Effects of hexagonal boron nitride on mechanical properties of bone cement (Polymethylmethacrylate).

OBJECTIVES: The aim of this study was to investigate the effects of adding hexagonal boron nitride at four different concentrations to polymethylmethacrylate (PMMA) bone cement, which is commonly used in orthopedic surgeries, on the mechanical properties and microarchitecture of the bone cement. MATERIALS AND METHODS: The study included an unaltered control group and groups containing four different concentrations (40 g of bone cement with 0.5 g, 1 g, 1.5 g, 2 g) of hexagonal boron nitride. The samples used for mechanical tests were prepared at 20±2ºC in operating room conditions, using molds in accordance with the test standards. As a result of the tests, the pressure values at which the samples deformed were determined from the load-deformation graphs, and the megapascal (MPa) values at which the samples exhibited strength were calculated. RESULTS: The samples with 0.5 g boron added to the bone cement had significantly increased mechanical strength, particularly in the compression test. In the group where 2 g boron was added, it was noted that, compared to the other groups, the strength pressure decreased and the porosity increased. The porosity did not change particularly in the group where 0.5 g boron was added. CONCLUSION: Our study results demonstrate that adding hexagonal boron nitride (HBN) to bone cement at a low concentration (0.5 g / 40 g PPMA) significantly increases the mechanical strength in terms of MPa (compression forces) without adversely affecting porosity. However, the incorporation of HBN at higher concentrations increases porosity, thereby compromising the biomechanical properties of the bone cement, as evidenced by the negative impact on compression and four-point bending tests. Boron-based products have gained increased utilization in the medical field, and HBN is emerging as a promising chemical compound, steadily growing in significance.

Biological Effects of PMMA and Composite Resins on Human Gingival Fibroblasts: An In Vitro Comparative Study.

The use of temporary resin for provisional restorations is a fundamental step to maintain the position of prepared teeth, to protect the pulpal vitality and the periodontal health as well as the occlusion. The present study aimed at evaluating the biological effects of two resins used in dentistry for temporary restorations, Coldpac (Yates Motloid) and ProTemp 4™ (3M ESPE ™), and their eluates, in an in vitro model of human gingival fibroblasts (hGFs). The activation of the inflammatory pathway NFκB p65/NLRP3/IL-1ß induced by the self-curing resin disks was evaluated by real-time PCR, Western blotting and immunofluorescence analysis. The hGFs adhesion on resin disks was investigated by means of inverted light microscopy and scanning electron microscopy (SEM). Our results suggest that hGF cells cultured in adhesion and with eluate derived from ProTemp 4™ (3M ESPE ™) resin evidenced a downregulation in the expression of the inflammatory mediators such as NFκB p65, NLRP3 and IL-1ß compared to the cells cultured with Coldpac (Yates Motloid) after 24 h and 1 week of culture. Furthermore, the cells cultured with ProTemp 4™ (3M ESPE ™) after 24 h and 1 week of culture reported a higher cell viability compared to the cells cultured with Coldpac (Yates Motloid), established by MTS cell analysis. Similar results were obtained when hGFs were placed in culture with the eluate derived from ProTemp 4™ (3M ESPE ™) resin which showed a higher cell viability compared to the cells cultured with eluate derived from Coldpac (Yates Motloid). These results highlighted the lower pro-inflammatory action and improved cell biocompatibility of ProTemp 4™ (3M ESPE ™), suggesting a better performance in terms of cells-material interaction.

Evaluating the antifungal effectiveness, leaching characteristics, flexural strength, and impact strength of polymethyl methacrylate added with small-scale silver nanoparticles - An in vitro study.

