Effect of hydroxyapatite nanoparticles coating of titanium surface on biofilm adhesion: An in vitro study.
Arch Oral Biol
; 164: 105986, 2024 Aug.
Article
em En
| MEDLINE
| ID: mdl-38723421
ABSTRACT
AIM:
To evaluate the adhesion of mono and duospecies biofilm on a commercially available dental implant surface coated with hydroxyapatite nanoparticles (nanoHA). MATERIAL ANDMETHODS:
Titanium discs were divided into two groups double acid-etched (AE) and AE coated with nanoHA (NanoHA). Surface characteristics evaluated were morphology, topography, and wettability. Mono and duospecies biofilms of Streptococcus sanguinis (S. sanguinis) and Candida albicans (C. albicans) were formed. Discs were exposed to fetal bovine serum (FBS) to form the pellicle. Biofilm was growth in RPMI1640 medium with 10% FBS and 10% BHI medium for 6 h. Microbial viability was evaluated using colony-forming unit and metabolic activity by a colorimetric assay of the tetrazolium salt XTT. Biofilm architecture and organization were evaluated by confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM).RESULTS:
AE surface had more pores, while NanoHA had even nanoHA crystals distribution. Roughness was similar (AE 0.59 ± 0.07 µm, NanoHA 0.69 ± 0.18 µm), but wettability was different (AE Θw= 81.79 ± 8.55°, NanoHA Θw= 53.26 ± 11.86°; P = 0.01). NanoHA had lower S. sanguinis viability in monospecies biofilm (P = 0.007). Metabolic activity was similar among all biofilms. In SEM both surfaces on C. albicans biofilm show a similar distribution of hyphae in mono and duospecies biofilms. AE surface has more S. sanguinis than the NanoHA surface in the duospecies biofilm. CLSM showed a large proportion of live cells in all groups.CONCLUSIONS:
The nanoHA surface reduced the adhesion of S. sanguinis biofilm but did not alter the adhesion of C. albicans or the biofilm formed by both species.Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Streptococcus sanguis
/
Propriedades de Superfície
/
Titânio
/
Candida albicans
/
Microscopia Eletrônica de Varredura
/
Implantes Dentários
/
Durapatita
/
Microscopia Confocal
/
Biofilmes
/
Nanopartículas
Idioma:
En
Revista:
Arch Oral Biol
Ano de publicação:
2024
Tipo de documento:
Article
País de afiliação:
Brasil