Effect of light-, chemical-, and dual-cured universal adhesives on the internal adaptation of resin composites to pulpal and gingival internal walls.

PURPOSE: To compare the internal adaptation of restorative systems bonded to mid-coronal and gingival dentin using light-cured, chemical-cured, and dual-cured adhesives, both immediately and after aging. METHODS: 60 molars were selected and received occluso-mesial preparations with dentin gingival margins. Restorations were performed using different restorative systems with light-cured, chemical-cured, and dual-cured adhesives. Internal adaptation was assessed by examining the percentage of continuous margin (%CM) at the pulpal and gingival dentin under a scanning electron microscope at x200 magnification. Half of the teeth were stored in sterile water for 24 hours, while the other half underwent 10,000 thermal cycles. Micro-morphological analysis was conducted on representative samples at x1,000 magnification. RESULTS: The restorative system with light-cured adhesive exhibited significantly lower %CM values at the gingival dentin, particularly after aging. Aging had a negative impact on the %CM values of the pulpal and gingival dentin in restorative systems with light-cured and dual-cured adhesives. Regional dentin variations influenced the %CM values, especially after aging, regardless of the restorative system used. The tested restorative system with chemical-cured adhesive is preferable for achieving improved internal adaptation when bonding to both mid-coronal and gingival dentin, compared to the other tested systems. CLINICAL SIGNIFICANCE: The study highlights the variations in adhesive performance between different regional dentin areas using the tested restorative systems.

Deep Margin Elevation - A Retrospective Clinical Study.

PURPOSE: The aim of this retrospective study was to assess the short- to mid-term restorative and periodontal outcome of deep margin elevation (DME) performed using resin composite. MATERIALS AND METHODS: Twenty-eight teeth treated with DME and indirect adhesive restorations were followed-up for a mean of 25.4 months (minimum: 12 months). Clinical and radiographic examination assessed the adaptation of the DME material and indirect restorations, presence of recurrent caries or discoloration, periodontal health at DME and non-DME sites, and periapical health. RESULTS: The overall success rate was 96.6%. One tooth showed signs and symptoms of apical pathology after 34 months following DME. No caries, discoloration, or periodontal pockets were detected in any of the treated teeth. DME had no detrimental effect on the gingival/periodontal health or plaque accumulation. There was no correlation between the distance from the DME material to the marginal bone level and pocket depth, gingival inflammation, and plaque accumulation (p > 0.05). CONCLUSION: Deep margin elevation might be considered a safe procedure for teeth with deep subgingival proximal caries in the short- and mid-term.

Fabrication trueness and internal fit of different lithium disilicate ceramics according to post-milling firing and material type.

OBJECTIVES: To evaluate whether post-milling firing and material type affect the fabrication trueness and internal fit of lithium disilicate crowns. METHODS: A prefabricated cobalt chromium abutment was digitized to design a mandibular right first molar crown. This design file was used to fabricate crowns from different lithium disilicate ceramics (nano-lithium disilicate (AM), fully crystallized lithium disilicate (IN), advanced lithium disilicate (TS), and lithium disilicate (EX)) (n = 10). Crowns, the abutment, and the crowns when seated on the abutment were digitized by using an intraoral scanner. Fabrication trueness was assessed by using the root mean square method, while the internal fit was evaluated according to the triple scan method. These processes were repeated after the post-milling firing of AM, TS, and EX. Paired samples t-tests were used to analyze the effect of post-milling firing within AM, TS, and EX, while all materials were compared with 1-way analysis of variance and Tukey HSD tests (α = 0.05). RESULTS: Post-milling firing reduced the surface deviations and internal gap of AM and EX (P ≤ 0.014). AM mostly had higher deviations and internal gaps than other materials (P ≤ 0.030). CONCLUSIONS: Post-milling firing increased the trueness and internal fit of tested nano-lithium disilicate and lithium disilicate ceramics. Nano-lithium disilicate mostly had lower trueness and higher internal gap; however, the maximum meaningful differences among tested materials were small. Therefore, the adjustment duration and clinical fit of tested crowns may be similar. CLINICAL SIGNIFICANCE: Tested lithium disilicate ceramics may be suitable alternatives to one another in terms of fabrication trueness and internal fit, considering the small differences in measured deviations and internal gaps.

Analysis of the Marginal Continuity in Different Designs of Monolithic Zirconia Inlay-Retained Fixed Dental Prostheses: An In Vitro Study.

