The Effect of Light-emitting Diode Light Intensities and Duration of Cure on Pulpal Wall Temperature among Different Classes of Teeth.

Introduction: The thermal changes during light curing of resin-based composites (RBCs) are recognized, but there is a lack of information about temperature changes in pulp tissue under different curing protocols, especially during bonding of orthodontic brackets onto the tooth surface. In the present study, pulpal temperature (PT) variation induced by the use of four different light cure intensities and different durations of cure among different classes of teeth was measured. Materials and methods: A total of 80 different classes of human extracted teeth (maxillary and mandibular central incisor, lateral incisor, canine, premolar, and molar) were irradiated at the same distances with four visible light curing intensities. Brackets (3M Unitek) were bonded with Transbond XT (3M Unitek, Monrovia, California) adhesive and light cured with a light-emitting diode (LED) light cure unit (LCU) (Bluephase). A J-type thermocouple wire was positioned in the center of the pulp chamber to assess the temperature difference. The results were analyzed with analysis of variance (ANOVA) and the Tukey's honestly significant difference (HSD) test. Results: Light-emitting diode with higher intensity induced significantly higher intra-PT changes than did the LED with lower intensity (p < 0.001). Mandibular central incisors had the highest intra-PT of about 45°C at 3000 mW/cm2, 3 seconds. Maxillary central incisors had the highest intra-PT of about 40°C at 3000 mW/cm2, 3 seconds. Mandibular and maxillary canines and molars had the lowest intra-PT of about 10°C at 800 mW/cm2, 20 seconds. Conclusion: Pulp chamber temperature changes were influenced by the intensity and duration of curing and the anatomy of the tooth (class/type of tooth). How to cite this article: S S, Anbarasu P, S SK, et al. The Effect of Light-emitting Diode Light Intensities and Duration of Cure on Pulpal Wall Temperature among Different Classes of Teeth. Int J Clin Pediatr Dent 2024;17(4):467-471.

Influence of radiant exposure and material shade on the degree of conversion and microhardness of a resin-based composite.

This in vitro study evaluated the influence of radiant exposure and material shade on the degree of conversion (DC) and microhardness of a resin-based composite (RBC). Sixty-four RBC specimens in shades A1E (enamel) and A4D (dentin) were light cured at a calibrated exitance of 1000 mW/cm2 for 5, 10, 15, or 20 seconds, resulting in radiant exposure levels of 5, 10, 15, or 20 J/cm2. The DC was determined using Fourier-transform infrared spectroscopy (n = 3 per shade per exposure level). The Knoop hardness number (KHN) was measured on the top and bottom surfaces of each specimen (n = 5 per shade per exposure level). Data were analyzed using 2- and 3-way analyses of variance and post hoc Tukey tests (α = 0.05). The RBC shade did not affect the DC (P = 0.860), and the lowest DC values were achieved with an exposure level of 5 J/cm2 (P < 0.001). The shade did not affect the KHN on the top surface, but the radiant exposure level did, with the application of 5 J/cm2 resulting in significantly lower values (P < 0.05). For the bottom surface, shade A1E showed significantly higher KHN values than A4D (P < 0.001). An increase in the radiant exposure led to increased DC and KHN for both shades of RBC until reaching a saturation point of 10 J/cm2 for A1E and the top surface of A4D. The darker and more opaque shade was not adequately polymerized at a 2-mm depth, even when the highest radiant exposure level was applied.

Color-Stable Formulations for 3D-Photoprintable Dental Materials.

Color stability is crucial for dental materials to ensure they perfectly match a patient's tooth color. This is particularly challenging in photoresist-based additive manufacturing. Although some studies have addressed this issue, the exact causes of discoloration and ways to minimize it remain unclear. In this study, the intrinsic causes of discoloration in materials intended for 3D printing are investigated by examining thin-film samples (1200 µm) of various compositions, which are stored under different conditions. The samples are evaluated by measuring the UV-Vis absorption spectra at regular intervals to monitor changes. The findings reveal that both the composition of the formulations and the storage conditions significantly influence the discoloration behavior. Furthermore, methods have been developed to reduce or completely prevent discoloration. The use of photoinitiators with sterically demanding benzoyl moieties, as well as the addition of stabilizers, effectively decreases the intensity of emerging discoloration. Furthermore, incorporating the oxidizing agent cumene hydroperoxide (CHP) results in materials that maintain color stability.

