[Effectiveness and characteristics of treating algae-laden raw water by stocking silver carp].

To reduce the negative effect of algae on conventional water treatment, a full-scale research of removing algae from algae-laden raw water by stocking filter-feeding silver carp was processed. After the pretreatment in a presedimentation tank with silver carp, the concentration of phytoplankton, the biomass of cyanobacteria and Microsystis flos-aquae in algae-laden raw water with Microsystis flos-aquae its dominant species decreased 61.8%, 76.1% and 78.2% respectively. This effective decrease of algae load on conventional process created favorable conditions for water treatment. Analysis indicates that food habit of silver carp and algae size are two causes of different removal efficiency between cyanobacteria and green algae. The results show that biomanipulation of silver carp is applicable for treating algae-laden raw water in which colonial cyanobacteria is dominant.

[Analysis of the characteristics of corrosion scale in drinking water distribution systems].

Scanning electron microscopy, X-ray fluorescence spectroscopy, X-ray diffraction and X-ray photoelectron spectroscopy were used to analyze the microstructure, chemical composition, crystalline structure and compound constitute of the corrosion scale from cast iron pipe and galvanized steel pipe in drinking water distribution systems. The outer of the corrosion scale was compact, while the inner was porous. Iron was the primary chemical element of the corrosion scale, and the composition of the scale was iron compounds. The outer scale were ferric compounds such as alpha-FeOOH, gamma-FeOOH, alpha-Fe2O3, gamma-Fe2O3, FeCl3, while the inner were ferrous compounds such as Fe3O4, FeCl2, FeCO3. The characteristics of the corrosion scale was lying on hydraulic conditions and water quality in distribution systems, and the characteristics of iron pipe materials.

[Analysis of influence factors and control methods on iron release phenomenon in drinking water distribution system].

Variation rule of iron in drinking water distribution systems was studied, and it was found that the iron released from the scale to the bulk water was the primary reason for iron overstep. The main chemical composition of the scale in cast iron pipe and galvanized steel pipe was iron in a northern city in China. In the drinking water distribution systems, when the value of dissolved oxygen or chlorine residual was low, the iron release phenomenon was severe. The reason for that was the passivation layer of the corrosion scale was destroyed in reductive condition and the result was a great amount of iron in ferrous form was released. According to the research results, the control methods for iron release and 'red water' phenomenon were indicated.

Iron stability in drinking water distribution systems in a city of China.

A field study on the estimation and analysis of iron stability in drinking water distribution system was carried out in a city of China. The stability of iron ion was estimated by pC-pH figure. It was found that iron ion was unstable, with a high Fe(OH)3 precipitation tendency and obvious increase in turbidity. The outer layer of the corrosion scale was compact, while the inner core was porous. The main composition of the scale was iron, and the possible compound constitutes of the outer scale were a-FeOOH, gamma-FeOOH, alpha-Fe2O3, gamma-Fe2O3, FeCl3, while the inner were Fe3O4, FeCl2, FeCO3. According to the characteristics of the corrosion scale, it was thought that the main reason for iron instability was iron release from corrosion scale. Many factors such as pipe materials, dissolved oxygen and chlorine residual affect iron release. Generally, higher iron release occurred with lower dissolved oxygen or chlorine residual concentration, while lower iron release occurred with higher dissolved oxygen or chlorine residual concentration. The reason was considered that the passivated out layer of scale of ferric oxide was broken down by reductive reaction in a condition of low oxidants concentration, which would result more rapid corrosion of the pipe and red water phenomenon.