Mechanical Properties of the Carbon Nanotube Modified Epoxy-Carbon Fiber Unidirectional Prepreg Laminates.

The effect of plasma treatment of the multi-walled carbon nanotube (MWCNT) surface on the fracture toughness of an aerospace grade epoxy resin and its unidirectional (UD) carbon fiber prepreg laminates has attracted scientific interest. A prepreg route eliminates the possible risk of carbon nanotube filtration by unidirectional carbon fibers. X-ray photoelectron spectroscopy results suggested that oxygen atom concentration at the nanotube surface was increased from 0.9% to 3.7% after plasma modification of the carbon nanotubes. A low number (up to 0.5 wt.%) of MWCNTs was added to epoxy resin and their carbon fiber prepreg laminates. Transmission electron micrographs revealed that the plasma treatment resulted in a better dispersion and distribution of MWCNTs in the epoxy resin. Plasma-treated MWCNTs resulted in a more pronounced resistance to the crack propagation of epoxy resin. During the production of the reference and nanotube-modified prepregs, a comparable prepreg quality was achieved. Neat nanotubes agglomerated strongly in the resin-rich regions of laminates lowering the interlaminar fracture toughness under mode I and mode II loading. However, plasma-treated nanotubes were found mostly as single particles in the resin-rich regions of laminates promoting higher energy dissipation during crack propagation via a CNT pull-out mechanism.

Effect of Curing Agent on the Compressive Behavior at Elevated Test Temperature of Carbon Fiber-Reinforced Epoxy Composites.

The aim of the underlying research is to understand the effect of elevated test temperatures on the mechanical properties of carbon fiber-reinforced laminates based on three different hardeners. A high-temperature stable adhesive was developed for the end tabs of the specimen. Bifunctional bisphenol A diglycidyl ether (DGEBA) epoxy cured with triethylenetetramine (TETA), isophorone diamine (IPDA), and 4,4'-diaminodiphenylsulfone (DDS) were cured and tested in a Celanese compressive test up to 250 °C. A model by Feih was applied, and sufficient accordance (R2 > 97%) with the compressive data was found. We showed that the network density and the chemical structure of the thermoset network influenced the compressive behavior.