Equilibrium and self-assembly of Janus particles at liquid-liquid interfaces for the film formation.

This article investigates the equilibrium arrangement, self-assembly process, and subsequent curing of amphiphilic snowman-shaped Janus particles at the oil-water interface. The independent Janus particles are in vertical equilibrium state and the contact position of the oil-water interface is at the largest cross section of the particle's hydrophobic phase. Under the effect of the surface tension and the adsorption of materials, Janus particles may form particle combinations including the particle pairs and the particle triangle, whose inner and outer sides have the liquid surface exhibiting completely opposite contact angles. Particle combinations form stable parallel double-chain structures with diverse shapes after the self-assembly process. However, the single Janus particles attain a state of mechanical equilibrium under the influence of surrounding particles, enabling them to assemble into regular array structures. The relationship of interfacial tension coefficient between phases can be changed by adjusting the oil-water system, which leads to variations in the self-assembly speed and the final arrangement results. The thin-film with uniformly distributed vertical particles is achieved by replacing the underlying deionized water with a curing agent. Based on the understanding of the interactions between irregularly shaped Janus particles at the oil-water interface, it will be convenient to achieve the controllable self-assembly and widely applications of these particles.

A Historical Perspective on Dental Composite Restorative Materials.

This review article will discuss the origin of resin-based dental composite materials and their adoption as potentially useful adjuncts to the primary material used by most dentists for direct restorations. The evolution of the materials, largely driven by the industry's response to the needs of dentists, has produced materials that are esthetic, strong, and versatile enough to be used in most areas of the oral cavity to replace or restore missing tooth structures. Significant advancements, such as the transition from chemical to light-curing materials, refinements in reinforcing particles to produce optimum polishing and wear resistance, formulating pastes with altered viscosities to create highly flowable and highly stiff materials, and creating materials with enhanced depth of cure to facilitate placement, will be highlighted. Future advancements will likely reflect the movement away from simply being a biocompatible material to one that is designed to produce some type of beneficial effect upon interaction within the oral environment. These new materials have been called "bioactive" by virtue of their potential effects on bacterial biofilms and their ability to promote mineralization of adjacent tooth structures.

Relationship between the polymerization distance of monowave and polywave light-curing units and the irradiance and physical properties of dental resin-based composites.

PURPOSE: To evaluate the influence of the polymerization distance of monowave and polywave light curing units (LCUs) on the measured irradiance relative to the value reported by the manufacturer in relation to the physical properties of resin-based composites (RBCs). METHODS: Four LCUs were used: one monowave and three polywave. The irradiance was measured with a digital radiometer. Depth of cure (DC) and flexural strength (FS) tests were performed according to ISO 4049:2019 at polymerization distances of 0 mm and 5 mm. RESULTS: The irradiance of all LCUs was higher than that reported by the manufacturer (>25-64%). The irradiance of the four LCUs was reduced when polymerization was performed at between 0 to 5 mm (paired t-test, P < 0.001). The DC at 0 mm was similar in all groups but was significantly decreased at 5 mm distance (ANOVA P < 0.001). FS showed differences among the LCUs at 0 mm (ANOVA P < 0.001) and was affected by the polymerization distance. The elastic modulus was unaffected by the LCU used or the distance (ANOVA P > 0.001). CONCLUSIONS: The LCU must be positioned as near as possible to RBCs during the polymerization process, as increased distance negatively affects the depth of cure and flexural strength.

Evaluation of the information provided in the instruction manuals of dental light-curing units.

OBJECTIVE: This study evaluated the completeness and accuracy of information in LCU instruction manuals from 40 manufacturers. MATERIALS AND METHODS: Instruction manuals from 40 LCUs (20 from leading manufacturers and 20 budget units) were reviewed. Twenty-eight parameters across five categories were assessed using a binary scale (0=incorrect/missing, 1=correct). The categories and their respective evaluation scores were: LCU characteristics (43%), instructions for use (7%), safety precautions (14%), maintenance recommendations (29%), and regulatory certification (7%). These scores were combined to produce a final score. RESULTS: Scores from leading manufacturers ranged between 46-86%, while the budget category ranged from 18-68%. All manuals provided information about the wavelength/spectrum of the LCU. Only Valo X and Valo Cordless reported power values and used the term "irradiance" instead of "intensity." Details such as LED type and active tip emission area were often missing. Instructions on how to use the LCU to photo-cure resins were frequently limited. Although most manuals addressed safety precautions, several lacked details on heat issues and general health precautions. All manuals included maintenance instructions, though information on replacement parts was often missing. Among the LCUs, 85% stated they were CE certified, 32% held both FDA and CE certification, and 63% claimed compliance with ISO and/or IEC standards. CONCLUSIONS: There were notable differences in the completeness and accuracy of the instruction manuals. Manuals from major manufacturers generally provided more comprehensive information than their budget counterparts. CLINICAL SIGNIFICANCE: Instruction manuals should contain accurate information to help clinicians deliver the highest standard of care. The lack of important information about the LCUs in the manuals is concerning.

