Evaluation of adhesive properties and enzymatic activity at the hybrid layer of a simplified adhesive loaded with 0.2 % Cu and 5 % ZnO nanoparticles: A Randomized Clinical Trial and ex vivo analysis.

OBJECTIVE: The aim of this study was to evaluate the effect of an adhesive loaded with 0.2 % copper (Cu) and 5 % zinc oxide (ZnO) nanoparticles (Nps) on its adhesive properties and enzymatic activity at the hybrid layer ex vivo in a randomized clinical model. METHODS: Fifteen patients participated in this study, and a total of 30 third molars were used. Occlusal cavities (4 × 4 × 2 mm) were made in each tooth, and randomly divided into 2 groups: (i) Experimental group: commercial adhesive loaded with 0.2wt % CuNps and 5wt % ZnONps; and (ii) Control Group: non-loaded commercial adhesive. Teeth were restored with resin composite. Thirty days later, extractions were performed. Extracted teeth were longitudinally sectioned. Nps in powder were characterized by field emission scanning electron microscope (FE-SEM) and energy dispersive X-ray (EDX) analysis. Microtensile bond strength (µTBS), degree of conversion (DC), and nanoleakeage (NL) tests were executed. In situ zymography (Zym) was performed to evaluate the gelatinolytic activity at the hybrid layer. Student's t-test (α = 0.05) was applied for all tests. RESULTS: µTBS and DC did not show significant differences (p > 0.05) between both groups. However, NL and gelatinolytic activity at the hybrid layer showed significant values (p < 0.05) for experimental group in comparison with control group. CONCLUSION: The addition of 0.2 % CuNps and 5 % ZnONps to a universal adhesive decreases NL and gelatinolytic activity at the hybrid layer, without jeopardizing its adhesive properties. SIGNIFICANCE: This randomized clinical trial with ex vivo analysis demonstrate that a commercial adhesive modified with 0.2wt % Cu and 5wt % ZnO Nps that does not affect its adhesive properties, reducing gelatinolytic activity and nanoleakage at the hybrid layer, which should contribute to an improvement of long term bonding-dentine clinical performance.

Physicochemical properties and antibiofilm activity of mineral trioxide aggregate associated with farnesol.

This study assessed the physicochemical and antibiofilm properties of white mineral trioxide aggregate (MTA) associated with 1 or 2% of farnesol. Setting time was evaluated based on ISO 6876/2012. Radiopacity was evaluated by radiographic analysis. pH was assessed after time intervals of 1, 3, 7, 14, 21, and 28 days. Solubility (% mass loss) and volumetric change (by micro-CT) of the cements were evaluated after immersion in distilled water. The presence of voids inside the materials was assessed by using micro-CT. Antibiofilm activity against Enterococcus faecalis was evaluated by crystal violet assay and the modified direct contact test performed with biofilm previously formed on bovine root dentin for 14 days. Data were submitted to ANOVA/Tukey tests with 5% significance level. The incorporation of farnesol into MTA increased its setting time, but decreased its solubility at 30 days and its volumetric loss in all periods (p < 0.05). Radiopacity and solubility after 7 days were similar among the materials (p > 0.05). The association of farnesol showed the highest pH value after 1 and 3 days (p < 0.05). The association of farnesol with MTA promoted a decrease in the presence of voids, and increased the antimicrobial activity on biofilm biomass of E. faecalis (p < 0.05). In conclusion, the addition of farnesol can be suggested to improve the antimicrobial properties and the consistency of MTA.

Influence of Battery Levels in Cordless LED Light-curing Units on Properties of Resin Cement and Glass Fiber Post Retention.

PURPOSE: This study aimed to assess the impact of battery levels in single-peak and multi-peak light-curing units (LCUs) on irradiance, and their effects on glass fiber post push-out bond strength to root dentin and the degree of conversion of dual-cure universal resin cement. METHODS AND MATERIALS: Sixty bovine roots underwent endodontic treatment and were randomly distributed into 6 groups (n=10), formed by combining two LCUs (single-peak and multipeak) and three battery levels (100%, 50%, and 10%). A spectrophotometer measured irradiance (mW/ cm2) and spectral irradiance (mW/cm2/nm). Push-out bond strength (PBS) tests occurred at three root regions (cervical, middle, and apical), with optical and scanning electron microscopy for failure mode analysis. Degree of conversion (DC) was evaluated across the root regions. Data were analyzed using two-way repeated measures ANOVA and the Tukey HSD test. The Fisher exact test verified failure modes (α=0.05). RESULTS: As multipeak LCU battery levels decreased, emitted irradiance also diminished, with notable PBS reductions in the apical thirds. Failure modes were influenced by different conditions, primarily exhibiting mixed modes. Battery levels significantly impacted DC in the multipeak LCU, particularly in the cervical region, while the single-peak LCU exhibited DC reduction at the 10% battery level in the cervical region. CONCLUSIONS: Emitted irradiance, resin cement DC, and glass fiber post bond strength to root dentin may be influenced by varying cordless LCUs and battery levels.

