In vitro and in vivo dissolution of biocompatible S59 glass scaffolds.

Fabrication of porous tissue-engineering scaffolds from bioactive glasses (BAG) is complicated by the tendency of BAG compositions to crystallize in thermal treatments during scaffold manufacture. Here, experimental biocompatible glass S59 (SiO2 59.7 wt%, Na2O 25.5 wt%, CaO 11.0 wt%, P2O5 2.5 wt%, B2O3 1.3 wt%), known to be resistant to crystallization, was used in sintering of glass granules (300-500 µm) into porous scaffolds. The dissolution behavior of the scaffolds was then studied in vivo in rabbit femurs and under continuous flow conditions in vitro (14 days in vitro/56 days in vivo). The scaffolds were osteoconductive in vivo, as bone could grow into the scaffold structure. Still, the scaffolds could not induce sufficiently rapid bone ingrowth to replace the strength lost due to dissolution. The scaffolds lost their structure and strength as the scaffold necks dissolved. In vitro, S59 dissolved congruently throughout the 14-day experiments, resulting in only a slight reaction layer formation. Manufacturing BAG scaffolds from S59 that retain their amorphous structure was thus possible. The relatively rapid and stable dissolution of the scaffold implies that the glass S59 may have the potential to be used in composite implants providing initial strength and stable, predictable release of ions over longer exposure times.

[Preparation and in vivo osteogenesis of acellular dermal matrix/dicalcium phosphate composite scaffold for bone repair].

Objective: To investigate the physicochemical properties, osteogenic properties, and osteogenic ability in rabbit model of femoral condylar defect of acellular dermal matrix (ADM)/dicalcium phosphate (DCP) composite scaffold. Methods: ADM/DCP composite scaffolds were prepared by microfibril technique, and the acellular effect of ADM/DCP composite scaffolds was detected by DNA residue, fat content, and α-1，3-galactosyle (α-Gal) epitopes; the microstructure of scaffolds was characterized by field emission scanning electron microscopy and mercury porosimetry; X-ray diffraction was used to analyze the change of crystal form of scaffold; the solubility of scaffolds was used to detect the pH value and calcium ion content of the solution; the mineralization experiment in vitro was used to observe the surface mineralization. Twelve healthy male New Zealand white rabbits were selected to prepare the femoral condylar defect models, and the left and right defects were implanted with ADM/DCP composite scaffold (experimental group) and skeletal gold ® artificial bone repair material (control group), respectively. Gross observation was performed at 6 and 12 weeks after operation; Micro-CT was used to detect and quantitatively analyze the related indicators [bone volume (BV), bone volume/tissue volume (BV/TV), bone surface/bone volume (BS/BV), trabecular thickness (Tb.Th), trabecular number (Tb.N), trabecular separation (Tb.Sp), bone mineral density (BMD)], and HE staining and Masson staining were performed to observe the repair of bone defects and the maturation of bone matrix. Results: Gross observation showed that the ADM/DCP composite scaffold was a white spongy solid. Compared with ADM, ADM/DCP composite scaffolds showed a significant decrease in DNA residue, fat content, and α-Gal antigen content ( P<0.05). Field emission scanning electron microscopy showed that the ADM/DCP composite scaffold had a porous structure, and DCP particles were attached to the porcine dermal fibers. The porosity of the ADM/DCP composite scaffold was 76.32%±1.63% measured by mercury porosimetry. X-ray diffraction analysis showed that the crystalline phase of DCP in the ADM/DCP composite scaffolds remained intact. Mineralization results in vitro showed that the hydroxyapatite layer of ADM/DCP composite scaffolds was basically mature. The repair experiment of rabbit femoral condyle defect showed that the incision healed completely after operation without callus or osteophyte. Micro-CT showed that bone healing was complete and a large amount of new bone tissue was generated in the defect site of the two groups, and there was no difference in density between the defect site and the surrounding bone tissue, and the osteogenic properties of the two groups were equivalent. There was no significant difference in BV, BV/TV, BS/BV, Tb.Th, Tb.N, and BMD between the two groups ( P>0.05), except that the Tb.Sp in the experimental group was significantly higher than that in the control group ( P<0.05). At 6 and 12 weeks after operation, HE staining and Masson staining showed that the new bone and autogenous bone fused well in both groups, and the bone tissue tended to be mature. Conclusion: The ADM/DCP composite scaffold has good biocompatibility and osteogenic ability similar to the artificial bone material in repairing rabbit femoral condylar defects. It is a new scaffold material with potential in the field of bone repair.

