Comparación del sellado apical de tres cementos endodónticos a base de resina (Estudio in vitro) / Comparison of the sealing apical of three resin-based root canal sealer (Study in vitro)
Endodoncia (Madr.)
; 26(4): 207-211, oct.-dic. 2008. tab, ilus
Artigo
em Espanhol
| IBECS
| ID: ibc-94620
Biblioteca responsável:
ES1.1
Localização: BNCS
RESUMEN
Objetivo. El propósito de este trabajo fue evaluar la capacidad de sellado apical de tres cementos endodóncicos a base de resina, Adseal®, EndoREZ ® y AH Plus®. Material y Métodos. Se utilizaron 68 raíces de dientes uniradiculares humanos extraídos, que se dividieron en 3 grupos experimentales de 20 cada uno y 8 para el control positivo y negativo. Se realizó tratamiento de conductos estandarizando la muestra 1 milímetro antes del ápice a un calibre 20 y obturando con la técnica de condensación latera y el cemento endodóntico correspondiente, posteriormente se incluyeron en una base de silicón, dejando libres 3 milímetros del tercio apical, que permanecieron en contacto con tinta china por 2 semanas a 37ºC. Resultados:
Los resultados se obtuvieron por medio de observación directa, una vez que los dientes fueron diafanizados y la prueba estadística de Chi cuadrado (p<0,05) demostró una capacidad de sellado eficiente con el cemento Adseal® y AH Plus® presentaron un sellado apical similar en comparación con el cemento EndoREZ®.Conclusiones:
Los cementos Adseal® y AH Plus® presentaron un sellado apical similar en comparación con el cemento EndoREZ® con diferencia estadísticamente significativa (AU)ABSTRACT
Objective:
The purpose in this work was to evaluate the ability of apical sealed in three endodontic cements Adseal®, EndoRez® and AH Plus® with resin base. Material andMethods:
68 extracted single root canal dentals organs humans were used, then divided in three experimental groups with 20 each one and 8 for the positive and negative control. Treatment in canals was performed standardizing the sample 1 millimeter before the apex at 20 gauge and obturing with lateral condensation technique and the endodontic cement corresponding, then were immersed in a silicon base, letting the apical third free for three millimeters, than remain in contact with Indian ink for 2 week at 37ºC.Results:
The results were obtained by direct observation, once that the teeth were transparented and the square Chi statistical test (p<0,05) showed and efficient sealed capacity with ADSEAL® cement, that was similar with AH Plus® and inefficient in EndoREZ® cement. Conclusions; The apical seal of both ADSEAL and AH Plus were similar compared with EndoRez sealer (AU)
Buscar no Google
Coleções:
Bases de dados nacionais
/
Espanha
Base de dados:
IBECS
Assunto principal:
Materiais Restauradores do Canal Radicular
/
Obturação do Canal Radicular
Limite:
Humanos
Idioma:
Espanhol
Revista:
Endodoncia (Madr.)
Ano de publicação:
2008
Tipo de documento:
Artigo
Instituição/País de afiliação:
Universidad del Ejército y Fuerza Aéreas México, D. F/México
/
Universidad del Ejército y Fuerzas Aéreas México D.F/México
/
Universidad del Ejército y Fuerza Aéreas México, D. F/México
/
Universidad del Ejército y Fuerzas Aéreas México D.F/México