Investigation of the Photochromism of WO3, TiO2, and Composite WO3-TiO2 Nanoparticles.

We report the synthesis of WO3, TiO2, and TiO2-WO3 nanoparticles by a polyol route, with the objective of studying the influence of the preparation method on their photochromic properties. By combining transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and diffuse reflectance experiments, we show that low W6+ concentrations and high ripening temperatures allow the preparation of WO3 nanoparticles with high photochromic efficiency. WO3-TiO2 nanocomposites (NCs) prepared by the introduction of a TiO2+ solution in a WO3 nanoparticle suspension exhibit a strong coloring photochromism, which is attributed to the TiO2 coating of the WO3 nanoparticles as it involves the formation of W-O-Ti oxo-bonds in place of W5+-νO defects. Especially, after an oxidative treatment in order to obtain an initial pale-yellow material, such WO3-TiO2 NCs exhibit a fully reversible photochromism with a large contrast between the colored and bleached state. They could therefore be incorporated in hybrid smart films for solar control on building window glasses. On the other hand, while the WO3-TiO2 NCs are functionalized with DPA (n-dodecyl phosphonic acid), the as-prepared nanocomposites exhibit exacerbated coloring contrast but with a nearly nonreversible photochromism (very limited bleaching), which makes them good candidates for the fabrication of smart UV-sensor devices that can indicate the cumulative UV dose which is received.

A tris(triazolate) ligand for a highly active and magnetically recoverable palladium catalyst of selective alcohol oxidation using air at atmospheric pressure.

High efficiency and selectivity, easy magnetic recovery and recycling, and use of air as the oxidant at atmospheric pressure are major objectives for oxidation catalysis in terms of sustainable and green processes. A tris(triazolyl) ligand, so far only used in copper-catalyzed alkyne azide cycloadditions, was found to be extremely efficient in SiO2 /γ-Fe2 O3 -immobilized palladium complexes. It was characterized by inductively coupled plasma (ICP) analysis, transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray photoelectron spectra (XPS) and found to fulfill the combined conditions for the selective oxidation of alcohols to aldehydes and ketones.

Efficient and magnetically recoverable "click" PEGylated γ-Fe2O3-Pd nanoparticle catalysts for Suzuki-Miyaura, Sonogashira, and Heck reactions with positive dendritic effects.

The engineering of novel catalytic nanomaterials that are highly active for crucial carbon-carbon bond formations, easily recoverable many times, and biocompatible is highly desirable in terms of sustainable and green chemistry. To this end, catalysts comprising dendritic "click" ligands that are immobilized on a magnetic nanoparticle (MNP) core, terminated by triethylene glycol (TEG) groups, and incorporate Pd nanoparticles (PdNPs) have been prepared. These nanomaterials are characterized by transmission electron microscopy (TEM), high-resolution TEM, inductively coupled plasma analysis, Fourier transform infrared spectroscopy, X-ray photoelectron spectra and energy-dispersive X-ray spectroscopy. They are shown to be highly active, dispersible, and magnetically recoverable many times in Suzuki, Sonogashira, and Heck reactions. In addition, a series of pharmacologically relevant or natural products were successfully synthesized using these magnetic PdNPs as catalyst. For comparison, related PdNP catalysts deposited on MNPs bearing linear "click" PEGylated ligands are also prepared. Strong positive dendritic effects concerning ligand loading, catalyst loading, catalytic activity, and recyclability are observed, that is, the dendritic catalysts are much more efficient than non-dendritic analogues.

Stabilisation of carbon-supported palladium nanoparticles through the formation of an alloy with gold: application to the Sonogashira reaction.

Oh my Gold! Gold atoms stabilise catalytically active palladium nanoparticles when engaged in an alloy heterogenised on carbon. The increased durability makes the Pd-Au/C catalyst more recyclable than the gold-free Pd/C catalyst for the Sonogashira reaction.

Rapid hydrothermal synthesis of VO2 (B) and its conversion to thermochromic VO2 (M1).

The present study provides a rapid way to obtain VO2 (B) under economical and environmentally friendly conditions. VO2 (B) is one of the well-known polymorphs of vanadium dioxide and is a promising cathode material for aqueous lithium ion batteries. VO2 (B) was successfully synthesized by rapid single-step hydrothermal process using V2O5 and citric acid as precursors. The present study shows that phase-pure VO2 (B) polytype can be easily obtained at 180 °C for 2 h and 220 °C for 1 h, that is, the lowest combination of temperature and duration reported so far. The obtained VO2 (B) is characterized by X-ray powder diffraction, high-resolution scanning electron microscopy, and Fourier transform infrared spectroscopy. In addition, we present an indirect way to obtain VO2 (M1) by annealing VO2 (B) under vacuum for 1 h.

Surface modification of polymers treated by various fluorinating media.