PURPOSE: To evaluate the marginal integrity of three inlay-retained fixed dental prosthesis (IRFDP) designs fabricated using monolithic zirconia. MATERIALS AND METHODS: In total, 30 IRFDPs were fabricated using 4-YTZP monolithic zirconia and randomly divided into three groups according to the cavity design. Groups ID2 and ID1.5 received an inlay cavity preparation, which includes a proximal box and an occlusal extension with a depth of 2 mm or 1.5 mm, respectively. Group PB received a proximal box cavity preparation without an occlusal extension. The restorations were fabricated and cemented using a dual-cure resin cement (Panavia V5) and subjected to an equivalent of 5 years of aging. The specimens were evaluated under an SEM to measure marginal continuity before and after the aging process. RESULTS: During the whole 5-year aging process, no specimens showed signs of cracking, fracture, or loss of retention in any restorations. In the SEM analysis, most marginal defects observed in the restorations were areas of microgaps at the tooth/cement interface (TC) or zirconia/cement interface (ZC), resulting in loss of adaptation. There was a significant difference between the groups after the aging process at both the TC (F = 4.762, P < .05) and ZC (F = 6.975, P < .05), with Group ID2 presenting the best performance. There was a significant difference between TC and ZC in all groups (P < .05), with ZC presenting more gaps in all groups. CONCLUSIONS: Inlay cavity designs including a proximal box and an occlusal extension exhibited better marginal stability than a proximal box without occlusal extension.

Precision Matters: The Evolution of Impression Systems and Materials.

The clinical success of indirect restorations is directly correlated with their specific anatomic shape and design as well as marginal accuracy and overall precision of fit. These factors require a precise impression of the preparation and, to the extent necessary and possible, other teeth and supporting hard and soft tissues.

Accuracy of Dental Restorations Fabricated Using Milling vs 3D-Printed Molds: A Pilot Study.

PURPOSE: To compare the accuracy of 12 different dental restorations fabricated with milling or 3D-printed molds and robotically controlled casting. MATERIALS AND METHODS: Twelve dental restorations (11 inlays and onlays and 1 crown) were made per restoration type, one per each of the 12 different teeth models (total of 24 restorations). On each tooth preparation, two restorations were manufactured using different CAD/ CAM techniques: (1) milling and (2) robotically controlled casting and 3D-printed molds. In addition, twolayer restorations were manufactured with 3D-printed molds. The marginal and internal gaps were evaluated at 120 points per restoration based on micro-CT 3D imaging. Internal gaps were evaluated using a replica technique with silicone. RESULTS: Median values (interquartile ranges) for marginal gaps, middle internal gaps, and central internal gaps were significantly lower for 3D-printed mold restorations (44.3 [65.4] µm, 95.4 [96.2] µm, and 104.6 [78.1] µm) compared to milled restorations (58.4 [93] µm, 145.9 [85.8] µm, and 138.6 [65.7] µm). Internal gaps in the 3D-printed mold group were 6% to 51% smaller than in the milled group. CONCLUSIONS: The accuracy of restorations fabricated with 3D-printed molds may be preferable compared to milled restorations, except in the case of crown restoration. However, additional studies with a larger number of samples and different types of restorations are needed to confirm the results.

Sixty-month comperative evaluation of a glass hybrid restorative and a composite resin in non-carious cervical lesions of bruxist individuals.

OBJECTIVE: To compare the clinical performance of a glass hybrid (GH) restorative and a nano-ceramic composite resin (CR) in the restoration of non-carious cervical lesions (NCCLs) of bruxist individuals in a 60-month randomized clinical trial. MATERIALS AND METHODS: Twenty-five bruxist candidates having NCCLs were recruited in this clinical study. The depth, height (cervico-incisal), width (mesio-distal), internal angles of the NCCLs, degree of tooth wear (TWI) and gingival index (GI) were measured. One hundred-and-forty-eight NCCLs were restored either with a GH restorative (Equia Forte Fil) or a CR (Ceram.X One Universal). Modified USPHS criteria was used to evaluate restorations after 1 week and 12, 24, 36 and 60 months. Pearson's Chi-Square, Fisher's Exact and Cochran Q tests were run for analysis. Survival rates of the restorations were compared with Kaplan-Meier analysis (p < 0.05). RESULTS: After 60 months, 97 restorations in 15 patients were examined. The recall rate was 60.0%. Retention rates were 73.5% for CR and 66.7% for GH. A total of 29 restorations were lost (13CR (26.5%), 16GH (33.3%)). There was not a significant difference between tested restoratives in retention (p = 0.464), marginal adaptation (p = 0.856) and marginal discoloration (p = 0.273). There was no relationship between internal angle, depth, height or width and retention of the GH or CR restorations (p > 0.05). The increase in retention loss and marginal discoloration of both restorations over time were significant (p < 0.001). Sensitivity or secondary caries were not detected after 60 months. CONCLUSION: GH and nano-ceramic CR showed similar clinical performances in NCCLs after 60 months in patients with bruxism. CLINICAL SIGNIFICANCE: After 60 months, CR and GH materials showed clinically acceptable performances in restoration of NCCLs in patients with bruxism.