Engineering a dysbiotic biofilm model for testing root caries interventions through microbial modulation.

BACKGROUND: This study aimed to engineer and optimise a dysbiotic biofilm model to develop in vitro root caries for investigating microbial modulation strategies. The model involved growing complex biofilms from a saliva inoculum collected from four volunteers using two strategies. In the first strategy ("pre-treatment strategy"), bovine root slabs were used, and two natural compounds were incorporated at time 0 of the 10-day biofilm experiment, which included sucrose cycles mimicking the cariogenic environment. In the second strategy ("post-treatment strategy"), mature biofilms were grown in a modified Calgary biofilm device coated with collagen and hydroxyapatite for 7 days and then were exposed to the same natural compounds. The metatranscriptome of each biofilm was then determined and analysed. Collagenase activity was examined, and the biofilms and dentine were imaged using confocal and scanning electron microscopy (SEM). Mineral loss and lesion formation were confirmed through micro-computed tomography (µ-CT). RESULTS: The pH confirmed the cariogenic condition. In the metatranscriptome, we achieved a biofilm compositional complexity, showing a great diversity of the metabolically active microbiome in both pre- and post-treatment strategies, including reads mapped to microorganisms other than bacteria, such as archaea and viruses. Carbohydrate esterases had increased expression in the post-treated biofilms and in samples without sugar cycles, while glucosyltransferases were highly expressed in the presence of sucrose cycles. Enrichment for functions related to nitrogen compound metabolism and organic cyclic component metabolism in groups without sucrose compared to the sucrose-treated group. Pre-treatment of the roots with cranberry reduced microbial viability and gelatinase (but not collagenase) activity (p < 0.05). SEM images showed the complexity of biofilms was maintained, with a thick extracellular polysaccharides layer. CONCLUSIONS: This root caries model was optimized to produce complex cariogenic biofilms and root caries-like lesions, and could be used to test microbial modulation in vitro. Pre-treatments before biofilm development and cariogenic challenges were more effective than post-treatments. The clinical significance lies in the potential to apply the findings to develop varnish products for post-professional tooth prophylaxis, aiming at implementing a strategy for dysbiosis reversal in translational research. Video Abstract.

Photo-crosslinkable hydrogel incorporated with bone matrix particles for advancements in dentin tissue engineering.

The objective of this study was to create injectable photo-crosslinkable biomaterials, using gelatin methacryloyl (GelMA) hydrogel, combined with a decellularized bone matrix (BMdc) and a deproteinized (BMdp) bovine bone matrix. These were intended to serve as bioactive scaffolds for dentin regeneration. The parameters for GelMA hydrogel fabrication were initially selected, followed by the incorporation of BMdc and BMdp at a 1% (w/v) ratio. Nano-hydroxyapatite (nHA) was also included as a control. A physicochemical characterization was conducted, with FTIR analysis indicating that the mineral phase was complexed with GelMA, and BMdc was chemically bonded to the amide groups of gelatin. The porous structure was preserved post-BMdc incorporation, with bone particles incorporated alongside the pores. Conversely, the mineral phase was situated inside the pore opening, affecting the degree of porosity. The mineral phase did not modify the degradability of GelMA, even under conditions of type I collagenase-mediated enzymatic challenge, allowing hydrogel injection and increased mechanical strength. Subsequently, human dental pulp cells (HDPCs) were seeded onto the hydrogels. The cells remained viable and proliferative, irrespective of the GelMA composition. All mineral phases resulted in a significant increase in alkaline phosphatase activity and mineralized matrix deposition. However, GelMA-BMdc exhibited higher cell expression values, significantly surpassing those of all other formulations. In conclusion, our results showed that GelMA-BMdc produced a porous and stable hydrogel, capable of enhancing odontoblastic differentiation and mineral deposition when in contact with HDPCs, thereby showing potential for dentin regeneration.

