Dentin erosive wear is reduced by fluoride varnishes containing nanosized sodium trimetaphosphate in vitro.

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Hard drugs use and tooth wear: a scoping review.

OBJECTIVES: This study aims to map evidence on the relationship between hard drug use and dental wear. The scoping review is guided by the question: What is the relationship between hard drug consumption and dental wear? MATERIALS AND METHODS: Adhering to PRISMA-ScR guidelines, searches were conducted across PubMed, Embase, and four databases in March 2024. Inclusion criteria included studies investigating the association between hard drug use and dental wear, regardless of publication date or language. Data were presented through narrative exposition, tables, and a conceptual framework. RESULTS: Twenty-eight studies (four case-control, three cross-sectional, five case reports, and sixteen literature reviews) were included. Among case-control studies, 75% observed an association between drug use and dental erosion; however, no cross-sectional studies demonstrated this association. Despite questionable quality, reviews established connections between drug use and dental erosion. Studies aimed to elucidate potential causes for dental erosion. CONCLUSIONS: Analysis suggests a potential link between hard drug use and dental wear, though indirect. Factors like bruxism and reduced salivary pH may contribute to dental wear among drug users. Further investigation through primary studies exploring this relationship is necessary. CLINICAL RELEVANCE: Dentists should focus not only on clinical characteristics of dental wear but also on mediating factors such as bruxism and decreased salivary pH associated with drug use. This holistic approach allows for a deeper understanding of dental wear mechanisms, enabling targeted preventive and therapeutic interventions.

Prevalence of erosive tooth wear and associated risk factors in Colombian adolescents.

Accurate determination of the prevalence of erosive tooth wear (ETW) and associated risk factors in adolescents can inform clinical management guidelines. The aim of this analytical cross-sectional study was to estimate the prevalence, severity, and risk factors of ETW in adolescents aged 12-15 years in the municipality of Usaquén in Bogotá, Colombia. Two calibrated examiners clinically assessed ETW using Basic Erosive Wear Examination (BEWE) Index (range: 0-3). All tooth surfaces (excluding proximal) were scored to allow estimation of the Highest (0-3) and Total BEWE (sum of Highest BEWE score per sextant: 0-18) scores per patient. Sociodemographic characteristics, ETW risk factors, and caries severity (ICDAS-epi-merged) were evaluated, and their association with the presence of ETW (indicated by a Highest BEWE score of 2-3) was examined using preliminary analyses and logistic regression models. The study sample included 454 adolescents (mean age: 13.5±1.1 years; female: 61.7%), and the prevalence of ETW was 71.6%. The majority of participants exhibited a Highest BEWE score of 3 (58.0%) and a Total BEWE score ≤8 (84.3%). The preliminary analysis showed an association between the presence of ETW and age, caries, and brushing teeth before eating (p-value < 0.05). Risk factors for ETW included always brushing teeth before eating [adjusted Prevalence Ratio (PRa) 1.31, p-value=0.014], presence of extensive carious lesions (PRa 1.23, p-value = 0.024), male gender (PRa 1.14, p-value = 0.028), and age > 14 years (PRa 1.17, p-value = 0.009). Although ETW was highly prevalent, most Colombian adolescents exhibited low Total BEWE scores. ETW was associated with frequent fruit intake, age, toothbrushing habits, caries lesions, and sex.

Effect of erosive conditions on different sealant materials used in paediatric dentistry.

To evaluate the effect of acidic challenge on erosion depth and topographic characteristics of different materials used as occlusal sealants. Two hundred specimens of five sealant materials (Fuji IX, Ketac Molar, Fuji II, Equia and Clinpro) and forty bovine teeth enamel samples (control) were prepared and exposed to acidic challenge. The specimens were immersed in four different solutions (orange juice, coke drink, citric acid or distilled water) under mildly shaken conditions for 3 days. The erosion depth profiles were measured using a profilometer and Scanning Electron Microscope (SEM). Two-way ANOVA with Tukey post-hoc test was performed to evaluate the interactions. Sealant material and acidic challenge had significant effects on erosion depth. Among the materials, Fuji II presented the highest mean of erosion depth after immersion in orange juice, coke drink, and citric acid. All materials groups presented higher erosion depth values after immersion in the citric acid solution, except Clinpro. Bovine enamel presented higher erosion depth values compared to all materials when submitted to erosive challenge. Sealant materials submitted to the acidic challenge presented different degrees of erosion and topographic modification; however, they are less susceptible to erosion than bovine teeth enamel.

