Impact of storage conditions on the fracture reliability and physical properties of a dental resin-based composite.

This study investigated the impact of 'storage condition' and 'period of storage' on selected physico-mechanical properties and fracture reliability of a resin-based composite (RBC). Specimens, prepared from a nanofilled RBC (Filtek Z350 XT; 3M ESPE), underwent tests for degree of conversion (DC), flexural strength (σ), flexural modulus (E), and hardness. The specimens were initially grouped into dry storage at 37°C or wet storage in distilled water at 37°C. Subsequently, they were further divided into four subgroups based on the period of storage: 6, 24, 72, or 168 hours. Specimens tested immediately after preparation served as control. Data analysis employed two-way ANOVA and Weibull analysis (α = 5%). Compared to the control, an increase in DC was observed only after 72 hours of dry storage; σ showed higher values after both dry and wet storage, regardless of the storage period (except for the group wet-stored for 168 hours); E increased with dry storage for at least 24 hours or wet storage for 72 hours; and hardness increased after dry storage for at least 24 hours or wet storage for up to 72 hours. The Weibull modulus remained unchanged under any of the distinct storage conditions. Dry storage resulted in greater characteristic strength than the control, whereas wet storage contributed to higher strength values only at shorter periods (up to 24 hours). Overall, the inherent properties of RBCs with a similar composition to that tested in this study may change with varying storage conditions and periods.

Dentin erosive wear is reduced by fluoride varnishes containing nanosized sodium trimetaphosphate in vitro.

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Effect of treatment with phosphate, casein phosphopeptide and fluoride on the remineralization: in vitro study.

This study aimed to evaluate in vitro the effect protocols and anticaries agents containing casein amorphous calcium fluoride phosphopeptide-phosphate (CPP-ACPF, MI Paste Plus), sodium trimetaphosphate (TMP) and fluoride (F), in remineralization of caries lesions. Bovine enamel blocks with initial caries lesions were divided into groups (n = 12): 1) Toothpaste without F-TMP-MI Plus (Placebo); 2) Toothpaste 1100 ppm F (1100F), 3) 1100F + MI Paste Plus (1100F-MI Paste Plus), 4) Toothpaste with 1100F + Neutral gel with 4,500 ppm F + 5%TMP (1100F + Gel TMP) and 5) Toothpaste with 1100F + Neutral gel with 9,000 ppm F (1100F + Gel F). For the 4 and 5 groups the gel was applied only once for 1 minute, initially to the study. For the 3 group, after treatment with 1100F, MI Paste Plus was applied 2x/day for 3 minute. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile and depth of the subsuperficial lesion (PLM); concentrations of F, calcium (Ca) and phosphorus (P) in enamel was determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). Treatment with 1100F alone led to ~ 28% higher remineralization when compared to treatment with 1100F associated with MI Paste Plus (p < 0.001). The 1100F and 1100F + Gel F groups showed similar values for %SHR (p = 0.150). 1100F + Gel TMP treatment also remineralized the enamel surface by ~ 30% and 20% when compared to the 1100F + Gel F and 1100F groups (p < 0.001). The lower lesion depth (ΔKHN) was observed for the 1100F + Gel TMP group (p < 0.001), where it was 54% and 44% lower in comparison to the 1100F and 1100F + Gel F groups (p < 0.001). Polarized light microscopy photomicrographs showed subsurface lesions in all groups, but these lesions were present to a lower extent in the 1100F + Gel TMP group (p < 0.001). Treatment with 1100F + Gel TMP promoted an increase in the concentration of Ca in the enamel by ~ 57% and ~ 26% when compared to the 1100F and 1100F + MI Paste Plus groups (p < 0.001), respectively. There were no significant differences between the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001). Similar values of P in the enamel were observed in the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001), except for the 1100F + Gel TMP group, which presented a high concentration (p < 0.001). We conclude that the 1100F+TMP gel treatment/protocol led to a significant increased remineralization when compared to the other treatments/protocols and may be a promising strategy for patients with early caries lesions.

Mathematical-Physical description of the oxygen-inhibited layer (OIL) in nanofilled dental polymers / Descripción físico-matemática de la capa inhibida por oxígeno en polímeros dentales nano rellenados

Abstract This research evaluates the presence of the oxygen-inhibited layer (OIL) on the top surface of a photopolymerized dental composite resin protected with a glycerin layer. This evaluation was conducted using physical and mathematical methods. Polymerized discs were fabricated to evaluate Vickers microhardness (VHN), and pre-and post-polymerized samples were used for the calculation of C-O/C-H ratios through Fourier Transform Infrared Spectroscopy (FTIR) (n=10), using two types of glycerin, one for medical use (MG) and another for dental use (DG). Surface hardness decreased from MG to DG to CO, and the increase in C-O/C-H ratios decreased in the same order (p<0.05). Samples protected with medical and dental glycerin layers are harder and exhibit lower C-O/C-H bond ratios than the control group.

