Adhesive strength of fiberglass posts treated with thio-urethane-based experimental silanes.
Eur Oral Res
; 55(2): 60-66, 2021 May 04.
Article
em En
| MEDLINE
| ID: mdl-34250471
ABSTRACT
PURPOSE:
The aim of this study was to evaluate the adhesive bond strength of fiberglass posts treated with experimental silanes based on thio-urethane and submitted to thermo and mechanical cycles. MATERIALS ANDMETHODS:
Bovine roots were divided into six groups RX-RU2 (RelyX CP + RelyX U200); PETMP-HDDI-RU2 (PETMP-HDDI + RelyX U200); PETMP-BDI-RU2 (PETMP-BDI + RelyX U200); RX-RU (RelyX CP + RelyX Ultimate); PETMP-HDDI-RU (PETMP-HDDI + RelyX Ultimate); PETMP-BDI-RU (PETMP-BDI + RelyX Ultimate). One slice from each root third (n=10) was submitted to the push-out test and the values evaluated with R Program statistical analysis, while the failure pattern assessed in percentage.RESULTS:
Among root thirds, RX-RU2 promoted greater strength at the cervical and apical thirds; PETMP-HDDI-RU2 showed highest values at the three thirds; and PETMP-BDI-RU2 was strongest at the apical third. RX-RU presented higher strength at the apical third, and PETMP-HDDI-RU and PETMP-BDI-RU had similar values at the three thirds. In each root third, PETMP-HDDI-RU2 showed similar strength at all thirds, and similar strength at the apical third was observed for other associations. Mixed and adhesive failures predominated.CONCLUSION:
Experimental silanes promoted different bond strength values in the adhesion of fiberglass posts to the root thirds, with better results for PETMP-HDDI silane. The root region did not influence the failure pattern and most slices showed mixed (MCDP) or adhesive (ADP) failure.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Eur Oral Res
Ano de publicação:
2021
Tipo de documento:
Article
País de afiliação:
Brasil