Oxygen vacancy induced room temperature ferromagnetism in Pr-doped CeO2 thin films on silicon.

Integration of functional oxides on Si substrates could open a pathway to integrate diverse devices on Si-based technology. Oxygen vacancies (Vo(··)) can strongly affect solid state properties of oxides, including the room temperature ferromagnetism (RTFM) in diluted magnetic oxides. Here, we report a systematical study on the RTFM of oxygen vacancy engineered (by Pr(3+) doping) CeO2 epitaxial thin films on Si substrates. High quality, mixed single crystalline Ce1-xPrxO2-δ (x = 0-1) solid solution films were obtained. The Ce ions in CeO2 with a fluorite structure show a Ce(4+)-dominant valence state in all films. The local crystal structures of the films were analyzed in detail. Pr doping creates both Vo(··) and PrO8-complex defects in CeO2 and their relative concentrations vary with the Pr-doping level. The RTFM properties of the films reveal a strong dependence on the relative Vo(··) concentration. The RTFM in the films initially increases with higher Pr-doping levels due to the increase of the F(+) center (Vo(··) with one occupied electron) concentration and completely disappears when x > 0.2, where the magnetic polaron concentration is considered to decline below the percolation threshold, thus long-range FM order can no longer be established. We thus demonstrate the possibility to directly grow RTFM Pr-doped CeO2 films on Si substrates, which can be an interesting candidate for potential magneto-optic or spintronic device applications.

Engineering of the chemical reactivity of the Ti/HfO2 interface for RRAM: experiment and theory.

The Ti/HfO2 interface plays a major role for resistance switching performances. However, clear interface engineering strategies to achieve reliable and reproducible switching have been poorly investigated. For this purpose, we present a comprehensive study of the Ti/HfO2 interface by a combined experimental-theoretical approach. Based on the use of oxygen-isotope marked Hf*O2, the oxygen scavenging capability of the Ti layer is clearly proven. More importantly, in line with ab initio theory, the combined HAXPES-Tof-SIMS study of the thin films deposited by MBE clearly establishes a strong impact of the HfO2 thin film morphology on the Ti/HfO2 interface reactivity. Low-temperature deposition is thus seen as a RRAM processing compatible way to establish the critical amount of oxygen vacancies to achieve reproducible and reliable resistance switching performances.