Gas-induced selective re-orientation of Au-Cu nanoparticles on TiO2 (110).

ABSTRACT

Au-Cu bimetallic nanoparticles (NPs) grown on TiO2(110) have been followed in situ using grazing incidence X-ray diffraction and X-ray photoemission spectroscopy from their synthesis to their exposure to a CO/O2 mixture at low pressure (P < 10-5 mbar) and at different temperatures (300 K-470 K). As-prepared samples are composed of two types of alloyed NPs randomly oriented and epitaxial NPs. Whereas the introduction of CO has no effect on the structure of the NPs, an O2 introduction triggers a Cu surface segregation phenomenon resulting in the formation of a Cu2O shell reducible by annealing the sample over 430 K. A selective re-orientation of the nanoparticles, induced by the exposure to a CO/O2 mixture, is observed where the randomly oriented NPs take advantage of the mobility induced by the Cu segregation to re-orient their Au-rich core relatively to the TiO2(110) substrate following specifically the orientation ((111)NPs//(110)TiO2) when others epitaxial relationships were observed on the as-prepared sample.