Calcium Hydroxide improves epoxy sealer adhesion on root dentin / O hidróxido de cálcio melhora a adesão de selante resinoso à dentina radicular
Braz. dent. sci
; 20(2): 108-113, 2017. graf, ilus
Artigo
em Inglês
| LILACS, BBO - Odontologia
| ID: biblio-846441
Biblioteca responsável:
BR243.1
RESUMO
Objetivo: O intuito deste estudo é avaliar a adesão de um cimento endodôntico (AH Plus) em canais radiculares após o uso de diferentes protocolos de EDTA 17% e o uso de medicação intracanal (ICM) à base de hidróxido de cálcio em veículo aquoso. Material e Métodos: Para isso, 72 dentes humanos unirradiculares foram instrumentadas até # 50 e divididos em seis grupos (n = 12). Grupo 1: EDTA por 3 min; Grupo 2: 3 mL de EDTA + 3 min de EDTA; Grupo 3: 3 ml de EDTA + 3 min de EDTA + 30 segundos de agitação ultra-sônica; Grupo 4: EDTA durante 3 min + ICM; Grupo 5: 3 ml de EDTA + 3 min de EDTA + ICM; Grupo 6: 3 ml de EDTA + 3 min de EDTA + 30 segundos de agitaçãosônica + ICM. Os canais radiculares foram preenchidos com cimento endodôntico após cada protocolo e, após 7 dias foram preparados para o teste de push-out. Os dados foram analisados utilizando ANOVA dois fatores (p < 0,05). Resultados: Não foi observado diferença estatística na resistência de união nos 3 diferentes protocolos de EDTA a 17%. No entanto, o uso de ICM aumentou significativamente a resistência de adesão. Conclusão: a medicação intracanal à base de hidróxido de cálcio melhorou a resistência de união do AH Plus às paredes dentinárias, independentemente do protocolo de EDTA. (AU)
ABSTRACT
Objective: The aim of this study is to evaluate the adhesion of an endodontic sealer (AHPlus) in root canals after the use of different protocols of 17% EDTA and the use of intracanal medication (ICM) based on calcium hydroxide in aqueous vehicle. Material and Methods: For this, 72 single-rooted human teeth were instrumented up to #50 and divided into six groups (n = 12). Group 1: EDTA for 3 min; Group 2: 3 mL of EDTA + 3 min of EDTA; Group 3: 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation; Group 4: EDTA for 3 min + ICM; Group 5: 3 mL of EDTA + 3 min of EDTA + ICM; Group 6: 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation + ICM. The root canals were filled with endodontic sealer after each protocol and after 7 days they were prepared to the push-out test. The data were analyzed using twoway ANOVA (p< 0.05). Results: It was observed no statistically difference in bond strength in the 3 different 17% EDTA protocols. However, the use of ICM increased significantly the resistance adhesion. Conclusion: Intracanal medication based on calcium hydroxide improved the bond strength of AHPlus to dentin walls, regardless of the EDTA protocol. (AU)
Texto completo:
Disponível
Coleções:
Bases de dados internacionais
Base de dados:
BBO - Odontologia
/
LILACS
Assunto principal:
Hidróxido de Cálcio
/
Ácido Edético
/
Dentina
Limite:
Humanos
Idioma:
Inglês
Revista:
Braz. dent. sci
Assunto da revista:
Odontologia
/
Sa£de Bucal
Ano de publicação:
2017
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
São Paulo State University/BR