RESUMO
The preparation of MOF composites is considered as an effective method to address the challenges of shaping MOFs and to create porous solids with enhanced properties and broader applications. In this study, CPO-27-Co was crystallized via a simple strategy within porous chitosan beads. The resulting CS@CPO-27-Co composites were tested for CO2 sorption and they demonstrated promising performances by exceeding 3 mmol(CO2) g-1. The versatility of this strategy was further demonstrated by replacing cobalt(II) ions with nickel(II), also leading to the isostructural CPO-27 framework.
RESUMO
Two titanium-based MOFs MIL-125 and MIL-125_NH2 are synthesized and characterized using high-temperature powder X-ray diffraction (PXRD), thermogravimetric analysis (TGA), N2 sorption, Fourier transformed infrared spectroscopy (FTIR), Raman spectroscopy, ultraviolet-visible spectroscopy (UV-Vis), and electron paramagnetic resonance (EPR). Stable up to 300 °C, both compounds exhibited similar specific surface areas (SSA) values (1207 and 1099 m2 g-1 for MIL-125 and MIL-125_NH2, respectively). EPR signals of Ti3+ are observed in both, whith MIL-125_NH2 also showing âNH2 â+ signatures. Both MOFs efficiently adsorbed iodine in continuous gas flow over five days, with MIL-125 trapping 1.9 g.g-1 and MIL-125_NH2 trapping 1.6 g.g-1. MIL-125_NH2 exhibited faster adsorption kinetics due to its smaller band gap (2.5 against 3.6 eV). In situ Raman spectroscopy conducted during iodine adsorption revealed signal evolution from "free" I2 to "perturbed" I2, and I3 -. TGA and in situ Raman desorption experiments showed that âNH2 groups improved the stabilization of I3 - due to an electrostatic interaction with NH2 â+BDC radicals. The Albery model indicated longer lifetimes for iodine desorption in I2@MIL-125_NH2, attributed to a rate-limiting step due to stronger interaction between the anionic iodine species and the âNH2 â+ radicals. This study underscores how MOFs with efficient charge separation and hole-stabilizer functional groups enhance iodine stability at higher temperatures.
RESUMO
A green synthesis of UiO-66-NH2 embedded in chitosan and deposited on textiles has been investigated for the degradation of chemical warfare agents. This method requires no heating or use of toxic solvents. The composite synthesized presents an interesting efficiency in detoxifying common simulants of chemical warfare agents, such as DMNP. In parallel, resistance and permeability tests were also realized in order to confirm the suitability of the composites for further applications.
RESUMO
The Zr-based Metal Organic Framework (MOF) UiO-66(Zr) is widely employed owing to its good thermal and chemical stabilities. Although the long-range structure of this MOF is preserved in the presence of water during several days, little is known about the formation of defects, which cannot be detected using diffraction techniques. We apply here 17 O solid-state NMR spectroscopy at 18.8â T to investigate the reactivity of UiO-66, through the exchange of oxygen atoms between the different sites of the MOF and water. For that purpose, we have selectively enriched in 17 O isotope the carboxylate groups of UiO-66(Zr) by using it with 17 O-labeled terephthalic acid prepared using mechanochemistry. In the presence of water at 50 °C and a following dehydration at 150 °C, we observe an overall exchange of O atoms between COO- and µ3 -O2- sites. Furthermore, we demonstrate that the three distinct oxygen sites, µ3 -OH, µ3 -O2- and COO- , of UiO-66(Zr) MOF can be enriched in 17 O isotope by post-synthetic hydrothermal treatment in the presence of 17 O-enriched water. These results demonstrate the lability of Zr-O bonds and the reactivity of UiO-66(Zr) with water.
RESUMO
This study investigates the use of chitosan hydrogel microspheres as a template for growing an extended network of MOF-type HKUST-1. Different drying methods (supercritical CO2, freeze-drying, and vacuum drying) were used to generate three-dimensional polysaccharide nanofibrils embedding MOF nanoclusters. The resulting HKUST-1@Chitosan beads exhibit uniform and stable loadings of HKUST-1 and were used for the adsorption of CO2, CH4, Xe, and Kr. The maximum adsorption capacity of CO2 was found to be 1.98 mmol·g-1 at 298 K and 1 bar, which is significantly higher than those of most MOF-based composite materials. Based on Henry's constants, thus-prepared HKUST-1@CS beads also exhibit fair selectivity for CO2 over CH4 and Xe over Kr, making them promising candidates for capture and separation applications.