AIM: (1) To assess the release of stable silver nanoparticles (AgNPs) of small scale dimension added to heat polymerized polymethyl methacrylate (PMMA) in 6 months. (2) Assessing the influence of incorporating minimal concentrations of stable AgNPs with nanoscale dimensions into heat polymerized PMMA over a 6 month period on its antifungal efficacy (AF), flexural strength (FS), and impact strength (IS). SETTINGS AND DESIGN: Incorporating nanoparticles with a very small scale may have minimal impact on mechanical properties due to their diminutive size. However, the influence of these small scaled nanoparticles on antimicrobial efficacy and potential escalation in toxicity to host cells through leaching remains unexplored. AgNPs were prepared using an Ultrasonic Probe sonicator and the addition of ammonia to obtain stabilized AgNPs (< 0.01 nm) of small scale dimension. The characterization of these AgNPs involved ultraviolet visible spectroscopy, X ray diffraction, Zetasizer, and transmission electron microscopy with energy dispersive spectroscopy (TEM). MATERIALS AND METHODS: The prepared AgNPs were then added in various percentages by weight (0%-0.5%) to fabricate 252 modified PMMA samples of sizes 10 mm × 3 mm (AF, n = 108), 65 mm × 10 mm × 3 mm (FS, n = 72), and 65 mm × 10 mm × 2.5 mm (IS, n = 72) as per ADA specification no. 12. These samples underwent testing for leaching out of AgNPs and efficacy against Candida albicans for 6 months. The effect on FS and IS was evaluated using the three point bending test and Charpy's Impact Tester, respectively. STATISTICAL ANALYSIS USED: Intergroup comparison of CFU between various concentrations of AgNP was done using the Kruskal-Wallis ANOVA test succeeded by Mann-Whitney test for pair wise comparisons. Difference in CFU of various concentrations over 6 months was seen using one way ANOVA test. Intergroup comparison of FS and IS was performed using a one way ANOVA test, followed by a post hoc Tukey's test for pair wise comparisons. RESULTS: Repeated tests showed no leaching out of AgNPs from the denture base resin into the storage medium. All concentrations of AgNPs incorporated in resin showed inhibition of Candida growth. Intergroup comparison of FS and IS revealed highly statistically significant differences (F = 15.076, P < 0.01 and F = 28.266, P < 0.01) between the groups showing a reduction in strength. CONCLUSION: The AgNPs of small scale dimension incorporated into the denture base resin imparted a strong antifungal effectiveness against C. albicans, which did not decline during the study period and did not cause any release of nanoparticles. 0.5% showed the best antifungal efficacy. This may prove to be a viable and highly effective treatment for the prevention of Candida associated denture stomatitis. However, the inclusion of these particles resulted in a decrease in both FS and IS, and this reduction was directly proportional to the percentage of added AgNPs, with 0.5% demonstrating the least IS and FS.

Detection and identification of single ribonucleotide monophosphates using a dual in-plane nanopore sensor made in a thermoplastic via replication.

We report the generation of ∼8 nm dual in-plane pores fabricated in a thermoplastic via nanoimprint lithography (NIL). These pores were connected in series with nanochannels, one of which served as a flight tube to allow the identification of single molecules based on their molecular-dependent apparent mobilities (i.e., dual in-plane nanopore sensor). Two different thermoplastics were investigated including poly(methyl methacrylate), PMMA, and cyclic olefin polymer, COP, as the substrate for the sensor both of which were sealed using a low glass transition cover plate (cyclic olefin co-polymer, COC) that could be thermally fusion bonded to the PMMA or COP substrate at a temperature minimizing nanostructure deformation. Unique to these dual in-plane nanopore sensors was two pores flanking each side of the nanometer flight tube (50 × 50 nm, width × depth) that was 10 µm in length. The utility of this dual in-plane nanopore sensor was evaluated to not only detect, but also identify single ribonucleotide monophosphates (rNMPs) by using the travel time (time-of-flight, ToF), the resistive pulse event amplitude, and the dwell time. In spite of the relatively large size of these in-plane pores (∼8 nm effective diameter), we could detect via resistive pulse sensing (RPS) single rNMP molecules at a mass load of 3.9 fg, which was ascribed to the unique structural features of the nanofluidic network and the use of a thermoplastic with low relative dielectric constants, which resulted in a low RMS noise level in the open pore current. Our data indicated that the identification accuracy of individual rNMPs was high, which was ascribed to an improved chromatographic contribution to the nano-electrophoresis apparent mobility. With the ToF data only, the identification accuracy was 98.3%. However, when incorporating the resistive pulse sensing event amplitude and dwell time in conjunction with the ToF and analyzed via principal component analysis (PCA), the identification accuracy reached 100%. These findings pave the way for the realization of a novel chip-based single-molecule RNA sequencing technology.

High-Density Microporous Drainage-Integrating Sheath Flow Generator for Streamlining Microfluidic Cell Sorting Systems.

