RESUMO
AIM: DENTIN CONDITIONED: with phosphoric acid (PA) Nd: YAP laser, and photoactivated-Ery(Erythrosine) on microleakage, shear bond strength (SBS) degree of conversion (DC), and rheological assessment of adhesive-infused with carbon nanotubes (CNTs). MATERIAL AND METHOD: Carious ninety-six human mandibular molars were included. Specimens were disinfected and allocated into three groups based on surface pretreatment (n=32) Group 1 (PA), Group 2 (Nd: YAP) laser, and Group 3 (Photoactivated-Ery). Conditioned groups were further divided into two 2 subgroups based on the application of unmodified ERA and CNTs-modified ERA. Composite restorations were placed on the CAD surface and thermal aging of the samples was performed. The microleakage assessment was conducted using a dye penetration test. Universal testing machine (UTM) assessed SBS bond failure was evaluated using a stereomicroscope. Scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) analyses of CNT, and Fourier Transform Infrared FTIR of adhesives were performed. One-way ANOVA and Tukey post hoc analyzed the outcomes. RESULTS: Group 1B samples (PA+ CNTs modified adhesive) presented the minimum marginal leakage and highest bond integrity. Group 2A (Nd:YAP laser+Unmodified adhesive) displayed the maximum scores of microleakage and lowest bond strength. CONCLUSION: Photoactivated Ery-PS can serve as an alternative to phosphoric acid for conditioning CAD. Incorporating CNT in adhesive significantly enhanced bond integrity and marginal seal with no significant difference in DC.
RESUMO
This in vitro study evaluated the influence of radiant exposure and material shade on the degree of conversion (DC) and microhardness of a resin-based composite (RBC). Sixty-four RBC specimens in shades A1E (enamel) and A4D (dentin) were light cured at a calibrated exitance of 1000 mW/cm2 for 5, 10, 15, or 20 seconds, resulting in radiant exposure levels of 5, 10, 15, or 20 J/cm2. The DC was determined using Fourier-transform infrared spectroscopy (n = 3 per shade per exposure level). The Knoop hardness number (KHN) was measured on the top and bottom surfaces of each specimen (n = 5 per shade per exposure level). Data were analyzed using 2- and 3-way analyses of variance and post hoc Tukey tests (α = 0.05). The RBC shade did not affect the DC (P = 0.860), and the lowest DC values were achieved with an exposure level of 5 J/cm2 (P < 0.001). The shade did not affect the KHN on the top surface, but the radiant exposure level did, with the application of 5 J/cm2 resulting in significantly lower values (P < 0.05). For the bottom surface, shade A1E showed significantly higher KHN values than A4D (P < 0.001). An increase in the radiant exposure led to increased DC and KHN for both shades of RBC until reaching a saturation point of 10 J/cm2 for A1E and the top surface of A4D. The darker and more opaque shade was not adequately polymerized at a 2-mm depth, even when the highest radiant exposure level was applied.
Assuntos
Resinas Compostas , Dureza , Teste de Materiais , Resinas Compostas/química , Resinas Compostas/uso terapêutico , Espectroscopia de Infravermelho com Transformada de Fourier , Cor , Humanos , Polimerização , Propriedades de Superfície , Lâmpadas de Polimerização Dentária , Técnicas In Vitro , Materiais Dentários/química , Cura Luminosa de Adesivos Dentários/métodosRESUMO
OBJECTIVES: To systematically compile data on the degree of conversion (DC) for bulk-fill composites using a network meta-analysis. METHODS: A systematic search for in vitro studies of DC of bulk-fill composites was performed in PubMed, Web of Science, Scopus, and Open Grey. Risk of bias within studies and due to missing evidence was assessed using the Joanna Briggs Institute scoring system and ROB-MEN tool, respectively. The primary outcome was the DC of bulk-fill composites. Surface Under the Cumulative Ranking curve (SUCRA) was used to rank relative performance. Inconsistencies in the model were investigated to ensure its validity and the level of confidence in the network meta-analysis (CINeMA) was assessed. RESULTS: A total of 28 studies were included in the quantitative analysis. The average DC values (%) for 0-h/top, 0-h/bottom, 24-h/top, and 24-h/bottom were 59.09, 57.14, 66.73, and 63.87, respectively. According to their SUCRA ranking, the best-performing composites were: SonicFill, Venus Bulk Fill, and SDR (0-h/top), Reveal HD, i-Flow Bulk Fill, and Venus Bulk- Fill (0-h/bottom), Venus Bulk Fill, SDR, and QuiXfil (24-h/top), and Venus Bulk Fill, Aura Bulk Fill, and i-Flow Bulk Fill (24-h/bottom). Incoherence between direct and indirect evidence was identified as the most significant factor affecting confidence. CONCLUSIONS: DC values of bulk-fill composites were within the range commonly reported for previous generations of "conventional" composites, with flowable composites tending to perform better than sculptable composites. High variability in DC data was observed, which may be attributed to incompletely understood methodological differences. CLINICAL SIGNIFICANCE: DC is a fundamental parameter that influences multiple mechanical and biological properties of resin composites and is particularly relevant for the group of bulk-fill composites that are designed for use in thick layers.