Development and effect of orodispersible film incorporated with Biosilicate for remineralization of dental enamel subjected to cariogenic and erosive challenge.

OBJECTIVES: The objective of this in vitro study was to assess the efficiency of incorporating Biosilicate particles (30 and 50 mg) into an experimental orodispersible film and its efficacy in the remineralization process of bovine dental enamel under cariogenic and erosive challenges. METHODS: Ninety-nine intact incisors, devoid of cracks or fractures, yielding 198 samples (6 × 6 × 2 mm) via vestibular sectioning using a low-speed diamond disc under water cooling. After flattening the enamel surface with 600, 1200, and 2000 grit sandpaper, the samples were divided into two groups based on the challenges they underwent: cariogenic (0.1 M lactic acid at pH 5.0) or erosive (0.05 M citric acid solution at pH 2.3). Samples from each challenge were further categorized into 11 groups (n = 9) according to the duration of cariogenic (3, 7, and 14 days) or erosive (3, 7, and 10 days) challenge, along with positive control groups (fragments untreated with challenges and treated with different Biosilicate concentrations) and negative controls (fragments treated with artificial saliva for the same periods established for cariogenic and erosive challenges). Treatments with orodispersible films containing Biosilicate (30 and 50 mg) were administered for 2 min per day for 15 days. RESULTS: The highest remineralizing potential was observed in samples treated with Biosilicate after 14 days of cariogenic challenge, irrespective of the concentration tested. For samples subjected to erosive challenge, erosion time did not affect Biosilicate's remineralizing potential. CONCLUSION: Biosilicate shows promise in terms of remineralizing potential in enamel subjected to cariogenic challenge due to its ability to form hydroxycarbonapatite in mineralized tissues.

[Risk analysis Erosive Tooth Wear (ETW): checklist for a quick assessment of the risk factors for ETW in the dental practice]. / Risikoanalyse Erosive Tooth Wear (ETW): Checkliste zur schnellen Bewertung der Risikofaktoren für ETW in der Zahnarztpraxis.

Erosive Tooth Wear (ETW) is the loss of tooth structure without bacterial involvement. As the resulting loss of tooth structure is irreversible, an early evaluation of the multifactorial etiology, accurate diagnosis and regular follow-up are essential. The ETW is dynamic and its progression should be continuously monitored. A risk analysis table was developed to systematically record risk factors for ETW (Fig. 2). This allows ETW management to be integrated more efficiently into clinical practice and the progression to be documented over the years. If ETW is assumed, the risk analysis should be performed and updated at least every two years. In the assessment, risk-promoting and risk-inhibiting factors are marked, added together and compared. If the negative factors pre-dominate, measures should be taken to minimize the risk for ETW. The main purpose of the risk analysis is therefore to evaluate the individual etiology, coun-teract negative factors, promote positive factors and prevent progression.

Practical training using BEWE aimed at improving the diagnosis ability of erosive tooth wear for dental students-A randomized trial.

INTRODUCTION: Erosive tooth wear (ETW) has been gaining attention due to its high prevalence. However, ETW clinical diagnosis is difficult and may go unnoticed by many professionals. The present study aimed to develop, implement and evaluate a theoretical-practical training using active methodologies in the development of undergraduate students' skills for the diagnosis of ETW compared to the traditional teaching method. MATERIALS AND METHODS: This randomized controlled study involved two parallel groups: control group (n = 22), with learning based only on theoretical content and test group (n = 24), learning by theoretical-practical activity mediated by monitors/tutors. The theoretical class covered the current concepts of ETW, aetiology, diagnosis, use of the BEWE index, prevention and treatment. The practical training included exercises and discussions based on the diagnosis using BEWE scores of a collection of images and extracted teeth. To evaluate the efficacy of the teaching-learning methods, a theoretical multiple-choice questionnaire and a practical test using images and extracted teeth were applied. The outcome was the number of correct answers. Groups were compared by Mann-Whitney (theoretical knowledge) and T tests (practical ability in diagnosis) (p < .05). RESULTS: There was no significant difference between groups in the theoretical evaluation (p = .866). The test group showed higher ability to diagnose ETW lesions compared to the control group in the practical tests (p = .001). The performance of ETW diagnosis was similar when images were used in comparison to extracted teeth (p = .570). CONCLUSION: The practical activity associated with theoretical classes can be a promising strategy to improve the development of undergraduate students' skills in the diagnosis of ETW.

