Biomimetically Inspired Highly Homogeneous Hydrophilization of Graphene with Poly(l-DOPA): Toward Electroconductive Coatings from Water-Processable Paints.

Water-based processing of graphene-typically considered as physicochemically incompatible with water in the macroscale-emerges as the key challenge among the central postulates of green nanotechnology. These problematic concerns are derived from the complex nature of graphene in the family of sp2-carbon nanoallotropes. Indeed, nanomaterials hidden under the common "graphene" signboard are very rich in morphological and physicochemical variants. In this work, inspired by the adhesion chemistry of mussel biomaterials, we have synthesized novel, water-processable graphene-polylevodopa (PDOPA) hybrids. Graphene and PDOPA were covalently amalgamated via the "growth-from" polymerization of l-DOPA (l-3,4-dihydroxyphenylalanine) monomer in air, yielding homogeneously PDOPA-coated (23 wt %) (of thickness 10-20 nm) hydrophilic flakes. The hybrids formed >1 year stable and water-processable aqueous dispersions and further conveniently processable paints of viscosity 0.4 Pa·s at 20 s-1 and a low yield stress τ0 up to 0.12 Pa, hence exhibiting long shelf-life stability and lacking sagging after application. Demonstrating their applicability, we have found them as surfactant-like nanoparticles stabilizing the larger, pristine graphene agglomerates in water in the optimized graphene/graphene-PDOPA weight ratio of 9:1. These characteristics enabled the manufacture of conveniently paintable coatings of low surface resistivity of 1.9 kΩ sq-1 (0.21 Ω·m) which, in turn, emerge as potentially applicable in textronics, radar-absorbing materials, or electromagnetic interference shielding.

The True Amphipathic Nature of Graphene Flakes: A Versatile 2D Stabilizer.

The fundamental colloidal properties of pristine graphene flakes remain incompletely understood, with conflicting reports about their chemical character, hindering potential applications that could exploit the extraordinary electronic, thermal, and mechanical properties of graphene. Here, the true amphipathic nature of pristine graphene flakes is demonstrated through wet-chemistry testing, optical microscopy, electron microscopy, and density functional theory, molecular dynamics, and Monte Carlo calculations, and it is shown how this fact paves the way for the formation of ultrastable water/oil emulsions. In contrast to commonly used graphene oxide flakes, pristine graphene flakes possess well-defined hydrophobic and hydrophilic regions: the basal plane and edges, respectively, the interplay of which allows small flakes to be utilized as stabilizers with an amphipathic strength that depends on the edge-to-surface ratio. The interactions between flakes can be also controlled by varying the oil-to-water ratio. In addition, it is predicted that graphene flakes can be efficiently used as a new-generation stabilizer that is active under high pressure, high temperature, and in saline solutions, greatly enhancing the efficiency and functionality of applications based on this material.

Inversion Algorithm of Fiber Bragg Grating for Nanofluid Flooding Monitoring.

In the current study, we developed an adaptive algorithm that can predict oil mobilization in a porous medium on the basis of optical data. Associated mechanisms based on tuning the electromagnetic response of magnetic and dielectric nanoparticles are also discussed. This technique is a promising method in rational magnetophoresis toward fluid mobility via fiber Bragg grating (FBG). The obtained wavelength shift due to Fe3O4 injection was 75% higher than that of dielectric materials. This use of FBG magneto-optic sensors could be a remarkable breakthrough for fluid-flow tracking in oil reservoirs. Our computational algorithm, based on piecewise linear polynomials, was evaluated with an analytical technique for homogeneous cases and achieved 99.45% accuracy. Theoretical values obtained via coupled-mode theory agreed with our FBG experiment data of at a level of 95.23% accuracy.

Microwave conductivity of sorted CNT assemblies.

Recent progress with tailored growth and post-process sorting enables carbon nanotube (CNT) assemblies with predominantly metallic or semi-conducting concentrations. Cryogenic and microwave measurements performed here show transport dimensionality and overall order increasing with increasing metallic concentration, even in atmospheric doping conditions. By 120 GHz, the conductivity of predominantly semi-conducting assemblies grew to 400% its DC value at an increasing growth rate, while other concentrations a growth rate that tapered off. A generalized Drude model fits to the different frequency dependent behaviors and yields useful quality control parameters such as plasma frequency, mean free path, and degree of localization. As one of the first demonstrations of waveguides fabricated from this material, sorted CNTs from both as-made and post-process sources were inserted into sections of practical micro-strip. With both sources, sorted CNT micro-strip increasingly outperformed the unsorted with increasing frequency-- illustrating that sorted CNT assemblies will be important for high frequency applications.