RESUMO
Aims: To evaluate hydroxyapatite-silver (HA-Ag) hybrid nanoparticles (NPs), as an antibacterial agent when integrated in self-etch (SE) adhesive. Blue light activated HA-Ag hybrid NP incorporation on mechanical properties, degree of conversion (DC), and microtensile bond strength (µTBS). Method: Eighty primary molar teeth have carious lesions reaching the dentin but not involving the pulp. The infected dentin was removed and carious-affected dentin (CAD) was preserved. Forty samples were inoculated with Streptococcus mutans. All primary teeth (n = 80) were allocated into four groups based on the incorporation of HA-Ag hybrid NPs in different concentrations (0%, 1%, 5%, and 10%). Group 1: 0% HA-Ag hybrid NPs + Clearfil SE bond primer, group 2: 1% HA-Ag hybrid NPs + Clearfil SE bond primer, group 3: 5 wt% HA-Ag NPs + Clearfil SE bond primer, and group 4: 10 wt% HA-Ag NPs + Clearfil SE bond primer. The survival rate assessment of S. mutans was conducted on 40 inoculated samples. On the remaining primary teeth (n = 40), Clearfil SE bonding agent was applied uniformly via a blue light source. The composite buildup was performed on the samples and µTBS and failure analysis assessed. Fourier transform infrared spectroscopy was performed to assess DC. Survival rates of S. mutans and µTBS among the tested groups were compared using ANOVA and Tukey post hoc analysis. Results: 10 wt % HA-Ag NPs + Clearfil SE bond primer exhibited the highest level of antibacterial efficacy (0.14 ± 0.02 CFU/mL) against S. mutans. The highest µTBS (18.38 ± 0.78 MPa) at the composite/CAD interface was in group 2 (1 wt % HA-Ag NPs + Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source). The highest DC was observed in the control group with Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source. Conclusion: 1 wt% HA-Ag hybrid NPs showed enhanced antibacterial effectiveness, DC, and bond strength of the SE adhesive to the primary CAD.
Assuntos
Cárie Dentária , Dentina , Durapatita , Nanopartículas Metálicas , Cimentos de Resina , Prata , Streptococcus mutans , Resistência à Tração , Dente Decíduo , Prata/química , Humanos , Streptococcus mutans/efeitos dos fármacos , Durapatita/química , Dentina/efeitos da radiação , Nanopartículas Metálicas/química , Cimentos de Resina/química , Antibacterianos/farmacologia , Adesivos Dentinários/química , Teste de Materiais , Técnicas In Vitro , Luz , Luz AzulRESUMO
OBJECTIVES: The first aim of this study was to determine whether there is a difference in degree of conversion (DC) of touch-cure cements polymerized by self-curing with adhesive or dual-curing under reduced light. The second aim was to compare interfacial adaptation of zirconia restoration cemented using touch-cure cements self-cured or dual-cured by reduced light. METHODS: The DC of touch-cure resin cements with adhesive was measured continuously using Fourier transform infrared spectrometry. Experimental groups differed depending on touch-cure cement. Each group had three subgroups of polymerization method. For subgroup 1, the DC was measured by self-curing. For subgroups 2 and 3, the DCs were measured by dual-curing with reduced light penetrating 3 mm and 1 mm zirconia blocks, respectively. For interfacial adaptation evaluation, Class I cavity was prepared on an extracted third molar, and zirconia restoration was fabricated. The restoration was cemented using the same cement. Groups and subgroups for interfacial adaptation were the same as those of the DC measurement. After thermo-cycling, interfacial adaptation at the tooth-restoration interface was evaluated using swept-source optical coherence tomography imaging. RESULTS: The DC of touch-cure cement differed depending on the measurement time, resin cement, and polymerization method (p < 0.05). Interfacial adaptation was different depending on the resin cement and polymerization method (p < 0.05). CONCLUSION: For touch-cure cement, light-curing with higher irradiance presented a higher DC and superior interfacial adaptation than light-curing with lower irradiance or self-curing. CLINICAL RELEVANCE: Although some adhesives accelerate the self-curing of touch-cure cement, light-curing for touch-cure cement is necessary for zirconia cementation.