Fabrication trueness and marginal quality of additively manufactured resin-based definitive laminate veneers with different restoration thicknesses.

OBJECTIVES: To evaluate how restoration thickness (0.5 mm and 0.7 mm) affects the fabrication trueness of additively manufactured definitive resin-based laminate veneers, and to analyze the effect of restoration thickness and margin location on margin quality. METHODS: Two maxillary central incisors were prepared either for a 0.5 mm- or 0.7 mm-thick laminate veneer. After acquiring the partial-arch scans of each preparation, laminate veneers were designed and stored as reference data. By using these reference data, a total of 30 resin-based laminate veneers were additively manufactured (n = 15 per thickness). All veneers were digitized and stored as test data. The reference and test data were superimposed to calculate the root mean square values at overall, external, intaglio, and marginal surfaces. The margin quality at labial, incisal, mesial, and distal surfaces was evaluated. Fabrication trueness at each surface was analyzed with independent t-tests, while 2-way analysis of variance was used to analyze the effect of thickness and margin location on margin quality (α = 0.05). RESULTS: Regardless of the evaluated surface, 0.7 mm-thick veneers had lower deviations (P < 0.001). Only the margin location (P < 0.001) affected the margin quality as labial margins had the lowest quality (P < 0.001). CONCLUSION: Restoration thickness affected the fabrication trueness of resin-based laminate veneers as 0.7 mm-thick veneers had significantly higher trueness. However, restoration thickness did not affect the margin quality and labial margins had the lowest quality. CLINICAL SIGNIFICANCE: Laminate veneers fabricated by using tested urethane-based acrylic resin may require less adjustment when fabricated in 0.7 mm thickness. However, marginal integrity issues may be encountered at the labial surface.

Assessment of the trueness of additively manufactured mol3% zirconia crowns at different printing orientations with an industrial and desktop 3D printer compared to subtractive manufacturing.

OBJECTIVES: This study endeavours to investigate the effect of printing orientation on the trueness of additively manufactured molar zirconia crowns. The areal surface roughness and the characteristics of the marginal regions of the crowns were also considered. METHODS: Twelve molar crowns were manufactured at 0°, 45°, and, 90° printing orientations in a Lithoz and AON zirconia printer, respectively. Twelve milled crowns were used as a comparison. Samples were scanned and analysed in metrology software to determine the trueness of the groups. Regions of interest were defined as the margins, intaglio surface and contact points. Areal surface roughness and print layer thickness were further analysed using a confocal laser scanning microscope. RESULTS: The results indicate that there are clear differences between the investigated desktop (AON) and industrial (Lithoz) 3D printer. The 45° Lithoz group is the only sample group showing no significantly different results in trueness for all regions analysed compared to the milled group. Areal surface roughness analysis indicates that the print layers in the marginal regions are within clinically tolerable limits and surface characteristics. CONCLUSIONS: The printing orientation for zirconia crowns is critical to trueness, and differences are evident between different AM apparatuses. Considerations for design and orientation between different apparatuses should therefore be considered when utilising direct additive manufacturing processes. The areal surface roughness of the marginal regions is within acceptable clinical limits for all manufacturing processes and print orientations considered. CLINICAL SIGNIFICANCE: The materials and apparatuses for additive manufacturing of zirconia crowns are now clinically acceptable from the perspective of the trueness of a final crown for critical functional surfaces and areal surface roughness of the marginal regions.

Comparison of 3D-Printed Single Crown Outcomes Among Different Computer-Aided Design Software Programs.

