RESUMO
The discarded solutions by the chemical nickel industry have high amounts of nickel, this is why they are considered hazardous wastes for the health and the environment. On the other side, Ni particles can have potential applications in the developing of magnetorheological fluids currently being used to improve the performance of mechanical devices. The present study raises the treatment of a residual effluent from a chemical nickel industry by applying a chemical precipitation which uses sodium hypophosphite as a reducer, and varying the order of the reagents involved in the conditioning of the reaction with respect to the reducer. The recovered solids were studied using different material characterization techniques to recognize the chemical composition (X-Ray Fluorescence, Inductively Coupled Plasma Mass Spectrometry), crystallinity and morphology (X-Ray Diffraction, Scanning Electron Microscope), surface charge and size distribution (Dynamic Light Scattering). By the chemical reduction treatment it was possible to decrease the amount of nickel in the residual between 97.25% and 99.50%, obtaining Ni particles that were then tested to be used in magnetic fluids. To this purpose a suspension was prepared by mixing the Ni particles with silicone oil in a constant solid/liquid ratio, and the rheological behavior of this suspension was evaluated as a function of the magnetic field and the deformation applied, revealing an interesting magnetorheological behavior.
RESUMO
In this research work, DEXTRAN- and polyethylene glycol (PEG)-coated iron-oxide superparamagnetic nanoparticles were synthetized and their cytotoxicity and biodistribution assessed. Well-crystalline hydrophobic Fe3 O4 SPIONs were formed by a thermal decomposition process with d = 18 nm and σ = 2 nm; finally, the character of SPIONs was changed to hydrophilic by a post-synthesis procedure with the functionalization of the SPIONs with PEG or DEXTRAN. The nanoparticles present high saturation magnetization and superparamagnetic behavior at room temperature, and the hydrodynamic diameters of DEXTRAN- and PEG-coated SPIONs were measured as 170 and 120 nm, respectively. PEG- and DEXTRAN-coated SPIONs have a Specific Power Absorption SPA of 320 and 400 W/g, respectively, in an ac magnetic field with amplitude of 13 kA/m and frequency of 256 kHz. In vitro studies using VERO and MDCK cell lineages were performed to study the cytotoxicity and cell uptake of the SPIONs. For both cell lineages, PEG- and DEXTRAN-coated nanoparticles presented high cell viability for concentrations as high as 200 µg/mL. In vivo studies were conducted using BALB/c mice inoculating the SPIONs intravenously and exposing them to the presence of an external magnet located over the tumour. It was observed that the amount of PEG-coated SPIONs in the tumor increased by up to 160% when using the external permanent magnetic as opposed to those animals that were not exposed to the external magnetic field.
Assuntos
Dextranos/farmacocinética , Compostos Férricos/farmacocinética , Campos Magnéticos , Nanopartículas , Animais , Chlorocebus aethiops , Dextranos/administração & dosagem , Dextranos/toxicidade , Cães , Portadores de Fármacos , Avaliação Pré-Clínica de Medicamentos , Feminino , Compostos Férricos/administração & dosagem , Compostos Férricos/toxicidade , Técnicas In Vitro , Injeções Intravenosas , Fígado/metabolismo , Pulmão/metabolismo , Células Madin Darby de Rim Canino , Nanopartículas de Magnetita/administração & dosagem , Nanopartículas de Magnetita/toxicidade , Neoplasias Mamárias Experimentais/metabolismo , Teste de Materiais , Camundongos , Camundongos Endogâmicos BALB C , Nanopartículas/administração & dosagem , Nanopartículas/toxicidade , Polietilenoglicóis , Pele/metabolismo , Espectroscopia de Infravermelho com Transformada de Fourier , Distribuição Tecidual , Células VeroRESUMO
We propose a new method for determining the quantity of superparamagnetic iron oxide nanoparticles (Fe3O4, SPIONs) embedded in animal tissue using magnetization measurements. With this method, the smallest detectable quantity of magnetite nanoparticles in a tissue sample is -1 microg. We showed that this method has proved being efficient. In this study, we focused in determining the quantity of SPION confined in lung and liver tissue of mice injected with -13 nm magnetite superparamagnetic nanoparticles. Furthermore, the method allowed us to detect the magnetite nanoparticles present in animal tissues without letting the natural iron ions present in the tissue or blood interfere with the measurements.
Assuntos
Dextranos/metabolismo , Fígado/metabolismo , Pulmão/metabolismo , Nanopartículas de Magnetita/química , Nanotecnologia/métodos , Animais , Camundongos , Camundongos Endogâmicos BALB C , Especificidade de ÓrgãosRESUMO
We report evidence of the quantization of the rotational motion of solid particles containing thousands of atoms. A system of CoFe2O4 nanoparticles confined inside polymeric cavities has been studied. The particles have been characterized by the x-ray diffraction, transmission electron microscopy, plasma mass spectroscopy, ferromagnetic resonance (FMR), and magnetization measurements. Magnetic and FMR data confirm the presence of particles that are free to rotate inside the cavities. Equidistant, temperature-independent jumps in the dependence of the microwave absorption on the magnetic field have been detected. This observation is in accordance with the expectation that orbital motion splits the low-field absorption line into multiple lines.