Assuntos
Teste de Materiais , Polimerização , Cimentos de Resina , Zircônio , Cimentos de Resina/química , Zircônio/química , Espectroscopia de Infravermelho com Transformada de Fourier , Autocura de Resinas Dentárias , Lâmpadas de Polimerização Dentária , Cura Luminosa de Adesivos Dentários , Propriedades de Superfície , Técnicas In Vitro , Humanos , Dente Serotino , Restauração Dentária Permanente/métodosRESUMO
OBJECTIVES: To investigate the effect of neutral 10-methacryloyloxydecyl dihydrogen phosphate salt (MDP-Na) on the dentin bond strength and remineralization potential of etch-&-rinse adhesive. METHODS: Two experimental etch-&-rinse adhesives were formulated by incorporating 0 wt% (E0) or 20 wt% (E20) neutral MDP-Na into a basic primer. A commercial adhesive, Adper Single Bond 2 (SB, 3 M ESPE), served as the control. Sixty prepared teeth were randomly allocated into three groups (n = 20) and bonded using either one of the experimental adhesives or SB. Following 24 h of water storage, the bonded specimens were sectioned into resin-dentin sticks, with four resin-dentin sticks obtained from each tooth for microtensile bond strength (MTBS) test. Half of the sticks from each group were immediately subjected to tensile loading using a microtensile tester at a crosshead speed of 1 mm/min, while the other half underwent tensile loading after 6-month incubation in artificial saliva (AS). The degree of conversion (DC) of both the control and experimental adhesives (n = 6 in each group) and the adsorption properties of MDP-Na on the dentin organic matrix (n = 5 in each group) were determined using Fourier-transform infrared spectrometry. Furthermore, the effectiveness of neutral MDP-Na in promoting the mineralization of two-dimensional collagen fibrils and the adhesive-dentin interface was explored using transmission electron microscopy and selected-area electron diffraction. Two- and one-way ANOVA was employed to assess the impact of adhesive type and water storage on dentin bond strength and the DC (α = 0.05). RESULTS: The addition of MDP-Na into the primer increased both the short- and long-term MTBS of the experimental adhesives (p = 0.00). No difference was noted in the DC between the control, E0 and E20 groups (p = 0.366). The MDP-Na remained absorbed on the demineralized dentin even after thorough rinsing. The intra- and extra-fibrillar mineralization of the two-dimensional collagen fibril and dentin bond hybrid layer was confirmed by transmission electron microscopy and selected-area electron diffraction when the primer was added with MDP-Na. CONCLUSIONS: The use of neutral MDP-Na results in high-quality hybrid layer that increase the dentin bond strength of etch-&-rinse adhesive and provides the adhesive with remineralizing capability. This approach may represent a suitable bonding strategy for improving the dentin bond strength and durability of etch-&-rinse adhesive.
Assuntos
Colagem Dentária , Adesivos Dentinários , Dentina , Metacrilatos , Resistência à Tração , Metacrilatos/química , Humanos , Colagem Dentária/métodos , Dentina/ultraestrutura , Dentina/efeitos dos fármacos , Adesivos Dentinários/química , Remineralização Dentária/métodos , Teste de Materiais , Microscopia Eletrônica de Varredura , Condicionamento Ácido do Dente/métodos , Análise do Estresse Dentário , Técnicas In Vitro , Cimentos de Resina/química , Espectroscopia de Infravermelho com Transformada de Fourier , Cimentos Dentários/química , Propriedades de SuperfícieRESUMO
This study aimed to assess the key physico-mechanical properties and bonding performance of orthodontic adhesives with graphene addition for bonding a fixed retainer. Transbond LR (3M) and Transbond LV (3M) with no graphene were set as the control groups. Graphene was added into LR and LV at concentrations of 0.01 wt%, 0.05 wt% and 0.1 wt%. The stickiness of the uncured samples (n = 5) and real-time degree of conversion (DC) of the samples (n = 3) were measured over a 24-h period using Fourier-transform infrared spectroscopy. The hardness and other mechanical parameters, including the Martens hardness (HM), indentation modulus (EIT), elastic index (ηIT) and creep (CIT), were measured (n = 5). To measure the shear bond strength (SBS), adhesive composites were applied using a mold to bond the retainer wire to the lingual surfaces of bovine incisors (n = 10). Fracture modes subsequent to the SBS test were examined under light microscopy. Statistical analysis was conducted using ANOVA and Tukey tests (α = 0.05). In the LR groups, the LR + 0.01 showed the highest SBS (12.6 ± 2.0 MPa) and HM (539.4 ± 17.9 N/mm2), while the LV + 0.05 (7.7 ± 1.1 MPa) had the highest SBS and the LV + 0.1 had the highest HM (312.4 ± 17.8 N/mm2) among the LV groups. The most frequent failure mode observed was adhesive fracture followed by mixed fracture. No statistical difference was found between the graphene-added groups and the control groups in terms of the EIT, ηIT and CIT, except that the CIT was significantly lower in the LR + 0.01 than in the control group. Graphene addition had no significant adverse effect on the stickiness and DC of both LR and LV.