Effect of shade and thickness on the microhardness of resin-based composite specimens at different points considering curing light beam's inhomogeneity.

BACKGROUND: Recent studies have reported the inhomogeneity in the light emitted by dental light-curing units (LCUs). It is essential to understand how this uneven light distribution affects the physical properties of resin-based composites (RBCs) at various points across their surfaces. This study aimed to evaluate the effect of LCU beam's inhomogeneity on the microhardness of RBCs with different shades and thicknesses. METHODS: Four body (A1B, A2B, A3B, and A4B), one dentin (A3D), and one enamel shade (A3E) of RBC (Filtek Z350 XT) were examined. The specimens were fabricated in four thicknesses (1, 2, 3, and 4 mm) and subjected to a 40-second light-curing. Vickers microhardness testing was performed at the center point, and 3 mm left and right from the center at the bottom surface of each sample. The LCU beam profile was characterized using a beam profiler, while irradiance after specimen passage was measured using a spectrometer. One-way analysis of variance (ANOVA) and Tukey's post-hoc tests were used to analyze the effects of shades and thicknesses on irradiance and microhardness, respectively. One-way repeated-measures ANOVA was used to compare the microhardness across different points. Pearson's correlation analysis examined the relationship between irradiance and microhardness. RESULTS: The beam profile of LCU revealed inhomogeneous light distribution. Light irradiance was decreased with both the increase in thickness and darker shade of the specimens (p < 0.05). Microhardness was found to decline with an increase in sample thickness (p < 0.05), and was consistently higher at the center point compared to the periphery, particularly in thicker (3 and 4 mm) and darker shades (A3B, A4B, and A3D). A positive correlation was found between the irradiance and microhardness across all evaluated points (p < 0.05). CONCLUSIONS: Inhomogeneous light emission from LCU significantly influences the microhardness of RBC samples, depending on the thicknesses and shades. The findings underline the importance of considering LCU beam inhomogeneity in clinical settings to ensure optimal polymerization of RBC.

New Perspectives in Overcoming Bulk-Fill Composite Polymerization Shrinkage: The Impact of Curing Mode and Layering.

BACKGROUND: The purpose of this study was to investigate the effect of different light curing modes on the polymerization shrinkage of a bulk-fill composite and to evaluate the impact of two layering techniques on the cuspal deflection. METHODS: Nine different light curing modes were tested on bulk-fill composite samples in aluminum MOD cavities. Intensity, duration, and illumination distance were the factors that changed during the different curing modes. The digital image correlation method was used to visually represent the displacement of carbon particles on the materials' surface caused by shrinkage along both the horizontal and vertical axes. For simulating cuspal deflection, a separate protocol was used, with a bulk and horizontal layering technique. RESULTS: The results showed that the largest horizontal displacements were present in the soft start group (6.00 ± 0.82 µm) and in the X-tra power group (5.67 ± 1.21 µm). The smallest horizontal displacements were detected in normal curing modes (4.00 ± 1.58 µm; 4.00 ± 2.68 µm). The largest vertical displacements, at the bottom layer, were present in the normal curing mode group with a 20 s curing time (5.22 ± 1.56 µm), while the smallest vertical displacements were shown in the X-tra power group (2.89 ± 0.60 µm). The observed particle displacements showing the shrinkage of the composite were correlated with the curing mode. The bulk-fill group showed less cuspal deflection than the horizontal layering group did, but the difference was not statistically significant (p = 0.575). CONCLUSIONS: Within the limitations of this in vitro study, it can be concluded that lower intensities of curing lights (1200 mW/cm2) may perform better from the point of view of material shrinkage than high and extreme light intensities do. The pulse delay mode might be recommended in the case of bulk-fill materials. The number of layers did not significantly affect the cuspal deflection in the case of the studied composite.

