Deposition of NiAl/Al3Ni2(CrB2) Coatings from Ni, Al and CrB2 Powders Using Mechanical Synthesis in Planetary Ball Mill.
Materials (Basel)
; 17(2)2024 Jan 19.
Article
em En
| MEDLINE
| ID: mdl-38276431
ABSTRACT
Interest in composite thick coatings with an intermetallic matrix stimulates the development of new deposition techniques like the co-milling of pre-alloyed NiAl powder with platelet-shaped substrates. Obtained coatings were up to several micrometers thick as cold-welding of intermetallic particles was effective only at the start of this process, while later, chipping prevailed over added material. The present experiment covered the co-milling in the planetary ball mill of Ni and Al elemental powders (11 molar ratio) with AISI 304 steel platelets for 32 h at 300 rpm. Next, this process was repeated with an admixture of 15 wt.% of CrB2 powder. In both cases, their milling succeeded in producing up to a 200 µm coating after 4 h. The use of light, scanning and transmission electron microscopy (LM/SEM/TEM) helped to establish that the coatings had gradient microstructures with more refined crystallites of NiAl, Al3Ni2 and CrB2 closer to the surface. With the addition of a ceramic phase, the coatings presented higher hardness and lower friction during dry wear tests both at RT and at 500 °C.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Materials (Basel)
Ano de publicação:
2024
Tipo de documento:
Article
País de afiliação:
Polônia
País de publicação:
CH
/
SUIZA
/
SUÍÇA
/
SWITZERLAND