Three-dimensional pore characterization of poly(lactic)acid/bamboo biodegradable panels.

ABSTRACT

In the context of novel environmental and energy regulations in construction (RE2020), biocomposites derived from bamboo fibers, bamboo powders, and biodegradable poly(lactic)acid polymer, all of which are renewable resources, have been investigated to meet the criteria of the novel regulations. In this work, the biocomposites were manufactured by twin-screw internal mixing at 170 °C for 5 min with a rotation speed of 60 rpm. The composites sheets were then shaped on a hydraulic press at 185 °C. Pore characterization including pore volume fraction, 3D-pore structure and morphology, and pore distribution of these materials were investigated using X-ray tomography combined with image processing (Avizo). The results show that when the bamboo fibers content is increased, an augmentation in the pore volume fraction and the number of large-volume pores could be observed. In turn, the bamboo powder-containing sheet had a significant increase in pore volume fraction, while a higher quantity of smaller pores, with uniform size, could be observed. The water absorption capacity of these composite increases with the increase of the amount of pore distribution, pore connection, and pore volume fraction. In addition, the orientation of the fibers in 3D observation, flexural mechanical properties, and thermal stability of the biocomposites are also reported in this study.