Salivary, acidic and enzymatic degradation of resin composite subjected to different finishing and polishing systems.

PURPOSE: To evaluate the effect of different finishing and polishing systems on the surface roughness of a resin composite subjected to simulated saliva-, acid-, and enzyme-induced degradation. METHODS: 160 specimens (n= 40) were fabricated with Filtek Z350 XT nanofilled composite and analyzed for average surface roughness (Ra). The specimens were finished and polished using: AD - Al2O3-impreginated rubberized discs (medium, fine, and superfine grit, Sof-Lex); SD - silicon carbide and Al2O3-impregnated rubberized discs (coarse, medium and fine grit, Jiffy,); MB - 12- and 30-multiblade burs. The control group (CT) (n= 40) comprised specimens with a Mylar-strip-created surface. Specimens from each group were immersed in 1 mL of one of the degradation methods (n= 10): artificial saliva (ArS: pH 6.75), cariogenic challenge (CaC: pH 4.3), erosive challenge (ErC: 0.05M citric acid, pH 2.3) or enzymatic challenge (EzC: artificial saliva with 700 µg/mL of albumin, pH 6.75). The immersion period simulated a time frame of 180 days. Ra measurements were also performed at the post-polishing and post-degradation time points. The data were evaluated by three-way ANOVA for repeated measures and the Tukey tests. RESULTS: There was significant interaction between the finishing/polishing system and the degradation method (P= 0.001). AD presented the greatest smoothness, followed by SD. After degradation, CT, AD and SD groups became significantly rougher, but not the MB group, which presented no difference in roughness before or after degradation. CT and AD groups showed greater roughness in CaC, ErC and EzC than in ArS. The SD group showed no difference in roughness when the specimens were polished with CaC, EzC or ArS, but those treated with ErC had greater roughness. In the MB group, the lower roughness values were found after using CaC and EzC, while the higher values were found using ErC or ArS. CLINICAL SIGNIFICANCE: As far as degradation resistance of nanofilled composite to hydrolysis, bacterial and dietary acids and enzymatic reactions is concerned, restorations that had been finished and polished with Al2O3-impregnated discs had the smoothest surfaces.

Risk indicators for the severity of erosive wear in deciduous dentition of Mexican schoolchildren aged 5 to 7 years.

The objective of this work was to estimate the prevalence and severity of erosive tooth wear (ETW), and to identify risk indicators of deciduous dentition of a group of schoolchildren from public schools in Tlalnepantla de Baz, State of Mexico. A cross-sectional study was carried out in 352 schoolchildren from 5 to 7 years old. The severity of the ETW was evaluated using the Basic Erosive Wear Examination (BEWE). Risk indicators were evaluated through a survey which included food and beverage consumption, consumption habits, vitamin C consumption, gastroesophageal reflux, heartburn, belching, xerostomia, vomiting and teeth grinding. Multinomial logistic regression models were fitted. The prevalence of ETW was 99.7% (n = 351). Regarding severity, 46.6% were at a null/mild level, 27.3% moderate, and 26.1% severe. Males were more likely to present severe ETW (odds ratio (OR) = 2.23, 95% confidence interval (CI), 1.27-3.93; p = 0.005). The risk indicators for the severity of ETW were the frequent consumption of citrus fruits (OR = 2.09, 95% CI, 1.12-3.89; p = 0.021), fruit juice (OR = 1.99, 95% CI, 1.06-3.75; p = 0.033), processed beverages (OR = 2.15, 95% CI, 1.23-3.78; p = 0.008) and hot sauce (OR = 1.82, 95% CI, 1.03-3.20; p = 0.036). The prevalence of ETW in the deciduous dentition was very high (99.7%) and ~1/3 for severe ETW. The dietary factors associated with severe ETW are part of the regular consumption of Mexican school-age children, which impact their oral health condition. It is important to establish intervention strategies from the infant stage, focused on both children and their caregivers.

Factors associated with prevalence and severity of erosive tooth wear in patients with reflux oesophagitis.

