RESUMO
Introduction: Blue covarine is a pigment that promotes optical changes in dental surfaces, providing whitening. Objective: To evaluate in vitro the effect of bleaching dentifrices containing Blue covarine in nanoparticulate composite resin subjected to artificial darkening. Material and method: One hundred sixty (160) specimens (PBs) of FILTEK Z350XT nanoparticulate composite resin were randomly divided into two experiments: Experiment I - 8 groups (n=10) submitted to brushing with an electric toothbrush for 1 month; Experiment II - 8 groups (n=10) submitted to simulated brushing for 6, 12 and 24 months. Groups were distributed according to the solution/dentifrice tested: CG (distilled water) and 7 test groups (GT1- Coltene Herjos, GT2- Colgate Total 12 Clean Mint, GT3- Colgate Luminous White Brilliant Mint, GT4- Oral B 3D White Perfection, GT5- Close Up White Now Glacier Fresh, GT6- Close Up White Attraction Diamond and GT7- Sorriso Xtreme White Evolution). Result In Experiment I, there was greater ∆E in GT6 in relation to CG, GT2, GT4 and GT5, with no differences among them. In Experiment II, after 24 months of brushing, there was greater ∆E in groups GT6 and GT7. After 24 months of simulated brushing, there was no change in roughness or loss of mass in any group. Conclusion: The whitening effect promoted by dentifrices containing the agent Blue covarine seems to be related to the association of this agent with the abrasives present in the formulations of whitening dentifrices.
Introdução: O Blue covarine é um pigmento que promove alterações ópticas nas superfícies dentárias proporcionando o seu branqueamento. Objetivo: Avaliar in vitro o efeito de dentifrícios branqueadores contendo Blue covarine em resina composta nanoparticulada submetida a escurecimento artificial. Material e método: 160 corpos de prova (CPs) de resina composta nanoparticulada FILTEK Z350XT foram divididos aleatoriamente em dois experimentos: Experimento I- 8 grupos (n=10) submetidos a escovação com escova elétrica por 1 mês; Experimento II- 8 grupos (n=10) submetidos a escovação simulada por 6, 12 e 24 meses. Os grupos foram distribuídos de acordo com a solução/dentifrício testado: GC (água destilada) e 7 grupos teste (GT1-Coltene Herjos, GT2- Colgate Total 12 Clean Mint, GT3- Colgate Luminous White Brilliant Mint, GT4- Oral B 3D White Perfection, GT5- Close Up White Now Glacier Fresh, GT6- Close Up White Attraction Diamond e GT7- Sorriso Xtreme White Evolution). Resultado: No experimento I, houve maior ∆E no GT6 com relação ao GC, GT2, GT4 e GT5, que não diferiram entre si. No experimento II, após 24 meses de escovação houve maior ∆E nos grupos GT6 e GT7. Após 24 meses de escovação simulada não houve alteração da rugosidade nem perda de massa em nenhum grupo. Conclusão: O efeito branqueador promovido pelos dentifrícios contendo o agente Blue covarine parece estar relacionado à associação deste agente com os abrasivos presentes nas formulações dos dentifrícios branqueadores.
Assuntos
Abrasão Dentária , Clareamento Dental , Técnicas In Vitro , Pigmentação , Resinas Compostas , Corantes , Escovação Dentária , DentifríciosRESUMO
The aim of this study is to evaluate the flexural resistance of three types of restorative materials: compomer (Freedom), resin-modified glass-ionomer (Vitremer) and composite resin (Esthet-X), observing whether the application of bleaching agent can cause alterations of their flexural properties. Sixty samples were made using a 10x1x1 mm brass mold, and divided into three groups: G1- Freedom (SDI); G2- Vitremer (3M ESPE); G3- Esthet-X (Dentsply). On half of the samples of each group (10 samples) the bleaching treatment was applied and the other half, used as control, was stored in distilled water at a temperature of 37oC. Whiteness HP Maxx bleaching system was applied on the sample surface following the manufacturer's recommendations, simulating the bleaching treatment at the clinic. After this period, a flexural strength (three-point bending) test was conducted using (EMIC DL 1000) machine until the samples fractured. The data were submitted to ANOVA and Tukey tests. Of the restorative materials studied, G3- (87.24±31.40MPa) presented the highest flexural strength, followed by G1-(61.67±21.32MPa) and G2-(61.67±21.32MPa). There was a statistical difference in flexural strength after the bleaching treatment. It was concluded that the use of a beaching agent can promote significant alteration of the flexural strength of these restorative materials.
O objetivo deste trabalho foi o de avaliar a resistencia flexural de tres tipos de materiais restauradores hibridos; compomero (Freedom), cimento de ionomero de vidro modificado por resina (CIV-RM) (Vitremer) e resina composta (Esthet-X) verificando se a aplicacao do agente clareador promove alteracoes em suas propriedades flexurais. Foram confeccionadas 60 amostras, com auxilio de uma matriz metalica 10x1x1mm, as quais foram divididas em tres grupos: G1- Freedom (SDI); G2- Vitremer (3M ESPE); G3- Esthet-X (Dentsply). Em metade das amostras de cada grupo, ou seja, 10 amostras, foi realizado o tratamento clareador permanecendo as demais armazenadas em agua destilada 37°C. Utilizou-se o sistema de clareamento Whiteness HP Maxx sobre a superficie das amostras seguindo as orientacoes do fabricante, simulando assim, o tratamento clareador realizado em consultorio. Decorrido este periodo, foi realizado o ensaio mecanico de resistencia a flexao de 3 pontos na maquina de testes universal (EMIC DL 1000) ate a fratura dos especimes. Os dados foram submetidos aos testes ANOVA-2 fatores e Tukey. Observou-se diferenca estatisticamente significante entre os materiais, sendo que G3-(87,24±31,40MPa) apresentou a maior resistencia flexural seguida pelo G1-(61,67±21,32MPa) e G2- (21,04±8,94MPa), e apos a realizacao do tratamento clareador. Concluiu-se que ha diferenca estatisticamente significante entre a resistencia flexural da resina composta, compomero e o CIVRM, sendo a aplicacao do agente clareador capaz de promover alteracoes na resistencia flexural destes materiais.