Composite bone graft of CaO-MgO-SiO2 glass-ceramics and CaSO4 ceramics for boosting bone formation rate.

This study develops a composite bone graft of CaO-MgO-SiO2 glass-ceramic and CaSO4 [abbreviated as (CMS)3-x(CS)x] via the sponge replication technique with weight fractions of x = 0, 1, 1.5, 2, and 3. The (CMS)1.5(CS)1.5 composite displays a superior degradability and, a suitable compressive strength of ∼3 MPa, and excellent cell proliferation and differentiation. The in vivo rat femur test in the hybrid-pore (CMS)1.5(CS)1.5 composite granules achieves a higher rate of bone formation, which is ∼2.7 times better than that of the commercial HAP/ß-TCP at 12 weeks. Improved expressions of osteocyte and mature osteocyte marker genes, namely (Spp1, Dmp1, and Fgf23), were observed in the (CMS)1.5(CS)1.5 group, indicating a faster differentiation into mature bone tissue. The ions release of (CMS)1.5(CS)1.5 through the ERK1/2 signaling pathway promotes osteogenic differentiation. The high bone generation rate can be attributed to faster active ions release and modified surface topography. This work highlights an excellent bone graft candidate for clinical applications in orthopedic surgery.

Performance of a multiphase bioactive socket plug with a barrier function for alveolar ridge preservation.

The natural healing process of extraction socket and traditional socket plug material could not prevent buccal bone wall resorption and down growth of epithelium from the socket orifice. A multiphase bioactive socket plug (BP) is designed to overcome the natural healing process by maintaining the three-dimensional (3D) volume of extraction sockets, particularly in sockets with wall defects, and later provide sufficient alveolar bone volume for implant placement. The study aimed to fabricate and evaluate the physical, chemical, and biological performance of BPin vitro. The BP was fabricated through freeze-drying and layer-by-layer assembly, comprised of a base serving as a scaffold, a central portion for promoting bone regeneration, an upper buccal portion for maintaining alveolar socket dimension with a covering collagen membrane (Memb) on the top and upper buccal surface to prevent soft tissue infiltration. The BP as the experimental group and a pure collagen plug (CP) as the control group were investigated and compared. Radiograph, scanning electron microscopy, and energy-dispersive spectroscopy mapping confirmed that the four-part BP was successfully assembled and fabricated. Swelling rate analysis indicated that BP, CP, and Memb reached swelling equilibrium within 1 hour. BP exhibited a high remaining weight percentage in collagenase solution (68.81 ± 2.21% on day 90) and sustained calcium ion release, reaching the maximum 0.13 ± 0.04 mmol l-1on day 14. In biological assays, BP exhibited excellent cell proliferation (The OD value increased from 0.02 on day 1 to 0.23 on day 21.). The BP group exhibited higher alkaline phosphatase activity and osteocalcin content than the CP group within 21 days. Memb and BP exhibited outstanding barrier function, as evidenced by Hematoxylin and eosin staining. In summary, the multiphase bioactive socket plug represents a promising scaffold for alveolar ridge preservation application.

Percutaneous microwave ablation, perfusion, and reconstruction combined with a synthetic bone substitute in symptomatic bone cysts: a minimum of 26 months follow-up.