Tremendous efforts have been made to develop practical and efficient microfluidic cell and particle sorting systems; however, there are technological limitations in terms of system complexity and low operability. Here, we propose a sheath flow generator that can dramatically simplify operational procedures and enhance the usability of microfluidic cell sorters. The device utilizes an embedded polydimethylsiloxane (PDMS) sponge with interconnected micropores, which is in direct contact with microchannels and seamlessly integrated into the microfluidic platform. The high-density micropores on the sponge surface facilitated fluid drainage, and the drained fluid was used as the sheath flow for downstream cell sorting processes. To fabricate the integrated device, a new process for sponge-embedded substrates was developed through the accumulation, incorporation, and dissolution of PMMA microparticles as sacrificial porogens. The effects of the microchannel geometry and flow velocity on the sheath flow generation were investigated. Furthermore, an asymmetric lattice-shaped microchannel network for cell/particle sorting was connected to the sheath flow generator in series, and the sorting performances of model particles, blood cells, and spiked tumor cells were investigated. The sheath flow generation technique developed in this study is expected to streamline conventional microfluidic cell-sorting systems as it dramatically improves versatility and operability.

Enhanced osteogenesis and physicochemical properties of PMMA bone cement with SrBG/HA porous core-shell microspheres.

Artificial bone graft with osteoconductivity, angiogenesis, and immunomodulation is promising clinical therapeutics for the reluctant healing process of bone defects. Among various osteogenic substitutes, polymethyl methacrylate (PMMA) bone cement is a quit competitive platform due to its easy deployment to the bone defects with irregular shape and biomimetic mechanical properties. However, the biologically inert essence of PMMA is reliant on the passive osseointegration and cannot provide sufficient biologic cues to induce fast bone repair. Bioactive glass could serve as an efficient platform for the active osteogenesis of PMMA via ionic therapy and construction of alkaline microenvironment. However, the direct of deployment of bioactive glass into PMMA may trigger additional cytotoxicity and hinder cell growth on its surface. Hence we incorporated ionic therapy as osteogenic cue into the PMMA to enhance the biomedical properties. Specifically, we synthesized core-shell microspheres with a strontium-doped bioactive glass (SrBG) core and hydroxyapatite (HA) shell, and then composited them with PMMA to introduce multifunctional effects of HA incorporation, alkaline microenvironment construction, and functional ion release by adding microsphere. We preparedxSrBG@HA/PMMA cements (x= 30, 40, 50) with varied microsphere content and evaluated impacts on mechanical/handling properties, ion release, and investigated the impacts of different composite cements on proliferation, osteogenic differentiation, angiogenic potential, and macrophage polarization. These findings provide new perspectives and methodologies for developing advanced bone biomaterials to promote tissue regeneration.

Polymeric optical fiber biosensor with PAMAM dendrimer-based surface modification and PlGF detection for pre-eclampsia diagnosis.

Pre-eclampsia (PE) is a life-threatening complication that occurs during pregnancy, affecting a large number of pregnant women and newborns worldwide. Rapid, on-site and affordable screening of PE at an early stage is necessary to ensure timely treatment and minimize both maternal and neonatal morbidity and mortality rates. Placental growth factor (PlGF) is an angiogenic blood biomarker used for PE diagnosis. Herein, we report the plasmonic fiber optic absorbance biosensor (P-FAB) strategy for detecting PlGF at femtomolar concentration using polymethyl methacrylate (PMMA) based U-bent polymeric optical fiber (POF) sensor probes. A novel poly(amidoamine) (PAMAM) dendrimer based PMMA surface modification is established to obtain a greater immobilization of the bioreceptors compared to a linear molecule like hexamethylenediamine (HMDA). Plasmonic sandwich immunoassay was realized by immobilizing the mouse anti-PlGF (3H1) on the U-bent POF sensor probe surface and gold nanoparticles (AuNP) labels conjugated with mouse anti-PlGF (6H9). The POF sensor probes could measure PlGF within 30 min using the P-FAB strategy. The limit-of-detection (LoD) was found to be 0.19 pg/mL and 0.57 pg/mL in phosphate-buffered saline and 10× diluted serum, respectively. The clinical sample testing, with eleven positive and eleven negative preeclamptic pregnancy samples, successfully confirmed the accuracy, reliability, specificity, and sensitivity of the P-FAB based POF sensor platform, thereby paving the way for cost-effective technology for PlGF detection and its potential for pre-eclampsia diagnosis.