RESUMO
PURPOSE: The main aim of the present study was to carry out a scoping review on the differences in degree of conversion of monomers regarding several types resin cements, indirect restorative materials, and light-curing procedures used in dentistry. METHOD: A bibliographic review was performed on PubMed using the following search items: "degree of conversion" OR "filler" AND "resin cement" OR "inorganic cement" AND "organic" OR "radiopacity" OR "refractive" OR "transmittance" OR "type" AND "resin composite." The search involved articles published in English language within the last thirteen years. A research question has been formulated following the PICO approach as follow: "How different is the degree of conversion of monomers comparing several types of resin-matrix cements?". RESULTS: Within the 15 selected studies, 8 studies reported a high degree of conversion (DC) of the organic matrix ranging from 70 up to 90% while 7 studies showed lower DC values. Dual-cured resin-matrix cements revealed the highest mean values of DC, flexural strength, and hardness when compared with light- and self-polymerized ones. DC mean values of resin-matrix cements light-cured through a ceramic veneer with 0.4 mm thickness were higher (~ 83%) than those recorded for resin-matrix cements light-cured through a thicker ceramic layer of 1.5 mm (~ 77%). CONCLUSIONS: The highest percentage of degree of conversion of monomers was reported for dual-cured resin-matrix cements and therefore both chemical and light-induced pathways promoted an enhanced polymerization of the material. Similar degree of conversion of the same resin-matrix cement were recorded when the prosthetic structure showed a low thickness. On thick prosthetic structures, translucent materials are required to allow the light transmission achieving the resin-matrix cement. CLINICAL RELEVANCE: The chemical composition of resin-matrix cements and the light-curing mode can affect the polymerization of the organic matrix. Thus, physical properties of the materials can vary leading to early clinical failures at restorative interfaces. Thus, the analysis of the polymerization pathways of resin-matrix cements is significantly beneficial for the clinical performance of the restorative interfaces.
Assuntos
Polimerização , Cimentos de Resina , Cimentos de Resina/química , Resinas Compostas/química , Teste de Materiais , Restauração Dentária Permanente/métodos , Humanos , Cura Luminosa de Adesivos DentáriosRESUMO
Aim: To prepare experimental adhesive (EA) with 1% and without chitosan nanoparticles on dentin conditioned with a conventional technique phosphoric acid (PA) compared with two different contemporary techniques: photodynamic therapy (PDT) and femtosecond laser (FSL). Method: The methodology consisted of synthesis of EA and 1% chitosan-modified adhesive (CMA). Scanning electron microscopy, dentin adhesive interface assessment, energy-dispersive spectroscopy, shear bond strength (SBS), degree of conversion (DC), and bond failure were assessed. Teeth were selected, disinfected, and mounted in acrylic up to the cementoenamel junction. Occlusal enamel was removed and teeth were randomly allocated into groups and conditioned. These included Group 1: samples treated with PA; Group 2: specimens conditioned with methylene blue photosensitizer (MBP) activated by PDT; and Group 3: samples conditioned with FSL. Following different conditioning regimes, specimens were bonded using 1% CMA and EA. The composite buildup was followed by SBS testing and a bond failure assessment. DC was assessed for both EA and CMA. Analysis of variance and Tukey's post hoc test were used to compare the mean and standard deviation of SBS and DC in different experimental groups, with a significance level of p < 0.05. Results: Dentin pretreated with etch and rinse demonstrated the highest bond strength with 1% CMA. Dentin conditioned with MBP activated by PDT and bonded to EA showed the lowest bond scores. Overall SBS values of 1% CMA were better than EA irrespective of the conditioning regime of dentin. The DC was higher in EA adhesive. This was followed by DC in 1% CMA. DC in EA was found to be comparable with 1% CMA. Conclusions: PA remains the gold standard for dentin conditioning. The incorporation of 1% chitosan in adhesive improves SBS and results in no change in DC. The use of FSL in dentin conditioning can be used as an alternative approach as it results in SBS within acceptable limits. The study was approved by the ethical board of King Saud University.
RESUMO
Although self-adhesive resin cements are convenient and less technique-sensitive materials for dental clinicians, they exhibit a lower degree of conversion due to acidic components in their composition. Supplementation of the initiator, accelerator, and activator in self-adhesive resin cements has been suggested to compensate for the lower degree of conversion. This study aimed to evaluate the effects of different combinations of self-curing initiators, self-curing activators, and accelerators on the degree of conversion (DC) of self-adhesive resin cements. A dual-cured self-adhesive resin was prepared using six combinations of initiators, activators, and accelerators. The change in the DC over time was evaluated with and without light curing. The film thickness, flow properties, and cytotoxicity of each formulation were assessed. The results showed that all supplemental components had an effect on increasing the DC, but a greater increase in the DC was observed in the following order: activator, accelerator, and initiator. The cytotoxicity of the resin cements was related to the DC values, as resin cements with lower DC values exhibited higher cytotoxicity. The film thickness met the ISO standards for all groups. The results suggest that utilizing an activator is the most effective approach to enhance the DC in self-adhesive resin cement and that cytotoxicity tended to increase with lower DC values, whereas film thickness and flow properties demonstrated no correlation with DC values.