RESUMO
Despite many efforts devoted toward the design of covalent organic frameworks (COFs) at the framework level by selecting the building blocks, their organization in the nano to meso regimes is often neglected. Moreover, the importance of processability for their applications has recently emerged and the synthesis of COF nanostructures without agglomeration is still a challenge. Herein, the first example of hybrid COF-polymer particles for which polymers are used to manipulate the 2D COF growth along a specific direction is reported. The study examines how the nature, chain-end functionality, and molar mass of the polymer influence the shaping of hybrid 2D boronate ester-linked COF-polymer particles. Catechol-poly(N-butyl acrylate) leads to the self-assembly of crystallites into quasi-spherical structures while catechol-poly(N-isopropylacrylamide) mediates the synthesis of raspberry-like COF-polymer particles with radial grain orientation. Scanning and transmission electron microscopies (SEM and TEM) and 4D-STEM-ACOM (automated crystal orientation mapping) highlight the single-crystal character of these domains with one plane family throughout the particles. Interestingly, the presence of PNIPAm on the particle surface allows their drying without co-crystallization and enables their resuspension. Kinetic investigations show that catechol-PnBuA acts as a modulator and catechol-PNIPAm induces a template effect, introducing supramolecular self-assembly properties into particles to create new morphologies with higher structural complexity, beyond the framework level.
RESUMO
Metal-organic frameworks (MOFs) have been largely investigated worldwide for their use in the capture of radioactive iodine due to its potential release during nuclear accident events and reprocessing of nuclear fuel. The present work deals with the capture of gaseous I2 under a continuous flow and its subsequent transformation into I3- within the porous structures of three distinct, yet structurally related, terephthalate-based MOFs: MIL-125(Ti), MIL-125(Ti)_NH2, and CAU-1(Al)_NH2. The synthesized materials exhibited specific surface areas (SSAs) with similar order of magnitude: 1207, 1099, and 1110 m2 g-1 for MIL-125(Ti), MIL-125(Ti)_NH2, and CAU-1(Al)_NH2, respectively. Because of that, it was possible to evaluate the influence of other variables over the iodine uptake capacityâsuch as band gap energies, functional groups, and charge transfer complexes (CTC). After 72 h of contact with the I2 gas flow, MIL-125(Ti)_NH2 was able to trap 11.0 mol mol-1 of I2, followed by MIL-125(Ti) (8.7 mol mol-1), and by CAU-1(Al)_NH2 (4.2 mol mol-1). The enhanced ability to retain I2 in the MIL-125(Ti)_NH2 was associated with a combined effect between its amino group (which has a great affinity toward iodine), its smaller band gap (2.5 eV against 2.6 and 3.8 eV for CAU-1(Al)_NH2 and MIL-125(Ti), respectively), and its efficient charge separation. In fact, the presence of a linker-to-metal charge transfer (LMCT) mechanism in MIL-125(Ti) compounds separates the photogenerated electrons and holes into the two distinct moieties of the MOF: the organic linker (which stabilizes the holes) and the oxy/hydroxy inorganic cluster (which stabilizes the electrons). This effect was observed using EPR spectroscopy, whereas the reduction of the Ti4+ cations into the paramagnetic Ti3+ species was evidenced after irradiation of the pristine Ti-based MOFs with UV light (<420 nm). In contrast, because CAU-1(Al)_NH2 exhibits a purely linker-based transition (LBT)âwith no EPR signals related to Al paramagnetic speciesâit tends to exhibit faster recombination of the photogenerated charge carriers as, in this case, both electrons and holes are located over the organic linker. Furthermore, the transformation of the gaseous I2 into In- [n = 5, 7, 9, ...] intermediates and then into I3- species was evaluated using Raman spectroscopy by following the evolution of their respective bands at about 198, 180, and 113 cm-1. This conversionâwhich is favored by an effective charge separation and smaller band gapsâincreases the I2 uptake capacity of the compounds by creating specific adsorption sites for these anionic species. In fact, because the -NH2 groups act as an antenna to stabilize the photogenerated holes, both In- and I3- are adsorbed into the organic linker via an electrostatic interaction with these positively charged entities. Finally, changes regarding the EPR spectra before and after the iodine loading were considered to propose a mechanism for the electron transfer from the MOFs structure to the I2 molecules considering their different characteristics.