BACKGROUND: Extrinsic factors for erosive tooth wear (ETW) have been widely reported, but the intrinsic factors for wear remain unclear. OBJECTIVES: The aim of this study was to evaluate the factors associated with the prevalence of ETW in patients with reflux oesophagitis (RO). To prevent severe ETW with RO, factors associated with severity of ETW were also evaluated. METHODS: A total of 270 patients with RO were recruited. A modified tooth wear index was used to evaluate the prevalence and severity of ETW. Salivary secretion and buffering capacity were assessed prior to endoscopy. Subjects were asked to complete a medical condition and oral self-care questionnaire. Univariate and multivariate analyses were employed to identify factors collectively associated with the prevalence and severity of ETW. RESULTS: A total of 212 cases were categorized as patients with ETW (148 with mild ETW and 64 with severe ETW). Multivariate analyses indicated that saliva secretion, severity of RO and proton pump inhibitor (PPI) resistance were associated with the prevalence of ETW, whereas age, BMI and severity of RO were associated with the severity of ETW. The odds ratio of saliva secretion and BMI were less than 1, meaning that higher saliva secretion resulted in a lower prevalence of ETW and lower BMI was associated with severe ETW. CONCLUSION: Saliva secretion, severity of RO and PPI resistance were associated with the prevalence of ETW, whereas age, BMI and severity of RO were associated with the severity of ETW. Lower saliva secretion and BMI were significant factors for ETW.

Effect of different brushing parameters on erosive tooth wear in primary bovine enamel and dentin.

This in-vitro study aimed to analyse the effect of brushing and different brushing parameters (kind of toothpaste, kind of toothbrush, brushing force) on erosive tooth wear of primary bovine enamel and dentin. Specimens were prepared from primary bovine enamel or dentin (each group n = 12) and cyclically eroded (6 × 60 s/d, citric acid, pH 2.4) and brushed with children's toothbrushes (2 × 15 s/d) over 5 days. The brushing parameters under investigation were: toothpaste (fluoridated, fluoride-free), toothbrush (manual; rotating-oscillating and sonic, each at two different activation modes) and brushing force (1 N, 2 N). Specimens that were only eroded and not brushed served as controls. Enamel and dentin wear was quantified using widefield confocal microscopy. Statistical analysis was performed using three- and one-way ANOVAs followed by Scheffe's (enamel) or Tamhane's (dentin) post-hoc tests (p < 0.05). Brushing with the fluoridated toothpaste was able to significantly reduce erosive wear in enamel (by 15 to 37%, 6 of 10 groups) and in dentin (by 58 to 72%, all groups), while brushing with the fluoride-free toothpaste was not different from the controls. Considering the kind of toothpaste and brushing force, slight differences between the toothbrushes were observed in enamel, but not in dentin. Within the same toothbrush and activation mode, almost no differences between 1 and 2 N brushing force were detected. In conclusion, erosive tooth wear on primary bovine dental hard tissue mainly depends on the kind of toothpaste, rather than on the kind of toothbrush and the brushing force.

Tooth surface loss: causes, management, and prevention.

OBJECTIVES: Tooth wear, also referred to as tooth surface loss, occurs due to causes other than caries. This involves the loss of hard tissues, namely enamel, dentin, and/or cementum. Types of tooth wear/tooth surface loss are abrasion, abfraction, attrition, and erosion. These multifactorial conditions can be caused by factors such as lifestyle, diet, or even habits, and may not be symptomatic. The focus of this article is to provide clinicians with detailed examples and explanations of the causes of tooth loss to aid in early diagnosis. Through early identification, the preventive measures outlined can be implemented to avoid excessive tooth wear. The provision of a treatment flowchart and general treatment recommendations aims to help clinicians determine when to restore these lesions and the most appropriate treatment measures for the four types of wear. METHOD AND MATERIALS: The PubMed (MEDLINE) search engine was used to gather information on teeth restricted to a 5-year period (26 August 2018 to 25 July 2022). Only English-language studies and reviews with the best balance of sensitivity and specificity were considered. A Boolean search of the PubMed dataset was implemented to combine a range of keywords: ("tooth wear" OR tooth attrition OR tooth erosion OR tooth abrasion OR tooth abfraction). Additional articles were selected through Google Scholar. RESULTS: By this process, many articles and studies were obtained, and the 48 most relevant published studies were chosen and used in the current review. CONCLUSION: Tooth wear affects an increasing number of individuals and can have detrimental effects physically, mentally, and emotionally. It is important to stress early diagnosis and management of tooth wear through monitoring, prevention, and treatment where indicated.

