RESUMO
In this paper, a series of eutectic hydrated salts was obtained by mixing Na2HPO4·12H2O (DHPD) with K2HPO4·3H2O (DHPT) in different proportions. With the increase in the content of DHPT, the phase transition temperature and melting enthalpy of eutectic hydrated salts decreased gradually. Moreover, the addition of appropriate deionized water improved the thermal properties of eutectic hydrated salts. Colloidal silicon dioxide (SiO2) was selected as the support carrier to adsorb eutectic hydrated salts, and the maximum content of eutectic hydrated salts in composite PCMs was 70%. When the content of the nucleating agent (Na2SiO3·9H2O) was 5%, the supercooling degree of composite PCMs was reduced to the minimum of 1.2 °C. The SEM and FT-IR test results showed that SiO2 and eutectic hydrated salts were successfully combined, and no new substances were formed. When the content of DHPT was 3%, the phase transition temperature and melting enthalpy of composite PCMs were 26.5 °C and 145.3 J/g, respectively. The results of thermogravimetric analysis and heating-cooling cycling test proved that composite PCMs had good thermal reliability and stability. The application performance of composite PCMs in prefabricated temporary houses was investigated numerically. The results indicated that PCM panels greatly increased the Grade I thermal comfort hours and reduced energy consumption. Overall, the composite PCM has great development potential building energy conservation.
RESUMO
The melting points of the phase change materials (PCMs) incorporated into the walls of buildings should be within the human thermal comfort temperature range. In this paper, 15 wt.% of MgCl2·6H2O was mixed with CaCl2·6H2O to obtain the eutectic with a melting point of 23.9 °C. SrCl2·6H2O suppresses the supecooling of the eutectic. The combination with expanded perlite (EP) via the impregnation method overcomes the phase separation and liquid leakage of the CaCl2â6H2O-MgCl2â6H2O mixture. The composite PCM is form-stable with the maximum loading mass fraction up to 50 wt.% and latent heat of 73.55 J/g. EP also significantly reduces the thermal conductivity of the CaCl2â6H2O-MgCl2â6H2O from 0.732 to 0.144 W/(m·K). The heating-cooling cycling test reveals that the composite PCM is thermally stable. The cheap eutectic salt hydrate, with little supercooling, no phase separation and liquid leakage, low thermal conductivity and good thermal reliability, show great potential as envelope materials to save energy consumption in buildings.
RESUMO
Here we demonstrate the mechanical properties, thermal conductivity, and thermal energy storage performance of construction elements made of cement and form-stable PCM-Rubitherm® RT 28 HC (RT28)/expanded perlite (EP) composite phase change materials (PCMs). The composite PCMs were prepared by adsorbing RT28 into the pores of EP, in which the mass fraction of RT28 should be limited to be no more than 40 wt %. The adsorbed RT28 is observed to be uniformly confined into the pores of EP. The phase change temperatures of the RT28/EP composite PCMs are very close to that of the pure RT28. The apparent density and compression strength of the composite cubes increase linearly with the mass fraction of RT28. Compared with the thermal conductivity of the boards composed of cement and EP, the thermal conductivities of the composite boards containing RT28 increase by 15%-35% with the mass fraction increasing of RT28. The cubic test rooms that consist of six boards were built to evaluate the thermal energy storage performance, it is found that the maximum temperature different between the outside surface of the top board with the indoor temperature using the composite boards is 13.3 °C higher than that of the boards containing no RT28. The thermal mass increase of the built environment due to the application of composite boards can contribute to improving the indoor thermal comfort and reducing the energy consumption in the buildings.