Injectable isoniazid-loaded bone cement based on hydrazone bonds achieving long-term release and decent mechanical properties.

A robust and easily manufactured high-strength and long-term release hydrazone-based isoniazid acrylic (HIA) bone cement is reported. The mechanical strength of HIA bone cement is similar to that of normal polymethyl methacrylate (PMMA) bone cement, far surpassing that of traditional isoniazid-containing antibiotic-loaded bone cement (INH bone cement). Isoniazid is connected to the bone cement through bioorthogonal hydrazone chemistry, and it possesses release properties superior to those of INH bone cement, allowing for the sustained release of isoniazid for up to 12 weeks. In vivo and in vitro studies also indicate that HIA cement exhibits better biocompatibility than INH bone cement. The results of this study not only signify progress in the realm of antimicrobial bone cement for addressing bone tuberculosis but also enhance our capacity to create and comprehend high-performing antimicrobial bone cement.

Mass Spectrometry-Based Proteomics of Poly(methylmethacrylate)-Embedded Bone.

Liquid chromatography-tandem mass spectrometry (LC-MS/MS) is a widely employed technique in proteomics research for studying the proteome biology of various clinical samples. Hard tissues, such as bone and teeth, are routinely preserved using synthetic poly(methyl methacrylate) (PMMA) embedding resins that enable histological, immunohistochemical, and morphological examination. However, the suitability of PMMA-embedded hard tissues for large-scale proteomic analysis remained unexplored. This study is the first to report on the feasibility of PMMA-embedded bone samples for LC-MS/MS analysis. Conventional workflows yielded merely limited coverage of the bone proteome. Using advanced strategies of prefractionation by high-pH reversed-phase liquid chromatography in combination with isobaric tandem mass tag labeling resulted in proteome coverage exceeding 1000 protein identifications. The quantitative comparison with cryopreserved samples revealed that each sample preparation workflow had a distinct impact on the proteomic profile. However, workflow replicates exhibited a high reproducibility for PMMA-embedded samples. Our findings further demonstrate that decalcification prior to protein extraction, along with the analysis of solubilization fractions, is not preferred for PMMA-embedded bone. The biological applicability of the proposed workflow was demonstrated using samples of human PMMA-embedded alveolar bone and the iliac crest, which revealed anatomical site-specific proteomic profiles. Overall, these results establish a crucial foundation for large-scale proteomics studies contributing to our knowledge of bone biology.

In vitro damping and strain distribution for implant-supported crowns using 5 different CAD-CAM crowns and 3 different luting cements.

STATEMENT OF PROBLEM: Dental implants are particularly susceptible to occlusal overloading because, unlike natural teeth, they lack a periodontal ligament to help absorb occlusal forces. However, studies evaluating the impact of different crown and luting materials on the damping behavior and strain distribution of implant-supported crowns are lacking. PURPOSE: The purpose of this in vitro study was to investigate the damping behavior and strain distribution of peri-implant bone associated with 5 different CAD-CAM implant-supported crowns and 3 luting materials. MATERIAL AND METHODS: A titanium implant was embedded in a plastic tube with epoxy resin and 5 different crown materials (polymethyl methacrylate, resin-infiltrated ceramic, lithium disilicate, titanium, and zirconia) luted to prosthetic abutments with 3 different luting materials (zinc oxide non-eugenol cement, zinc phosphate cement, and adhesive resin cement) and an uncemented condition were tested (n=5). Strain gauges were attached at the crestal and apical levels of the implant model. All specimens were load tested from 0 to 200 N. Slopes of load/time, microstrain/time, and time required to reach the maximum load were examined to represent the damping behavior. Absolute maximum strain (AMS) and its occurrence level were examined to represent the strain distribution. Two-way ANOVA, followed by the Tukey HSD test, were used for statistical analysis (α=.05). RESULTS: All slopes and times to reach the maximum load in each crown material were statistically similar (P>.05), except for the polymethyl methacrylate group, which showed less steepness in all slopes and more time required to reach the maximum load significantly (P<.05). Both the polymethyl methacrylate group (224.5 ±30.2) and the titanium group (224.0 ±24.3) exhibited significantly higher AMS at the crestal level compared with the resin-infiltrated ceramic group (210.6 ±5.0) (P<.05). The lithium disilicate (218.1 ±15.0) and zirconia groups (217.3 ±14.8) demonstrated comparable AMS values with the others (P>.05). The uncemented group demonstrated steeper slopes and less time required to reach the maximum load compared with the adhesive resin group (P<.05), while slopes and times of the zinc phosphate and zinc oxide non-eugenol groups were comparable (P>.05). The uncemented group (242.7 ±25.3) exhibited significantly higher AMS at the crestal level than the other groups (P<.05). CONCLUSIONS: The crown material significantly affected the damping behavior of peri-implant bone, unlike the luting material. Polymethyl methacrylate with a high damping behavior exhibited high strain at the crestal level. In contrast, resin-modified ceramic with a moderate damping behavior exhibited low strain at the crestal level. Strain at the crestal level could be effectively reduced by approximately 13% through cementation.