In vitro effect of fluoride gels supplemented with nano-sized sodium trimetaphosphate on enamel erosive wear.

OBJECTIVE: To assess the protective effect of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) against enamel erosion in vitro. METHODS: Bovine enamel blocks (n = 140) were selected according to their surface hardness, and randomly divided into seven groups (n = 20/group), according to the gels tested: Placebo (without F/TMP), 4,500 µg F/g (4500F), 9,000 µg F/g (9000F), 4500F plus 2.5 % TMPnano (2.5 % Nano), 4500F plus 5 % TMPnano (5 % Nano), 4500F plus 5 % TMPnano (Micro 5 %) and 12,300 µg F/g (Acid gel). Blocks were treated once during one minute with the gels, and submitted to erosive (ERO, n = 10/group) or erosive plus abrasive (ERO+ABR, n = 10/group) challenges 4 times/day, for 90 s for each challenge (under reciprocating agitation), during consecutive 5 days. Blocks were analyzed by profilometry, and by surface (SH) and cross-sectional hardness (∆KHN). Data were submitted to two-way ANOVA, and Fisher's LSD test (p < 0.05). RESULTS: For ERO, both TMPnano-containing gels promoted enamel wear significantly lower than Placebo and 4500F, reaching levels similar to both positive controls (9000F and acid gel); significantly lower softening was observed for enamel treated with 4500F+5 % Micro and 4500F+2.5 % Nano. Also, the lowest ∆KHN values were observed for 4500F+2.5 % TMPnano among the TMP-containing gels. For ERO+ABR, the lowest enamel wear was achieved by the use of 4500F+5 % Nano among all gels, including both positive controls; lower softening was observed for Placebo and 9000F groups. CONCLUSION: The addition of 5 % nano-sized TMP to a low-fluoride gel produced superior protective effects for enamel under both challenges conditions, when compared with micrometric TMP, reaching values similar to or superior than both positive controls, respectively for ERO and ERO+ABR. CLINICAL SIGNIFICANCE: The supplementation of low-F gels with TMP was shown to significantly improve their effects on enamel erosive wear, and the use of nano-sized TMP further enhances this protective action.

Preventive dental erosion with silver diamine fluoride: An in vitro study.

OBJECTIVES: To evaluate the erosion preventive effect of 38 % silver diamine fluoride (SDF) solution in enamel and dentin of human permanent teeth. METHODS: Ninety enamel and ninety dentin blocks were prepared from permanent molars and allocated into three groups. Gp-SDF received a one-off application of 38 % SDF solution. Gp-SNF received a one-off application of a solution containing 800 ppm stannous chloride and 500 ppm fluoride. Gp-DW received a one-off application of deionized water. The blocks were submitted to acid challenge at pH 3.2, 2 min, 5 times/day for 7 days. All blocks were immersed in human saliva between cycles for one hour. The crystal characteristics, percentage of surface microhardness loss (%SMHL), surface loss, and elemental analysis and surface morphology were examined by X-ray diffraction (XRD), microhardness test, non-contact profilometry, and energy-dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM), respectively. Data of%SMHL and surface loss were analyzed by one-way ANOVA. RESULTS: XRD spectra revealed that fluorapatite and silver compounds formed in Gp-SDF, while fluorapatite and stannous compounds formed in Gp-SNF. Gp-DW presented only hydroxyapatite. The median (interquartile range) of%SMHL in Gp-SDF, Gp-SNF and Gp-DW were 27.86(3.66), 43.41(2.45), and 46.40(3.54) in enamel (p< 0.001), and 14.21(1.57), 27.99(1.95), and 33.18(1.73) in dentin, respectively (p < 0.001). The mean (standard deviation, µm) of surface loss of Gp-SDF, Gp-SNF, and Gp-DW were 2.81(0.59), 4.28(0.67), and 4.63(0.64) in enamel (p < 0.001) and 4.13(0.69), 6.04(0.61), and 7.72(0.66) in dentin, respectively (p < 0.001). SEM images exhibited less enamel corruption and more dentinal tubular occlusion in Gp-SDF compared to Gp-SNF and Gp-DW. EDS analysis showed silver was detected in Gp-SDF while stannous was detected in the dentin block of Gp-SNF. CONCLUSION: 38 % SDF yielded superior results in protecting enamel and dentin blocks from dental erosion compared to SNF and DW. CLINICAL SIGNIFICANCE: Topical application of 38 % SDF is effective in preventing dental erosion in human enamel and dentin.

