Preparation of hydrothermally solidified materials from waste cathode ray tube panel glass for construction applications.
Environ Sci Pollut Res Int
; 29(38): 57516-57522, 2022 Aug.
Article
em En
| MEDLINE
| ID: mdl-35355179
ABSTRACT
Solidification of cathode ray tube (CRT) panel glass was carried out using a hydrothermal processing method. In this way, the glass powder was first compacted in a mold at 20 MPa, and then hydrothermally cured in an autoclave under saturated steam pressure at 200 â for 6 h. The CRT panel glass was then hydrothermally solidified by the formation of tobermorite (Ca5Si6O16(OH)2·4H2O), which was encouraged by the addition of slaked lime (Ca(OH)2). The strength of solidified specimen heavily depended on the amount of tobermorite formed, with higher concentrations of tobermorite producing commensurately greater mechanical strength. With the addition of Ca(OH)2 at 20-30% by mass, the specimen achieved a bending strength of approximately 16 MPa, which was sufficiently great for using as a construction material. As such, there is cause to believe that the hydrothermal processing method used here may have great potential for resource utilization of CRT panel glass, and the performance of the product is suitable for use as building materials.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Tubo de Raio Catódico
Idioma:
En
Revista:
Environ Sci Pollut Res Int
Assunto da revista:
SAUDE AMBIENTAL
/
TOXICOLOGIA
Ano de publicação:
2022
Tipo de documento:
Article
País de afiliação:
China