Resumen La presente investigación evalúa la presencia de la capa inhibida por oxígeno OIL en la última superficie fotocurada de una resina compuesta de uso odontológica que fue protegida con una capa de glicerina. Esta evaluación se hizo a partir de métodos físicos y matemáticos. Se fabricaron discos polimerizados para evaluar la microdureza Vickers (VHN) y pre y post polimerizados para el cálculo de tasas C-O/C-H por medio de Espectroscopía Infrarroja Transformada de Fourier (FTIR) (n=10) usando dos tipos de glicerina, una de uso médico (MG) y otra de uso dental (DG). La dureza superficial disminuyó de MG a DG a CO y el aumento de tasas C-O/C-H disminuyó en ese mismo orden (p<0,05). Las muestras protegidas con capas de glicerina médica y odontológica son más duras y presentan menos cantidad tasas de enlaces C-O/C-H que el grupo control.

Effect of Water and Chlorhexidine with Different Pressures of Oral Irrigation Device on the Surface Roughness and Topography of Giomer

Abstract Objective: To evaluate the effect of different pressures of an oral irrigation device (OID) and the irrigation solution type on the surface roughness of the giomer restorative material. Material and Methods: In this in vitro study, disk-shaped giomer samples were fabricated and assigned to 5 groups (n=23): Group 1, storage in distilled water (control); Group 2, OID #7 pressure/ water; Group 3, OID #10 pressure/ water; Group 4, OID #7 pressure/ 0.05% CHX; Group 5, OID #10 pressure/ 0.05% CHX. The samples' treatment simulated a one-year application of OID. Surface roughness (Ra) and topography of the giomer were evaluated using profilometry and scanning electron microscopy. The data were analyzed with Paired t-test, Tukey, and ANOVA tests (α=0.05). Results: The Ra of the samples increased significantly after treatment with OID (p<0.001). The roughness increase in groups with a pressure of 10 was higher than those with a pressure of 7 (p<0.001). The effect of pressure on surface changes was significant (p<0.001). However, the solution type and the cumulative effect of these two factors were insignificant (p=0.08 and p=0.43, respectively). Conclusion: Oral irrigation device with both solutions significantly increased the surface roughness and topographic changes of the giomer. The severity of these changes was related to the device's pressure.

The influence of general knowledge test performance on self-ratings of and perceived relationships between intelligence, knowledge, and memory.

The present study examined how taking a general knowledge (GK) test affects perceptions of one's intelligence, memory, and knowledge and the relationship between these three constructs. Participants rated their abilities on each construct and the strength of the relationships between them before and after completing an easy or hard GK test or control task. In Experiment 1, participants were (mis)informed that GK questions were correctly answered by 50% of the population; in Experiment 2, no such information was provided. Regardless of (mis)information about others' performance, participants in the Hard condition believed they had a worse memory, were less knowledgeable, and were less intelligent post-task. However, the strength of the perceived relationship between GK and intelligence decreased only when participants were misled. Judgments of one's intelligence, memory, and knowledge can be manipulated by taking a GK test, and individuals engage in self-protective behavior to reduce the potential threat to one's self-concept.

Comparison between different fracture toughness techniques in zirconia dental ceramics.

Vickers indentation (IF) and single-edge-V-notched beam (SEVNB), to measure the fracture toughness (KIC ) of zirconia-based dental ceramics and mathematical models were proposed to establish a correlation between both. Zirconia (ZrO2 ) stabilized with 3 mol. % of Y2 O3 (3Y-TZP) and 5 mol% of Y2 O3 (5Y-PSZ) were compacted (n = 42) and sintered for 2 h at different temperatures (1475°C, 1500°C, 1550°C, or 1600°C). After sintering, they were characterized by relative density using the ASTM C373-88 standard, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The average grain size was measured according to the ASTM E1382-97 standard. The fracture toughness (KIC ) was determined using two methods: Vickers indentation fracture toughness (KIC-IF ): method based on mathematical modeling that considers the parameters used for the Vickers hardness test and Fracture toughness by the single-edge-V-notch-beam (KIC-SEVNB ): method proposed by ISO 23146:08. The main phases of the 3Y-TZP and 5Y-PSZ ceramics were ZrO2 -tetragonal and ZrO2 -cubic, respectively. The 3Y-TZP specimens showed equiaxed grains with average grain sizes ranging from 0.55 to 0.79 µm. The grain sizes of 5Y-PSZ of specimens sintered at 1475°C and 1600°C were 0.62 and 2.32 µm, respectively. For all ceramics the crack size ratio was c/a < 2.5, suggesting a Palmqvist-type crack system. The fracture toughness measured by the Vickers indentation method (KIC-IF ) and by the SEVNB method (KIC-SEVNB ) was the same when the experimental data were fit to a mathematical model.

