Stress distribution and failure load of multilayer and monolayer glass ceramic / Distribuição de tensão e carga para fratura de cerâmica vítrea em multicamada e em monocamada

ABSTRACT

This short report evaluated the differences in stress concentration and the load to fracture of multilayered and monolayer glass ceramic discs. Using a simulated static structural analysis, the 3D model of the samples received a load of 150 N and results in maximum principal stress were obtained. For the in vitro analysis, the samples (ø 12 mm) were submitted to a compressive test (100 kgf, 1 mm/min). The data was analyzed using one-way analysis of variance and Tukey test (α = 5%). The monolayer group showed a lower stress peak (129.24 MPa) and higher load to fracture (118.38 N) than the multilayered group with 211.04MPa and 48.34N, respectively. All samples presented catastrophic failure with its origin on the tensile surface. Therefore, the monolayer ceramic group showed superior mechanical behavior than the multilayered group. (AU)

RESUMO

Este relato avaliou a diferença na concentração de tensão e a carga para fratura de discos de cerâmica vítrea em multicamada e monocamada. Usando uma análise estática estrutural simulada, o modelo 3D das amostras recebeu uma carga de 150 N e resultados de tensão máxima principal foram obtidos. Para a análise in vitro, as amostras (ø 12 mm) foram submetidas a um teste de compressão (100 kgf, 1 mm / min). Os dados foram analisados por análise de variância e teste de Tukey (α = 5%). O grupo em monocamada mostrou um menor pico de tensão (129,24 MPa) e maior carga para fratura (118,38N) do que o grupo multicamada com 211,04 MPa e 48,34 N, respectivamente. Todas as amostras apresentaram falha catastrófica com sua origem na superfície de tração. Portanto, o grupo em monocamada apresentou comportamento mecânico superior ao grupo multicamadas. (AU)