PURPOSE: The objective was to describe the technique and clinical outcome of microwave thermal ablation (MWA) and perfusion combined with synthetic bone substitutes in treating unicameral bone cysts (UBCs) in adolescents. MATERIALS AND METHODS: A total of 14 consecutive patients were enrolled by percutaneous MWA and saline irrigation combined with synthetic bone substitutes. Clinical follow-up included the assessment of pain, swelling, and functional mobility. Radiological parameters included tumor volume, physis-cyst distance, cortical thickness of the thinnest cortical bone, and the Modified Neer classification system. RESULTS: The mean follow-up was 28.9 months (26-52 months). All UBCs were primary, and all patients underwent the MWA, saline perfusion, and reconstruction combined with a synthetic bone substitute session, except for one patient (7.1%) who required a second session. All patients had good clinical results at the final follow-up. Satisfactory cyst healing was achieved in 13 cases according to radiological parameters. Tumor volume decreased from a mean of 49.7 cm3 before surgery treatment to 13.9 cm3 at the final follow-up (p < 0.01). The physis-cyst distance increased from a mean of 3.17-4.83 cm at the final follow-up (p < 0.01). Cortical thickness improved from a mean of 1.1 mm to 2.0 mm at the final follow-up (p < 0.01). According to the proposed radiological criteria, our results were considered successful (Grading I and II) in 13 patients (92.9%) at the final follow-up. CONCLUSION: Percutaneous microwave ablation combined with a bone graft substitute is a minimally invasive, effective, safe, and cost-effective approach to treating primary bone cysts in the limbs of adolescents.

Titanium-doped phosphate glasses containing zinc and strontium applied in bone regeneration.

Phosphate bioactive glass has been studied for its advanced biodegradability and active ion release capability. Our previous research found that phosphate glass containing (P2O5)-(Na2O)-(TiO2)-(CaO)-(SrO) or (ZnO) showed good biocompatibility with MG63 and hMSCs. This study further investigated the application of 5 mol% zinc oxide or 17.5 mol% strontium oxide in titanium-doped phosphate glass for bone tissue engineering. Ti-Ca-Na-Phosphate glasses, incorporating 5% zinc oxide or 17.5% strontium oxide, were made with melting quenching technology. The pre-osteoblast cell line MC3T3-E1 was cultured for indirect contact tests with graded diluted phosphate glass extractions and for direct contact tests by seeding cells on glass disks. The cell viability and cytotoxicity were analysed in vitro over 7 days. In vivo studies utilized the tibial defect model with or without glass implants. The micro-CT analysis was performed after surgery and then at 2, 6, and 12 weeks. Extractions from both zinc and strontium phosphate glasses showed no negative impact on MC3T3-E1 cell viability. Notably, non-diluted Zn-Ti-Ca-Na-phosphate glass extracts significantly increased cell viability by 116.8% (P < 0.01). Furthermore, MC3T3-E1 cells cultured with phosphate glass disks exhibited no increase in LDH release compared with the control group. Micro-CT images revealed that, over 12 weeks, both zinc-doped and strontium-doped phosphate glasses demonstrated good bone incorporation and longevity compared to the no-implant control. Titanium-doped phosphate glasses containing 5 mol% zinc oxide, or 17.5 mol% strontium oxide have promising application potential for bone regeneration research.

Maxillary Sinus Augmentation with Anorganic Bovine Bone Mineral of Different Particle Sizes: A Split-Mouth Study with Histomorphometric, Radiographic, and Clinical Analyses.