Flexural strength and Vickers hardness of milled and 3D-printed resins for provisional dental restorations

Various forms of temporary resins are offered on the market; however, the properties of temporary resins obtained by milling and 3D printing have not been fully examined. This study aimed to compare the flexural strength and Vickers hardness of milled and 3D-printed resins. Methods: Three resins were tested: Evolux PMMA (milled resin), Cosmos Temp (3D-printed resin), and Structur 2 SC (bis-acrylic resin, group control). Specimens were prepared with rectangular shapes (n = 12) for flexural strength measurements and disc shapes (n = 9) for Vickers hardness tests. Flexural strength tests were performed at a crosshead speed of 0.75 mm/min, and the Vickers hardness was measured under a load of 20 N for 10 s. The obtained data were subjected to the Kruskal­Wallis test. Results: A significant difference (p < 0.05) in flexural strength was observed among the three sample groups: Evolux PMMA (111.76 MPa), Structur 2 SC (87.34 MPa), and Cosmos Temp (56.83 MPa). No significant difference (p < 0.05) was observed between the Vickers hardness values of Structur 2 SC (33.37 VHN) and Evolux PMMA (29.11 VHN); however, both materials were statistically superior to Cosmos Temp (10.90 VHN). Conclusion: While the mechanical properties of the milled resin were superior or similar to those of the bisacrylic resin, the 3D-printed resin was statistically inferior to both the milled and bis-acrylic resins

Effects of black tea tooth staining previously to 35% hydrogen peroxide bleaching

Aim: To determine if the artificial staining with black tea (BT) influences the enamel microhardness before in-office bleaching and if BT staining is necessary to evaluate the efficacy of bleaching with 35% hydrogen peroxide Methods: Enamel/dentin blocks were randomized into groups according to the staining protocol (n=5/group): (CO) control ­ maintained in artificial saliva solution (AS); (BT4) immersed in black tea solution for 4 h; (BT24) immersed in black tea solution for 24 h. After the staining protocols, all specimens were kept in AS for one week, followed by bleaching (three sessions of HP application for 40 min). Knoop surface microhardness (kgF/mm2) was determined at baseline (T0), after staining (T1), after 7 days of storage in AS (T2), and after bleaching (T3). The color (∆E00) and coordinate changes (∆L, ∆a, ∆b) were measured using a digital spectrophotometer at T0 and T3. Data were submitted to one-way (∆E00, ∆L, ∆a, ∆b) or two-way ANOVA repeated measures (kgF/mm2) and Tukey's test (a=5%). Results: The staining protocols (BT4 and BT24) promoted significantly lower microhardness (T1 and T2, p<0.05) than CO, whereas CO was the only group to maintain microhardness values over time. Bleaching promoted perceptible ∆E00 without a significant difference among the groups regardless of the staining protocol (p=0.122). CO and BT4 showed no differences in terms of ∆L and ∆a (p>0.05), but BT4 displayed a higher ∆b than CO. Conclusion:The artificial staining with BT negatively affected the enamel surface microhardness and was not essential to evaluate the efficacy of 35% hydrogen peroxide bleaching

Avaliação in vitro da razão base/topo de dureza e da resistência de união push-out entre uma resina composta contendo diatomita e uma resina composta bulk-fill / In vitro evaluation of the base/top hardness ratio and push-out bond strength between a diatomite-containing composite resin and a bulk-fill composite resin

A escassez de dados científicos que validem os benefícios da diatomita para as propriedades físicas da resina composta Zirconfill® torna imperioso a realização de novos estudos, principalmente no tocante a utilização dessa resina contendo diatomita em restaurações semidiretas. Objetivo: Avaliar in vitro a polimerização e resistência de união entre uma resina composta contendo diatomita e de uma resina composta bulk-fill após 24 horas e após 06 meses de envelhecimento em água. Materiais e métodos: Foram utilizados 28 incisivos bovinos para produzir cavidades dentinárias cônicas (4,8 mm de diâmetro maior x 2,8 mm de diâmetro menor x 4 mm de espessura) e fator C de magnitude 3,1. Esses preparos cavitários (n=28) foram restaurados com as resinas compostas Filtek™ One Bulk-fill (BF) (3M ESPE) ou Zirconfill ® (ZF) (BM4), através da técnica semidireta, utilizando o sistema adesivo Single Bond Universal (3M ESPE) e o cimento resino dual Relyx™ Ultimate (3M ESPE). A análise da polimerização foi realizada através da razão base/topo (B/T) de dureza Vickers. E a resistência de união RU foi realizada através do teste de extrusão push-out em máquina de ensaio universal. As amostras foram armazenadas em água destilada a 37 ºC por 24 horas ou 06 meses, mas apenas a RU avaliou as amostras após 06 meses de envelhecimento. Os dados da B/T e da RU foram submetidos à análise de variância (ANOVA) a um e a dois critérios, respectivamente, com pós-teste de Tukey (p <0.05). Resultados: Não houve diferença estatisticamente significativa entre as resinas compostas na B/T. Para a RU, a resina composta ZF mostrou valores maiores do que a resina BF em ambos os tempos avaliados. Não houve diferença estatisticamente significativa de nenhuma resina na avaliação ao longo do tempo. Conclusão: A resina composta contendo diatomita mostrou-se promissora quando utilizada em restaurações semidiretas, visto que obteve resultados similar e até superior a resina composta bulk-fill (AU).

