Paste Aging Spontaneously Tunes TiO2 Nanoparticles into Reproducible Electrosprayed Photoelectrodes.

In this study, the spontaneous microstructure tuning of TiO2 was observed by aging the ethanol/water TiO2 paste for up to 20 days at ambient conditions. A dynamic light scattering study reveals that it formed the outstanding reproducible TiO2 microstructure with a ∼200 nm average particle size and stabilizes in 6 to 20 days under an ambient atmosphere. Interestingly, the as-deposited day 15 sample spontaneously changed its crystallinity upon keeping the paste at ambient conditions; meanwhile the day 0 sample showed an amorphous structure. A dense, uniform, and stable TiO2 electrode was cast on a fluorine doped-tin oxide substrate using the electrospray technique. We exploit the spontaneous evolution of the TiO2 nanopowder to revisit the fabrication procedure of the TiO2 photoelectrode for dye-sensitized solar cells (DSSCs). The controlled microstructure TiO2 film was used in DSSCs, which, to the best of our knowledge, achieved the highest power conversion efficiency of 9.65% using N719 dye in sensitizing the TiO2 photoanode.

Ionic Liquid-Assisted MAPbI3 Nanoparticle-Seeded Growth for Efficient and Stable Perovskite Solar Cells.

With the rapid improvement of perovskite solar cells (PSCs), long-life operational stability has become a major requirement for their commercialization. In this work, we devised a pristine cesium-formamidinium-methylammonium (termed as CsFAMA) triple-cation-based perovskite precursor solution into the ionic liquid (IL)-assisted MAPbI3 nanoparticles (NPs) through a seeded growth approach in which the host IL-assisted MAPbI3 NPs remarkably promote high-quality perovskite films with large single-crystal domains, enhancing the device performance and stability. The power conversion efficiency (PCE) of the MAPbI3 NP-seeded growth of MAPbI3 NPs/CsFAMA-based PSCs is as high as 19.44%, which is superior to those of MAPbI3 NPs and pristine CsFAMA films as the photoactive layer (9.52 and 17.33%, respectively). The long-term light-soaking and moisture stability of IL-aided MAPbI3 NPs/CsFAMA-based devices (non-encapsulated) remain above 90 and 80%, respectively, of their initial output after 2 h of light illumination (1 sun) and 6000 h storage at ambient with a relative humidity range of 30-40%. The use of the IL-assisted MAPbI3 NP-seeded growth for PSCs is a significant step toward developing stable and reliable perovskite photovoltaic devices.

Metal Oxide Compact Electron Transport Layer Modification for Efficient and Stable Perovskite Solar Cells.

Perovskite solar cells (PSCs) have appeared as a promising design for next-generation thin-film photovoltaics because of their cost-efficient fabrication processes and excellent optoelectronic properties. However, PSCs containing a metal oxide compact layer (CL) suffer from poor long-term stability and performance. The quality of the underlying substrate strongly influences the growth of the perovskite layer. In turn, the perovskite film quality directly affects the efficiency and stability of the resultant PSCs. Thus, substrate modification with metal oxide CLs to produce highly efficient and stable PSCs has drawn attention. In this review, metal oxide-based electron transport layers (ETLs) used in PSCs and their systemic modification are reviewed. The roles of ETLs in the design and fabrication of efficient and stable PSCs are also discussed. This review will guide the further development of perovskite films with larger grains, higher crystallinity, and more homogeneous morphology, which correlate to higher stable PSC performance. The challenges and future research directions for PSCs containing compact ETLs are also described with the goal of improving their sustainability to reach new heights of clean energy production.