PURPOSE: The aim of the present study was to compare the histomorphometrically evaluated new bone formation (NB), the radiographically measured graft stability, and the clinical implant outcome for maxillary sinus augmentation grafted with deproteinized bovine bone mineral (DBBM) with either small (Bio-Oss-S, Geistlich) or large (Bio-Oss-L, Geistlich) particles. MATERIALS AND METHODS: Using a split-mouth study design, bilateral maxillary sinus augmentation was performed in 13 patients either with Bio-Oss-S particles (0.25 to 1 mm) or Bio-Oss-L particles (1 to 2 mm). After a healing period of 6 months, bone biopsies were axially retrieved in the molar region for histologic/histomorphometric analysis of NB, including subsequent staged implant placement. To determine graft stability, the maxillary sinus augmentation vertical graft heights were radiographically measured immediately after sinus augmentation, at implant placement, and at the 2- and 4-year post-augmentation follow-ups. In addition, the clinical implant-prosthodontic outcome (survival/ success/marginal bone loss) was assessed at 1 and 3 years post-loading. RESULTS: A total of 22 sinuses from 11 patients with split-mouth evaluation were ultimately available for data and statistical analysis. Histomorphometric analysis of the axially retrieved bone biopsies revealed the presence of NB (S: 25.5% ± 7.0% vs L: 23.6% ± 11.9%; P = .640), residual graft particles (S: 19.6% ± 9.2% vs L: 17.5% ± 6.3%; P = .365) as well as connective tissue (S: 54.9% ± 9.2% vs L: 58.9% ± 12.5%; P = .283), without significant differences between the use of small (Bio-Oss-S) and large (Bio-Oss-L) particles. However, there was significantly (P = .021) higher bone-to-graft contact (BGC) for the small-particle graft sites (27.9% ± 14.8%) compared to the large-particle graft sites (19.9% ± 12.9%), representing a significantly higher osteoconductivity. Both particle sizes showed significant (P < .01) vertical graft height reduction over time (4 years) of about 10%, with predominant graft reduction in the time period between sinus augmentation and implant placement compared to any follow-up periods after implant placement. At the 3-year post-loading implant evaluation, all implants and prostheses survived (100%), and the peri-implant marginal bone loss (S: 0.52 ± 0.19 mm; L: 0.48 ± 0.15 mm) as well as the peri-implant health conditions (S: 87.5%, L:81.2%) did not differ between implants inserted with the two different xenograft particles used. CONCLUSIONS: The use of small and large bovine xenograft particles for maxillary sinus augmentation provides for comparable bone formation, ensuring stable graft dimensions combined with high implant success and healthy peri-implant conditions. However, small particle size resulted in a higher BGC, providing for higher osteoconductivity than with the larger particle size.

Effect of mineralized dentin matrix on the prognosis of bone defect and retained root after coronectomy.

OBJECTIVE: To investigate the impact of mineralized dentin matrix (MDM) on the prognosis on bone regeneration and migration of retained roots after coronectomy. MATERIALS AND METHODS: Patients were divided into three groups based on the type of bone graft after coronectomy: Group C (n = 20, collagen), Group T (n = 20, tricalcium phosphate (TCP) + collagen), and Group D (n = 20, MDM + collagen). CBCT scans, conducted immediately and 6 months after surgery, were analyzed using digital software. Primary outcomes, including changes in bone defect depth and retained root migration distance, were evaluated 6 months after surgery. RESULTS: After 6 months, both Groups D and T exhibited greater reduction of the bone defect and lesser retained root migration than Group C (p < 0.001). Group D had greater regenerated bone volume in the distal 2 mm (73 mm3 vs. 57 mm3, p = 0.011) and lesser root migration (2.18 mm vs. 2.96 mm, p < 0.001) than Group T. The proportion of completely bone embedded retained roots was also greater in Group D than in Group C (70.0% vs. 42.1%, p = 0.003). CONCLUSIONS: MDM is an appropriate graft material for improving bone defect healing and reducing retained root migration after coronectomy. CLINICAL RELEVANCE: MDM is an autogenous material prepared chairside, which can significantly improve bone healing and reduce the risk of retained root re-eruption. MDM holds promise as a routine bone substitute material after M3M coronectomy.

Progress of research on the surface functionalization of tantalum and porous tantalum in bone tissue engineering.

Tantalum and porous tantalum are ideal materials for making orthopedic implants due to their stable chemical properties and excellent biocompatibility. However, their utilization is still affected by loosening, infection, and peripheral inflammatory reactions, which sometimes ultimately lead to implant removal. An ideal bone implant should have exceptional biological activity, which can improve the surrounding biological microenvironment to enhance bone repair. Recent advances in surface functionalization have produced various strategies for developing compatibility between either of the two materials and their respective microenvironments. This review provides a systematic overview of state-of-the-art strategies for conferring biological functions to tantalum and porous tantalum implants. Furthermore, the review describes methods for preparing active surfaces and different bioactive substances that are used, summarizing their functions. Finally, this review discusses current challenges in the development of optimal bone implant materials.

The effect of a barrier membrane on the incorporation of deproteinized bovine bone mineral (DBBM) in experimental defects at the time of early implant placement. A preclinical study.

