This paper reports on recycling of industrial wastes (three pharmaceutical industrial sludges) into environmental friendly value-added materials. Stabilization/Solidification (S/S or bricks) process was applied to make a safer way for the utilization of pharmaceutical waste. The additives in this study include binders (cement, lime and bentonite) and strengthening material (pulverized fuel ash (PFA), silica fume and quarry dust) was used at different compositions. Bricks were cured for 28 days, and the following analysis-like compressive strength, leachability of heavy metals, mineralogical phase identity by X-ray diffraction (XRD) spectroscopy, Fourier transform infrared spectroscopy (FTIR) and thermal behaviour by thermogravimetric-differential thermal analysis (TG-DTA) had done. All the bricks were observed to achieve the standard compressive strength as required for construction according to BIS standards. Metal concentration in the leachate has reached the dischargeable limits according to Brazilian standards. Results of this study demonstrate that production of bricks is a promising and achievable productive use of pharmaceutical sludge.
Assuntos
Resíduos Industriais , Força Compressiva , Materiais de Construção/análise , Indústria Farmacêutica , Metais Pesados/química , Reciclagem/métodos , Esgotos , Difração de Raios XRESUMO
In the present paper, the performance of electrocoagulation (EC) for the treatability of mixed metals (chromium (Cr), copper (Cu), lead (Pb), nickel (Ni), and zinc (Zn)) from metal plating industrial wastewater (EPW) has been investigated. The study mainly focused on the affecting parameters of EC process, such as electrode material, initial pH, distance between electrodes, electrode size, and applied voltage. The pH 8 is observed to be the best for metal removal. Fe-Fe electrode pair with 1-cm inter-electrode distance and electrode surface area of 40 cm(2) at an applied voltage of 8 V is observed to more efficient in the metal removal. Experiments have shown that the maximum removal percentage of the metals like Cr, Ni, Zn, Cu, and Pb are reported to be 96.2, 96.4, 99.9, 98, and 99.5 %, respectively, at a reaction time of 30 min. Under optimum conditions, the energy consumption is observed to be 51.40 kWh/m(3). The method is observed to be very effective in the removal of metals from electroplating effluent.