Characterization of dental light-curing resin composites incorporating multiple modified low-shrink monomers.

OBJECTIVE: Polymerization shrinkage poses a significant challenge in dental resin composites. The objective of this study is to introduce spiroorthocarbonate monomer 3,9-dimethylene-1,3,5,7-tetraoxa-spiro[5,5]undecane (BMSOC) and epoxy resin monomer 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate (ECHM-ECHC) into bisphenol-S-bis(3-methacrylato-2-hydroxy propyl)ether (BisS-GMA) based resin composites to develop composites with reduced shrinkage properties. METHODS: BMSOC and BisS-GMA were synthesized and thoroughly mixed with ECHM-ECHC, followed by inorganic fillers and photoinitiators. Based on the composition of the resin matrix, five groups of experimental composites were prepared, with traditional bisphenol A-dimethacrylate glycidyl ester (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) based composite serving as the control. The polymerization properties, including degree of conversion (DC) and polymerization shrinkage (PS), as well as marginal microleakage, wettability, flexural strength (FS), flexural modulus (FM), and biocompatibility were evaluated. RESULTS: The results demonstrated that compared with the control group, the PS of BisS-GMA based composites containing BMSOC and ECHM-ECHC were significantly reduced (P < 0.05), and the lowest PS (0.96 ± 0.08 %) was observed when the ratio of BisS-GMA: (Epoxy + BMSOC) was 4:6. Additionally, the experimental composites also exhibited improved DC, minimal microleakage, low hydrophilicity, enhanced mechanical properties, qualified in vivo biocompatibility, and slight/moderate in vitro biocompatibility. SIGNIFICANCE: The resin composites incorporating multiple modified low-shrink monomers are promising for dental applications to prevent various clinical problems caused by PS and extend restoration longevity.

Effect of Polywave and Monowave Light Curing Units on the Microtensile Bond Strength and Failure Types of Different Bulk-Fill Resin Composites: An in vitro Study.

Aim: This study aimed to evaluate the effects of polywave and monowave light-emitting diode curing units on the microtensile bond strength and failure types of three bulk-fill resin composites. Materials and Methods: This in vitro experimental study was performed on 180 microbars obtained from human third molars and were distributed into 12 groups according to the type of bulk-fill resin composite and the light-curing unit. Third molars were restored using Filtek One Bulk Fill Restorative, Tetric® N-Ceram Bulk Fill, and Opus Bulk Fill resin composites was light-cured with Elipar Deep Cure L and Valo in three modes: standard, high power, and extra power. Subsequently, microtensile analysis was carried out with a universal testing machine and the type of failure with an optical stereomicroscope. For statistical analysis, the Kruskal-Wallis H-test was used, with the Bonferroni post hoc test and Fisher's exact test, considering a significance of p<0.05. Results: There were significant differences in the microtensile bond strength between the Filtek One Bulk Fill restorative and Opus Bulk-Fill (p = 0.042) when light was cured with the polywave unit at standard power. On the other hand, the Filtek One Bulk Fill Restorative and Opus Bulk Fill resins showed significant differences in microtensile bond strength when light was cured with the monowave unit compared with the polywave unit (p<0.05). Conclusion: The presence of alternative photoinitiator systems that are more reactive than camphorquinone produced higher microtensile bond strength in Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins when light-cured with a high and standard polywave unit, respectively, compared to Filtek One Bulk Fill resins. Finally, Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins had the highest percentage of mixed failures, while Filtek One Bulk Fill resin had adhesive failures, which was related to its lower microtensile bond strength.

Tunable and fast-cured hyaluronic acid hydrogel inspired on catechol architecture for enhanced adhesion property.

Hyaluronic acid-based hydrogels have been broadly used in medical applications due to their remarkable properties such as biocompatibility, biodegradability, super hydroscopicity, non-immunogenic effect, etc. However, the inherent weak and hydrophilic polysaccharide structure of pure hyaluronic acid (HA) hydrogels has limited their potential use in muco-adhesiveness, wound dressing, and 3D printing. In this research, we developed in-situ forming of catechol-modified HA hydrogels with improved mechanical properties involving blue-light curing crosslinking reaction. The effect of catechol structure on the physicochemical properties of HA hydrogels was evaluated by varying the content (0-40 %). The as-synthesized hydrogel demonstrated rapid prototyping, excellent wetting adhesiveness, and good biocompatibility. Furthermore, an optimized hydrogel precursor solution was used as a blue light-cured bio-ink with high efficiency and good precision and successfully prototyped a microstructure that mimicked the human hepatic lobule by using DLP 3D printing method. This catechol-modified HA hydrogel with tunable physicochemical and rapid prototyping properties has excellent potential in biomedical engineering.