The scarcity of data validating scientific diatomite benefits for physical properties of Zirconfill® resin composite makes essential to develop new studies, especially regarding the use of this resin composite containing diatomite in semi-direct restorations. Aim: To evaluate in vitro the cure and bond strength between a resin composite containing diatomite and a bulk-fill resin composite after 24 hours and after 06 months of water storage. Materials and methods: Twenty-eight bovine incisors (n=28) were used to produce conical dentinal cavities (4,8 mm of larger diameter x 2,8 mm of smaller diameter x 4 mm of thickness) and C-factor of magnitude 3.1. These cavities were restored with Filtek™ One Bulk-Fill (BF) (3M ESPE) or Zirconfill® (ZF) (BM4) resin composites, through the semi-direct technique, using Scotchbond™ Universal (3M ESPE) adhesive system and Relyx™ Ultimate (3M ESPE) dual resin cement. The cure analysis was performed through bottom-to-top (B/T) ratio of vickers hardness, while bond strength (RU) was performed through the push-out test in a universal testing machine. The specimens were stored in distilled water at 37 ºC for 24 hours or 06 months, but only RU analyzed the specimens after 06 months aging. B/T and RU data were, respectively, submitted to one-way and two-way analysis of variance (ANOVA) with Tukey's post-test (p <0.05). Results: There was no statistically significant difference between the composite resins in B/T. For RU, the ZF composite resin showed higher values than the BF resin at both evaluated times. However, there was no statistically significant difference in resin composites over time. Conclusion: The resin composite containing diatomite showed promise when used in semi-direct restorations since it obtained similar or even superior results to bulk-fill resin composite (AU).

Influência do clareamento dentário de consultório na dureza superficial de resinas compostas: um estudo in vitro / Influence of in-office tooth whitening on the surface hardness of composite resins: An In Vitro Study

O estudo objetivou avaliar a dureza superficial de três resinas compostas (Filtek Z350 - 3M ESPE, Zirconfil - TECHNEW, Vitra ­ FGM), após processo de clareamento dental de consultório a base de peróxido de Hidrogênio a 40%. Foram confeccionados 60 corpos de prova, com espessuras de 6,0 x 2,0 mm, sendo 20 corpos de cada material restaurador (n=20). Após processo de acabamento e polimento, os espécimes foram divididos aleatoriamente em dois grupos para cada material restaurador (n=10), onde o grupo controle G1-C, foi mantido em saliva artificial e o grupo experimental G2-E, foi submetido ao gel clareador de consultório a base de peróxido de hidrogênio a 40% de acordo com a indicação do fabricante. O teste de dureza utilizado foi o de Vickers. Para cada corpo de prova, foram realizadas quatro leituras consecutivas e equidistantes, com uma carga de 300g de força durante 15s. Os valores de dureza para resinas testadas foram estatisticamente mais elevadas no grupo controle, do que no grupo teste. Sendo que a maior diferença nos valores das médias entre os grupos ocorreu na resina Z350XT e para a margem de erro fixada (5%) se comprova diferença significativa (p < 0,05) entre os grupos teste e controle para cada resina. O uso do peróxido de hidrogênio 40% pela técnica de consultório, promoveu mudanças significativas na dureza superficial das resinas testadas. Além disso, a resina Z350XT apresentou dureza superior as demais resinas, porém foi a mais afetada pelo agente clareador (AU).

The study aimed to evaluate the surface hardness of three composite resins (Filtek Z350 - 3M ESPE, Zirconfil - TECHNEW, Vitra - FGM), after an in-office tooth whitening process using 40% hydrogen peroxide. Sixty specimens were made, with thicknesses of 6.0 x 2.0 mm, with 20 specimens of each restorative material (n=20). After finishing and polishing, the specimens were randomly divided into two groups for each restorative material (n=10), where the control group G1-C was maintained in artificial saliva and the experimental group G2-E was subjected to gel in-office bleaching agent based on 40% hydrogen peroxide, according to the manufacturer's instructions. The hardness test used was the Vickers hardness test and for each specimen, four consecutive and equidistant readings were performed, with a load of 300g of force for 15s. Hardness values for tested resins were statistically higher in the control group than in the test group. The greatest difference in mean values between the groups occurred in the Z350XT resin and for the fixed margin of error (5%) there is a significant difference (p < 0.05) between the test and control groups for each resin. The use of 40% hydrogen peroxide by the in-office technique promoted significant changes in the surface hardness of the tested resins. In addition, the Z350XT resin presented higher hardness than the other resins, but was the most affected by the bleaching agent (AU).

Comparative evaluation of fiber-reinforced, bulk-fill and conventional dental composites: Physical characteristics and polymerization properties.

BACKGROUND: Resin composites have various applications. At the same time, they have some drawbacks, such as polymerization shrinkage. Conventional composites are polymerized in 2-mm thick layers. However, in posterior restoration, the 2-mm depth of cure is not satisfactory. To find a solution, resin composites have been vastly improved in terms of fillers, matrix and initiators. OBJECTIVES: To evaluate polymerization properties and physical characteristics of fiber-reinforced composites and compare them with bulk-fill composites that are designed for large posterior restorations. MATERIAL AND METHODS: Samples were prepared from each resin composite. The 3-point bending test was performed to evaluate the flexural strength of all composites. The depth of cure of the composite from 1 mm to 4 mm of depth was analyzed using Vickers hardness test (VHN). To analyze the degree of conversion, Fourier-transform infrared spectroscopy (FTIR) of the top and bottom surfaces of the samples with 4-mm thickness was calculated. The data were analyzed using one-way analysis of variance (ANOVA) test followed by post hoc test (95% confidence interval (95% CI)). RESULTS: The Filtek showed the highest flexural strength followed by everX and X-tra fil. At 1-mm depth, X-tra fil had the highest and Gradia had the lowest microhardness. At the 4-mm depth, the microhardness trend was as follows: everX > Filtek > X-tra fil > Gradia > Beautifil. The everX composite had the lowest reduction of the degree of conversion at 4-mm thickness, which showed a significant difference in comparison with Filtek, Gradia and X-tra fil composites. CONCLUSIONS: Based on the results of our study, it can be concluded that the fiber-reinforced composite everX showed more favorable results regarding polymerization properties, such as the degree of conversion and the depth of cure. However, the flexural strength results in Filtek were better than those in everX.