Reflection and transmission coefficient of yttrium iron garnet filled polyvinylidene fluoride composite using rectangular waveguide at microwave frequencies.

The sol-gel method was carried out to synthesize nanosized Yttrium Iron Garnet (YIG). The nanomaterials with ferrite structure were heat-treated at different temperatures from 500 to 1000 °C. The phase identification, morphology and functional groups of the prepared samples were characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR), respectively. The YIG ferrite nanopowder was composited with polyvinylidene fluoride (PVDF) by a solution casting method. The magnitudes of reflection and transmission coefficients of PVDF/YIG containing 6, 10 and 13% YIG, respectively, were measured using rectangular waveguide in conjunction with a microwave vector network analyzer (VNA) in X-band frequencies. The results indicate that the presence of YIG in polymer composites causes an increase in reflection coefficient and decrease in transmission coefficient of the polymer.

Carbon nanotubes fibres/aluminium-NiZnFe2O4 based electromagnetic transmitter for improved magnitude versus offset (MVO) in a scaled marine environment.

In seabed logging the magnitude of electromagnetic (EM) waves for the detection of a hydrocarbon reservoir in the marine environment is very important. Having a strong EM source for exploration target 4000 m below the sea floor is a very challenging task. A new carbon nanotubes (CNT) fibres/aluminium based EM transmitter is developed and NiZn ferrite as magnetic feeders was used in a scaled tank to evaluate the presence of oil. Resistive scaled tank experiments with a scale factor of 2000 were carried out. X-ray Diffraction (XRD), Raman Spectroscopy and Field Emission Scanning Electron Microscope (FESEM) were done to characterize the synthesized magnetic feeders. Single phase Ni0.76Mg0.04Zn0.2Fe2O4, obtained by the sol-gel method and sintered at 700 degrees C in air, has a [311] major peak. FESEM results show nanoparticles with average diameters of 17-45 nm. Samples which have a high Q-factor (approximately 50) was used as magnetic feeders for the EM transmitter. The magnitude of the EM waves of this new EM transmitter increases up to 400%. A curve fitting method using MATLAB software was done to evaluate the performance of the new EM transmitter. The correlation value with CNT fibres/aluminium-NiZnFe2O4 base transmitter shows a 152.5% increase of the magnetic field strength in the presence of oil. Modelling of the scale tank which replicates the marine environment was done using the Finite Element Method (FEM). In conclusion, FEM was able to delineate the presence of oil with greater magnitude of E-field (16.89%) and the B field (4.20%) due to the new EM transmitter.

Encapsulation of Ni0.8Zn0.2Fe2O4 single crystals in multiwall carbon nanotubes.

Magnetic nanoparticles in the hollow region of carbon nanotubes have attraction due to their changing physical electrical and magnetic properties. Nickel zinc ferrite plays an important role in many applications due to its superior magnetic properties. Ni0.8Zn0.2Fe2O4 single crystals were encapsulated in multiwall carbon nanotubes (MWCNTs). The magnetic nano crystals were prepared using a sol-gel self combustion method at the sintering temperature of 750 degrees C and were characterized by XRD, FESEM, TEM and VSM. Initial permeability, Q-factor and relative loss factor were measured by impedance vector network analyzer. XRD patterns were used for the phase identification. FESEM images show morphology and dimensions of the grains of Ni0.8Zn0.2Fe2O4 single crystals and Ni0.8Zn0.2Fe2O4 single crystals in MWCNTs. TEM images were used to investigate single crystal and encapsulation of Ni0.8Zn0.2Fe2O4 single crystals in the MWCNTs. VSM results confirmed super paramagnetic behaviour of encapsulated Ni0.8Zn0.2Fe2O4 single crystals. It was also attributed that encapsulated Ni0.8Zn0.2Fe2O4 single crystals in MWCNTs showed a higher initial permeability (51.608), Q-factor (67.069), and low loss factor (0.0002) as compared to Ni0.8Zn0.2Fe2O4 single crystals. The new encapsulated Ni0.8Zn0.2Fe2O4 single crystals in the MWCNTs may have potential applications in electronic and medical industries.

Synthesis and characterization of YBa2Cu3O7(Y123) via sol-gel method for development of superconducting quantum interference device magnetometer.