Evaluation of pre-heated composite resins with soft-start polymerization and conventional composite restorations in class-I carious lesions - A randomized clinical trial.

Background: By increasing fluidity and conversion, pre-heated composites enhance adaptability and strength, while soft-start polymerization decreases internal stresses. Aim: Over a period of a year, this split-mouth design, randomized controlled clinical trial (RCT) compared pre-heated composites with soft-start polymerization to conventional composites in class-I lesions, with the goal of improving restoration outcomes. Methods: and Findings: Immediately following ethical approval and registration with CTRI, 37 patients with in-formed permission who met specified inclusion and exclusion criteria for class-I lesions were chosen for enrollment. Using a 1:1 ratio, teeth were randomly assigned to Group-A (pre-heated composite with soft-start polymerization) or Group-B (traditional composite restoration). At three-time intervals, the evaluation was blinded and calibrated using Modified United States Public Health Service (USPHS) criteria: baseline, six-month, and one-year marks. Statistical analysis was performed using SPSS 21.0 and the Mann-Whitney U test for inter-group comparisons and the Friedman test for intra-group comparisons. Interpretation: Pre-heated composites with soft-start polymerization performed better in terms of marginal adaptation with a statistically significant difference (p = 0.019) and in terms of color match they performed better clinically (p = 0.062) at 12 months. Other variables like marginal discolouration, sec-ondary caries, anatomic form, post-operative sensitivity, surface texture and retention showed no statistically significant difference (p < 0.05). Pre-heated composites with soft-start mode performed marginally better than nanofilled composites. However, both techniques can be used to successfully restore simple class-I carious lesions.

The power of light - From dental materials processing to diagnostics and therapeutics.

Harnessing the power of light and its photonic energy is a powerful tool in biomedical applications. Its use ranges from biomaterials processing and fabrication of polymers to diagnostics and therapeutics. Dental light curable materials have evolved over several decades and now offer very fast (≤ 10 s) and reliable polymerization through depth (4-6 mm thick). This has been achieved by developments on two fronts: (1) chemistries with more efficient light absorption characteristics (camphorquinone [CQ], ~30 L mol-1 cm1 [ʎmax 470 nm]; monoacylphosphine oxides [MAPO], ~800 L mol-1 cm-1 [ʎmax 385 nm]; bisacylphosphine oxide [BAPO], ~1,000 L mol-1 cm-1 [ʎmax 385 nm]) as well mechanistically efficient and prolonged radical generation processes during and after light irradiation, and; (2) introducing light curing technologies (light emitting diodes [LEDs] and less common lasers) with higher powers (≤ 2 W), better spectral range using multiple diodes (short: 390-405 nm; intermediate: 410-450 nm; and long: 450-480 nm), and better spatial power distribution (i.e. homogenous irradiance). However, adequate cure of materials falls short for several reasons, including improper selection of materials and lights, limitations in the chemistry of the materials, and limitations in delivering light through depth. Photonic energy has further applications in dentistry which include transillumination for diagnostics, and therapeutic applications that include photodynamic therapy, photobiomodulation, and photodisinfection. Light interactions with materials and biological tissues are complex and it is important to understand the advantages and limitations of these interactions for successful treatment outcomes. This article highlights the advent of photonic technologies in dentistry, its applications, the advantages and limitations, and possible future developments.

Monowave vs. Polywave Light - Curing Units: Effect on Light Transmission of Composite without Alternative Photoinitiators.

