Extraction and characterization of Bougainvillea glabra fibers: A study on chemical, physical, mechanical and morphological properties.

ABSTRACT

Bougainvillea glabra fibers (BGFs) present a promising avenue for sustainable material development owing to their abundance and favorable properties. This study entails a thorough investigation into the composition, physical characteristics, mechanical behavior, structural properties, thermal stability, and hydrothermal absorption behavior of BGFs. Chemical analysis reveals the predominant presence of cellulose (68.92 %), accompanied by notable proportions of hemicellulose (12.64 %), lignin (9.56 %), wax (3.72 %), moisture (11.78 %), and ash (1.75 %). Physical measurements ascertain a mean fiber diameter of approximately 232.63 ± 8.59 µm, while tensile testing demonstrates exceptional strength, with stress values ranging from 120 ± 18.26 MPa to a maximum of 770 ± 23.19 MPa at varying strains. X-ray diffraction (XRD) elucidates a crystalline index (CI) of 68.17 % and a crystallite size (CS) of 9.42 nm, indicative of a well-defined crystalline structure within the fibers. Fourier-transform infrared spectroscopy (FTIR) confirms the presence of characteristic functional groups associated with cellulose, hemicellulose, wax, and water content. Thermogravimetric analysis (TGA) delineates distinct thermal degradation stages, with onset temperatures ranging from 102.76 °C for water loss to 567.55 °C for ash formation. Furthermore, hydrothermal absorption behavior exhibits temperature and time-dependent trends, with absorption percentages ranging from 15.26 % to 32.19 % at temperatures between 30 °C and 108 °C and varying exposure durations. These comprehensive findings provide essential insights into the properties and potential applications of BGFs in diverse fields such as bio-composites, textiles, and environmentally friendly packaging solutions.