Pyrene-Benzimidazole Derivatives as Novel Blue Emitters for OLEDs.

Three novel small organic heterocyclic compounds: 2-(1,2-diphenyl)-1H-benzimidazole-7-tert-butylpyrene (compound A), 1,3-di(1,2-diphenyl)-1H-benzimidazole-7-tert-butylpyrene (compound B), and 1,3,6,8-tetra(1,2-diphenyl)-1H-benzimidazolepyrene (compound C) were synthesized and characterized for possible applications as blue OLED emitters. The specific molecular design targeted decreasing intermolecular aggregation and disrupting crystallinity in the solid-state, in order to reduce dye aggregation, and thus obtain efficient pure blue photo- and electroluminescence. Accordingly, the new compounds displayed reasonably high spectral purity in both solution- and solid-states with average CIE coordinates of (0.160 ± 0.005, 0.029 ± 0.009) in solution and (0.152 ± 0.007, 0.126 ± 0.005) in solid-state. These compounds showed a systematic decrease in degree of crystallinity and intermolecular aggregation due to increasing steric hindrance, as revealed using powder X-ray diffraction analysis and spectroscopic studies. An organic light-emitting diode (OLED) prototype fabricated using compound B as the non-doped emissive layer displayed an external quantum efficiency (EQE) of 0.35 (±0.04)% and luminance 100 (±6) cd m-2 at 5.5 V with an essentially pure blue electroluminescence corresponding to CIE coordinates of (0.1482, 0.1300). The highest EQE observed from this OLED prototype was 4.3 (±0.3)% at 3.5 V, and the highest luminance of 290 (±10) cd m-2 at 7.5 V. These values were found comparable to characteristics of the best pure blue OLED devices based on simple fluorescent small-molecule organic chromophores.

Pyrenylpyridines: Sky-Blue Emitters for Organic Light-Emitting Diodes.

A novel sky-blue-emitting tripyrenylpyridine derivative, 2,4,6-tri(1-pyrenyl)pyridine (2,4,6-TPP), has been synthesized using a Suzuki coupling reaction and compared with three previously reported isomeric dipyrenylpyridine (DPP) analogues (2,4-di(1-pyrenyl)pyridine (2,4-DPP), 2,6-di(1-pyrenyl)pyridine (2,6-DPP), and 3,5-di(1-pyrenyl)pyridine (3,5-DPP)). As revealed by single-crystal X-ray analysis and computational simulations, all compounds possess highly twisted conformations in the solid state with interpyrene torsional angles of 42.3°-57.2°. These solid-state conformations and packing variations of pyrenylpyridines could be correlated to observed variations in physical characteristics such as photo/thermal stability and spectral properties, but showed only marginal influence on electrochemical properties. The novel derivative, 2,4,6-TPP, exhibited the lowest degree of crystallinity as revealed by powder X-ray diffraction analysis and formed amorphous thin films as verified using grazing-incidence wide-angle X-ray scattering. This compound also showed high thermal/photo stability relative to its disubstituted analogues (DPPs). Thus, a nondoped organic light-emitting diode (OLED) prototype was fabricated using 2,4,6-TPP as the emissive layer, which displayed a sky-blue electroluminescence with Commission Internationale de L'Eclairage (CIE) coordinates of (0.18, 0.34). This OLED prototype achieved a maximum external quantum efficiency of 6.0 ± 1.2% at 5 V. The relatively high efficiency for this simple-architecture device reflects a good balance of electron and hole transporting ability of 2,4,6-TPP along with efficient exciton formation in this material and indicates its promise as an emitting material for design of blue OLED devices.

Three-Dimensional Morphology Control Yielding Enhanced Hole Mobility in Air-Processed Organic Photovoltaics: Demonstration with Grazing-Incidence Wide-Angle X-ray Scattering.