Objective: The aim of this study was to compare the light transmission of monowave and polywave-curing devices by a bulk-fill composite containing only camphorquinone as a photoinitiator. Materials and methods: Three light-curing devices were used to cure bulk-fill composite QuiXfil: one monowave (Translux® Wave) and two polywave (VALO Cordless and Bluephase® PowerCure. The NIST-calibrated spectrometer (MARC Resin Calibrator, BlueLight Analytics Inc.) was used to measure the incident and transmitted light through a 2-mm composite specimen over 20 s. Light transmittance was calculated from the ratio of the amount of transmitted and incident light. For data analysis (ANOVA, α = 0.05), total irradiation of the entire spectrum, irradiation with wavelengths of 360-420 nm for the violet spectrum, and 420-540 nm for the blue spectrum were selected. Results: Monowave curing unit Translux® Wave had the lowest light transmission (13.78 ± 0.5%), similar to the violet light transmission of polywave devices (12.02 ± 0.94% and 13.81 ± 1.72% for Valo Cordless and Bluephase PowerCure, respectively). Blue light transmittance (32.15-23.70%) was more than twofold higher than for the wavelengths in the violet region of the spectrum (13.81-12.02%) for the two polywave devices. VALO Cordless showed the highest total and blue light transmission (p<0.001). There was no significant difference in the transmission of the violet part of the spectrum between VALO Cordless and Bluephase® PowerCure (p = 0.465). Conclusion: Within the limitations of this study, we could conclude that polywave curing devices can be used for the polymerization of the bulk-fill composite with camphorquinone as the sole photoinitiator.

Assessment of a Bracket-Bonding System's Shear Bond Strength after it has been Cured using Various Light-Curing Units at Different Time Intervals.

Objectives: To assess a bracket-bonding system's shear bond strength cured with dissimilar light-curing units at different time intervals. Materials and Method: Sixty premolar teeth removed for orthodontic purposes were categorized into four types based on the light-curing unit and exposure times used. The specimens in the halogen group were exposed to light for 15 (Group I) and 30 (Group II) sec, respectively. The specimens were exposed to light for 10 (Group III) and 15 sec in the LED group (Group IV). The amount of adhesive still present on the teeth was measured using a stereomicroscope at a magnification of 10 and was then assessed with the help of adhesive remnant index (ARI). Result: The group with the highest mean SBS was in Group II followed by Group I, Group III, and the group with the lowest mean SBS. The ARI was unaffected by the light-curing technique, with score 2 predominating. Conclusion: In all groups, polymerization using halogen and LED led to SBS values that were clinically suitable for orthodontic procedures.

Post-polymerization of three-dimensional printing resin using a dental light curing unit.

Background/Purpose: In vat photopolymerization, post-polymerization of the three-dimensional (3D) printing resin is necessary to ensure the optimum physical properties of the printed objects. This study aimed to evaluate the potential use of a handheld polywave light-emitting diode (LED) dental light-curing unit (LCU) for post-polymerizing 3D printed resins by measuring the microhardness and biaxial flexural strength of the post-polymerized resin. Material and methods: 3D printed 1- and 2-mm-thick disks were irradiated with a dental LCU at 3200 mW/cm2. Post-polymerization was repeated either on one side from the top surface: two cycles (T2), four cycles (T4), and eight cycles (T8), or on both sides from the top and bottom surfaces: one cycle (T1B1), two cycles (T2B2), and four cycles (T4B4) for each side. The microhardness and biaxial strength of the disks were compared to those post-polymerized by a conventional desktop polymerizing unit (PC) and those without post-polymerization (NC). Results: Microhardness of the disks varied between the top and bottom surfaces of the 1-mm and 2-mm-thick disks, depending on the post-polymerization methods. T8 and T4B4 produced comparable microhardness on the top surface to PC for both thicknesses. In contrast, PC, T2B2, and T4B4 exhibited the highest microhardness on the bottom surface. Except for NC, the 1-mm-thick disks had a higher biaxial flexural strength than the 2-mm-thick disks. T4B4 resulted in the highest biaxial flexural strength for both thicknesses, which was comparable to that of the desktop polymerizing unit. Conclusion: The microhardness and biaxial flexural strengths of the post-polymerized 3D-printed disks increase with polymerization time. With sufficient polymerization from both sides, the polywave LCU has the potential to be a viable alternative to desktop polymerization units.

Automotive Technology Revolutionized Restorative Dentistry Discovery of Alpha-diketone/Amine Catalyst: Part II -Reflections on Photopolymerization from Conception to Development of Composite Resin and Activator Light.