PURPOSE: Low-cost resin 3D printers have been used to produce affordable interim single crowns in public and private dental practices. The purpose of this study was to assess the impact of different computer-aided design (CAD) software programs on 3D trueness, microscopic marginal and internal gaps, time to design, and interproximal contacts of low-cost 3D-printed single crowns. MATERIALS AND METHODS: This in vitro study was performed on a total of 90 standardized resin-prepared teeth adapted to a dental manikin. For comparison among CAD software programs, 45 tooth preparations received 3D-printed crowns designed with one of three CAD software programs by an experienced technician and identified as groups TRIOS (n = 15), EXOCAD (n = 15), and ZZ (Zirkonzahn; n = 15). To assess interoperator reproducibility, 15 additional crowns were designed by a dental clinician (group ZZ-DENT) and 15 by a dental prosthetic technician (group ZZ-PROS), both with basic 1-week CAD/CAM training. Finally, as a control group, 15 crowns were milled using a high-end five-axis milling device (group ZZ-CONTROL). Statistically significant differences for 3D trueness, microscopic gaps, time to design, and interproximal contacts among groups were assessed with the Kruskal-Wallis test. RESULTS: No statistically significant differences in 3D trueness or marginal or internal gaps were found, either among different software programs or CAD operators (P > .05). However, Group TRIOS took significantly longer to design than EXOCAD and ZZ groups (P = .001). Less-experienced operators were significantly outperformed in time and interproximal contacts (P = .001) by the CAD technician using the same software program. Finally, control milled crowns (ZZ-CONTROL) significantly outperformed the respective 3D-printed copies (ZZ) in all assessed variables (P < .001). CONCLUSIONS: Different CAD software programs may affect the time required to design, but they do not significantly affect clinical outcomes of low-cost 3D-printed resin crowns if designed by an experienced CAD technician.

The clinical performance of dental resin composite repeatedly preheated: A randomized controlled clinical trial.

OBJECTIVES: To assess the clinical performance of class II restorations performed by repeatedly preheated resin composite "RC" at 68 °C up to ten times. METHODS: 105 patients were selected and randomized into three groups, each comprising 35 patients. Each patient was provided with a single class II Bulk-fill resin composite "BF-RC" posterior restoration based on the number of preheating cycles; group I (H0): The BF-RC was packed non-heated, group II (H1): BF-RC preheated once, and group III(H10): BF-RC preheated ten cycles. These restorations were evaluated at 1, 3,6, and 12 months, using the modified United States Public Health Service "USPHS". Statistical analysis was performed using Kruskal-Wallis test, Mann Whitney U test, and Friedmann test, where p = 0.05. RESULTS: All the 105 restorations did not suffer from any clinical situation that recommended replacement regarding retention, fracture, secondary caries, or anatomical form. Although all performed restorations did have Alpha and Bravo scores with good clinical performance, the non-preheated RC restorations"" suffered from relatively inferior clinical performance through the follow-up period regarding marginal adaptation, marginal discoloration, and color matching when compared to preheated groups. One and ten times of preheating conducted better clinical performance. CONCLUSIONS: After 12-months follow-up, although no restoration needed replacement or repair in the 3 tested groups, restorations with single and ten times of preheating aided in better clinical performance of RC restorations compared to the non-preheated restorations. Preheating of RC for 10 times could be used safely with good clinical performance of restorations. CLINICAL SIGNIFICANCE: By continually preheating RC syringe up to ten times, the dentist will not only benefit from the enhanced clinical performance and easiness of application but also will use preheated RC syringes without hesitation, relying on the absence of drawbacks related to multiple preheating cycles.

Does the Build Orientation Parameter Affect the Fit of Fixed Partial Dentures Fabricated by Additive Manufacturing?

PURPOSE: This in vitro study evaluated the adaptation of cobalt-chromium (Co-Cr) fixed dental prostheses (FDPs) fabricated by selective laser melting (SLM) with different build angles. MATERIALS AND METHODS: Maxillary right first premolars and first molars from a typodont were prepared with 1-mm chamfer, 2-mm occlusal reduction, and total taper of 8 degrees to receive three-unit FDPs. After framework design, data were sent to a laser machine, and 30 specimens were fabricated from Co-Cr metal powder by SLM. Specimens were assigned to three groups (n = 10 per group) with different build angles of 0 (A0), 30 (A30), and 45 (A45) degrees. Marginal and internal fit were evaluated. Results were compared among build orientation groups and abutments. Data were analyzed using the Levene test, t test, and analysis of variance (α = .05). RESULTS: A statistical difference was found between different angle groups (P = .015). At the abutment level, a significant difference was found in the gap values between build orientation groups for the molars (P = .048). Group A0 reported the smallest mean discrepancy values, and group A45 the highest. Statistical differences were found between group A45 and groups A0 (P < .001) and A30 (P < .024). CONCLUSIONS: The fit of printed metal FDPs was affected by the build orientation but remained clinically acceptable.