RESUMO
Background/purpose: Recently, a group of universal single-shade resin-based composites (RBCs) has been developed to simplify the process of shade selection. Excellent mechanical and physical properties are crucial for the ultimate success and clinical longevity of restorations. Therefore, evaluating the properties of the single-shaded RBCs is imperative. This study aimed to determine the flexural strength (FS) and degree of conversion (DC) of universal single-shade RBCs. Materials and methods: In this study, four commercial RBCs were used; three universal single-shade RBCs; Omnichroma (OC), Charisma® Diamond ONE (CD), and Vittra APS Unique (VU), and a conventional nanohybrid composite Filtek™ Z250 XT (FT) which was used as a control. Sixty composite beams and 40 composite discs were used for FS and DC, respectively. A universal test machine with a three-point bending test was used to measure the FS, whereas the DC was measured using a Fourier-transform infrared spectrometer (FTIR). Three fractured specimens from each resin composite group were qualitatively analyzed using scanning electron microscopy. Results: ANOVA was used to compare the mean values of FS and DC among the four RBCs (OC, CD, VU, and FT). Highly significant differences were observed in the mean FS and DC values (F = 673.043, p < 0.001 and F (=782.4, p < 0.0001), respectively. The highest FS was observed in the CD group, followed by FT and VU groups; the lowest value was observed in the OC group. In addition, a statistically significant difference was identified in DC values. The highest DC value was observed in VU, followed by OC and CD, and the lowest DC value was observed in FT. Conclusion: Universal single-shade RBCs demonstrated a good FS, except for OC, which exhibited a significantly low FS. The DC of the universal single-shade RBCs was higher than that of the conventional nanohybrid composite restorative material.
RESUMO
Assessment of the antimicrobial, micro tensile bond strength (µTBS), and degree of conversion (DC) of fifth-generation adhesive modified using photoactivated 0.5% rose bengal (RB) and photoactivated RB-doped titanium dioxide nanoparticles (TiO2NPs) in different concentrations (2% and 5%) as compared with the unmodified adhesive bonded to the carious affected dentin (CAD). Forty mandibular molars with caries progression up to the middle third of the dentin, as per the International Caries Detection and Assessment System (ICDAS) score of 4 and 5 were included. Specimens were divided into four groups based on etch and rinse adhesive (ERA) modification group 1: unmodified ERA, group 2: photoactivated 0.5% RB photosensitizer (PS) modified ERA, group 3: photoactivated RB-doped 2 wt% TiO2NPs adhesive, group 4: photoactivated RB-doped 5 wt% TiO2NPs adhesive. Followed by adhesive and composite restoration on the CAD surface. All the specimens were thermocycled and an assessment of µTBS and failure pattern analysis was performed. The antibacterial potency of RB and RB-doped TiO2NPs (2% and 5%) followed by their activation using visible light against Streptococcus mutans (S.mutans) were tested. The survival rate of S.mutans was assessed using the Kruskal-Wallis test. The analysis of µTBS involved the use of ANOVA, followed by a post-hoc Tukey honestly significant difference (HSD) multiple comparisons test. Group 1 (Unmodified ERA) (0.52 ± 0.31 CFU/mL) treated samples unveiled the highest means of bacterial survival and lowest µTBS (11.32 ± 0.63 MPa). Nevertheless, group 4: photoactivated RB-doped 5 wt% TiO2NPs adhesive displayed the lowest outcomes of S.mutans survival (0.11 ± 0.02 CFU/mL) and highest bond strength (18.76 ± 1.45 MPa). The photoactivated RB-doped 2 wt% TiO2NPs in adhesive demonstrated promising enhancements in both µTBS and antibacterial efficacy against S.mutans. However, it is noteworthy that this modification led to a decrease in the DC of the adhesive. RESEARCH HIGHLIGHTS: Unmodified ERA-treated samples unveiled the highest bacterial survival and the lowest µTBS. Photoactivated RB-doped 5 wt% TiO2NPs adhesive displayed the lowest S.mutans survival rate and highest bond strength. DC decreased with an increase in concentration of TiO2.
RESUMO
OBJECTIVES: To investigate the flexural strength (FS), elastic modulus (E), Martens hardness (HM), water sorption (wsp), water solubility (wsl) and degree of conversion (DC) of 3D-printed, milled and injection molded splint materials. METHODS: Specimens (N = 1140) were fabricated from five 3D-printed (GR-22 flex, GR-10 guide, ProArt Print Splint clear, V-Print Splint, V-Print Splint comfort), five milled (BioniCut, EldyPlus, ProArt CAD Splint clear, Temp Premium Flexible, Thermeo) and two injection molded (PalaXPress clear, Pro Base Cold) materials. FS, E, HM, wsp, wsl and DC were tested initially (24 h, 37 °C, H2O), after water storage (90 d, 37 °C, H2O) as well as after thermal cycling (5000 thermal cycles, 5/55 °C). Data were analyzed with Kolmogorov-Smirnov, Kruskal- Wallis, Mann-Whitney U test and Spearman's correlation (p < 0.05). RESULTS: Initially, the mean flexural strength values ranged from 1.9 to 90.7 MPa for printed, 3.8 to 107 MPa for milled and 99.7 to 102 MPa for injection molded materials. The initial mean elastic modulus values were 0.0 to 2.4 GPa for printed, 0.1 to 2.7 GPa for milled and 2.8 GPa for injection molded materials. The initial mean Martens hardness values were 14.5 to 126 N/mm2 for printed, 50.2 to 171 N/mm2 for milled and 143 to 151 N/mm2 for injection molded materials. Initially, the mean water sorption values ranged from 23.1 to 41.2 µg/mm3 for printed, 4.5 to 23.5 µg/mm3 for milled and from 22.5 to 23.3 µg/ mm3 for injection molded materials. The initial mean water solubility values ranged from 2.2 to 7.1 µg/mm3 for printed, 0.0 to 0.5 µg/mm3 for milled and 0.1 to 0.3 µg/mm3 for injection molded materials. After water storage and thermal cycling most of the values decreased and some increased. The mean DC values ranged initially from 72.3 to 94.5 %, after water storage from 74.2 to 96.8 % and after thermal cycling from 75.6 to 95.4 % for the printed materials. SIGNIFICANCE: The mechanical and physical properties of printed, milled and injection molded materials for occlusal devices vary and are influenced by aging processes. For clinical applications, materials need to be chosen according to the specific indications.