[Comparison of polymethyl methacrylate skull implant fixation by three types of titanium fasteners]. / Sravnenie sposobov fiksatsii implantov cherepa iz polimetilmetakrilata tremya vidami titanovykh krepezhei.

OBJECTIVE: To evaluate mechanical strength of three methods of polymethyl methacrylate skull implant fixation in two experimental models. MATERIAL AND METHODS: The first experiment was performed on a plastic model that was as close as possible to bone in structural characteristics. The second experiment was performed on a biological specimen (a ram's head). We assessed the quality of implant fixation to bone window edges by craniofixes, ties and microscrews and lateral intercortical screws. RESULTS: Craniofixes are feasible for small flat flaps, but not advisable for wide highly curved implants. They are also the most expensive method of fixation. Implant fixation by ties and microscrews is a universal method comparable in price to craniofix. Lateral intercortical fixation is effective both for small flat implants and wide implants with large curvature. However, this method is not always applicable. CONCLUSION: Combined fixation by lateral intercortical screws and ties allows for the most effective fixation while reducing the overall price of consumables.

Preclinical Evaluation of Bioactive Small Intestinal Submucosa-PMMA Bone Cement for Vertebral Augmentation.

In vertebroplasty and kyphoplasty, bioinert poly(methyl methacrylate) (PMMA) bone cement is a conventional filler employed for quick stabilization of osteoporotic vertebral compression fractures (OVCFs). However, because of the poor osteointegration, excessive stiffness, and high curing temperature of PMMA, the implant loosens, the adjacent vertebrae refracture, and thermal necrosis of the surrounding tissue occurs frequently. This investigation addressed these issues by incorporating the small intestinal submucosa (SIS) into PMMA (SIS-PMMA). In vitro analyses revealed that this new SIS-PMMA bone cement had improved porous structure, as well as reduced compressive modulus and polymerization temperature compared with the original PMMA. Furthermore, the handling properties of SIS-PMMA bone cement were not significantly different from PMMA. The in vitro effect of PMMA and SIS-PMMA was investigated on MC3T3-E1 cells via the Transwell insert model to mimic the clinical condition or directly by culturing cells on the bone cement samples. The results indicated that SIS addition substantially enhanced the proliferation and osteogenic differentiation of MC3T3-E1 cells. Additionally, the bone cement's biomechanical properties were also assessed in a decalcified goat vertebrae model with a compression fracture, which indicated the SIS-PMMA had markedly increased compressive strength than PMMA. Furthermore, it was proved that the novel bone cement had good biosafety and efficacy based on the International Standards and guidelines. After 12 weeks of implantation, SIS-PMMA indicated significantly more osteointegration and new bone formation ability than PMMA. In addition, vertebral bodies with cement were also extracted for the uniaxial compression test, and it was revealed that compared with the PMMA-implanted vertebrae, the SIS-PMMA-implanted vertebrae had greatly enhanced maximum strength. Overall, these findings indicate the potential of SIS to induce efficient fixation between the modified cement surface and the host bone, thereby providing evidence that the SIS-PMMA bone cement is a promising filler for clinical vertebral augmentation.