Relined fiberglass posts: influence of resin opacity on the bond strength to intraradicular dentin.

This study aimed to evaluate the bond strength between relined fiberglass posts with different composite resin opacities in different thirds of the intraradicular dentin. Thirty single-rooted premolars were endodontically treated and divided into three groups (n=10): fiberglass posts relined with translucent composite resin, fiberglass posts relined with opaque composite resin, and fiberglass posts without relining. After cementation of the posts, the specimens were cut perpendicular to the long axis of the tooth in slices of approximately 1.3 mm of each third to be analyzed (cervical, middle, and apical) and then subjected to the push-out test. The bond strength (MPa) data were subjected to Shapiro-Wilk normality tests and two-way repeated measures analysis of variance, considering the experimental groups and different regions as study factors. Tukey's post-hoc test (p<.05) was applied for comparisons between the groups. In the cervical third, higher values of bond strength were found for the group relined with translucent resin, with a statistically significant difference for the other groups. In the other regions, both opaque and translucent resins showed similar results, but both showed higher values of bond strength compared to fiberglass posts without relining. The bond strength of fiberglass posts to different thirds of intraradicular dentin is influenced by composite resin relining as well as the opacity of the resin. The use of translucent composite resin is a more effective alternative for fiberglass posts relining.

Effects of blood and root-dentin cleaning on the porosity and bond strength of a collagen bioceramic material.

To assess the effect of cleaning protocols on dentin contaminated with blood in reparative endodontic materials, bovine root samples were divided: no contamination (N); contamination (P); contamination and cleaning with saline (S), 2.5% NaOCl+saline (Na) or 2.5% NaOCl+17% EDTA+saline (NaE) and filled with: mineral trioxide aggregate (MTA), calcium-aluminate-cement (C), or C+collagen (Ccol) (n=13). The samples were evaluated for porosity, chemical composition, and bond strength. MTA porosity was lower than C (p=0.02) and higher than Ccol (p<0.001). P and NaE were similar (p=1.00), but higher than the other groups (p<0.001). MTA bond strength was similar to Ccol (p=0.777) and lower than C (p=0.028). P presented lower bond strength than the N (p<0.001); S and Na were similar to each other (p=0.969), but higher than P and lower than N (p<0.001). It was observed a predominance of mixed and cohesive failures. None of the samples showed Ca/P ratio values similar to human hydroxyapatite. This study showed that contamination with blood increased the materials porosity, but dentin cleaning with 2.5% NaOCl reduced this effect, and the collagen additive reduced the material porosity. Furthermore, blood contamination reduced the materials bond strength, and cleaning with saline or 2.5% NaOCl diminished this effect.

Dentinal Tubule Occluding Efficacy Of Er: YAG Laser And Universal Adhesive Loaded With Nano-Carbonated Apatite.

ER:YAG laser and experimental resin-based dental adhesive loaded with functionalized carbonated apatite filler were used in this study to evaluate the dentin interaction in terms of penetration and occlusion of the dentinal tubules aiding in the control of dentin hypersensitivity (DH). Spheroidal Carbonated apatite nanoparticles (N-CAP), with an average size of 20±5 nm diameter, were synthesized, characterized, and incorporated in a universal adhesive "All Bond Universal, Bisco, USA", in (2% weight) concentration. Er:YAG laser "Lightwalker, FOTONA, EU" was adjusted to an energy output of 40mJ/ pulse and pulse repetition of 10 Hz for 10 seconds. Dentin specimens were prepared from the buccal surface of 75 extracted sound human molars. The specimens were randomly divided into five groups (n=15) according to the surface treatment: Group (L): Laser only; Group (LB): Laser in combination with adhesive; Group (LBN): Laser in combination with adhesive loaded with N-CAP; Group (B): adhesive only; and Group (BN): adhesive loaded with N-CAP. Depth of penetration and occlusion of the dentinal tubules were assessed using Environmental Scanning Electron Microscope Examination (ESEM). One-way ANOVA was used to compare groups, followed by a pairwise test for multiple comparisons (α=0.05). Groups (LB), and (LBN) showed the highest mean of dentinal tubules' penetration, with a non-significant difference between them. In contrast, the specimens treated with laser only (L) showed the most minor penetration. The employment of ER-YAG laser irradiation with the adhesive loaded with N-CAP was evaluated to be effective in penetrating and occluding the opened dentinal tubules.

