Microshear bond strength of self-adhesive composite to ceramic after mechanical, chemical and laser surface treatments.

OBJECTIVES: This study aimed to assess the microshear bond strength of a repairing self-adhesive flowable composite to ceramic after mechanical, chemical and laser treatment of the ceramic surface. MATERIALS AND METHODS: Forty zirconia and forty feldspathic ceramic blocks measuring 8 x 8 x 2 mm were fabricated. Feldspathic blocks were divided into four groups of control (1), laser (2780 nm) (2), sandblasting + hydrofluoric (HF) acid + silane (3) and laser (2780 nm) + HF acid + silane (4). Zirconia blocks were also divided into four groups of control (1), laser (2780 nm) (2), sandblasting + Z-Prime Plus (3) and laser (2780 nm) + Z-Prime Plus (4). Vertise Flow composite was bonded to treated ceramic surfaces as a repairing material, then the samples were subjected to 1000 thermal cycles. Repair bond strength was measured by Instron machine and data were analyzed using one-way ANOVA and post hoc test (P < 0.05). RESULTS: Maximum and minimum bond strength values were observed in zirconia-control (22.57 ± 4.76 MPa) and feldspathic-control (8.65 ± 6.41 MPa) groups, respectively. There was no significant differences between subgroups within the zirconia or feldspathic groups (P > 0.05), however the bond strength of zirconia subgroups was significantly higher than that of feldspathic subgroups. CONCLUSION: Vertise Flow provides relatively good bond strength to ceramic even with no surface treatment.