RESUMO
To investigate the influence of different rhenium contents on the helium desorption behavior in tungsten-rhenium alloys, pure tungsten and tungsten-rhenium alloys were irradiated with helium under the same conditions. All irradiated samples were characterized using TDS and DBS techniques. The results indicate that the addition of rhenium can reduce the total helium desorption quantity in tungsten-rhenium alloys and slightly accelerate the reduction in the concentration of vacancy-type defects accompanying helium dissociation. The desorption activation energy of helium is approximately 2 eV at the low-temperature peak (~785 K) and about 4 eV at the high-temperature peak (~1475 K). An increase in rhenium content causes the desorption peak to shift towards higher temperatures (>1473 K), which is attributed to the formation of the stable complex structures between rhenium and vacancies. Besides, the migration of He-vacancy complexes towards traps and dynamic annealing processes both lead to the recovery of vacancy-type defects, resulting in a decrease in the positron annihilation S parameters.
RESUMO
The oxidation behavior of body-centered cubic (bcc) structure Cr20Mn17Fe18Ta23W22 refractory high-entropy alloy (RHEA) and the microdefects induced by hydrogen ions before and after oxidation were investigated. The results revealed that compared with oxidizing Cr20Mn17Fe18Ta23W22 at 800 °C (6.7 °C/min) for 4 h (ST3, Ar:O2 = 3:1), the heating procedure of oxidizing Cr20Mn17Fe18Ta23W22 at 300 °C (6 °C/min) for 2 h and then increased to 800 °C (5 °C/min) for 4 h is more conducive to the production of oxides without spalling on the surface, i.e., HT1 (Ar:O2 = 1:1), HT2 (Ar:O2 = 2:1) and HT3 (Ar:O2 = 3:1) samples. The oxidation of Cr20Mn17Fe18Ta23W22 RHEA is mainly controlled by the diffusion of cations instead of affinities with O. Additionally, HT1 and HT3 samples irradiated with a fluence of 3.9 × 1022 cm-2 hydrogen ions (60 eV) were found to have a better hydrogen irradiation resistance than Cr20Mn17Fe18Ta23W22 RHEA. The microdefects in irradiated Cr20Mn17Fe18Ta23W22 mainly existed as hydrogen bubbles, hydrogen-vacancy (H-V) complexes and vacancy/vacancy clusters. The microdefects in irradiated HT3 were mainly vacancies and H-V complexes, while the microdefects in irradiated HT1 mainly existed as vacancies and vacancy clusters, as large amounts of hydrogen were consumed to react with oxides on the HT1 surface. The oxides on the surface of the HT3 sample were more stable than those on HT1 under hydrogen irradiation.
RESUMO
In this work, we studied the evolution of vacancy-like defects and the formation of brittle precipitates in a reduced-activation V-Cr-Mn medium-entropy alloy. The evolution of local electronic circumstances around Cr and Mn enrichments, the vacancy defects, and the CrMn3 precipitates were characterized by using scanning electron microscopy with energy-dispersive spectroscopy, X-ray diffraction, and positron annihilation spectroscopy. The microstructure measurements showed that the Mn and Cr enrichments in the as-cast sample significantly evolved with temperature, i.e., from 400 °C, the Cr/Mn-segregated regions gradually dissolved into the matrix and then disappeared, and from 900 °C to 1000 °C, they existed as CrMn3 precipitates. The crystallite size of the phase corresponding to CrMn3 precipitates was about 29.4 nm at 900 °C and 43.7 nm at 1000 °C. The positron annihilation lifetime results demonstrated that the vacancies mediated the migration of Cr and Mn, and Cr and Mn segregation finally led to the formation of CrMn3 precipitates. The coincidence Doppler broadening results showed that the characteristic peak moved to the low-momentum direction, due to an increase in the size of the vacancy defects at the interface and the formation of CrMn3 precipitates.
RESUMO
The atomic-scale defects such as (deuterium, helium)-vacancy clusters in nuclear energy materials are one of the causes for the deterioration of the macroscopic properties of materials. Unfortunately, they cannot be observed by transmission electron microscopy (TEM) before they grow to the nanometer scale. Positron annihilation spectroscopy (PAS) has been proven to be sensitive to open-volume defects, and could characterize the evolution of the size and concentration of the vacancy-like nanoclusters. We have investigated the effects of He-D interaction on the formation of nanoscale cavities in Fe9Cr alloys by PAS and TEM. The results show that small-sized bubbles are formed in the specimen irradiated with 5 × 1016 He+/cm2, and the subsequent implanted D-ions contribute to the growth of these helium bubbles. The most likely reason is that helium bubbles previously formed in the sample captured deuterium injected later, causing bubbles to grow. In the lower dose He-irradiated samples, a large number of small dislocations and vacancies are generated and form helium-vacancy clusters with the helium atoms.