Dentin erosive wear is reduced by fluoride varnishes containing nanosized sodium trimetaphosphate in vitro.

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Effects on dentin nanomechanical properties, cell viability and dentin wettability of a novel plant-derived biomodification monomer.

OBJECTIVES: To evaluate the effects of dentin biomodification agents (Proanthocyanidin (PAC), Cardol (CD) and Cardol-methacrylate (CDMA) on dentin hydrophilicity by contact angle measurement, viability of dental pulp stem cells (DPSCs) and nanomechanical properties of the hybrid layer (HL). METHODS: CDMA monomer was synthesized from cardol through methacrylic acid esterification. Human extracted third molars were used for all experiments. For nanomechanical tests, specimens were divided in four groups according to the primer solutions (CD, CDMA, PAC and control) were applied before adhesive and composite coating. Nanomechanical properties of the HL were analyzed by nanoindentation test using a Berkovich probe in a nanoindenter. Wettability test was performed on dentin surfaces after 1 min biomodification and measured by contact angle analysis. Cytotoxicity was assessed by a MTT assay with DPSCs after 48 and 72 h. Data were analyzed with Student's t test or Two-way ANOVA and Tukey HSD test (p < 0.05). RESULTS: CD and CDMA solutions achieved greater hydrophobicity and increased the water-surface contact angles when compared to PAC and control groups (p < 0.05). PAC group showed a greater reduction of elastic modulus in nanoindentation experiments when compared to CD and CDMA groups (p < 0.05) after 4 months of aging. CD inhibited cell proliferation compared to all further materials (p < 0.05), whilst CDMA and PAC indicated no cell cytotoxicity to human DPSCs. SIGNIFICANCE: Cardol-methacrylate provided significantly higher hydrophobicity to dentin and demonstrated remarkable potential as collagen crosslinking, attaining the lowest decrease of HL's mechanical properties. Furthermore, such monomer did not affect pulp cytotoxicity, thereby highlighting promising feasibility for clinical applications.

Biocompatibility, bioactivity, porosity, and sealer/dentin interface of bioceramic ready-to-use sealers using a dentin-tube model.

This study evaluated the biocompatibility, bioactivity, porosity, and sealer/dentin interface of Sealer Plus BC (SP), Bio-C Sealer (BIOC), TotalFill BC Sealer (TF), and AH Plus (AHP). Dentin tubes filled with the sealers and empty tubes (control group) were implanted in the subcutaneous tissue of rats for different periods (n = 6 per group/period). Number of inflammatory cells (ICs), capsule thickness, von Kossa reaction, interleukin-6 (IL-6) and osteocalcin (OCN) were evaluated. Porosity and voids in the interface dentin/sealers were assessed by micro-computed tomography. The data were submitted to ANOVA/Tukey's tests (α = 0.05). Greater capsule thickness, ICs and IL-6 immunolabeling cells were observed in AHP. No significant difference in thickness of capsule, ICs, and IL-6- immunolabeling cells was detected between SP and TF, in all periods, and after 30 and 60 days between all groups. At 60 days all groups had reduction in capsule thickness, ICs and IL-6 immunolabeling cells. Von Kossa-positive and birefringent structures were observed in the capsules around the sealers. BIOC, SP, and TF exhibited OCN-immunolabeling cells. All sealers had porosity values below 5%, besides low and similar interface voids. BIOC, SP and TF are biocompatible, bioactive, and have low porosity and voids. The dentin-tube model used is an alternative for evaluating bioceramic materials.

Aspects of glass and hybridization protocols for bonding of fiber posts to root dentine.

This study evaluated bond strength of glass fiber posts to root dentin using push-out (PO) and diametral compression (DC), testing glycolic acid as a conditioner and varying dentin moisture. An additional aim was to test whether DC can be an alternative test to PO for bond strength assessment. Eighty bovine teeth were divided into eight groups (n = 10) defined by the use of either 37% glycolic acid or 37% phosphoric acid (PA) on moist or wet dentin before bonding with either Adapter SingleBond/RelyX ARC or One Step Plus/Duo-Link Bisco. Each tooth provided discs with an internal diameter of 2 mm, external diameter of 5 mm, and height of 2 mm, which underwent PO and DC. Finite element analysis (FEA) was carried out on 3D models. When analyzing PO results through linear regression, the highest values of bond strength were observed using glycolic acid on wet dentin in the cervical and middle thirds of the teeth. Analyzing DC results, the only statistical influence on values was the dental thirds. The scatterplot of the DC results and the PO bond strength values indicated no relationship between the results of the two tests (r = 0.03; p = 0.64). PO test detected more sensitive changes in bond strength values than DC.