OBJECTIVES: This study aimed to assess membrane use with a bone substitute graft for guided bone regeneration (GBR) in experimental dehiscence defects. MATERIALS AND METHODS: Maxillary second incisors (I2) in 9 dogs were extracted. Six weeks later, implants were inserted and experimental dehiscence defects (5 × 3 mm) created on the buccal aspect. The defects and surrounding bone were grafted with deproteinized bovine bone mineral. One side (test) was covered with a resorbable collagen membrane whereas the contralateral side (control) was not. After 6 weeks, histomorphometrical analysis was performed to evaluate: (a) first bone-to-implant contact (fBIC), (b) buccal bone thickness at 1 mm increments from implant shoulder, (c) regenerated area (RA), (d) area and percentages of new bone (B), bone substitute (BS) and mineralized tissue (MT). RESULTS: The histological appearance was similar between test and control sites. At central and lateral sections, there were no differences between groups for fBIC, buccal bone thickness, RA, BS, B, %B, MT and %MT. At central sections, membrane use favoured more %BS and %MT (p = 0.052). There was significantly more B, %B and MT at lateral compared to central sections. CONCLUSIONS: Membrane use tended to retain more bone substitute, but had no effect on new bone ingrowth. Lateral sections showed significantly more bone ingrowth and mineralized tissue compared to central sections, confirming that new bone ingrowth takes place mainly from the lateral walls of the defect. CLINICAL RELEVANCE: Preclinical research to clarify the dynamics of bone regeneration in GBR procedures is relevant in clinical practice.

Hydroxyapatite synthesis and characterization from waste animal bones and natural sources for biomedical applications.

Hydroxyapatites (HAps) synthesized from waste animal bones have recently gained attention due to their outstanding properties. This is because there is a need to fabricate scaffolds with desirable mechanical strength, ability to withstand high temperatures, and insoluble in solvents such as water, acetone, ethanol, and isopropyl alcohol. This study is an extensive summary of many articles on the routes of synthesis/preparation of HAp, and the optimum processing parameter, and the biomedical application areas, such as: drug administration, dental implants, bone tissue engineering, orthopedic implant coatings, and tissue regeneration/wound healing. A broad catalog of the synthesis methods (and combination methods), temperature/time, shape/size, and the calcium-to-phosphorous (Ca/P) value of diverse waste animal bone sources were reported. The alkaline hydrolysis method is proposed to be suitable for synthesizing HAp from natural sources due to the technique's ability to produce intrinsic HAp. The method is also preferred to the calcination method owing to the phase transformation that takes place at high temperatures during calcinations. However, calcinations aid in removing impurities and germs during heating at high temperatures. When compared to calcination technique, alkaline hydrolysis method results in crystalline HAp; the higher degree of crystallinity is disadvantageous to HAp bioactivity. In addition, the standardization and removal of impurities and contaminants, thorough biocompatibility to ensure clinical safety of the HAp to the human body, and improvement of the mechanical strength and toughness to match specific requirements for the various biomedical applications are the important areas for future studies.

[Design and performance study of bone trabecular scaffolds based on triply periodic minimal surface method].

Triply periodic minimal surface (TPMS) is widely used because it can be used to control the shape of porous scaffolds precisely by formula. In this paper, an I-wrapped package (I-WP) type porous scaffolds were constructed. The finite element method was used to study the relationship between the wall thickness and period, the morphology and mechanical properties of the scaffolds, as well as to study the compression and fluid properties. It was found that the porosity of I-WP type scaffolds with different wall thicknesses (0.1 ~ 0.2 mm) and periods (I-WP 1 ~ I-WP 5) ranged from 68.01% ~ 96.48%, and the equivalent elastic modulus ranged from 0.655 ~ 18.602 GPa; the stress distribution of the scaffolds tended to be uniform with the increase of periods and wall thicknesses; the equivalent elastic modulus of the I-WP type scaffolds was basically unchanged after the topology optimization, and the permeability was improved by 52.3%. In conclusion, for the I-WP type scaffolds, the period parameter can be adjusted first, then the wall thickness parameter can be controlled. Topology optimization can be combined to meet the design requirements. The I-WP scaffolds constructed in this paper have good mechanical properties and meet the requirements of repairing human bone tissue, which may provide a new choice for the design of artificial bone trabecular scaffolds.