RESUMO
A clay-based TiO2 nanocomposite material was synthesized by a facile method, to investigate its structure and photocatalytic efficiency. The supported TiO2 nanoparticles were generated using a sol-gel method, and subsequently, mixed with a suspension of sepiolite. The material was recovered in powder form (Mc-80) and then calcined to properly arrange the crystal lattice of the TiO2 particles for use in heterogeneous photocatalysis (Mc-80-500). A powder X-ray diffractogram of Mc-80-500 revealed a dispersion of anatase and rutile phase TiO2 particles on the clay surface, exhibiting a size in the order of 4-8 nm. TEM images of Mc-80-500 confirmed the presence of isolated TiO2 beads on the surface of the fibrous sepiolite. The specific surface area of Mc-80-500 was larger than that of raw sepiolite and that of free TiO2 nanoparticles. Mc-80-500 was found to be more efficient in heterogeneous photocatalysis compared to other TiO2 materials based on sepiolite. Total depollution of a reactive dye (Orange G) was achieved after 1 h irradiation time, which is relatively quick compared to previous reports. The photocatalyst material can be washed with distilled water without chemical additives or calcination, and can be reused several times for photocatalysis, without loss of efficiency.
RESUMO
106Ru is a radioactive isotope usually generated by the nuclear industry within power plant reactors. During a nuclear accident, 106Ru reacts with oxygen, leading to the production of highly volatile ruthenium tetroxide RuO4. The combination of volatility and radioactivity makes 106RuO4, one of the most radiotoxic species and justifies the development of a specific setup for its capture and immobilization. In this study, we report for the first time the capture and immobilization of gaseous RuO4 within a porous metal-organic framework (UiO-66-NH2). We used specific installation for the production of gaseous RuO4 as well as for the quantification of this gas trapped within the filtering medium. We proved that UiO-66-NH2 has remarkable affinity for RuO4 capture, as this MOF exhibited the worldwide highest RuO4 decontamination factor (DF of 5745), hundreds of times higher than the DF values of sorbents daily used by the nuclear industry (zeolites or activated charcoal). The efficiency of UiO-66-NH2 can be explained by its pore diameters well adapted to the capture and immobilization of RuO4 as well as its conversion into stable RuO2 within the pores. This conversion corresponds to the reactivity of RuO4 with the MOF organic sub-network, leading to the oxidation of terephthalate ligands. As proved by powder X-ray diffraction and NMR techniques, these modifications did not decompose the MOF structure.
RESUMO
The reactivity of 2,3-pyridine-dicarboxylic (known as quinolinic or H2qui) acid and 2,5-pyridine-dicarboxylic (known as isocinchomeronic or H2icc) acid has been investigated as a complexing agent toward the niobium(IV) tetrachloride precursor (NbCl4·2THF) in different organic solvent mixtures. It resulted in the isolation of four crystalline assemblies of mononuclear coordination complexes 1-4 [Nb(HL)4·solvent], where HL is the monoprotonated quinolinate (Hqui) ligand (complexes 1-3) or the monoprotonated isocinchomeronate ligand (complex 4). For each complex, the discrete niobium(IV) center is eightfold coordinated to four oxygen atoms from the deprotonated carboxylate arm and four nitrogen atoms from the pyridine part of the dicarboxyl ligand with a dodecahedral environment [NbO4N4]. The remaining carboxyl arm (either in 3 or in 5 position) remained under its protonated form, leading to neutral [Nb(HL)4] moieties for compounds 1, 2, and 4, or the anionic [Nb(qui)(Hqui)3]- moiety for compound 3. The complexes are observed in various molecular arrangements, involving intercalated solvent molecules such as acetonitrile in compound 1 ([Nb(Hqui)4·0.8(CH3CN)], obtained at room temperature), a mixture of acetonitrile and pyridine in compound 2 ([Nb(Hqui)4·0.7CH3CN·2PYR], obtained via the solvothermal reaction at 80 °C), a mixture of pyridine and triethylamine, in addition with water and chloride species, in compound 3 ([Nb(qui)(Hqui)3·Cl·HPYR·HTEA·1.5H2O], obtained via solvothermal reaction at 80 °C), and N,N-dimethylformamide in compound 4 ([Nb(Hicc)4·6DMF], obtained at room temperature). The d1 configuration expected for the niobium(IV) centers has been analyzed by magnetic measurements, as well as by EPR and XPS. An anti-ferromagnetism transition has been observed at very low temperatures for complexes 1 (3.6 K) and 4 (3.3 K), for which the shortest Nb···Nb interatomic lengths occur.