Influence of fluoride characteristics on tooth surface protection in an erosive condition: A multifaceted characterization approach.

OBJECTIVE: To evaluate the effect of fluoride consistency and composition to protect enamel and dentin against the dental erosion. MATERIALS AND METHODS: Bovine enamel and dentin specimens were treated with artificial saliva, neutral fluoride gel (NFG), acidulated phosphate fluoride gel (AFG), neutral fluoride foam (NFF), and acidulated phosphate fluoride foam. The samples were subjected to cycling. Micro energy-dispersive X-ray fluorescence spectrometry, surface roughness (Ra), contact angle (CA), and scanning electron microscopy (SEM) were performed. Composition, CA and Ra data were analyzed by ANOVA and multiple comparison test (p < 0.05). RESULTS: The dentin protected had a significantly higher mineral content than in the control. Eroded unprotected enamel had higher Ra values than normal surfaces. Fluoride treatments increased the Ra in dentin samples. AFG increased the CA in enamel. Fluoride foams increased CA in dentin with reduced mineral loss. SEM analysis found a deposited layer on enamel treated with AFG and remnants of deposits on dentin treated with NFG and NFF. CONCLUSION: Regardless of the form of application, fluoride provided protection against erosion, however with different levels. CLINICAL SIGNIFICANCE: Applying the adequate fluoride form is relevant since the formulations have different effects on both enamel and dentin.

Toothpaste containing TiF4 and chitosan against erosive tooth wear in situ.

OBJECTIVE: This study compared the protective effect of an experimental TiF4/Chitosan toothpaste with a commercial toothpaste on the prevention of erosive tooth wear (ETW) in situ. METHODS: Fifteen subjects took part in this crossover and double-blind study, in which they wore a palatal appliance containing 4 bovine enamel and 4 dentin in 3 phases (5 days each). Half of the samples were subjected to erosive challenges (90 s in 0.1 % citric acid, pH 2.5, 4 times/day), and the other half to erosive plus abrasive challenges (15 s plus 45 s of contact, 2 times/day). The phases corresponded to the application of the different toothpastes: 1) TiF4 (1400 ppm F-) plus Chitosan, 2) Elmex®, Erosion Protection (1400 ppm F-, Chitosan), and 3) Placebo (negative control). Tooth wear was measured using contact profilometry (µm) and submitted to two-way RM ANOVA/Tukey test (p < 0.05). RESULTS: No significant differences were detected between the experimental and commercial toothpastes, regardless of the challenge on both tissues. Both significantly reduce ETW compared to negative control (p < 0.0006). Tooth wear was increased by brushing only on eroded enamel (p < 0.01), but not on dentin (p = 0.6085). TiF4/Chitosan [erosion 2.98 ± 1.12 µm vs. erosion and abrasion 3.12 ± 1.33 µm] and Elmex® toothpastes [erosion 2.35 ± 0.93 µm vs. erosion and abrasion 2.98 ± 1.0 µm] minimized the impact of brushing compared to placebo on enamel [erosion 4.62 ± 1.48 µm vs. erosion and abrasion 5.15 ± 1.50 µm]. CONCLUSIONS: TiF4 plus chitosan toothpastes showed to be effective in minimizing the ETW as the commercial toothpaste is in situ. CLINICAL RELEVANCE: The experimental toothpaste has similar effect against ETW compared to the commercial toothpaste. Considering the increased ETW prevalence worldwide, this result supports clinical trials and a possible application of this experimental anti-erosive toothpaste in the future.

Prevention and management of dental erosion and decay.

The 2017 Global Disease Study revealed 2.3 billion untreated cavities and 139 million other oral conditions like dental erosion. Modern treatments prioritise controlling etiological factors and preventing related diseases. This Editorial invites researchers to contribute to the collection, 'Prevention and management of dental erosion and decay'.

Protective effect of various toothpastes and mouthwashes against erosive and abrasive challenge on eroded dentin: an in vitro study.