Efficacy of sintered Zinc-doped fluorapatite scaffold as an antimicrobial regenerative bone filler for dental applications.

OBJECTIVES: The objective of this study was to assess whether zinc-doped fluorapatite (ZnFA) could serve as an effective antimicrobial dental bone filler for bone regeneration compared to autografts. METHODS: FA and 2 % zinc-doped FA (2ZnFA) were synthesized and characterized in-house. Compressed and sintered FA and 2ZnFA disks were incubated with bacteria to assess antimicrobial properties. Adipose-derived stem cells were cultured on these discs to evaluate the surfaces' ability to support cell growth and promote osteogenic differentiation. Surfaces exhibiting the highest expressions of the bone markers osteopontin and osteocalcin were selected for an in vivo study in a rat mandibular defect model. Twenty rats were divided into 5 groups, equally, and a 5 mm surgical defect of the jaw was left untreated or filled with 2ZnFA, FA, autograft, or demineralized bone matrix (DBM). At 12 weeks, the defects and surrounding tissues were harvested and subjected to microCT and histological evaluations. RESULTS: Standard techniques such as FTIR, ICP-MS, fluoride probe, and XRD revealed the sintered FA and ZnFA's chemical compositions and structures. Bacterial studies revealed no significant differences in surface bacterial adhesion properties between FA and 2ZnFA, but significantly fewer bacterial loads than control titanium discs (p < 0.05). Cell culture data confirmed that both surfaces could support cell growth and promote the osteogenic differentiation of stem cells. MicroCT analysis confirmed statistical similarities in bone regeneration within FA, 2ZnFA, and autograft groups. CONCLUSION: The data suggests that both FA and 2ZnFA could serve as alternatives to autograft materials, which are the current gold standard. Moreover, these bone fillers outperformed DBM, an allograft material commonly used as a dental bone void filler. CLINICAL SIGNIFICANCE: The use of FA or 2ZnFA for treating mandibular defects led to bone regeneration statistically similar to autograft repair and significantly outperformed the widely used dental bone filler, DBM. Additional translational research may confirm FA-based materials as superior substitutes for existing synthetic bone fillers, ultimately enhancing patient outcomes.

Comparing the effects of Bone+B® xenograft and InterOss® xenograft bone material on rabbit calvaria bone defect regeneration.

BACKGROUND: The bone regeneration therapy is often used in patients with inadequate bone support for implants, particularly following tooth extractions. Xenografts derived from animal tissues are effective bone reconstructive options that resist resorption and pose a low risk of transmitting disease. Therefore, these implants may be a good option for enhancing and stabilizing maxillary sinuses. The purpose of this study was to compare two xenografts, Bone+B® and InterOss®, for the reconstruction of rabbit calvaria defects. METHODS AND MATERIALS: The study involved seven male New Zealand white rabbits. In the surgical procedure, 21 spots were created on both sides of the midline calvarium by creating three 8-millimeter defects. A control group was used, as well as two treatment groups utilizing Bone+B® Grafts and InterOss® Grafts. After 3 months, the rabbits were euthanized, followed by pathological evaluation. Analysis of these samples focused on bone formation, xenograft remaining material, and inflammation levels, using Adobe Photoshop CS 8.0 and SPSS version 24. RESULTS: With the application of Bone+B® graft, bone formation ranged from 32% to 45%, with a mean of 37.80% (±5.63), and the remaining material ranged from 28% to 37%, with a mean of 32.60% (±3.65). Using InterOss® grafts, bone formation was 61% to 75%, the mean was 65.83% (±4.75), and the remaining material was 9% to 18%, with a mean of 13.17% (±3.06). The bone formation in the control group ranged from 10% to 25%, with a mean of 17.17% (±6.11). InterOss® had lower inflammation levels than other groups, but the difference was not statistically significant (p > .05). CONCLUSION: InterOss® bone powder is the best option for maxillofacial surgery and bone reconstruction. This is due to more bone formation, less remaining material, and a lower inflammation level. Compared to the control group, Bone+B® improves healing and bone quality, thus making it an alternative to InterOss®.

Synchrotron Analysis of Damaged Extraction Sockets Augmented Using a Synthetic Bone Block: A Pilot Study.