Aging processes in dental thermoplastics - Thermoanalytical investigations and effects on Vickers as well as Martens hardness.

OBJECTIVE: The influence of various aging protocols, representing and accelerating influences present in the dental context, on possible changes in the microstructure and mechanical properties of thermoplastics was investigated. In order to minimize the complexity of the systems, first pure polymers and then later the equivalent dental polymeric materials were analyzed. MATERIALS AND METHODS: Pure polymers (Poly(methyl methacrylate) - PMMA, Polyoxymethylene homopolymer - POM-H, Polyether ether ketone - PEEK, Nylon 12 - PA12, Polypropylene - PP) were analyzed before as well as after applying different aging protocols relevant to the oral environment (ethanol, thermocycling, alkaline and acidic setting) by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The thermoanalytical parameters used were glass transition temperature (Tg), melting peak and crystallization peak temperature (Tpm, Tpc) and decomposition behavior. In a second step selected commercially available dental products (Telio CAD - PMMAD, Zirlux Acetal - POMD, Juvora Natural Dental Disc - PEEKD) aged by the protocol that previously showed strong effects were examined and additionally tested for changes in their Vickers and Martens hardness by Mann-Whitney-U test. RESULTS: The combinations of pure polymers and viable aging protocols analyzed within this study were identified via TGA or DSC as PA12 & thermocycling, POM-H & denture cleanser/lactic acid/ethanol, PP & lactic acid. The dental polymeric materials PMMAD and POMD due to aging in lactic acid showed slight but significantly (p < 0.01) reduced Vickers and partly Martens hardness. PEEK showed the greatest material resistance within this study.

A meta-analysis comparing the efficacy of mineralized collagen-polymethylmethacrylate and polymethylmethacrylate bone cements in the treatment of vertebral compression fractures.

PURPOSE: Vertebral compression fractures are often treated with vertebroplasty, and filling the injured vertebrae with bone cement is a key part of vertebroplasty. This meta-analysis was performed to compare the clinical efficacy and safety of mineralized collagen-polymethylmethacrylate (MC-PMMA) and polymethylmethacrylate (PMMA) bone cement in the treatment of vertebral compression fractures by vertebroplasty. METHODS: A computerized search of the published literature on mineralized collagen-polymethylmethacrylate and polymethylmethacrylate bone cement in the treatment of vertebral compression fractures was conducted in the China National Knowledge Infrastructure (CNKI), Wanfang database, PubMed, Embase, and Cochrane Library. The search was carried out from the time the database was created to March 2023 and 2 researchers independently conducted literature searches to retrieve a total of 884 studies, of which 12 were included in this meta-analysis. Cochrane systematic review methods were used to assess the quality of the literature and a meta-analysis was performed using ReviewManager 5.4 software. RESULTS: The results of the present meta-analysis showed that in postoperative adjacent vertebral fractures [OR = 0.25; 95% CI (0.15, 0.41)], postoperative cement leakage [OR = 0.45; 95% CI (0.30, 0.68)], Oswestry Disability Index (ODI) scores in the first 3 days after surgery [OR = -0.22; 95% CI (-0.42, -0.03)], ODI score at 6-12 months postoperatively [OR = -0.65; 95% CI (-0.97, -0.32)], visual analog scale (VAS) score at 6-12 months postoperatively [OR = -0.21; 95% CI (-0.46, 0.04)], and 1-year postoperative CT values [OR = 5.56; 95% CI (3.06, 8.06)], the MC-PMMA bone cement group was superior to the PMMA bone cement group. However, the differences between the two groups were not statistically different in terms of cement filling time, cement filling volume, operation time, intraoperative bleeding, hospitalization time, postoperative (<1 week, 3-6 months) vertebral body posterior convexity Cobb's angle, postoperative (<1 week, 6-12 months) vertebral body anterior margin relative height, postoperative (≤3 days, 1-3 months) pain VAS score and postoperative (1-3 months) ODI score. CONCLUSIONS: Compared with PMMA bone cement, the application of MC-PMMA bone cement is advantageous in reducing postoperative complications (adjacent vertebral fracture rate, cement leakage rate), pain relief, and functional recovery in the long-term postoperative period (>6 months), but there is still a need for more high-quality randomized controlled studies to provide more adequate evidence.