Preparation of medical Mg-Zn alloys and the effect of different zinc contents on the alloy.

In recent years, along with the development and application of magnesium alloys, magnesium alloys have been widely used in automotive, aerospace, medicine, sports, and other fields. In the field of medical materials, magnesium not only has the advantage of light weight, high strength, and a density similar to that of human bone, but also has good biocompatibility and promotes the growth of human bone. However, the mechanical properties and corrosion resistance of magnesium alloys need to be further improved to meet the requirements for human biodegradable implants. In this study, three alloys (mass fractions: Mg-10Zn, Mg-20Zn, and Mg-30Zn (wt.%)) were prepared using powder metallurgy by homogeneously mixing powders of the above materials in a certain amount with magnesium as the substrate through the addition of zinc elements, which also have good biocompatibility. The effect of zinc on the microstructure, mechanical properties, wear performance, and corrosion resistance of magnesium-zinc alloys was studied when the zinc content was different. The results show that compared with the traditional magnesium alloy using powder metallurgy, prepared magnesium alloy has good resistance to compression and bending, its maximum compressive stress can reach up to 318.96 MPa, the maximum bending strength reached 189.41 MPa, and can meet the mechanical properties of the alloy as a human bone-plate requirements. On the polarization curve, the maximum positive shift of corrosion potential of the specimens was 73 mv and the maximum decrease of corrosion-current density was 53.2%. From the comparison of the above properties, it was concluded that the three prepared alloys of which Mg-20% Zn had the best overall performance. Its maximum compressive stress, maximum bending strength, and corrosion-current density reached 318.96 MPa, 189.41 MPa and 2.08 × 10-5 A·cm-2 respectively, which are more suitable for use as human implant bone splints in human-body fluid environment. The mechanical properties of the sintered Mg-Zn alloys were analyzed using powder-metallurgy techniques, and their microstructure, micromotion wear properties, electrochemical corrosion properties and composition of the physical phases were analyzed and discussed.

Influence of calcium lactate and sodium fluoride solution mouthwashes on enamel microhardness and dentin permeability during in-office bleaching / Influência das soluções enxaguatórias de lactato de cálcio e fluoreto de sódio na microdureza do esmalte e permeabilidade dentinária durante o clareamento em consultório

Objective: This study evaluated the influence of calcium lactate and sodium fluoride mouthwashes on enamel microhardness and dentin permeability during in-office bleaching. Material and Methods: For the microhardness evaluation, enamel blocks were randomly submitted to different treatments associated with in-office bleaching agent using 40% hydrogen peroxide (Opalescence Boost PF 40%/ Ultradent; 3 sessions x 40-minute each) (n = 10): 1) Control: application of bleaching agent; 2) Calcium lactate: 1-minute immersion before bleaching treatment; 3) Sodium fluoride: immersion for 1 minute before bleaching treatment; 4) Calcium lactate + sodium fluoride: 1 minute immersion in calcium lactate solution, followed by 1 minute immersion in sodium fluoride before bleaching treatment. Dentin discs received the same treatment protocols (n = 10) to evaluate permeability. Knoop microhardness and dentin permeability assessments were performed twice (at baseline and 48 hours after the end of bleaching treatment). Results: The generalized linear model considering the design of repeated measures over time showed that there was no significant difference between treatments (p = 0.9577) and between assessments (p = 0.3267) regarding Knoop microhardness. Kruskal Wallis and Dunn tests showed that calcium lactate immersion before bleaching treatment provided higher dentin permeability than other groups (p = 0.0009). Conclusion: The use of sodium fluoride solution and calcium lactate in association with in-office bleaching treatment did not influence the microhardness of tooth enamel, although calcium lactate may increase dentin permeability. (AU)

Objetivo: Este estudo avaliou a influência dos enxaguatórios bucais com lactato de cálcio e fluoreto de sódio na microdureza do esmalte e na permeabilidade da dentina durante o clareamento em consultório. Material e Métodos: Para avaliação da microdureza, blocos de esmalte foram submetidos aleatoriamente a diferentes tratamentos associados a agente clareador em consultório com peróxido de hidrogênio 40% (Opalescence Boost PF 40% / Ultradent; 3 sessões x 40 minutos cada) (n = 10): 1) Controle: aplicação de agente clareador; 2) Lactato de cálcio: imersão de 1 minuto antes do tratamento clareador; 3) Fluoreto de sódio: imersão por 1 minuto antes do tratamento clareador; 4) Lactato de cálcio + fluoreto de sódio: 1 minuto de imersão em solução de lactato de cálcio, seguido de 1 minuto de imersão em fluoreto de sódio antes do tratamento clareador. Os discos de dentina receberam os mesmos protocolos de tratamento (n = 10) para avaliar a permeabilidade. As avaliações da microdureza Knoop e da permeabilidade dentinária foram realizadas duas vezes (no início do estudo e 48 horas após o término do tratamento clareador). Resultados: O modelo linear generalizado considerando o delineamento de medidas repetidas ao longo do tempo mostrou que não houve diferença significativa entre os tratamentos (p = 0,9577) e entre as avaliações (p = 0,3267) em relação à microdureza Knoop. Os testes de Kruskal Wallis e Dunn mostraram que a imersão de lactato de cálcio antes do tratamento clareador proporcionou maior permeabilidade dentinária do que os outros grupos (p = 0,0009). Conclusão: O uso de fluoreto de sódio e lactato de cálcio associado ao clareamento em consultório não influenciou a microdureza do esmalte dentário, embora o lactato de cálcio possa aumentar a permeabilidade dentinária (AU)