Electromagnetic (EM) waves transmitted by Horizontal Electric Dipole (HED) source to detect contrasts in subsurface resistivity termed Seabed Logging (SBL) is now an established method for hydrocarbon exploration. However, currently used EM wave detectors for SBL have several challenges including the sensitivity and its bulk size. This work exploits the benefit of superconductor technology in developing a magnetometer termed Superconducting Quantum Interference Device (SQUID) which can potentially be used for SBL. A SQUID magnetometer was fabricated using hexagon shape-niobium wire with YBa2Cu37O, (YBCO) as a barrier. The YBa2Cu37O, samples were synthesized by sol-gel method and were sintered using a furnace and conventional microwave oven. The YBCO gel was dried at 120 degrees C in air for 72 hours. It was then ground and divided into 12 parts. Four samples were sintered at 750 degrees C, 850 degrees C, 900 degrees C, and 950 degrees C for 12 hours in a furnace to find the optimum temperature. The other eight samples were sintered in a microwave with 1100 Watt (W) with a different sintering time, 5, 15, 45 minutes, 1 hour, 1 hour 15 minutes, 1 hour 30 minutes, 1 hour 45 minutes and 2 hours. A DEWAR container was designed and fabricated using fiberglass material. It was filled with liquid nitrogen (LN2) to ensure the superconducting state of the magnetometer. XRD results showed that the optimum sintering temperature for the formation of orthorhombic Y-123 phase was at 950 degrees C with the crystallite size of 67 nm. The morphology results from Field Emission Scanning Electron Microscopy (FESEM) showed that the grains had formed a rod shape with an average diameter of 60 nm. The fabricated SQUID magnetometer was able to show an increment of approximately 249% in the intensity of the EM waves when the source receiver offset was one meter apart.

Observation of a cubical-like microstructure of strontium iron garnet and yttrium iron garnet prepared via sol-gel technique.

This is our initial response towards preparation of nano-inductors garnet for high operating frequencies strontium iron garnet (Sr3Fe5O12) denoted as SrIG and yttrium iron garnet (Y3Fe5O12) denoted as YIG. The garnet nano crystals were prepared by novel sol-gel technique. The phase and crystal structure of the prepared samples were identified by using X-ray diffraction analysis. SEM images were done to reveal the surface morphology of the samples. Raman spectra was taken for yttrium iron garnet (Y3Fe5O12). The magnetic properties of the samples namely initial permeability (micro), relative loss factor (RLF) and quality factor (Q-Factor) were done by using LCR meter. From the XRD profile, both of the Y3Fe5O12 and Sr3Fe5O12 samples showed single phase garnet and crystallization had completely occurred at 900 degrees C for the SrIG and 950 degrees C for the YIG samples. The YIG sample showed extremely low RLF value (0.0082) and high density 4.623 g/cm3. Interesting however is the high Q factor (20-60) shown by the Sr3Fe5O12 sample from 20-100 MHz. This high performance magnetic property is attributed to the homogenous and cubical-like microstructure. The YIG particles were used as magnetic feeder for EM transmitter. It was observed that YIG magnetic feeder with the EM transmitter gave 39% higher magnetic field than without YIG magnetic feeder.

Morphology and magnetic characterisation of aluminium substituted yttrium-iron garnet nanoparticles prepared using sol gel technique.

Aluminum substituted yttrium iron garnet nano particles with compositional variation of Y(3.0-x) A1(x)Fe5O12, where x = 0.0, 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 were prepared using sol gel technique. The X-ray diffraction results showed that the best garnet phase appeared when the sintering temperature was 800 degrees C. Nano-crystalline particles with high purity and sizes ranging from 20 to 100 nm were obtained. It was found that the aluminum substitution had resulted in a sharp fall of the d-spacing when x = 2, which we speculated is due to the preference of the aluminum atoms to the smaller tetrahedron and octahedron sites instead of the much larger dodecahedron site. High resolution transmission electron microscope (HRTEM) and electron diffraction (ED) patterns showed single crystal nanoparticles were obtained from this method. The magnetic measurement gave moderate values of initial permeability; the highest value of 5.3 was shown by sample Y3Fe5O12 at more than 100 MHz which was attributed to the morphology of the microstructure which appeared to be homogeneous. This had resulted in an easy movement of domain walls. The substitution of aluminum for yttrium is speculated to cause a cubic to rhombodedral structural change and had weakened the super-exchange interactions thus a fall of real permeability was observed. This might have created a strain in the sub-lattices and had subsequently caused a shift of resonance frequencies to more than 1.8 GHz when x > 0.5.