Synthesis and electrochemical properties of stannous oxide clinopinacoid as anode material for lithium ion batteries.

ABSTRACT

Tin monoxide is a significant functional semiconductor material which employed to a wide area of applications especially optical and energy storage devices. Presently, template free hydrothermal technique has been employing to synthesize stannous oxide (SnO) clinopinacoid type controlled morphology using SnCl2 x 2H2O, NH3, and H2O as raw materials. The crystalline phase, morphology, particle size and component were characterized by X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS) and field-emission scanning electron microscopy (FESEM). FESEM results exhibited the large scale homogeneous growth of clinopinacoid architecture with the obvious size of 5 - 7 micrometers. The XRD results showed that the average crystallite size of the tetragonal phase romarchite SnO was about 29 nm calculated from the FWHM of X-ray diffraction pattern. The dominant Raman active modes A(1g) = 205 cm(-1), B(1g) = 105-107 cm(-1) and about 6 cm(-1) redshift were observed by the Raman spectroscopy, which further confirmed the existence of the nano tetragonal phase SnO. The electrochemical performance of as-synthesized SnO clinopinacoid structure as the anode material for lithium ion batteries was investigated. It was observed that the first discharge capacity of the two samples could reach a very high value of 1502 mA h g(-1) and 1422 mA h g(-1) respectively. The effect of nitrogen concentration on morphology as well as cyclic performance of Li-Ion-batteries was also discussed.