Influence of CAD-CAM milling strategies on the outcome of indirect restorations: A scoping review.

STATEMENT OF PROBLEM: The influence of computer-aided manufacturing (CAM) parameters and settings on the outcomes of milled indirect restorations is poorly understood. PURPOSE: The purpose of this scoping review was to summarize the current CAM systems, parameters, and setting changes, and their effects on different outcomes of milled indirect restorations and aspects related to their manufacture. MATERIAL AND METHODS: The protocol of this review is available online (https://osf.io/x28ps/). Studies that used at least 2 different parameters (CAM units, number of axes, digital spacers, or protocols with different rotatory instruments, grit-sizes, milling speed, or others) for milling indirect restorations were included. A structured search up to July 2023 was performed by 2 independent reviewers for articles written in English in LILACS, MEDLINE via PubMed, EMBASE, Web of Science, and Scopus. RESULTS: Of 1546 studies identified, 22 were included in the review. Discrepancies were found between the planned and actual measured cement space, with a decreasing linear relationship impacting restoration adaptation at different points. The CEREC MC XL milling machine was the most used system in the included studies, with variations in bur types, milling modes, and number of burs uses affecting internal fit and surface trueness. The results demonstrated the better adaptation of restorations made with 5-axis over 3-axis milling machines. Lithium disilicate and zirconia were the most commonly used materials, and crowns and inlays were popular designs. Marginal and internal adaptation were the primary outcomes assessed using the various techniques. CONCLUSIONS: The study presented a comprehensive exploration of CAM systems and parameters, and their influence on indirect restorations. The planned cement space was not properly reproduced by the milling. Bur characteristics can affect restoration fit and trueness. The 5-axis units seem to result in better-adapted restorations compared with 3- and 4-axis units.

Marginal Fit and Internal Adaptation of Monolithic Zirconia 3-Unit Fixed Dental Prosthesis: In Vitro Study.

PURPOSE: To compare the marginal and internal fit of monolithic zirconia (MZ) 3-unit fixed dental prostheses (FDPs) fabricated using two CAD/CAM workflows: full-chairside (FCH) and lab (LAB). MATERIALS AND METHODS: The right maxillary first premolar and first molar were prepared for MZ 3-unit FDPs on a typodont. CEREC Primescan digitized the typodont model 15 Omes. A total of 30 FDPs was fabricated using two processes: FCH (n = 15) and LAB (n = 15). FCH and LAB FDPs were designed using CEREC SW 4.5.1 and Exocad and milled using CEREC MC X and Zirkonzhan 600/V3, respectively. A fast-sintering protocol was used in both groups. A dual-scan technique was used to assess the cement space at the occlusal surface (OC), axial wall (AX), and margin (MA). Statistical analysis of the results was performed using univariate ANOVA with Scheff. post hoc test (a = .05). RESULTS: Measurements in the FCH and LAB groups were within the clinically acceptable marginal and internal fit. The fit of FCH FDPs at MA, AX, and OC was 77.50 ± 29.99 µm, 99.67 ± 21.58 µm, and 150.03 ± 30.78 µm, respectively. The fit of LAB FDPs at MA, AX, and OC was 100.27 ± 27.06 µm, 116.53 ± 17.90 µm, and 142.30 ± 19.00 µm, respectively. The difference between the two groups was not statistically significant. CONCLUSIONS: MZ 3-unit FDPs fabricated using FCH have clinically acceptable marginal and internal fit. This result verifies the ability of FCH workflow to fabricate MZ mulOunit FDPs in a single visit.

Influence of glazing and aging on the marginal, axial, axio-occlusal, and occlusal fit of 3-unit monolithic zirconia restorations fabricated using additive and subtractive techniques.