Assuntos
Módulo de Elasticidade , Resistência à Flexão , Dureza , Teste de Materiais , Impressão Tridimensional , Materiais Dentários/química , Solubilidade , Água/químicaRESUMO
OBJECTIVE: This study investigated the influence of photoinitiator types on degree of conversion (DC), rate of polymerization (RP), flexural strength (FS), flexural modulus (FM), and light transmittance (LT) of filled and unfilled light-curable resin cements through different thicknesses and shades of lithium disilicate ceramics. METHODS: Lithium disilicate ceramic discs (IPS Emax Press, background [0.0], 0.5, 1.0, 2.0, 3.0, and 4.0 mm, shades A1 and BL3) were prepared. Experimental resin-based cements [TEGDMA/BisGMA (50/50 mass%)] were prepared using either camphorquinone (CQ)/amine (0.44/1.85 mol%) or TPO (0.44 mol%)], and a micro and nanofiller loads of nil (unfilled); 40/10 mass%; and 50/10 mass%). Resin cements (0.2 mm thick) were placed on the lower surface of the ceramic specimens and light-activated for 30 s from the upper surface using a Bluephase Style curing light (exitance at tip: 1236 mW/cm2 ± 1.20). LT and distribution of irradiance through the ceramics were measured using a UV-vis spectrometer and a beam profile camera, respectively (n = 3). The DC and RP were measured in real-time using mid infrared spectroscopy in attenuated total reflectance (ATR) mode (n = 3). FS and FM were measured using a universal testing machine (n = 5). Statistical analyses were performed on LT, DC, RP, FS, and FM data using a general linear model, and supplementary ANOVA and post hoc Tukey multiple comparison test were also performed (α = .05). RESULTS: Thicknesses, shades, photoinitiator type, and fillers load significantly influenced the optical and mechanical characteristics of the resin-based materials (p < 0.05). The BL3 shade ceramic provided higher values of DC, RP, FS, FM, and LT compared with the A1 shade (p < 0.05). Increasing ceramic thickness decreased the properties of the resin-based materials (p < 0.05). Generally, TPO improved mechanical properties of the resin cement compared with CQ (p < 0.05). SIGNIFICANCE: The luting process of indirect restorations may be improved by using high molar absorptivity, more reactive, and more efficient photoinitiators such as TPO, as opposed to conventional CQ. The use of such initiator may allow the placement of thicker and more opaque indirect restorations.
Assuntos
Cerâmica , Porcelana Dentária , Resistência à Flexão , Cura Luminosa de Adesivos Dentários , Teste de Materiais , Polimerização , Cimentos de Resina , Cimentos de Resina/química , Porcelana Dentária/química , Cerâmica/química , Ácidos Polimetacrílicos/química , Polietilenoglicóis/química , Fotoiniciadores Dentários/química , Bis-Fenol A-Glicidil Metacrilato/química , Propriedades de Superfície , Terpenos/química , Cânfora/análogos & derivadosRESUMO
Short glass fibers are generally used in posterior dental restorations to enhance the mechanical properties and improve the material microstructure. Two resin-based composites (S0 and SF) were formulated and characterized to investigate the influence of zirconium in their characteristics and properties. The organic part of the investigated materials was the same (BisGMA, TEGDMA, and a photochemical polymerization system), and in the inorganic part, besides quart, glassA, and hydroxylapatite with Zn, sample S0 contained strontium glass with zirconium and sample SF contained fiber powder of chopped zirconium. The samples were characterized by the degree of conversion (DC), mechanical properties, water sorption (WS), scanning electron microscopy (SEM), atomic force microscopy (AFM) before and after the WS test, and antimicrobial properties. The results obtained were subjected to one-way ANOVA and Tukey's statistical tests. Both samples had a high DC. Regarding the mechanical properties, both samples were very similar, except DTS, which was higher for the composite without fibers. After 14 days, the WS value of the SF sample was lower than that of the S0 sample. Water caused significant changes in the topography of the SF sample, but thanks to its antimicrobial properties and the diffusion phenomenon, SF had a more pronounced antimicrobial effect. This study shows that the addition of appropriate amounts of Sr-Zr-glass powder gives the material in which it is added similar properties to material containing chopped zirconium glass fiber powder. According to the antimicrobial test results, resin composites containing experimental zirconia fillings can be considered in future in vitro clinical studies for posterior reconstructions with significantly improved mechanical properties.