Polymer organic photovoltaic (OPV) device performance is defined by the three-dimensional morphology of the phase-separated domains in the active layer. Here, we determine the evolution of morphology through different stages of tailored solvent vapor and thermal annealing techniques in air-processed poly(3-hexylthiophene-2,5-diyl)/phenyl-C61-butyric acid methyl ester-based OPV blends. A comparative evaluation of the effect of solvent type used for vapor annealing was performed using grazing-incidence wide-angle X-ray scattering, atomic force microscopy, and UV-vis spectroscopy to probe the active-layer morphology. A nonhalogenated orthogonal solvent was found to impart controlled morphological features within the exciton diffusion length scales, enhanced absorbance, greater crystallinity, increased paracrystalline disorder, and improved charge-carrier mobility. Low-boiling, fast-diffusing isopropanol allowed the greatest control over the nanoscale structure of the solvents evaluated and yielded a cocontinuous morphology with narrowed domains and enhanced paths for the charge carrier to reach the anode.

Model System Study of Environmentally Persistent Free Radicals Formation in a Semiconducting Polymer Modified Copper Clay System at Ambient Temperature.

This paper systematically investigates how environmentally persistent free radicals (EPFRs) are formed in a phenol contaminated model soil. Poly-p-phenylene (PPP) modified and copper-loaded montmorillonite (MMT) clays were developed and used as models of soil organic matter and the clay mineral component, respectively, with phenol being employed as a precursor pollutant. The polymer modification of the clays was carried out via surface-confined Kumada catalyst-transfer chain-growth polymerization. The presence and location of the polymer were confirmed by a combination of thermogravimetric analysis (TGA), Raman spectroscopy, and X-ray diffraction data. EPFRs were formed by the Cu(II)-clay (Cu(II)CaMMT) and poly-p-phenylene-Cu(II)clay (PPP-Cu(II)CaMMT) composite systems under environmentally relevant conditions. The g-factor and concentration of EPFRs formed by the Cu(II)CaMMT and PPP-Cu(II)CaMMT systems were found to be 2.0034 and 1.22 × 1017 spins/g and 2.0033 and 1.58 × 1017spins/g, respectively. These g-factors are consistent with the formation of phenoxyl radicals. Extended X-Ray absorption fine structure (EXAFS) analysis shows that there are distinct differences in the local stuctures of the phenoxyl radicals associated with only the Cu(II) redox centers and those formed in the presences of the PPP polymer. X-ray absorption near edge spectroscopy (XANES) results provided evidence for the reduction of Cu(II) to Cu(I) in the EPFR forming process. The 1/e lifetimes of the formed EPFRs revealed a decay time of ~20 h for the Cu(II)CaMMT system and a two-step decay pattern for the PPP-Cu(II)CaMMT system with decay times of ~13.5 h and ~55.6 h. Finally, the generation of reactive oxygen species (hydroxyl radical; •OH) by these clay systems was also investigated, with higher concentrations of •OH detected for the phenol-dosed Cu(II)CaMMT and PPP-Cu(II)CaMMT systems, compared to the non-EPFR containing undosed PPP-Cu(II)CaMMT system.

Preparation of gradient polyacrylate brushes in microchannels.

Gradient poly(2-hydroxyethyl methacrylate) brushes were synthesized by surface-initiated atom transfer radical polymerization (ATRP) confined within a microfluidic system on a silicon wafer. For ATRP, surface initiator, 11-((2-bromo, 2-methyl) propionyloxy) undecyltrichlorosilane (BUC), was synthesized, and allowed to self-assemble in a monolayer on the Si wafer, as analyzed by XPS to confirm the presence of an ester group of BUC. A solution containing 2-hydroxyethylmethacrylate, Cu catalyst, and bipyridin was allowed to flow in a microchannel and polymerize, resulting in the brushes with a gradient of thickness on the Si wafer. Using ellipsometry and ATR-IR, we verified the gradients of well established brushes on the Si wafer. AFM and contact angle data showed that wettability of the brushes did not exhibit a linear relationship with hydrophilicity.

Supramolecular ordering of tripod dyes at the air/water interface.

Monolayers of 2-(3,4,5-(trisdodecyloxyl)phenyl)[1,3,4]oxadiazole based "tripod" dye, P2G, has been studied at the air/water interface with in situ X-ray reflectivity. Compression of the disordered Langmuir-Blodgett monolayer film induces a transition to a unique ordered phase, representing a supramolecular assembly with a unique spatial distribution and orientation of the molecules. At low pressure, the molecules having face-on orientation are interdigitated by the three arms. After first transition in the pi-A isotherm, the molecular conformation is turned into an edge-on orientation, where the molecules are self-assembled into supramolecular structures.