This study aimed to investigate the dimensional stability and quality of the alveolar ridge augmented using a synthetic bone block (SBB) at damaged extraction sockets. Four participants were included, and socket augmentation was performed using SBB and a collagen membrane. Intraoral and CBCT scans were performed before extraction (baseline), immediately postoperative (IP), and at 6 months postoperative (6M). At 6M, a trephine biopsy sample was obtained during implant placement, and the sample was observed using synchrotron. Soft tissue profile changes were assessed using profilometric analysis of the intraoral scan data, while dimensional changes in hard tissue were evaluated based on CBCT measurements. Bone quality was analyzed using synchrotron imaging. There were minimal changes in the soft tissue profile between baseline and IP, baseline and 6M, and IP and 6M (0.11 ± 1.08 mm3, 0.02 ± 0.8 mm3, and -0.65 ± 0.82 mm3, respectively). Horizontal bone width was measured at 1-mm increments from the augmented bone crest to 5 mm apically and revealed only a slight reduction (< 1 mm) at all levels between IP and 6M. The augmented bone height was well maintained from IP until 6M (-0.21 ± 0.53 mm). Synchrotron analysis revealed low to moderate bone quality after 6M (percentage of new bone: 16.49% ± 4.91%). Socket augmentation using SBB appears to be a viable technique for regenerating damaged extraction sockets, with the augmented ridge dimensions maintained up to 6M. Further long-term randomized clinical trials are needed.

Novel Synthetic Carbonate Apatite as a Bone Substitute in Implant Treatments: Case Reports.

Bone graft materials are often used in implant treatment to optimize functional and esthetic outcomes. The requirements for bone grafting materials are the ability to maintain space for bone regeneration to occur and the capability of being resorbed by osteoclasts and replaced with new bone tissue occurring in passive chemolysis and bone remodeling. Carbonate apatite (CO3Ap) granules (Cytrans Granules, GC) are a chemically synthetic bone graft material similar to autogenous bone minerals and more biocompatible than allografts and xenografts. The aim of this report is to evaluate the efficacy of CO3Ap granules in implant treatments when used alone or in combination with autogenous bone. The clinical findings and the radiographic and histologic assessments in three cases of immediate implant placement and lateral and vertical guided bone regeneration are reported. Despite the short-term follow-ups, histologic findings showed that CO3Ap granules were efficiently resorbed and replaced bone in clinical use. Furthermore, the clinical findings showed that CO3Ap granules maintained their morphology around the implant. This limited short-term case report suggests that this bone substitute is effective. However, further clinical studies and long-term reports of this new biomaterial are needed.

Application and Perspectives: Magnesium Materials in Bone Regeneration.

The field of bone regeneration has always been a hot and difficult research area, and there is no perfect strategy at present. As a new type of biodegradable material, magnesium alloys have excellent mechanical properties and bone promoting ability. Compared with other inert metals, magnesium alloys have significant advantages and broad application prospects in the field of bone regeneration. By searching the official Web sites and databases of various funds, this paper summarizes the research status of magnesium composites in the field of bone regeneration and introduces the latest scientific research achievements and clinical transformations of scholars in various countries and regions, such as improving the corrosion resistance of magnesium alloys by adding coatings. Finally, this paper points out the current problems and challenges, aiming to provide ideas and help for the development of new strategies for the treatment of bone defects and fractures.

Comparison Between Corticocancellous Allograft and Bovine Xenograft for Sinus Augmentation: A Radiographic, Histologic, and Histomorphometric Clinical Study.