Association between underlying dentin shadows (ICDAS 4) and OHRQoL among adolescents from southern Brazil.

This study aimed to assess the association between underlying dentin shadows (UDS) and oral health-related quality of life (OHRQoL) among 15-19-year-old adolescents from southern Brazil. This population-based cross-sectional study included a representative sample of 1,197 15-19-year-old adolescents attending 31 public and private schools from Santa Maria, Brazil. The Oral Health Impact Profile-14 (OHIP-14) was used to evaluate the OHRQoL, and clinical examinations were performed by two calibrated examiners (intra/interexaminer kappa values for caries examination ≥ 0.80) to diagnose UDS (ICDAS code 4 caries lesions). Sociodemographic information and clinical characteristics (overall caries experience, traumatic dental injury, malocclusion, and gingivitis) were also collected as adjusting variables. Multilevel Poisson regression models were used to assess the association between UDS and OHRQoL. Rate ratios (RR) and 95% confidence intervals (CI) were estimated. The UDS prevalence was 8.8% (n = 106 adolescents). In the adjusted models, adolescents with UDS had poorer OHRQoL than those without UDS, and the strength of the association was dependent on the number of lesions per individual. Individuals with 1-2 UDS had a mean OHIP-14 score 8% higher (RR = 1.08; 95%CI: 1.01-1.17) than adolescents without UDS, while those with 3-4 UDS had a mean score 35% higher (RR = 1.35; 95%CI: 1.12-1.63). This negative association was related to physical disability, psychological disability, social disability, and handicap domains. This study showed that UDS was associated negatively with OHRQoL among 15-19-year-old adolescents from southern Brazil. The negative effect of UDS on OHRQoL emphasizes the importance of addressing issues regarding OHRQoL even in the posterior teeth of adolescents.

Er,Cr:YSGG and 980nm diode lasers influence dentin surface volume after cariogenic challenge: in vitro study.

This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey's post-hoc test. The VL values were analyzed using the Kruskal-Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge.

Ultrasonic activation of adhesive systems increases bond strength and intratubular penetration of resin cement in root dentin subjected to radiation therapy.

OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.

In vitro effect of TiF4/NaF solution on the development of radiation-induced dentin caries.

OBJECTIVE: To evaluate the protective effect of an experimental solution containing TiF4/NaF on the development of radiation-induced dentin caries lesions. METHODOLOGY: bovine root samples were irradiated (70Gy) and distributed as following (n=12/group): Commercial Saliva (BioXtra), NaF (500 ppm F-), TiF4 (500 ppm F), TiF4/NaF (TiF4: 300 ppm F-, NaF: 190 ppm F-), and Phosphate buffer solution (PBS, negative control). Biofilm was produced using biofilm from irradiated patients and McBain saliva (0.2% of sucrose, at 37oC and 5% CO2) for five days. The treatments were applied 1x/day. Colony-forming units (CFU) were counted and demineralization was quantified by transversal microradiography. The ANOVA/Tukey test was applied for all parameters. RESULTS: All treatments reduced CFU for total microorganisms. TiF4 reduced Lactobacillus sp. (7.04±0.26 log10 CFU/mL) and mutans streptococci (7.18±0.28) CFU the most, when compared to PBS (7.58±0.21 and 7.75±0.17) and followed by NaF (7.12±0.31 and 7.34±0.22) and TiF4/NaF (7.16±0.35 and 7.29± 0.29). TiF4 and Commercial saliva showed the lowest integrated mineral loss (ΔZ-vol%.mm) (1977±150 and 2062±243, respectively) when compared to PBS (4540±335), followed by NaF (2403±235) and TiF4/NaF (2340±200). Commercial saliva was the only to significantly reduce mineral loss (LD-µm) (111±25) compared to PBS (153±24).Mean mineral loss (R-vol%) decreased by 35.2% for TiF4 (18.2±3.3) when compared to PBS (28.1±2.9) Conclusion: TiF4/NaF has a comparable anti-cariogenic effect to TiF4 and Commercial saliva under the model in this study.