Influence of fluoride-releasing materials in the inhibition of enamel and dentin demineralization around restorations / Influência de materiais liberadores de flúor na inibição da desmineralização do esmalte e da dentina ao redor de restaurações

Objective: The aim was to evaluate the influence of fluoride-releasing restorative materials in enamel and dentin microhardness. Material and Methods: 40 blocks (5x5x3 mm) from cervical third of human molars received a cavity preparation between the enamel and dentin, and the restorations were subjected to in vitro caries model. Specimens were randomly restored with (n=10): conventional glass ionomer cement (Ketac Cem, 3M ESPE); polyacid-modified composite resin (Ionoseal, VOCO); resin-modified glass ionomer cement (Ionofast, Biodinâmica); or microhybrid composite resin (Filtek Z250, 3M ESPE). The specimens were sectioned longitudinally and enamel and dentin Knoop microhardness were determined at different distances from the restorative material (100, 200 and 300 µm) and depth of surface (20, 40 and 60 µm). The data were submitted to three-way repeated measures ANOVA and Tukey ́s test ( α =0.05). Results: For enamel, the double interactions between material x distance and material x depth were statistically significant. In all depths and distances, the highest values of enamel microhardness were observed for Ketac Cem. In dentin, the materials differed statistically from each other, and Ionoseal obtained higher microhardness values than those found in Ionofast. Conclusion: Conventional glass ionomer cement is more effective in preventing enamel demineralization around restoration followed by the polyacid-modified composite resin. In dentin, the polyacid-modified composite resin obtained better performance than resin-modified glass ionomer cement. (AU)

Objetivo: O objetivo foi avaliar a influência de materiais restauradores liberadores de flúor na microdureza do esmalte e da dentina. Material e Métodos: 40 blocos (5x5x3 mm) do terço cervical de molares humanos receberam preparo cavitário entre esmalte e dentina, e após a restauração foram submetidas a um modelo in vitro de cárie. As amostras foram restauradas aleatoriamente com (n=10): cimento de ionômero de vidro convencional (Ketac Cem, 3M ESPE); resina composta modificada por poliácidos (Ionoseal, VOCO); cimento de ionômero de vidro modificado por resina (Ionofast, Biodinâmica); ou resina composta microhíbrida (Filtek Z250, 3M ESPE). As amostras foram seccionadas longitudinalmente e a microdureza Knoop de esmalte e dentina foi determinada em diferentes distâncias do material restaurador (100, 200 e 300 µm) e profundidade de superfície (20, 40 e 60 µm). Os dados foram submetidos à ANOVA para medidas repetidas de três fatores e teste de Tukey (α =0,05). Resultados: Para o esmalte, as duplas interações entre material x distância e material x profundidade foram estatisticamente significativas. Em todas as profundidades e distâncias, os maiores valores de microdureza do esmalte foram observados para o Ketac Cem. Na dentina, Ionoseal obteve valores de microdureza superiores aos encontrados no Ionofast. Conclusão:O cimento de ionômero de vidro convencional é mais eficaz na prevenção da desmineralização do esmalte ao redor da restauração, seguido pela resina composta modificada por poliácidos. Na dentina, a resina composta modificada por poliácidos obteve melhor desempenho que o cimento de ionômero de vidro modificado por resina. (AU)

Cyclic Fatigue Resistance and Surface Roughness of Rotary NiTi Instruments after Simulated Clinical Use in Curved Root Canals - An Atomic Force Microscopy Study

Abstract Objective: To examine the cyclic fatigue resistance and surface topography of TruNatomy and ProTaper Gold nickel-titanium rotary files and evaluate the presence of alterations to surface topography following instrumentation in simulated curved canals. Material and Methods: Twenty-four nickel-titanium instruments, twelve each of TN and PTG file systems, were evaluated for cyclic fatigue resistance. The rotary files were rotated in a simulated root canal with standardized diameter, angle of curvature, and radius of curvature in a custom-made cyclic fatigue testing device until the instrument fracture occurred. The time to fracture for each instrument was recorded with a stopwatch; in seconds in each group. Fractured instruments were subjected to atomic force microscopy analysis measuring the average roughness and the root mean square values to investigate surface features of endodontic files. Mean values and standard deviation were calculated. Data were analyzed using the Mann-Whitney U test. Results: Time to fracture was marginally higher in PTG instruments than in the TN file systems. PTG files exhibited higher surface roughness when compared with TN files (p<0.05). Conclusion: TN file system had a higher cyclic fatigue resistance than PTG. Cyclic fatigue causing file breakage did affect the surface topography of the files. PTG files showed a higher surface porosity value than the TN files (AU).