RESUMO
The reactivity of aryl monocarboxylic acids (benzoic, 1- or 2-naphtoic, 4'-methylbiphenyl-4-carboxylic, and anthracene-9-carboxylic acids) as complexing agents for the ethoxide niobium(V) (Nb(OEt)5 precursor has been investigated. A total of eight coordination complexes were isolated with distinct niobium(V) nuclearities as well as carboxylate complexation states. The use of benzoic acid gives a tetranuclear core Nb4 (µ2 -O)4 (L)4 (OEt)8 ] (L=benzoate (1)) with four Nb-(µ2 -O)-Nb linkages in a square plane configuration. A similar tetramer, 7, was obtained with 2-naphtoic acid by using a 55 % humid atmosphere synthetic route. Two types of dinuclear brick were identified with one central Nb-(µ2 -O)-Nb linkage; they differ in their complexation state, with one bridging carboxylate ([Nb2 (µ2 -O)(µ2 -OEt)(L)(OEt)6 ], with L=1-naphtoate (3) or anthracene-9-carboxylate (5)) or two bridging carboxylate groups ([Nb2 (µ2 -O)(L)2 (OEt)6 ], with L=4'-methylbiphenyl-4-carboxylic (4) or anthracene-9-carboxylate (6)). An octanuclear moiety [Nb8 (µ2 -O)12 (L)8 (η1 -L)4-x (OEt)4+x ] (with L=2-naphtoate, x=0 or 2; 8) was obtained by using a solvothermal route in acetonitrile; it has a cubic configuration with niobium centers at each node, linked by 12â µ2 -O groups. The formation of the niobium oxo clusters was characterized by infrared and liquid 1 H NMR spectroscopy in order to analyze the esterification reaction, which induces the release of water molecules that further react through oxolation with niobium atoms, in different {Nb2 O}, {Nb4 O4 } and {Nb8 O12 } nuclearities.
RESUMO
Many works reported the encapsulation of iodine in metal-organic frameworks as well as the I2 â I3- chemical conversion. This transformation has been examined by adsorbing gaseous iodine on a series of UiO-66 materials and the different Hf/Zr metal ratios (0-100% Hf) were evaluated during the evolution of I2 into I3-. The influence of the hafnium content on the UiO-66 structure was highlighted by PXRD, SEM images, and gas sorption tests. The UiO-66(Hf) presented smaller lattice parameter (a = 20.7232 Å), higher crystallite size (0.18 ≤ Φ ≤ 3.33 µm), and smaller SSABET (818 m2·g-1) when compared to its parent UiO-66(Zr) â a = 20.7696 Å, 100 ≤ Φ ≤ 250 nm, and SSABET = 1262 m2·g-1. The effect of replacing Zr atoms by Hf in the physical properties of the UiO-66 was deeply evaluated by a spectroscopic study using UV-vis, FTIR, and Raman characterizations. In this case, the Hf presence reduced the band gap of the UiO-66, from 4.07 eV in UiO-66(Zr) to 3.98 eV in UiO-66(Hf). Furthermore, the UiO-66(Hf) showed a blue shift for several FTIR and Raman bands, indicating a stiffening on the implied interatomic bonds when comparing to UiO-66(Zr) spectra. Hafnium was found to clearly favor the capture of iodine [285 g·mol-1, against 230 g·mol-1 for UiO-66(Zr)] and the kinetic evolution of I2 into I3- after 16 h of I2 filtration. Three iodine species were typically identified by Raman spectroscopy and chemometric analysis. These species are as follows: "free" I2 (206 cm-1), "perturbed" I2 (173 cm-1), and I3- (115 and 141 cm-1). It was also verified, by FTIR spectroscopy, that the oxo and hydroxyl groups of the inorganic [M6O4(OH)4] (M = Zr, Hf) cluster were perturbed after the adsorption of I2 into UiO-66(Hf), which was ascribed to the higher acid character of Hf. Finally, with that in mind and considering that the EPR results discard the possibility of a redox phenomenon involving the tetravalent cations (Hf4+ or Zr4+), a mechanism was proposed for the conversion of I2 into I3- in UiO-66âbased on an electron donor-acceptor complex between the aromatic ring of the BDC linker and the I2 molecule.
