Gas response behaviour and photochemistry of borondiketonate in acrylic polymer matrices for sensing applications.

The fluorescent spectra in combination with gas response behavior of acrylic polymers doped with dibenzoyl(methanato)boron difluoride (DBMBF2) were studied by fluorescence spectroscopy and time-resolved fluorescence lifetime. The role of acrylic matrix polarity upon the fluorescence spectra and fluorescence lifetime was analyzed. Changes in emission of the dye doped polymers under exposure to toluene, n-hexane and ethanol were monitored. The fluorescence lifetimes were measured for the singlet excited state as well as the exciplex formed between DBMBF2 and toluene. A reduction of the transition energy to the first singlet-excited state in the four polymers was observed, compared to solution. Reversible exciplex formation, viz. a red shifted fluorescence emission was perceived when exposing the polymers to toluene, while for hexane and ethanol only reversible reduction of the fluorescence occurred. Longer singlet and shorter exciplex lifetimes were observed for non-polar matrixes. The latter mechanism is explained in function of the lower charge transfer character of the exciplex in non-polar matrixes. Additionally, the quantum yield of the dye in the polymer matrix increased almost seventh-fold compared to values for solution.

Single Layer Broadband Anti-Reflective Coatings for Plastic Substrates Produced by Full Wafer and Roll-to-Roll Step-and-Flash Nano-Imprint Lithography.

Anti-reflective coatings (ARCs) are used to lower the reflection of light on the surface of a substrate. Here, we demonstrate that the two main drawbacks of moth eye-structured ARCs-i.e., the lack of suitable coating materials and a process for large area, high volume applications-can be largely eliminated, paving the way for cost-efficient and large-scale production of durable moth eye-structured ARCs on polymer substrates. We prepared moth eye coatings on polymethylmethacrylate (PMMA) and polycarbonate using wafer-by-wafer step-and-flash nano-imprint lithography (NIL). The reduction in reflection in the visible field achieved with these coatings was 3.5% and 4.0%, respectively. The adhesion of the coating to both substrates was good. The moth eye coating on PMMA demonstrated good performance in three prototypical accelerated ageing tests. The pencil hardness of the moth eye coatings on both substrates was <4B, which is less than required for most applications and needs further optimization. Additionally, we developed a roll-to-roll UV NIL pilot scale process and produced moth eye coatings on polyethylene terephthalate (PET) at line speeds up to two meters per minute. The resulting coatings showed a good replication of the moth eye structures and, consequently, a lowering in reflection of the coated PET of 3.0%.

Fabrication of transistors on flexible substrates: from mass-printing to high-resolution alternative lithography strategies.

In this report, the development of conventional, mass-printing strategies into high-resolution, alternative patterning techniques is reviewed with the focus on large-area patterning of flexible thin-film transistors (TFTs) for display applications. In the first part, conventional and digital printing techniques are introduced and categorized as far as their development is relevant for this application area. The limitations of conventional printing guides the reader to the second part of the progress report: alternative-lithographic patterning on low-cost flexible foils for the fabrication of flexible TFTs. Soft and nanoimprint lithography-based patterning techniques and their limitations are surveyed with respect to patterning on low-cost flexible foils. These show a shift from fabricating simple microlense structures to more complicated, high-resolution electronic devices. The development of alternative, low-temperature processable materials and the introduction of high-resolution patterning strategies will lead to the low-cost, self-aligned fabrication of flexible displays and solar cells from cheaper but better performing organic materials.

Double-layer imprint lithography on wafers and foils from the submicrometer to the millimeter scale.

In this paper, a thermal imprint technique, double-layer nanoimprint lithography (dlNIL), is introduced, allowing complete filling of features in the dimensional range of submicrometer to millimeter. The imprinting and filling quality of dlNIL was studied on Si substrates as a model system and compared to results obtained with regular NIL (NIL) and reverse NIL (rNIL). Wavy foils were imprinted with NIL, rNIL and dlNIL and the patterning results compared and discussed. With dlNIL, a new application possibility was introduced in which two different resists having, for example, a different etch resistance to a certain plasma were combined within one imprint step. dlNIL allows extension to many resist combinations for tailored nanostructure fabrication.

Effect of water content on the structural reorganization and elastic properties of biopolymer films: a comparative study.

In this work, the effect of water uptake on the structural reorganization and elastic properties of three types of biopolymer films was studied. The water-biopolymer interaction for hydroxypropyl cellulose (HPC), gelatin, and cassava starch films prepared from aqueous solutions was studied and compared using Fourier-transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), X-ray diffraction, dynamic vapor sorption (DVS), and dynamic mechanical thermal analysis with humidity generator and controller (DMTA) techniques. The FTIR spectral variations due to the water sorption were generalized into two-dimensional (2D) correlation graphs for each biopolymer, and the effect of water on the molecular conformation was compared. The water sorption isotherms were fitted with Guggenheim-Anderson-De Boer (GAB) and D'Arcy and Watt models. The water content in the mono- and multilayers predicted by both models for each biopolymer was discussed and compared. The correlation of the fitted data obtained from the sorption isotherms to the DMTA data allowed us to conclude that the elastic properties of the HPC films depended on the total water content in contrast to the elastic properties of the gelatin and cassava starch films, which decrease only with the appearance of multilayer water.