Antimicrobial Efficacy and Dentin Collagen Damage Caused by Calcium Hypochlorite and Sodium Hypochlorite.

This study aimed to evaluate the antimicrobial activity of calcium hypochlorite (Ca (OCl)2) and sodium hypochlorite (NaOCl) using confocal laser scanning microscopy (CLSM) and dentin organic matrix alteration by picrosirius staining and light microscopy (LM). Samples of human extracted teeth were infected with Enterococcus faecalis by centrifugation of the bacterial suspension and were treated with Ca(OCl)2 or NaOCl at 0.5%, 2.5%, and 6% for 15, 30, and 60 seconds. CLSM and viability staining were used to quantitatively analyze the proportions of dead/live bacteria in the canal lumen and border of the root canal. The data were analyzed by ANOVA and Fisher test. For LM analysis, one hundred bovine teeth were randomly divided into 10 test groups (n=10): G1- Without treatment; G2- 17% EDTA; G3- 6% NaOCl; G4- 6% NaOCl + EDTA; G5- 0.5% Ca(OCl)2; G6- 0.5% Ca(OCl)2 + EDTA; G7- 2.5% Ca(OCl)2; G8- 2.5% Ca(OCl)2 + EDTA; G9- 6% Ca(OCl)2; G10- 6% Ca(OCl)2 + EDTA. The samples were fragmented and stained with Picrosirius. Data were analyzed by Kruskal-Wallis and Dunn (P<0.05). There was a strong correlation between the results of the canal lumen and the border of the root canal (r=0.962). Both hypochlorites at a concentration of 0.5% showed less microbial reduction compared to 2.5% and 6% (P<0.05). There was less antimicrobial activity at 15 seconds compared to 30 and 60 seconds (P<0.05). Ca(OCl)2 and NaOCl showed similar results at the same concentrations (P>0.05). In conclusion, Ca(OCl)2 caused fewer alterations to the dentin organic matrix at concentrations of 0.5% and 2.5%. Ca(OCl)2 presents antimicrobial activity similar to NaOCl, and collagen damage is concentration-dependent.

Transdentinal effects of S-PRG fillers on odontoblast-like cells.

OBJECTIVES: To investigate the transdentinal effects of surface reaction-type pre-reacted glass-ionomer (S-PRG) fillers on odontoblast-like cells. METHODS: An eluate of S-PRG fillers was obtained by dissolving the particles in distilled water (1:1 m/v). Dentin discs with similar permeability were mounted into artificial pulp chambers and MDPC-23 cells were seeded on their pulpal surface. The occlusal surface was treated with (n = 10): ultrapure water (negative control - NC), hydrogen peroxide (positive control - PC), S-PRG eluate exposure for 1 min (S-PRG 1 min), or S-PRG filler eluate exposure for 30 min (S-PRG 30 min). After 24 h, cell viability (alamarBlue) and morphology (SEM) were evaluated. The extract obtained from transdentinal diffusion was applied to MDPC-23 pre-cultured in plates for another 24 h to evaluate viability (alamarBlue, 1, 3, and 7 days), gene expression of Col1a1, Alpl, Dspp, and Dmp1 (RT-qPCR, 1 and 7 days), and mineralization (Alizarin Red, 7 days). Data were analyzed with ANOVA (α = 5 %). RESULTS: While S-PRG 1 min did not differ from NC, S-PRG 30 min reduced 17.9 % viability of cells from discs. S-PRG treatments resulted in low cell detaching from dentin, and the remaining cells exhibited typical morphology or minor cytoplasmic contraction. S-PRG 30 min slightly increased cell viability (6 %) 1 day after contact with the extract. S-PRG treatments upregulated the expression of the investigated genes, especially after 1 day. S-PRG 30 min stimulated mineralization activity by 39.7 %. CONCLUSIONS: S-PRG filler eluate does not cause transdentinal cytotoxicity on odontoblast-like cells, and long-term exposure can stimulate their dentinogenic-related mineralization activity. SIGNIFICANCE: The transdentinal elution of ions from S-PRG fillers is not expected to be harmful to the dental pulp and may exert bioactive effects by inducing dentin matrix deposition through the metabolism of underlying odontoblasts.

Fatigue and failure mode analyses of glass infiltrated 5Y-PSZ bonded onto dentin analogues.

