Development and characterization of films from Campomanesia xanthocarpa and commercial citrus pectins with different degrees of methyl-esterification.

In this study, pectins from commercial citrus and isolated from gabiroba (Campomanesia xanthocarpa) fruits, were obtained with different degrees of methyl-esterification (DM) and applied in the films. The DM ranged from 0 % to 62.5 % and the gradual de-esterification process was confirmed by mono-dimensional analysis (1H NMR). In order to investigate the influence of DM values in pectin film properties, PCP (DM: 62.5 %); PCP-5 (DM: 37.4 %); PCP-15 (DM: 19.1 %), and a fully de-esterified sample PCP-35 (DM: 0 %) were selected. The functional properties of the films clearly showed that the DM and cross-linking process are necessary to obtain a material with water resistance. Furthermore, pectin isolated from the fruits of gabiroba was purified (GW-Na, DM: 51.9 %) and partially de-esterified (GW-Na-5, DM: 37.1 %). These pectins were used, for the first time, in development of films and the physical and mechanical properties were compared with films made with PCP and PCP-5 samples. GW-Na and GW-Na-5 films presented suitable properties, with reduced solubility reduced (57.1 and 26.2 %), high degree of swelling (2.14 and 2.26), low flexibility (18.05 and 6.11 MPa), respectively. High strength and rigidity (99.36 and 1040.9 MPa), for both films (GW-Na and GW-Na-5) were demonstrated, similar to that obtained by analyzed citrus pectin.

Isolation, NMR characterization and bioactivity of a (4-O-methyl-α-D-glucurono)-ß-D-xylan from Campomanesia xanthocarpa Berg fruits.

Hemicellulose-type polysaccharides were isolated from Campomanesia xanthocarpa fruits by alkaline extraction and submitted to fractionation processes giving rise to eluted (GE-300) and retained (GR-300) fractions. GE-300 presented a mixture of galactoglucomannans (GGM) and glucuronoxylans (MGX), while the GR-300 fraction is composed only of MGX. In this way, the chemical structure of MGX, investigated by 1D 1H, 13C and 2D 1H-13C HSQC, 1H-1H COSY and 1H-13C HMBC NMR spectroscopy, revealed that the chemical structure of polysaccharide is a (4-O-methyl-α-D-glucurono)-D-xylan. Deep and precise NMR chemical shift determination of clean and specific 1H NMR glycosyl units were developed by 1D TOCSY and 1D NOESY analysis. This approach demonstrated unequivocally that 4-O-methyl-α-D-glucopyranosyl uronic acid group is linked to O-2 of a (1 â†’ 4)-ß-D-xylan in the main chain. Furthermore, MGX scavenged DPPH radical (0.5 to 1.0 mg mL-1) and was not cytotoxic to human dermal fibroblasts at concentrations up to 1.0 mg mL-1, as demonstrated by neutral red and crystal violet assays, evidencing in vitro biocompatibility. The structure elucidation of GR-300 together with its bioactivity assessment contributed to better understand the chemical characteristics of C. xanthocarpa hemicelluloses and may provide structural basis for future structure-property studies.

Pectins from the pulp of gabiroba (Campomanesia xanthocarpa Berg): Structural characterization and rheological behavior.

The pulp of gabiroba fruits was submitted to a hot water extraction, giving rise to a crude pectin named GW. GW was shown to be composed mainly of arabinose (54.5%), galacturonic acid (33.5%), galactose (7.6%), and rhamnose (1.6%). GW was characterized by chromatographic and spectroscopic methods indicating the presence of homogalacturonans (HG) with a degree of methyl-esterification (DM) of 60% and rhamnogalacturonans I (RG-I). HG domain represents 31.9% and RG-I domain 65.3%. Furthermore, GW was submitted to sequential fractionation methods, giving rise to GWP-TEP fraction, structurally characterized by the predominance of HG regions, and confirmed by NMR analysis. The rheological behavior of GW was analyzed at 1%, 3%, and 5% (w/v) concentration with 0.1 mol L-1 NaCl. All samples showed shear thinning behavior. In the oscillatory measurements, the 1% GW showed a liquid-like behavior, while the 3% presented a concentrated solution behavior and the 5% GW a gel behavior.