RESUMO
Magnetization and AC susceptibility measurements have been performed on â¼3 nm NiO nanoparticles in powder form. The results indicate that the structure of the particles can be considered as consisting of an antiferromagnetically ordered core, with an uncompensated magnetic moment, and a magnetically disordered surface shell. The core magnetic moments block progressively with decreasing temperature, according to the distribution of their anisotropy energy barriers, as shown by a broad maximum of the low field zero-field-cooled magnetization (M(ZFC)) and in the in-phase component χ' of the AC susceptibility, centred at â¼70 K. On the other hand, surface spins thermally fluctuate and freeze in a disordered spin-glass-like state at much lower temperature, as shown by a peak in M(ZFC) (at 17 K, for H = 50 Oe) and in χ'. The temperature of the high temperature χ' peak changes with frequency according to the Arrhenius law; instead, for the low temperature maximum a power law dependence of the relaxation time was found, τ = τ(0)(T(g)/(T(ν)-T(g)))(α), where α = 8, like in spin glasses, τ(0) = 10(-12) s and T(g) = 15.9 K. The low temperature surface spin freezing is accompanied by a strong enhancement of magnetic anisotropy, as shown by the rapid increase of coercivity and high field susceptibility. Monte Carlo simulations for core/shell antiferromagnetic particles, with an antiferromagnetic core and a disordered shell, reproduce the qualitative behaviour of the temperature dependence of the coercivity. Interparticle interactions lead to a shift to a high temperature of the distribution of the core moment blocking temperature and to a reduction of magnetization dynamics.
RESUMO
We report interparticle interactions effects on the magnetic structure of the surface region in Fe3O4 nanoparticles. For that, we have studied a desirable system composed by Fe3O4 nanoparticles with (d) = 9.3 nm and a narrow size distribution. These particles present an interesting morphology constituted by a crystalline core and a broad (approximately 50% vol.) disordered superficial shell. Two samples were prepared with distinct concentrations of the particles: weakly-interacting particles dispersed in a polymer and strongly-dipolar-interacting particles in a powder sample. M(H, T) measurements clearly show that strong dipolar interparticle interaction modifies the magnetic structure of the structurally disordered superficial shell. Consequently, we have observed drastically distinct thermal behaviours of magnetization and susceptibility comparing weakly- and strongly-interacting samples for the temperature range 2 K < T < 300 K. We have also observed a temperature-field dependence of the hysteresis loops of the dispersed sample that is not observed in the hysteresis loops of the powder one.
Assuntos
Cristalização/métodos , Compostos Férricos/química , Magnetismo , Modelos Químicos , Nanoestruturas/química , Nanoestruturas/ultraestrutura , Nanotecnologia/métodos , Simulação por Computador , Substâncias Macromoleculares/química , Teste de Materiais , Conformação Molecular , Tamanho da Partícula , Propriedades de SuperfícieRESUMO
Morphological, structural and magnetic properties of 4.8 nm iron oxide nanoparticles have been investigated after annealing under inert atmosphere at different temperatures. The as-prepared iron oxide nanoparticles have been synthesized by chemical route from high temperature reaction of Fe(acac)3 solution in presence of oleic acid and oleylamine surfactant. Annealing the particles at low temperatures (Tann = 573 K) produces an increment of the mean size from 4.8 nm to 6.0 nm, preserving the same morphology. The coercive field of the annealed sample has a small increasing with respect to the as-prepared sample in agreement with the mean particle volume change. Annealing at higher temperature (Tann = 823 K) leads to a bimodal size distribution of the iron oxide nanoparticles with 6.0 nm and 17 nm mean sizes respectively, where the bigger particles dominate the observed magnetic properties.
Assuntos
Compostos Férricos/química , Nanopartículas Metálicas/química , Nanotecnologia/métodos , Aminas/química , Óxido Ferroso-Férrico/química , Ferro/química , Magnetismo , Microscopia Eletrônica de Transmissão , Nanopartículas/química , Nanoestruturas/química , Ácido Oleico/química , Tamanho da Partícula , Tensoativos/química , Temperatura , Difração de Raios XRESUMO
The magnetic properties of the ground state of a low-density free-electron gas in three dimensions have been the subject of theoretical speculation and controversy for seven decades. Not only is this a difficult theoretical problem to solve, it is also a problem which has not hitherto been directly addressed experimentally. Here we report measurements on electron-doped calcium hexaboride (CaB6) which, we argue, show that-at a density of 7× 1019 electrons cm-3-the ground state is ferromagnetically polarized with a saturation moment of 0.07 µB per electron. Surprisingly, the magnetic ordering temperature of this itinerant ferromagnet is 600 K, of the order of the Fermi temperature of the electron gas.