Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment
Braz. oral res. (Online)
; 29(1): 1-2, 2015. tab, ilus
Article
em En
| LILACS
| ID: lil-777224
Biblioteca responsável:
BR1.1
ABSTRACT
This study evaluated the influence of an alternative surface treatment on the microshear bond strength (μsbs) of zirconia-based ceramic. Thirty-five zirconia disks were assigned to five groups according to the following treatments Control (CO), glass and silane were not applied to the zirconia surface; G1, air blasted with 100μm glass beads + glaze + silane; G2, a gel containing 15% (by weight) glass beads applied to the ceramic surface + glaze + silane; G3, a gel containing 25% (by weight) glass beads applied to the ceramic surface + glaze + silane; and G4, a gel containing 50% (by weight) glass beads applied to the ceramic surface + glaze + silane. The specimens were built up using RelyX ARC®, according to the manufacturer’s recommendations, and inserted in an elastomeric mold with an inner diameter of 0.8 mm. The μsbs test was performed using a testing machine at a crosshead speed of 0.5 mm/min. ANOVA and Tukey’s test (p < 0.05) were applied to the bond strength values (in MPa). CO (15.6 ± 4.1) showed the lowest μsbs value. There were no statistical differences between the G1 (24.9 ± 7.4), G2 (24.9 ± 2.3), G3 (35.0 ± 10.3) and G4 (35.3 ± 6.0) experimental groups. Those groups submitted to surface treatments with higher concentrations of glass showed a lower frequency of adhesive failures. In conclusion, the glass application improved the interaction between the ceramic and the luting cement.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
LILACS
Assunto principal:
Zircônio
/
Cerâmica
/
Cimentação
/
Cimentos Dentários
/
Vidro
Tipo de estudo:
Evaluation_studies
/
Guideline
Idioma:
En
Revista:
Braz. oral res. (Online)
Assunto da revista:
ODONTOLOGIA
Ano de publicação:
2015
Tipo de documento:
Article
País de afiliação:
Brasil