RESUMO
This research assessed the effects of pre-heating on the physical-mechanical-chemical properties of different resin composites. For this, resin composites were evaluated in 6 levels: Admira/ADM, Vitra/VIT, Filtek Supreme/FS, Filtek Supreme Flowable/FSF, Filtek One/FO, and Filtek Bulk Fill Flowable/FBF; temperature was evaluated in 4 levels using a composite heater: room temperature/22 ºC, 37 ºC, 54 ºC, and 68 ºC. Response variables were: degree of conversion/DC, flexural strength/FS and color stability/ΔE (immediately after light curing/LC, after 7 days of dark-dry-storage, and after 24 h and 3 days of artificial aging in water at 60 ºC). Data were subjected to 2-way ANOVA (DC and FR) and 3-way repeated measurements ANOVA (ΔE), all followed by Tukey's test (α = 5%). DC were similar (FBF, FS, and FSF) or increased (ADM, FO, and VIT) as the temperature increased. Results of FR were unchanged or increased for all composites except VIT and ADM. High-viscosity composites (VIT and FS) showed higher FR values than low-viscosity composite (FSF). For bulk-fill composites, FBF and FO showed similar results, but lower than high-viscosity composites. Results of color stability showed acceptable values up to 3 days aging except for ADM and FSF. ΔE was not influenced by pre-heating and, overall, ΔE: FS < VIT < FO < FSF < ADM < FBF. Only VIT and FS showed ΔE ≤ 3.3 (clinical threshold). Therefore, the effects of pre-heating depend on the material. The tested materials generally showed similar or enhanced properties after pre-heating (except ADM and VIT).
RESUMO
To evaluate the degree of conversion (DC), surface hardness (SH), and flexural strength (FS) of resin-based core build-up materials. Core build-up materials used were: MultiCore Flow (MCF); Activa (ACT); Core-X Flow (CXF); and everX flow (EVX), and DC, SH and FS were measured. An increase of DC was identified for all materials post-cure, except for EVX. The DC change percentage ranged from 5%-33%, and EVX was displayed the greatest DC rate. All materials displayed an SH increase after 30 days and the greatest increase was observed in ACT. At 1 h, the SH of EVX and CXF was different from the other materials. At 30 days, MCF displayed the greatest SH. All materials displayed an increase in their FS after 30 days except for EVX, and ranging 3%-36% were noticed. Differences observed between materials, thus clinician should be acquainted mechanical properties of these materials to ensure the success of the restorations.
Assuntos
Resinas Compostas , Resistência à Flexão , Dureza , Teste de Materiais , Propriedades de Superfície , Resinas Compostas/química , Materiais Dentários/química , Análise do Estresse Dentário , Polimerização , Vidro/químicaRESUMO
BACKGROUND: To evaluate the physical properties of bioactive glass-modified universal multimode adhesive and its micro-tensile bond strength (µTBS) to artificially induced caries-affected dentin. METHODS: All bond universal adhesive was used in the study. Specimens were divided into 2 main groups: control unmodified adhesive and 5 wt% BAG modified adhesive. The degree of conversion, pH, bioactivity, and viscosity of the adhesives were tested with n = 5 for each test. Micro-tensile bond strength evaluation was done in etch & rinse (ER) and selective-etch (SE) modes, where 24 human molar teeth were used (n = 3), 12 teeth for immediate bond strength, and the other 12 were tested after 6 months of storage in simulated body fluid (SBF). RESULTS: No significant difference was found between the control and the 5wt% BAG groups regarding the degree of conversion (61.01 ± 0.43 and 60.44 ± 0.61 respectively) and the viscosity (109.77 ± 22.3 and 124.3 ± 9.92 respectively). The control group revealed significantly lower pH values than the 5wt% BAG group (3.16 ± 0.5 and 4.26 ± 0.09 respectively). Immediate bond strength results revealed that the 5wt% BAG in the ER mode had the highest bond strength followed by the control group in the ER mode (44.16 ± 7.53 and 44.00 ± 7.96 respectively). SE groups showed that the immediate strength of the 5wt% BAG group was higher than the control group (42.09 ± 6.02 and 39.29 ± 6.64 respectively). After 6 months of storage, bond strength results revealed a decrease in bond strength values for the control groups but not for the 5wt% BAG in both application modes. CONCLUSIONS: The incorporation of BAG (5wt%) improved the universal adhesive micro-tensile bond strength and bond durability for both adhesive application modes without affecting its degree of conversion or viscosity.