Fluorination processes of polymer surfaces are able to lead to drastic modifications of the surface properties without changing the bulk characteristics of the virgin material. In this paper, two types of polymers, i.e. ultrahigh molecular weight polyethylene (UHMWPE) and high density polyethylene (HDPE), are considered. The surface of these materials have been modified using two different fluorination routes, both carried out at room temperature: the direct fluorination with 10% F2 + 90% He gaseous mixtures and the radio-frequency plasma-enhanced fluorination (PEF) using either O2/CF4 mixtures or c-C4F8. The effect of these processes on the surface of the polymer samples are compared using mostly XPS results. The different components of the C1s spectra are assigned in term of CFx bonding, giving valuable information on the surface fluorination rate.

Controlling differentiation of stem cells via bioactive disordered cues.

Ideal bone tissue engineering is to induce bone regeneration through the synergistic integration of biomaterial scaffolds, bone progenitor cells, and bone-forming factors. Biomimetic scaffolds imitate the native extracellular matrix (ECM) and are often utilized in vitro as analogues of the natural ECM to facilitate investigations of cell-ECM interactions and processes. In vivo, the cellular microenvironment has a crucial impact on regulating cell behavior and functions. A PET surface was activated and then functionalized with mimetic peptides to promote human mesenchymal stem cell (hMSC) adhesion and differentiation into an osteogenic lineage. Spray technology was used to randomly micropattern peptides (RGD and BMP-2 mimetic peptides) on the PET surface. The distribution of the peptides grafted on the surface, the roughness of the surfaces and the chemistry of the surfaces in each step of the treatment were ascertained by atomic force microscopy, fluorescence microscopy, time-of-flight secondary ion mass spectrometry, Toluidine Blue O assay, and X-ray photoelectron spectroscopy. Subsequently, cell lineage differentiation was evaluated by quantifying the expression of immunofluorescence markers: osteoblast markers (Runx-2, OPN) and osteocyte markers (E11, DMP1, and SOST). In this article, we hypothesized that a unique combination of bioactive micro/nanopatterns on a polymer surface improves the rate of morphology change and enhances hMSC differentiation. In DMEM, after 14 days, disordered micropatterned surfaces with RGD and BMP-2 led to a higher osteoblast marker expression than surfaces with a homogeneous dual peptide conjugation. Finally, hMSCs cultured in osteogenic differentiation medium (ODM) showed accelerated cell differentiation. In ODM, our results highlighted the expression of osteocyte markers when hMSCs were seeded on PET surfaces with random micropatterns.

Sequential chiral induction between organic and inorganic supramolecular helical assemblies for the in situ formation of chiral carbon dots.

Self-organised helical bilayers of dicationic gemini surfactants confined in helical silica nanospace were transformed in situ to carbon dots (CDots) via pyrolysis. These water-dispersible CDots exhibit electronic absorption spanning the UV and visible range and possess symmetrical circular dichroism (CD) signals, the sign of which depends on the handedness of the helices.

Peptide immobilization on polyethylene terephthalate surfaces to study specific endothelial cell adhesion, spreading and migration.

To control specific endothelial cell (EC) functions, cell adhesive RGDS, EC specific REDV and YIGSR peptides, and angiogenic SVVYGLR sequences were covalently immobilized onto polyethylene terephthalate (PET) surfaces for the purpose of cell culture. X-ray photoelectron spectroscopy, atomic force microscopy, fluorescence microscopy and contact angle measurement were employed for characterization of surface modifications. The peptide density on PET surfaces was evaluated by fluorescence microscopy. The surfaces immobilized with peptides were exposed to human umbilical vein endothelial cells to study their specific effects onto EC functions. The results showed that the surface functionalized by these peptides enhanced the EC adhesion, spreading and migration as compared with native PET surfaces. Specifically, the RGDS peptides induced more cell adhesion than other peptides. The YIGSR and SVVYGLR sequences induced more cell spreading and cell migration, represented by intense focal adhesion at the leading edges of cell spreading and migration. The bi-functionalization of RGDS and SVVYGLR peptides (MIX) combined the advantages of both peptides and induced significant EC adhesion, spreading and migration. Our study indicates that the surface functionalization by peptides specific for ECs, especially the combination of RGDS with SVVYGLR or YIGSR peptides, has potential applications in promoting endothelialization of vascular prostheses and for construction of vascularized tissues in tissue engineering.

Topotactic fluorination of intermetallics as an efficient route towards quantum materials.

Intermetallics represent an important family of compounds, in which insertion of light elements (H, B, C, N) has been widely explored for decades to synthesize novel phases and promote functional materials such as permanent magnets or magnetocalorics. Fluorine insertion, however, has remained elusive so far since the strong reactivity of this atypical element, the most electronegative one, tends to produce the chemical decomposition of these systems. Here, we introduce a topochemical method to intercalate fluorine atoms into intermetallics, using perfluorocarbon reactant with covalent C-F bonds. We demonstrate the potential of this approach with the synthesis of non-stoichiometric mixed anion (Si-F) LaFeSiFx single-crystals, which are further shown to host FeSi-based superconductivity. Fluorine topochemistry on intermetallics is thus proven to be an effective route to provide functional materials where the coexistence of ionic and metallo-covalent blocks, and their interactions through inductive effects, is at the root of their functional properties.