RESUMO
Since the emergence of chemical, biological, radiological, and nuclear risks, significant efforts have been made to create efficient personal protection equipment. Recently, metal-organic framework (MOF) materials have emerged as new promising candidates for the capture and degradation of various threats, like chemical warfare agents (CWAs) or radioactive species. Herein, we report a new synthesis method of MOF-textile composites by microwave irradiation, with direct anchoring of MOFs on textiles. The resistance of the composite has been tested using normed abrasion measurements, and non-stable samples were optimized. The protection capacity of the MOF-textile composite has been tested against dimethyl 4-nitrophenyl phosphate, a common CWA simulant, showing short degradation half-life (30 min). Radiological/nuclear protection has also been tested through uranium uptake (up to 15 mg g-1 adsorbent) and the capture of Kr or Xe gas at 0.9 and 2.9 cm3/g, respectively.
RESUMO
The use of an extrusion-spheronization process was investigated to prepare robust and highly porous extrudates and granules starting from UiO-66 and UiO-66_NH2 metal-organic framework powders. As-produced materials were applied to the capture of gaseous iodine and the adsorption of xenon and krypton. In this study, biosourced chitosan and hydroxyethyl cellulose (HEC) are used as binders, added in low amounts (less than 5 wt % of the dried solids), as well as a colloidal silica as a co-binder when required. Characterizations of the final shaped materials reveal that most physicochemical properties are retained, except the textural properties, which are impacted by the process and the proportion of binders (BET surface area reduction from 5 to 33%). On the other hand, the mechanical resistance of the shaped materials toward compression is greatly improved by the presence of binders and their respective contents, from 0.5 N for binderless UiO-66 granules to 17 N for UiO-66@HEC granules. UiO-66_NH2-based granules demonstrated consequent iodine capture after 48 h, up to 527 mg/g, in line with the pristine UiO-66_NH2 powder (565 mg/g) and proportionally to the retaining BET surface area (-5% after shaping). Analogously, the shaped materials presented xenon and krypton sorption isotherms correlated to their BET surface area and high predicted xenon/krypton selectivity, from 7.1 to 9.0. Therefore, binder-aided extrusion-spheronization is an adapted method to produce shaped solids with adequate mechanical resistance and retained functional properties.
RESUMO
A series of Zr-based UiO-n MOF materials (n=66, 67, 68) have been studied for iodine capture. Gaseous iodine adsorption was collected kinetically from a home-made set-up allowing the continuous measurement of iodine content trapped within UiO-n compounds, with organic functionalities (-H, -CH3 , -Cl, -Br, -(OH)2 , -NO2 , -NH2 , (-NH2 )2 , -CH2 NH2 ) by in-situ UV-Vis spectroscopy. This study emphasizes the role of the amino groups attached to the aromatic rings of the ligands connecting the {Zr6 O4 (OH)4 } brick. In particular, the preferential interaction of iodine with lone-pair groups, such as amino functions, has been experimentally observed and is also based on DFT calculations. Indeed, higher iodine contents were systematically measured for amino-functionalized UiO-66 or UiO-67, compared to the pristine material (up to 1211â mg/g for UiO-67-(NH2 )2 ). However, DFT calculations revealed the highest computed interaction energies for alkylamine groups (-CH2 NH2 ) in UiO-67 (-128.5â kJ/mol for the octahedral cavity), and pointed out the influence of this specific functionality compared with that of an aromatic amine. The encapsulation of iodine within the pore system of UiO-n materials and their amino-derivatives has been analyzed by UV-Vis and Raman spectroscopy. We showed that a systematic conversion of molecular iodine (I2 ) species into anionic I- ones, stabilized as I- â â â I2 or I3 - complexes within the MOF cavities, occurs when I2 @UiO-n samples are left in ambient light.