Integrated Experimental and Mathematical Exploration of Modular Tissue Cultures for Developmental Engineering.

Developmental engineering (DE) involves culturing various cells on modular scaffolds (MSs), yielding modular tissues (MTs) assembled into three-dimensional (3D) tissues, mimicking developmental biology. This study employs an integrated approach, merging experimental and mathematical methods to investigate the biological processes in MT cultivation and assembly. Human dermal fibroblasts (HDFs) were cultured on tissue culture plastics, poly(lactic acid) (PLA) discs with regular open structures, or spherical poly(methyl methacrylate) (PMMA) MSs, respectively. Notably, HDFs exhibited flattened spindle shapes when adhered to solid surfaces, and complex 3D structures when migrating into the structured voids of PLA discs or interstitial spaces between aggregated PMMA MSs, showcasing coordinated colonization of porous scaffolds. Empirical investigations led to power law models simulating density-dependent cell growth on solid surfaces or voids. Concurrently, a modified diffusion model was applied to simulate oxygen diffusion within tissues cultured on solid surfaces or porous structures. These mathematical models were subsequently combined to explore the influences of initial cell seeding density, culture duration, and oxygen diffusion on MT cultivation and assembly. The findings underscored the intricate interplay of factors influencing MT design for tissue assembly. The integrated approach provides insights into mechanistic aspects, informing bioprocess design for manufacturing MTs and 3D tissues in DE.

Interfacial blending in co-axially electrospun polymer core-shell fibers and their interaction with cells via focal adhesion point analysis.

Electrospun polymer scaffolds have gained prominence in biomedical applications, including tissue engineering, drug delivery, and wound dressings, due to their customizable properties. As the interplay between cells and materials assumes fundamental significance in biomaterials research, understanding the relationship between fiber properties and cell behaviour is imperative. Nevertheless, altering fiber properties introduces complexity by intertwining mechanical and surface chemistry effects, challenging the differentiation of their individual impacts on cell behaviour. Core-shell fibers present an appealing solution, enabling the control of mechanical properties of scaffolds, flexibility in material and drug selection, efficient encapsulation, strong protection of bioactive drugs against harsh environments, and controlled, prolonged drug release. This study addresses a key challenge in core-shell fiber design related to the blending effect between core and shell polymers. Two types of fibers, PMMA and core-shell PC-PMMA, were electrospun, and thorough analyses confirmed the desired core-shell structure in PC-PMMA fibers. Surface chemistry analysis revealed PC diffusion to the PMMA shell of the core-shell fiber during electrospinning, subsequently prompting an investigation of the fiber's surface potential. Conducting cellular studies on osteoblasts by super-resolution confocal microscopy provided insights into the direct influence of interfacial polymer blending and, consequently, altered fiber surface and mechanical properties on cell focal adhesion points, bridging the gap between material attributes and cell responses in core-shell fibers.

Prolonged post-washing in ethanol decreases bond strength of additively manufactured crown materials.

OBJECTIVES: This study aimed to investigate the effect of post-washing duration and crown thickness on the bond strength between additively manufactured crown materials and dental cement in vitro. METHODS: Rectangular-shaped specimens of two thicknesses (1.5 and 2.0 mm) were additively manufactured from permanent VarseoSmile Crown (VC) and long-term temporary NextDent (ND) materials. The specimens were post-washed (n = 160) in ethanol for 5 min, 10 min, 1 h, and 8 h then cemented with dual-cure resin cement. Twenty PMMA (TC) were milled as a control. A chevron-notch test was performed to measure the maximum load until failure (N). Interfacial bond strength (J/m2) was calculated and statistically analysed. The mode of failure was analysed by scanning electron microscopy (SEM). RESULTS: There was a significant difference in the bond strength between all groups (p < 0.01). VC at 1.5mm thickness post-washed for 10 min showed the highest mean bond strength (1.77 ±0.96 J/m2) while VC at 2.0mm thickness post-washed for 8 h showed the lowest (0.22 ±0.10 J/m2). Exposure to ethanol for 8 h resulted in lower bond strength. Within the type of material, there were no differences in bond strength between the thicknesses when post-washed for the same duration. CONCLUSIONS: Prolonged post-washing of AM crown materials can significantly decrease the bond strength to resin cement. There were no differences between the permanent and long-term temporary AM materials. When post-washed for 5 min, AM materials observed comparable or higher bond strength values compared to PMMA. CLINICAL SIGNIFICANCE: The output of this research serves as a guide for dental practitioners, emphasising the importance of adhering to correct post-washing procedures for optimal bond strength of additively manufactured crown materials.