STATEMENT OF PROBLEM: Studies are sparse on how glazing and aging influence the fit of additively fabricated monolithic zirconia restorations. PURPOSE: The purpose of this in vitro study was to assess the effect of glazing and aging on the fit of 3-unit monolithic zirconia restorations fabricated using different techniques. MATERIAL AND METHODS: A total of 32 monolithic zirconia restorations were fabricated for a typodont model by using 4 distinct techniques (subtractive fabrication [SF], stereolithography [SLA], digital light processing [DLP], and lithography-based ceramic manufacturing [LCM]). The silicone replica approach was adopted to measure the discrepancy values for premolar and molar abutments after sintering, glazing, and 1 year of aging. The silicone replicas were sliced into mesiodistal and buccopalatal cross-sections, and digital micrographs of the cross-sections were made with a ×80 stereomicroscope. An inherent measuring program was run to record the discrepancy values (µm). Repeated-measures 2-way ANOVAs with the Bonferroni post hoc test were used to statistically analyze the acquired data. (α=.05). RESULTS: From the repeated measures 2-way ANOVAs, both the glazing×fabrication technique and the aging×fabrication technique interactions were not statistically significant (P>.05). Glazing significantly influenced premolar abutment marginal (P=.022) and occlusal (P=.007) discrepancy values, as well as molar abutment marginal discrepancy values (P=.047). Aging had a statistically significant effect on premolar abutment marginal (P=.008) and occlusal (P=.011) discrepancy values, as well as molar abutment occlusal discrepancy values (P=.039). In both the glazing and aging data, for all areas of interest, statistically significant differences were detected among the fabrication techniques (P<.05). The LCM group had the lowest discrepancy values, followed by the SLA, SF, and DLP groups. CONCLUSIONS: The LCM and SLA groups outperformed the other groups in terms of fit accuracy. The glazing and aging procedures altered the discrepancy values. The marginal discrepancy values of all groups were below the threshold of clinical acceptability (<120 µm).

Comparison of wear and marginal fitness of 3D-printed deciduous molar crowns: An in vitro study.

This study aimed to evaluate the wear resistance of primary tooth enamel and 3 kinds of 3D printing materials and to compare the marginal fitness and internal suitability of prefabricated all-ceramic crowns, computer-aided design/manufacturing (CAD/CAM) all-ceramic crowns, and three 3D-printed deciduous molar crowns. Multifunctional friction wear testing machine was used to image the wear surface of the sample and calculate the maximum wear depth and volume loss value of each sample. The internal fit evaluation used the silicon replica method, The four points were measured using scanning electron microscopy (SEM). The obtained data were statistically analyzed using ANOVA and Tukey HSD-test with a fully randomized design (p<0.05). The results showed the wear resistance of E-Dent400 was better than that of PEEK and three different 3D printed materials have good wear resistance compared with the primary tooth enamel. The measured values at M1 and M4 of E-Dent400 were both the smallest.

Clinical evaluation of posterior restorations over wet and dry dentin using an etch-and-rinse adhesive: A 36-month randomized clinical trial.

OBJECTIVES: To evaluate the clinical performance of posterior restorations over wet and dry dentin with an etch-and-rinse adhesive after 36 months of clinical service. METHODS: Forty-five participants were recruited, each one had at least two posterior teeth that needed restoration. Ninety restorations were placed on Class I or Class II cavities. For the restoration protocol, a simplified etch-and-rinse adhesive (Adper Single Bond 2) was applied over wet (WD) or dry dentin (DD) and later restored with a bulk-fill composite (Filtek Bulk Fill) under rubber dam isolation. Each restoration was evaluated using the World Dental Federation (FDI) criteria after 6, 12, and 36 months of clinical service, regarding the following principal restoration characteristics: postoperative sensitivity, marginal discoloration, marginal adaptation, fracture of material and retention, and recurrence of caries. Kruskal Wallis analysis of variance rank (α = 0.05) and Kaplan-Meier survival analysis were used for statistical analysis. RESULTS: After 36 months of clinical evaluation, no significant difference between groups was observed in each FDI criterion (p > 0.05). Twenty restorations (WD=10, DD=10) showed minor marginal staining, and twenty-two restorations (WD=11, DD=11) presented small marginal adaptation defects (p > 0.05). Four restorations were lost (WD = 2, DD = 2) and the fracture rates (95% confidence interval) were 94.9% for each one, without significant difference between wet and dry dentin (p > 0.05). SIGNIFICANCE: The degree of dentin moisture does not seem to affect the clinical performance of a simplified etch-and-rinse adhesive in posterior restorations when the adhesive is applied vigorously over the dentine surface.

Noninvasive assessment of novel nanohybrid resin cement adaptation using cross-polarization optical coherence tomography.