Effect of acid challenge and photoactivation distance on microhardness and roughness of flow bulk-fill composite resins / Efeito do desafio ácido e distância de fotoativação na microdureza e rugosidade de resinas compostas bulk-fill flow

Abstract Introduction composite resins are indicated to the reconstruction of proximal walls and the evaluation of properties of flow bulk-fill composite resins exposed to acid challenge is necessary. Objective to evaluate the microhardness and roughness at different depths of photoactivation of bulk-fill flow composites (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) and conventional composite resin (control, Filtek Z350 XT) subjected to acid challenge. Material and method forty composites brick shaped specimens (3x3x4 mm) were made using a polyacetal matrix. To simulate pH challenges, the samples were immersed in a demineralizing solution. Each sample had Knoop microhardness (KHN) and roughness (Ra) evaluated at three depths (superficial, medium, and cervical), considering the lateral surface of the sample. Data were submitted to Kruskal-Wallis, Friedman's and Dunn's tests with a significance level of 5%. Result comparing the composites among themselves, in superficial (p=0.693), medium (p=0.053) and cervical (p=0.176) regions, there was no difference in the KHN values. There were also no differences in roughness between the composites in superficial (p=0.356), medium (p=0.734) and cervical (p=0.207) regions. Only the Filtek Z350 XT (p=0.027) showed less difference in KHN in the middle region caused by acid challenge. Changes in roughness showed that the greatest difference was at the cervical region for Bulk Fill Flow SDR (p=0.014) and Tetric N-Ceram Bulk Fill (p = 0.003) with an increase after acid challenge. Conclusion after acid challenge, bulk-fill flow composites showed alterations similar to those presented by the conventional nanoparticulate resin composite.

Resumo Introdução as resinas compostas são indicadas para reconstrução de paredes proximais e a avaliação das propriedades das resinas compostas bulk-fill flow expostas ao desafio ácido mostra-se necessária. Objetivo avaliar a microdureza e rugosidade em diferentes profundidades de fotoativação de resinas compostas bulk-fill flow (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) e convencional (controle, Filtek Z350 XT) submetidas ao desafio ácido. Material e método quarenta amostras retangulares (3x3x4 mm) foram confeccionadas utilizando uma matriz de poliacetal. Para simular o desafio ácido, as amostras foram imersas em uma solução desmineralizante. Cada amostra teve a microdureza Knoop (KHN) e rugosidade (Ra) avaliadas em três profundidades (superficial, média e cervical), considerando a superfície lateral da amostra. Os dados foram submetidos aos testes de Kruskal-Wallis, Friedman e Dunn com nível de significância de 5%. Resultado comparando as resinas compostas entre si, nas regiões superficial (p=0,693), média (p=0,053) e cervical (p=0,176), não houve diferença nos valores de KHN. Também não houve diferenças na rugosidade entre os materiais nas regiões superficial (p=0,356), média (p=0,734) e cervical (p=0,207). Apenas o Filtek Z350 XT (p=0,027) apresentou menor diferença de KHN na região intermediária causada pelo desafio ácido. As mudanças na rugosidade mostraram que a maior diferença foi na região cervical para Bulk Fill Flow SDR (p=0,014) e Tetric N-Ceram Bulk Fill (p=0,003), com aumento após o desafio ácido. Conclusão após desafio ácido, as resinas compostas bulk-fill flow apresentaram alterações semelhantes às apresentadas pela resina composta convencional nanoparticulada.

O método de fotopolimerização é capaz de influenciar nos valores de microdureza das resinas compostas? Um estudo in vitro / Is the photopolimerization method able to influence on the microhardness values of composite resins? An in vitro study

Introdução: a inovação dos métodos de fotopolimerização foi proposta na tentativa de diminuir o estresse de contração de polimerização das resinas compostas e proporcionar maior conforto ao paciente, reduzindo o tempo de atendimento odontológico. Objetivo: avaliar a microdureza de duas resinas compostas nanoparticuladas submetidas a diferentes técnicas de polimerização. Material e método: quarenta espécimes foram divididos em quatro grupos (n=10) da seguinte forma: Filtek Z350 XT® + técnica imediata (GI); Filtek One Bulkfill® + técnica imediata (GII); Filtek Z350 XT® + técnica de pulso tardio (GIII); Filtek One Bulkfill® + técnica de pulso tardio (GIV). Após o armazenamento em água destilada à temperatura ambiente, os corpos de prova foram direcionados para a medição de microdureza. Utilizou-se teste T para comparação de técnicas e teste Two-Way ANOVA para calcular os efeitos das resinas compostas, técnicas de polimerização e interações referentes à variável dependente (p ≤0,05). Resultado: a resina Filtek Z350 XT® apresentou maior dureza na técnica imediata (GI - 312,45 ± 64,37) e pulso tardio (GIII - 244,50 ± 75,63) comparado à resina Filtek One Bulkfill®, em ambas as técnicas. Observaram-se maiores valores de dureza referentes à técnica imediata, com diferença estatística significativa em relação à resina testada (p = 0,04 - Filtek Z350 XT®; p = 0,03 - Filtek One Bulkfill®). Ambos os fatores isolados (resina e técnicas) apresentaram efeito nos valores de microdureza (p = 0,02 e p < 0,01, respectivamente). Conclusão: a técnica convencional demonstrou atingir maiores valores de dureza quando comparada à técnica de polimerização alternativa.