Rapid prototyping of PMMA-based microfluidic spheroid-on-a-chip models using micromilling and vapour-assisted thermal bonding.

The application of microfluidic devices as next-generation cell and tissue culture systems has increased impressively in the last decades. With that, a plethora of materials as well as fabrication methods for these devices have emerged. Here, we describe the rapid prototyping of microfluidic devices, using micromilling and vapour-assisted thermal bonding of polymethyl methacrylate (PMMA), to create a spheroid-on-a-chip culture system. Surface roughness of the micromilled structures was assessed using scanning electron microscopy (SEM) and atomic force microscopy (AFM), showing that the fabrication procedure can impact the surface quality of micromilled substrates with milling tracks that can be readily observed in micromilled channels. A roughness of approximately 153 nm was created. Chloroform vapour-assisted bonding was used for simultaneous surface smoothing and bonding. A 30-s treatment with chloroform-vapour was able to reduce the surface roughness and smooth it to approximately 39 nm roughness. Subsequent bonding of multilayer PMMA-based microfluidic chips created a durable assembly, as shown by tensile testing. MDA-MB-231 breast cancer cells were cultured as multicellular tumour spheroids in the device and their characteristics evaluated using immunofluorescence staining. Spheroids could be successfully maintained for at least three weeks. They consisted of a characteristic hypoxic core, along with expression of the quiescence marker, p27kip1. This core was surrounded by a ring of Ki67-positive, proliferative cells. Overall, the method described represents a versatile approach to generate microfluidic devices compatible with biological applications.

Magnetic macroporous chitin microsphere as a support for covalent enzyme immobilization.

In this study, a novel magnetic macroporous chitin microsphere (MMCM) was developed for enzyme immobilization. Chitin nanofibers were prepared and subsequently subjected to self-assembly with magnetic nanoparticles and PMMA (polymethyl methacrylate). Following this, microspheres were formed through spray drying, achieving a porous structure through etching. The MMCM serves as an effective support for immobilizing enzymes, allowing for their covalent immobilization both on the microsphere's surface and within its pores. The substantial surface area resulting from the porous structure leads to a 2.1-fold increase in enzyme loading capacity compared to non-porous microspheres. The MMCM enhances stability of the immobilized enzymes under various pH and temperature conditions. Furthermore, after 20 days of storage at 4 °C, the residual activity of the immobilized enzyme was 2.93 times that of the free enzyme. Even after being recycled 10 times, the immobilized enzyme retained 56.7 % of its initial activity. It's noteworthy that the active sites of the enzymes remained unchanged after immobilization using the MMCM, and kinetic analysis revealed that the affinity of the immobilized enzymes rivals that of the free enzymes.

Antibiotic-Loaded Ultrahigh Molecular Weight Polyethylenes.

The occurrence of periprosthetic joint infections (PJI) after total joint replacement constitutes a great burden for the patients and the healthcare system. Antibiotic-loaded polymethylmethacrylate (PMMA) bone cement is often used in temporary spacers during antibiotic treatment. PMMA is not a load-bearing solution and needs to be replaced by a functional implant. Elution from the ultrahigh molecular weight polyethylene (UHMWPE) bearing surface for drug delivery can combine functionality with the release of clinically relevant doses of antibiotics. In this study, the feasibility of incorporating a range of antibiotics into UHMWPE is investigated. Drug stability is assessed by thermo-gravimetric analysis and nuclear magnetic resonance spectroscopy. Drug-loaded UHMWPEs are prepared by compression molding, using eight antibiotics at different loading. The predicted intra-articular concentrations of drugs eluted from UHMWPE are above minimum inhibitory concentration for at least 3 weeks against Staphylococci, which are the major causative bacteria for PJI. The antibacterial efficacy is confirmed for samples covering 2% of a representative knee implant in vitro over 72 h, showing that a small fraction of the implant surface loaded with antibiotics may be sufficient against Staphylococci.