OBJECTIVES: Zein-coated magnesium oxide nanoparticles (zMgO NPs) can potentially improve cement adaptation to the tooth-restoration interface, which would aid in minimizing marginal leakage and secondary caries. The aim of this study was to assess the effect of incorporating zMgO NPs on the adaptation of self-adhesive resin cement using cross-polarization optical coherence tomography (CP-OCT) and scanning electron microscopy (SEM). METHODS: Resin inlays were fabricated to be cemented in Class-I cavities of extracted human molars. All specimens were randomly divided into five groups (n = 10), and the resin inlays were cemented using self-adhesive resin cement with various concentrations of zMgO NPs (0% [control], 0.3%, 0.5%, 1%, 2%). Characterization was done by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and SEM. The specimens were examined for interfacial adaptation under CP-OCT. Floor and wall adaptation measurements were analyzed by software on 20 B-scans, and samples were sectioned for interfacial measurement by SEM. RESULTS: Results for CP-OCT and SEM showed a statistically significant increase of adaptation in the floor and wall of resin cement filled with zMgO NPs compared to the control. The samples enhanced with 0.3% and 0.5% showed a statistically significantly better adaptation in floor and wall in CP-OCT and SEM. However, there was no significant difference between the 1%, 2%, and control groups for CP-OCT and SEM analysis. SIGNIFICANCE: The incorporation of zMgO NPs in self-adhesive resin cement can enhance the cement's properties by significantly improving its wall and floor adaptation.

Evaluation of surface microhardness and gingival marginal adaptation of three different bulk-fill flowable resin composites: A comparative study.

OBJECTIVES: To evaluate surface microhardness and gingival marginal adaptation of three different bulk-fill flowable resin composites (FB-RBCs) in Class V cavities with enamel or dentin margins before and after thermocycling (TMC). MATERIALS AND METHODS: Three available FB-RBCs were used; Palfique Bulk Flow (PaBF) (Tokuyama Dental), SDR Flow+ Bulk Fill Flowable (Dentsply Sirona), and I-Flow Bulk Fill (I-Dental). Thirty discs were prepared from each type of FB-RBCs. The discs were subjected to Vickers microhardness tester machine. Class V cavities were prepared on 180 molars. Gingival margins of half the specimens were prepared above CEJ and the other half below CEJ. Cavities were restored with FB-RBCs for gingival marginal adaptation test. Two-way ANOVA was used in microhardness, while three-way ANOVA was used for marginal adaptation. RESULTS: The used materials showed statistically significant differences in microhardness and marginal adaptation. CONCLUSIONS: Regarding microhardness, PaBF showed the highest value before TMC and SDR was the highest after TMC. Regarding marginal adaptation, SDR revealed the best marginal adaptation than PaBF and I-flow, either subjected to TMC or not. CLINICAL SIGNIFICANCE: The longevity of cervical restorations depend on both the location of the cavity margin and the material used. The microfractures in resin composite surface due to low surface microhardness as well as marginal gaps seen in laboratory studies could be considered as an indicative parameter for clinical problem associated with marginal differences.

Evaluation of marginal and internal adaptation of veneers generated by the guided prosthetic tooth preparation system.

OBJECTIVE: This in vitro study aimed to assess and contrast the marginal and internal adaptation of all-ceramic prefabricated veneers manufactured via the FirstFit guided tooth preparation system against all-ceramic veneers produced using the chairside Computer-Aided Design/Computer Aided Manufacture (CAD/CAM) system following identical guided preparation protocols. MATERIALS AND METHODS: Two main groups were included, with 16 lithium disilicate veneers per group. Four typodonts were used for the test (FirstFit) and control CAD/CAM groups. Intraoral scans created master casts and preparation guides. Guides performed preparations on typodont teeth (two central incisors and two lateral incisors). Prepared teeth were scanned (CEREC Omnicam) to design and mill CAD/CAM veneers. Marginal gap thickness and cement space thickness were measured using light microscopy at four locations: marginal, cervical internal, middle internal, and incisal internal. RESULTS: No significant difference existed between groups for marginal adaptation (p = 0.058) or incisal internal adaptation (p = 0.076). The control group had significantly lower values for middle internal adaptation (p = 0.023) and cervical internal adaptation (p = 0.019). CONCLUSIONS: Guided preparation evaluation showed no significant differences in marginal or incisal internal adaptation. The CAD/CAM group had significantly lower middle and cervical internal adaptation values.