Introduction: the innovation of photopolymerization methods was proposed in an attempt to reduce the polymerization shrinkage stress of composite resins and also provide more comfort to patient reducing the chair time. The aim of this in vitro study was to assess the microhardness of two nanofilled composite resins subject to different curing techniques. Objective: assess the microhardness of two nanofilled composite resins subject to different curing techniques. Material and method: forty specimens were divided into four groups (N=10) as follows: Filtek Z350 XT® + immediate technique (GI); Filtek One Bulkfill® + immediate technique (GII); Filtek Z350 XT® + delayed pulse technique (GIII); Filtek One Bulkfill® + delayed pulse technique (GIV). After storage in distilled water at room temperature the specimens were assessed for microhardness measurement. T-test was used for comparison of techniques and two-way ANOVA used to calculate the effects of composite resins, curing techniques and their interactions on dependent variable (p set at 0.05). Result: Filtek Z350 XT® resin presented greater hardness on immediate technique (GI - 312,45 ± 64.37) and delayed pulse (GIII - 244,50 ± 75.63) compared to Filtek One Bulkfill® under both techniques. Overall, it was observed greater hardness values under immediate technique with a significant statistical difference apart of tested resin (p = 0.04 - Filtek Z350 XT®; p = 0.03 - Filtek One Bulkfill®). Both isolated factors (resin and techniques) presented effect on microhardness values (p = 0.02 and p < 0.01, respectively). Conclusion: the conventional technique demonstrated to reach higher hardness values when compared to the alternative polymerization technique

Prediction of quality attributes (mechanical strength, disintegration behavior and drug release) of tablets on the basis of characteristics of granules prepared by high shear wet granulation.

High shear wet granulation is commonly applied technique for commercial manufacturing of tablets. Granulation process for tablets manufacturing is generally optimized by hit and trial which involves preparation of granules under different processing parameters, compression of granules and evaluation of the resultant tablets; and adjustment is made in granulation process on the basis of characteristics of tablets. Objective of the study was to optimize the process of high shear wet granulation and prediction of characteristics of tablets on the basis of properties of granules. Atenolol granules were prepared by high shear wet granulation method, using aqueous solution of polyvinyl pyrrolidone (PVP k-30) as binder. Concentration of binder solution and granulation time were taken as process variables, both studied at three levels. Different combinations of process variables were determined by Design Expert software. Granules were evaluated for different parameters on the basis of SeDeM-ODT (Sediment Delivery Model-Oro Dispersible Tablets) expert system. Granules from all the trials were compressed using round (10.5 mm) flat faced punches at compression weight of 250 mg/tablet. Tablets were evaluated of different quality control parameters as per USP. Results showed that both the process variables had positive effect on mechanical strength of tablets and negative effect on disintegration and dissolution rate. Granule prepared with highest level of binder concentration (15%) and highest granulation time (60 sec) resulted in tablets with highest crushing strength (11.8 kg), specific crushing strength (0.328 kg/mm2), tensile strength (0.208 kg/mm2), lowest value of friability (0.19%) and highest disintegration time (10.9 min), as predicted from granules characteristics on the basis of SeDeM-ODT expert system. Drug release from Trial-13 (processed under highest level of both process parameters) was also lower than rest of the trials. It is concluded from the study that quality characteristics of tablets can be predicted from granules characteristics using SeDeM-ODT expert system. Furthermore, SeDeM-ODT expert system can also be used for optimization of the process of high shear wet granulation.

Application of Er,Cr:YSGG laser versus photopolymerization after silver diamine fluoride in primary teeth.

Examine the effect of dental curing light and laser treatments applied after Silver Diamine Fluoride (SDF) on dentin hardness in carious primary molars. This in-vitro study consisted of 30 extracted primary molars with caries extending into dentin without pulpal involvement. The collected teeth were randomly divided into three groups: group 1: received SDF then Sub-ablative low-energy of Er,Cr:YSGG laser, group 2: received SDF followed by application of curing light for 40 s, group 3: had SDF treatment only. In all groups, 38% Ag (NH3)2F SDF was used. Vickers hardness test was performed on sound dentin below carious lesion. Kruskal-Wallis Test was used to determine the mean difference in dentin hardness of the groups at 5% Significance level using SPSS software. Surface hardness of sound dentin below the carious lesion was statistically significantly higher in the laser + SDF group (891.24 ± 37.33 kgf/mm2) versus the two other groups (Light cure + SDF = 266.65 ± 90.81 kgf/mm2 and SDF only = 117.91 ± 19.19 kgf/mm2) with p-value ≤ 0.001. Although Photopolymerization of SDF increases the surface hardness of sound dentin below the carious lesion, applying laser after SDF has the highest surface hardness due to the laser's sub-ablation of dentin.