Sinus floor augmentation is one of the most common approaches to obtain sufficient bone availability for placing implants in cases with severe bone atrophy in the posterior maxilla. Several bone substitutes are indicated for sinus augmentation, but they may achieve different clinical outcomes. This study aims to compare bovine bone mineral (BBM) with freeze-dried bone allograft (FDBA) in a two-stage lateral window sinus grafting approach. Twenty patients received a lateral window sinus elevation with either FDBA or BBM. Postoperative graft height was measured with CBCT. Implants were placed 6 months later, at which time biopsy samples were taken for histologic analysis and new CBCT scans were performed to measure graft height. The mean height reduction at 6 months was 20.27% ± 4.94% for FDBA samples and 5.36% ± 2.41% for BBM samples. The histologic analysis revealed a mean ratio of newly formed bone of 43.70% ± 5.29% for the FDBA group and 38.11% ± 4.03% for the BBM group. The FDBA group also showed a higher amount of residual biomaterial (17.25% ± 10.10%) and connective tissue (14.63% ± 4.38%) compared to the BBM group (15.53% ± 5.42% and 13.11% ± 4.42%, respectively). The differences between groups were statistically significant for the height reduction and newly formed bone (P ≤ .05) but not for the amounts of residual biomaterial and nonmineralized connective tissue (P ≥ .05). Six months after performing a lateral window sinus elevation, the percentage of newly formed bone was significantly higher when using FDBA than when using BBM, although the graft height reduction was also significantly higher for the FDBA group.

Contour Augmentation for Periodontal Defects (CAPD) for Periodontally Compromised Teeth with Horizontal Bone Loss: A Prospective Cohort Assessment at 1 Year.

This study assessed the effects of buccal contour augmentation for periodontally compromised teeth with horizontal bone loss. A total of 30 subjects were divided into Group A or Group B (n = 15 subjects per group). Group A received open-flap debridement (OFD) with buccal contour augmentation using deproteinized bovine bone mineral (DBBM), jointly referred to as contour augmentation for periodontal defects (CAPD; test group). Group B received only OFD (control group). Bleeding on probing (BOP), clinical attachment level (CAL), probing depth (PD), gingival recession (GR), keratinized mucosa width (WKM), keratinized mucosa thickness (TKM), and labial cortical plate thickness were compared at baseline and 1 year. BOP, CAL, PD, and GR did not show significant differences. TKM increased by 1.76 mm for Group A but decreased by 1 mm for Group B. WKM increased from 2.86 ± 0.4 mm to 3.6 ± 0.71 mm (P < .001) and from 2.93 ± 0.32 mm to 3 ± 0.7 mm (P = 0.5) for Groups A and B, respectively, which showed statistical significance. Labial cortical plate thickness increased from 0.94 ± 0.3 mm to 1.95 ± 0.54 mm (P < .001) for Group A but decreased from 0.87 ± 0.45 mm to 0.68 ± 0.31 mm for Group B. Visual analog scale scores for pain perception showed no difference between the two groups. CAPD for periodontally compromised teeth improves WKM and TKM. Long-term analyses are needed to determine its benefits in daily clinical practice.

Evaluation optimum ratio of synthetic bone graft material and platelet rich fibrin mixture in a metal 3D printed implant to enhance bone regeneration.

BACKGROUND: This study aims to evaluate the optimal ratio of synthetic bone graft (SBG) material and platelet rich fibrin (PRF) mixed in a metal 3D-printed implant to enhance bone regeneration. METHODS: Specialized titanium hollow implants (5 mm in diameter and 6 mm in height for rabbit; 6 mm in diameter and 5 mm in height for pig) were designed and manufactured using 3D printing technology. The implants were divided into three groups and filled with different bone graft combinations, namely (1) SBG alone; (2) PRF to SBG in 1:1 ratio; (3) PRF to SBG in 2:1 ratio. These three groups were replicated tightly into each bone defect in distal femurs of rabbits (nine implants, n = 3) and femoral shafts of pigs (fifteen implants, n = 5). Animal tissue sections were obtained after euthanasia at the 8th postoperative week. The rabbit specimens were stained with analine blue, while the pig specimens were stained with Masson-Goldner's trichrome stain to perform histologically examination. All titanium hollow implants were well anchored, except in fracture specimens (three in the rabbit and one fracture in the pig). RESULT: Rabbit specimens under analine blue staining showed that collagen tissue increased by about 20% and 40% in the 1:1 ratio group and the 2:1 ratio group, respectively. Masson-Goldner's trichrome stain results showed that new bone growth increased by 32% in the 1:1 ratio PRF to SBG, while - 8% in the 2:1 ratio group. CONCLUSION: This study demonstrated that placing a 1:1 ratio combination of PRF and SBG in a stabilized titanium 3D printed implant resulted in an optimal increase in bone growth.