The purpose of this study was to evaluate the fatigue survival of 5Y-PSZ zirconia infiltrated with an experimental glass and bonded onto dentin analogues. Disc-shaped specimens of a 5Y-PSZ (Katana UTML Kuraray Noritake) were cemented onto dentin analogs (NEMA G10) and divided into four groups (n = 15): Zctrl Group (control, without infiltration); Zglz Group (Glaze, compression surface); Zinf-comp Group (Experimental Glass, compression surface); Zinf-tens Group (Experimental Glass, tension surface). Surface treatments were varied. Cyclic fatigue loading, oblique transillumination, stereomicroscope examination, and scanning electron microscopy were performed. Fatigue data were analyzed (failure load and number of cycles) using survival analysis (Kaplan-Meier and Log-Rank Mantel-Cox). There was no statistically significant difference in fatigue survival between the Zglz, Zctrl, and Zinf-comp groups. The Zinf-tens group presented a significantly higher failure load when compared to the other groups and exhibited a different failure mode. The experimental glass effectively infiltrated the zirconia, enhancing structural reliability, altering the failure mode, and improving load-bearing capacity over more cycles, particularly in the group where the glass was infiltrated into the tensile surface of the zirconia. Glass infiltration into 5Y-PSZ zirconia significantly enhanced structural reliability and the ability to withstand loads over an increased number of cycles. This approach has the potential to increase the durability of zirconia restorations, reducing the need for replacements and save time and resources, promoting efficiency in clinical practice.

Clinical, Radiographic, and Histological Changes in Enamel and Dentin, According to Caries Care International™ Evaluation, In Permanent Posterior Teeth: An Observational Study / Cambios Clínicos, Radiográficos e Histológicos en Esmalte y Dentina, Según Evaluación de Caries Care International™, en Dientes Posteriores Permanentes: Un Estudio Observacional

SUMMARY: CariesCare International ™ practical guide is a tool for the comprehensive assessment and treatment of caries that synthesizes clinical and radiographic diagnosis and risk factors, classifying the severity, progression, and activity of lesions. The objective of this study was to analyze the validity and prediction characteristics of the proposed dental caries classification in the CariesCare International ™ practical guide as a reference through clinical and radiographic evaluation versus histological evaluation. Ninety-seven permanent posterior teeth were evaluated, and clinical and radiographic diagnoses were determined according to parameters defined in the CariesCare International™ guide as a reference. Subsequently, histological evaluation was performed to compare each stage of dental caries progression, and statistical analysis was applied. When comparing the validity and prediction values between radiographic and clinical diagnoses in relation to histological evaluation, a low sensitivity and high specificity relationship was found. The sensitivity and specificity percentages between the clinical and radiographic methods show that the clinical method has a lower number of false negatives. Histological changes in dental tissue were evident from the earliest stages of lesions, even in those not related to the caries process, indicating that the dentist should be careful when deciding on a treatment plan and take into account all variables involved in the caries process, as proposed by the CariesCare International ™ guide.

La guía práctica CariesCare International™ es una herramienta para la evaluación y tratamiento integral de la caries que sintetiza el diagnóstico clínico y radiográfico y los factores de riesgo, clasificando la gravedad, progresión y actividad de las lesiones. El objetivo de este estudio fue analizar la validez y características de predicción de la clasificación de caries dental propuesta en la guía práctica CariesCare International™ como referencia a través de la evaluación clínica y radiográfica versus la evaluación histológica. Se evaluaron noventa y siete dientes posteriores permanentes y se determinaron diagnósticos clínicos y radiográficos según parámetros definidos en la guía CariesCare International™ como referencia. Posteriormente se realizó una evaluación histológica para comparar cada etapa de progresión de la caries dental y se aplicó análisis estadístico. Al comparar los valores de validez y predicción entre los diagnósticos radiológicos y clínicos en relación con la evaluación histológica, se encontró una relación de baja sensibilidad y alta especificidad. Los porcentajes de sensibilidad y especificidad entre el método clínico y radiográfico muestran que el método clínico tiene un menor número de falsos negativos. Los cambios histológicos en el tejido dental fueron evidentes desde las primeras etapas de las lesiones, incluso en aquellas no relacionadas con el proceso de caries, lo que indica que el odontólogo debe tener cuidado al decidir un plan de tratamiento y tener en cuenta todas las variables involucradas en el proceso de caries, tal como propone la guía CariesCare International™.