The study aimed to compare various toothpastes and mouthwashes on permanent tooth dentin after erosive and abrasive challenges. 130 sound premolars dentin were randomly submitted to an initial erosive challenge and a cycle of erosive and abrasive challenges for five days. The five experimental groups (n = 26) were: (1) Control group (artificial saliva), (2) Elmex erosion protection toothpaste and mouthwash, (3) Vitis anticaries biorepair toothpaste and mouthwash, (4) Oral B Pro-expert toothpaste and Oral B Fluorinse mouthwash, and (5) MI Paste ONE toothpaste and Caphosol mouthwash. Microhardness, surface roughness values, and the topographical characteristics of the dentin surface were assessed. The highest percentage of recovered dentin microhardness (%RDMH) value was observed in groups 2 and 4, followed by groups 5 and 3, respectively. The %RDMH values in groups 2 and 4 did not demonstrate a significant difference (p = 0.855). The highest percentage of improvement in surface roughness was recorded in groups 2 and 4, with no significant differences (p = 0.989). The atomic force microscopy (AFM) findings were consistent with the surface roughness data. The best recovery of dentin microhardness and roughness were measured with the Elmex and Oral B toothpaste and mouthwash, followed by MI Paste ONE toothpaste and Caphosol mouthwash and Vitis anticaries biorepair toothpaste and mouthwash.

The erosive effect of pomegranate juice on enamel: An in vitro study.

AIM: Dental erosion is a chemical-mechanical process that leads to the loss of dental hard tissues. This study aimed to investigate the effect of pomegranate juice on the enamel. METHODS: Enamel blocks were randomly divided into three groups: deionized water, cola, and pomegranate juice. The blocks were immersed in the solutions four times a day for 14 days, and stored in artificial saliva for the remaining period. The surface hardness was measured on days 7 and 14. The surface structures of the demineralized blocks were observed via scanning electron microscopy (SEM), and the depth of demineralization was observed via confocal laser scanning microscopy (CLSM). The pH, calcium, and phosphorus levels of the three solutions were analyzed. RESULTS: The microhardness values of the blocks in the pomegranate juice and cola groups decreased with the increase in the demineralization time. The blocks in the pomegranate juice group exhibited large fractures in the enamel column, whereas those in the cola group had pitted enamels with destruction of the interstitial enamel column. Compared with cola group, fluorescent penetration increased in pomegranate juice (P < 0.01). The pH of cola (2.32 ± 0.09) was lower than that of pomegranate juice (3.16 ± 0.16). Furthermore, the calcium content in pomegranate juice was significantly higher than that in cola (P < 0.01). Alternatively, the concentration of phosphorous in cola was significantly higher than that in pomegranate juice (P < 0.01). CONCLUSION: These findings indicate that pomegranate juice can cause enamel demineralization with an erosive potential comparable to that of cola.

Low-fluoride gels supplemented with nano-sized sodium trimetaphosphate reduce dentin erosive wear in vitro.

OBJECTIVE: The study assessed the effect of low-fluoride gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. DESIGN: Bovine dentin blocks (n = 154) were selected by surface microhardness and randomly allocated into seven groups (n = 22/group), according to the gels: Placebo; 4500 ppm F (4500F); 9000 ppm F (9000F); 5% TMP microparticulate plus 4500F (5TMPm+4500F); 2.5% TMP nanoparticulate plus 4500 F (2.5TMPn+4500F); 5% TMP nanoparticulate plus 4500F (5TMPn+4500F); and 12,300 ppm F acid gel (APF). All blocks were treated only once for 60 s and cyclically eroded (ERO, citric acid, 4 × 90 s/day) or eroded and brushed (4 × 15 s/day, five strokes/s, ERO+ABR) over five days (each subgroup n = 11). Dentin wear and integrated hardness loss in depth (ΔKHN) were determined, and the data were submitted to two-way ANOVA, followed by Tukey's test, and Spearman's correlation (p < 0.05). RESULTS: For ERO, all gels containing 4500F supplemented with TMP significantly reduced dentin wear compared with their counterpart without TMP, reaching values similar to 9000F. For ERO+ABR, 5TMPn+ 4500F gel led to significantly lower wear than all its counterparts, reaching values similar to 9000F and APF. As for ΔKHN, all gels containing TMP promoted superior protective effects compared with 4500F, reaching values similar to 9000F and APF under both challenges. A positive correlation between dentin wear and mineral content in depth was verified. CONCLUSIONS: Gels containing 4500F supplemented with TMP significantly reduced dentin erosive wear compared with pure 4500F, with additional benefit from the use of nanoparticles.