Assuntos
Colagem Dentária , Cárie Dentária , Humanos , Cimentos Dentários , Adesivos Dentinários/química , Cimentos de Resina/química , Suscetibilidade à Cárie Dentária , Teste de Materiais , Resistência à Tração , DentinaRESUMO
To incorporate different concentrations of Al2O9Zr3 (1%, 5%, and 10%) nanoparticles (NP) into the ER adhesive and subsequently assess the impact of this addition on the degree of conversion, µTBS, and antimicrobial efficacy. The current research involved a wide-ranging examination that merged various investigative techniques, including the application of scanning electron microscopy (SEM) for surface characterization of NP coupled with energy-dispersive x-ray spectroscopy (EDX), Fourier-transform infrared (FTIR) spectroscopy, µTBS testing, and microbial analysis. Teeth were divided into four groups based on the application of modified and unmodified three-step ER adhesive primer. Group 1 (0% Al2O9Zr3 NPs) Control, Group 2 (1% Al2O9Zr3 NPs), Group 3 (5% Al2O9Zr3 NPs), and Group 4 (10% Al2O9Zr3 NPs). EDX analysis of Al2O9Zr3 NPs was performed showing elemental distribution in synthesized NPs. Zirconium (Zr), Aluminum (Al), and Oxides (O2). After primer application, an assessment of the survival rate of Streptococcus mutans was completed. The FTIR spectra were analyzed to observe the characteristic peaks indicating the conversion of double bonds, both before and after the curing process, for the adhesive Etch and rinse containing 1,5,10 wt% Al2O9Zr3 NPs. µTBS and failure mode assessment were performed using a Universal Testing Machine (UTM) and stereomicroscope respectively. The µTBS and S.mutans survival rates comparison among different groups was performed using one-way ANOVA and Tukey post hoc (p = .05). Group 4 (10 wt% Al2O9Zr3 NPs + ER adhesive) specimens exhibited the minimum survival of S.mutans (0.11 ± 0.02 CFU/mL). Nonetheless, Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) displayed the maximum surviving S.mutans (0.52 ± 0.08 CFU/mL). Moreover, Group 2 (1 wt% Al2O9Zr3 NPs + ER adhesive) (21.22 ± 0.73 MPa) samples displayed highest µTBS. However, the bond strength was weakest in Group 1 (0 wt% Al2O9Zr3 NPs + ER adhesive) (14.13 ± 0.32 MPa) study samples. The etch-and-rinse adhesive exhibited enhanced antibacterial activity and micro-tensile bond strength (µTBS) when 1% Al2O9Zr3 NPs was incorporated, as opposed to the control group. Nevertheless, the incorporation of Al2O9Zr3 NPs led to a decrease in DC. RESEARCH HIGHLIGHTS: 10 wt% Al2O9Zr3 NPs + ER adhesive specimens exhibited the minimum survival of S.mutans. 1 wt% Al2O9Zr3 NPs + ER adhesive samples displayed the most strong composite/CAD bond. The highest DC was observed in Group 1: 0 wt% Al2O9Zr3 NPs + ER adhesive.
Assuntos
Alumínio , Antibacterianos , Dentina , Microscopia Eletrônica de Varredura , Streptococcus mutans , Resistência à Tração , Zircônio , Zircônio/química , Streptococcus mutans/efeitos dos fármacos , Alumínio/química , Alumínio/análise , Alumínio/farmacologia , Antibacterianos/farmacologia , Humanos , Dentina/química , Dentina/efeitos dos fármacos , Dentina/microbiologia , Cárie Dentária/microbiologia , Nanopartículas/química , Espectroscopia de Infravermelho com Transformada de Fourier/métodos , Cimentos Dentários/química , Cimentos Dentários/farmacologia , Espectrometria por Raios X/métodos , Colagem Dentária , Propriedades de Superfície , Adesivos/químicaRESUMO
OBJECTIVES: The study aimed to introduce a novel two-step optical fiber-based photo-activation of dental resin-based composites (RBCs) for reducing polymerization shrinkage stress (PSS). METHODS: Proposed protocol design - in the first step, two flexible plastic optical fibers connected to a dental light curing unit (LCU), were used as light guides inserted into the filling to initiate low-irradiance polymerization from within; in the second step, fibers were extracted and remaining voids were filled with RBC, followed by conventional high-irradiance curing to finalize polymerization. Three bulk-fill RBCs were tested (Beautifil-Bulk Restorative, Filtek Bulk-fill Posterior, Tetric PowerFill) using tooth cavity models. Three non-invasive examination techniques were employed: Digital Holographic Interferometry, Infrared Thermography, and Raman spectroscopy for monitoring model deformation, RBC temperature change, and degree of conversion (DC), respectively. A control group (for each examined RBC) underwent conventional photo-activation. RESULTS: The experimental protocol significantly reduced model deformation by 15 - 35 %, accompanied by an 18 - 54 % reduction in RBC temperature change, emphasizing the impact of thermal shrinkage on PSS. Real-time measurements of deformation and temperature provided indirect insights into reaction dynamics and illuminated potential mechanisms underlying PSS reduction. After a 24-hour dark-storage period, DC outcomes comparable to conventional curing were observed, affirming the clinical applicability of the method. CONCLUSIONS: Protocol involving the use of two 1.5 mm fibers in the first step (300 mW/cm2 x 10 s), followed by a second conventional curing step (1000 mW/cm2 x 10 s), is recommended to achieve the desired PSS reduction, while maintaining adequate DC and ensuring efficient clinical application. CLINICAL SIGNIFICANCE: Obtained PSS reduction offers promise in potentially improving the performance of composite restorations. Additionally, leveraging the flexibility of optical fibers improves light guide approach for restorations on posterior teeth. Meanwhile, implementation in clinical practice is easily achievable by coupling the fibers with commercial dental LCUs using the provided plastic adapter.