The biopolymer produced in the alternative medium had greater thermal stability, as degradation began at 240°C, while degradation of the biopolymer produced in the HS medium began at 195°C. Both biopolymers exhibited high crystallinity. The mechanical tensile test revealed the maximum breaking strength and the elongation of the break of hydrated and dry pellicles. The dry BC film supported up to 48 MPa of the breaking strength and exhibited greater than 96.98% stiffness in comparison with the hydrated film. The dry film supported up to 48 MPa of the breaking strength and exhibited greater than 96.98% stiffness in comparison with the hydrated film. The values obtained for the Young's modulus in the mechanical tests in the hydrated samples indicated low values for the variable rigidity. The presence of water in the interior and between the nanofibers of the hydrated BC only favored the results for the elasticity, which was 56.37% higher when compared to the dry biomaterial.