RESUMO
Organic pollutants have been a significant source of concern in recent years due to their facile dissemination and harmful effects. In this work, two different metal-organic frameworks (MOFs) were initially prepared by hydrothermal treatment, namely aluminum trimesate (MIL-100(Al)) and copper trimesate (HKUST-1). These materials were subsequently submitted to a post-synthetic modification step to grow titania nanoparticles on their surface. Anatase nanoparticles with sizes around 5 nm were successfully anchored on MIL-100(Al), and the concentration of TiO2 in this sample was about 68 wt.%. This is the first time that this composite (TiO2@MIL-100(Al)) is reported in the literature. It showed an improved photocatalytic activity, removing 90% of methylene blue (k app = 1.29 h-1), 55% of sodium diclofenac (k app = 0.21 h-1), and 62% of ibuprofen (k app = 0.37 h-1) after four hours of illumination with UV-A light. A significant concentration (14 µM) of reactive oxygen species (ROS) was detected for this composite. HKUST-1 showed a structural collapse during its post-synthetic modification, leading to a non-porous material and providing fewer sites for the heterogeneous nucleation of titania. This behavior led to a low concentration of rutile nanoparticles on HKUST-1 (9 wt.%). However, the obtained composite (TiO2@HKUST) also showed an improved photoactivity compared to HKUST-1, increasing the photodegradation rates evaluated for methylene blue (0.05 h-1 vs. 0.29 h-1), sodium diclofenac (negligible vs. 0.03 h-1), and ibuprofen (0.01 h-1 vs. 0.02 h-1). This work brings new insights concerning the preparation of photocatalysts by growing semiconductor nanoparticles on trimesate-based MOFs.
RESUMO
In the present work, we aim to investigate the ability of the zirconium-based MOF-type compound UiO-66-NH2, to immobilize molecular gaseous iodine under conditions analogous to those encountered in an operating Filtered Containment Venting System (FCVS) line. Typically, the UiO-66-NH2 particles were exposed to 131I (beta and gamma emitters) and submitted to air/steam at 120 °C, under gamma irradiation (1.9 kGy h-1). In parallel to this experiment under simulated accidental conditions, the stability of the binderless UiO-66-NH2 granules under steam and gamma irradiation was investigated. In order to fit with the specifications required by typical venting systems, and to compare the efficiency of the selected MOF to porous materials commonly used by the industry, scale-up syntheses and UiO-66-NH2 millimetric-size shaping were realized. For this task, we developed an original binderless method, in order to analyze solely the efficiency of the UiO-66-NH2 material. The shaped MOF particles were then submitted separately to gamma irradiation, steam and temperature, for confirming their viability in a venting process. Their structural, textural and mechanical behaviors were characterized by the means several techniques including gas sorption, powder X-ray diffraction, infrared spectroscopy and crushing tests. Promising results were obtained to trap gaseous molecular iodine in severe accidental conditions.
RESUMO
The reactivity of the N-(1-adamantyl)acetamide ligand (L = adam) has been evaluated as precipitating agent for the hexavalent uranyl cation ([U] = 20-60 g L-1) in concentrated nitric acid aqueous solution (0.5-5 M). It results in the formation of a crystalline complex (UO2)(adam)2(NO3)2·2(adam) (1), in which the uranyl center is 8-fold coordinated to two chelating nitrate groups and two N-(1-adamantyl)acetamide (= adam) ligands through the oxygen atom of the amide function. Two other noncoordinating adam moieties are also observed in the crystal structure packing and interact through a hydrogen-bond scheme with the uranyl-centered species. A similar molecular assembly has been obtained with the plutonyl(VI) cation, in the complex (PuO2)(adam)2(NO3)2·2(adam) (2). Precipitation studies indicate high (UO2)(adam)2(NO3)2·2(adam) formation yields (up to 99%U for an L/U molecular ratio of 5/1) for HNO3 concentration in the 0.5-5 M range. However, the precipitation kinetics is rather slow and the reaction is completed after several hours (3-4 h). The calcination of the resulting solid under an air atmosphere led to the formation of the U3O8 oxide from 400 °C through a transient phase UO2 fluorite-type (from 200 °C).
RESUMO
The industrial fluorination of UO2 to UF4 is based on a complex process involving the manipulation of a large amount of HF, a very toxic and corrosive gas. We present here a safer way to accomplish this reaction utilizing ionic liquid [Bmim][PF6] as a unique reaction medium and fluoride source.