A full account of the preceded early research tribulation that led to the development of the first visible light activated composite resin and the first visible light activator source is documented. The events took place over four years since early 1974 when a raw industrial composite resin that was radiolucent, stiff paste, universal optically opaque white color, polymerized by exposure to a prototype visible light for 120 seconds was given to developed. Four years later, the developed restorative composite resin ended up as a radiopaque, optically translucent, universal color with an additional three shades that possessed the biologic, esthetic, mechanical and physical characteristics with proven efficacy be used for esthetic zone. This conservative account of early development of a technology that must count as one of a small number of inventions during the seventies, over the years has revolutionized restorative dental practice. We were privileged and very lucky to be associated with developmental stages, stumbling blocks, and final success of the first LC Composite resin that ignited the thought process worldwide and laid the foundation for modern esthetic restoratives practiced today.

Polymerization efficiency of different bulk-fill resin composites cured by monowave and polywave light-curing units: a comparative study.

OBJECTIVES: The objective was to evaluate the polymerization efficiency of different bulk-fill resin-based composites cured by monowave and polywave light-curing units, by assessment of the degree of conversion and Vickers microhardness at different depths. METHOD AND MATERIALS: Two commercially available bulk-fill resin-based composites were used: Filtek One Bulk Fill Restorative (3M ESPE) and Tetric N-Ceram Bulk Fill (Ivoclar Vivadent). The light-curing units utilized were two LED light-curing units: a monowave LED light-curing unit (BlueLEX LD-105, Monitex) and a polywave LED light-curing unit (Twin Wave GT-2000, Monitex). For each test, 20 cylindrical specimens (4 mm diameter, 4 mm thickness) were prepared from each bulk-fill resin-based composite using a split Teflon mold. Ten specimens were light-cured by the monowave light-curing unit and the other ten were light-cured by the polywave light-curing unit according to the manufacturer's recommendations. Attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR) was used to assess the degree of conversion, and a Vickers microhardness tester was used to assess Vickers microhardness. Statistical analysis was performed using three-way ANOVA and Tukey post-hoc tests (P < .05). RESULTS: The degree of conversion and Vickers microhardness in bulk-fill resin-based composites containing only camphorquinone as photoinitiator were similar when cured with either monowave or polywave light-curing units. However, bulk-fill resin-based composites containing a combination of photoinitiators exhibited significantly higher degree of conversion and Vickers microhardness when cured with a polywave light-curing unit. Although all groups showed statistically significant differences between the top and bottom surfaces regarding degree of conversion and Vickers microhardness, all of them showed bottom/top ratios > 80% regarding degree of conversion and Vickers microhardness. CONCLUSION: The polywave light-curing unit enhanced the polymerization efficiency of bulk-fill resin-based composites especially when the latter contained a combination of photoinitiators, but does not prevent the use of a monowave light-curing unit.

Biofabricated poly (γ-glutamic acid) bio-ink reinforced with calcium silicate exhibiting superior mechanical properties and biocompatibility for bone regeneration.

Background/purpose: The modification in 3D hydrogels, tissue engineering, and biomaterials science has enabled us to fabricate novel substitutes for bone regeneration. This study aimed to combine different biomaterials by 3D technique to fabricate a promising all-rounded hydrogel for bone regeneration. Materials and methods: In this study, glycidyl methacrylate (GMA)-modified poly γ-glutamic acid (γ-PGA-GMA) hydrogels with calcium silicate (CS) hydrogel of different concentrations were fabricated by a 3D printing technique, and their biocompatibility and capability in bone regeneration were also evaluated. Results: The results showed that CS γ-PGA-GMA could be successfully fabricated, and the presence of CS enhanced the rheological and mechanical properties of γ-PGA-GMA hydrogels, thus making them more adept at 3D printing and implantations. SEM images of the surface structure showed that higher CS concentrations (5% and 10%) contributed to denser surface architectures, thus achieving improved cellular adhesion and stem cell proliferation. Furthermore, higher concentrations of CS resulted in elevated expressions of osteogenic-related markers such as alkaline phosphatase (ALP) and osteocalcin (OC), as well as enhanced calcium deposition represented by the increased Alizarin Red S staining. In vivo studies referring to critical defects of rabbit femur further showed that the existence of hydrogels alone was able to induce partial bone regeneration, demonstrated by the results from quantitative and qualitative analysis of micro-CT scans. However, CS alterations caused significant increases in bone regeneration, as indicated by micro-CT and histological staining. Conclusion: These results robustly suggest combining different biomaterials is crucial to producing a well-rounded hydrogel for tissue regeneration. We hope this study could be applied as a platform for others to brainstorm potential out-of-the-box solutions, contributing to developing high-potential biomaterials for bone regeneration.