Dual lithium insertion and conversion mechanisms in a titanium-based mixed-anion nanocomposite.

The electrochemical reaction of lithium with a vacancy-containing titanium hydroxyfluoride was studied. On the basis of pair distribution function analysis, NMR, and X-ray photoelectron spectroscopy, we propose that the material undergoes partitioning upon initial discharge to form a nanostructured composite containing crystalline Li(x)TiO(2), surrounded by a Ti(0) and LiF layer. The Ti(0) is reoxidized upon reversible charging to an amorphous TiF(3) phase via a conversion reaction. The crystalline Li(x)TiO(2) is involved in an insertion reaction. The resulting composite electrode, Ti(0)-LiF/Li(x)TiO(2) ⇔ TiF(3)/ Li(y)TiO(2), allows reaction of more than one Li per Ti, providing a route to higher capacities while improving the energy efficiency compared to pure conversion chemistries.

Design of Metal@Titanium Oxide Nano-heterodimers by Laser-Driven Photodeposition: Growth Mechanism and Modeling.

In order to circumvent the usual nucleation of randomly distributed tiny metallic dots photodeposited on TiO2 nanoparticles (NPs) induced by conventional UV lamps, we propose to synthesize well-controlled nanoheterodimers (NHDs) using lasers focused inside microfluidic reactors to strongly photoactivate redox reactions of active ions flowing along with nanoparticles in water solution. Since the flux of photons issued from a focused laser may be orders of magnitude higher than that reachable with classical lamps, the production of electron-hole pairs is tremendously increased, ensuring a large availability of carriers for the deposition and favoring the growth of a single metallic dot as compared to secondary nucleation events. We show that the growth of single silver or gold nanodots can be controlled by varying the beam intensity, the concentration of the metallic salt, and the flow velocity inside the microreactor. The confrontation to a build-in model of the metallic nanodot light-induced growth onto the surface of TiO2 NPs shows the emergence of a predictable "master behavior" on which individual growths obtained from various tested conditions do collapse. We also characterized the associated quantum yield. Eventually, we successfully confronted our model to growth data from the literature in the case of silver on TiO2 and gold on II-VI semiconducting NPs triggered by UV lamps. It shows that for the photosynthesis of NHDs the efficiency of the electron-hole pair production rate matters much more than the number of pairs produced and that the use of laser light can provide a photodeposition-based synthesis at the nanoscale.

Series of M(I)[Co(bpy)3][Mo(CN)8] x nH2O (M(I) = Li (1), K (2), Rb (3), Cs (4); n = 7-8) exhibiting reversible diamagnetic to paramagnetic transition coupled with dehydration-rehydration process.

In this paper we report the synthesis and the structural and magnetic properties of the series of ionic compounds with general formula: M(I)[Co(bpy)(3)][Mo(CN)(8)] x nH(2)O (M(I) = Li, n = 8 (1), M(I) = K, n = 8 (2), M(I) = Rb, n = 8 (3), M(I) = Cs, n = 7.5 (4)). Solids 1-4 are characterized by the optical outer-sphere metal-to-metal charge transfer (MMCT) transition from Mo(IV) center to Co(III) center in the visible region and the Co(III)Mo(IV) <==> Co(II)Mo(V) spin equilibrium strongly dominated by the Co(III)Mo(IV) form. We show a gentle thermal treatment of diamagnetic compounds 1-4 leading to the dehydrated forms 1a-4a, which reveal a significant increase of paramagnetic contribution (from 0.5 to 2% to 30-40%). The rehydration allows to recover the diamagnetic phases 1b-4b of compositions and properties similar to those of 1-4. The irradiation of the dehydrated form 2a within the MMCT band in the Superconducting Quantum Interference Device (SQUID) cavity at T = 10 K causes further increase of the Co(II)Mo(V) contribution giving the metastable phase annealed back to the 2a phase after heating above T = 290 K. The IR, electron paramagnetic resonance (EPR), and X-ray photoelectron spectroscopy (XPS) spectroscopic data along with the magnetic data are interpreted in terms of strong modification of the Co(III)Mo(IV) <==> Co(II)Mo(V) equilibrium occurring in these systems.

Photochromic Behavior of ZnO/MoO3 Interfaces.

ZnO/MoO3 powder mixture exhibits a huge photochromic effect in comparison with the corresponding single oxides. The coloring efficiency of such combined material after UV-light irradiation was studied in terms of intensity, kinetics, and ZnO/MoO3 powder ratio. Additionally, the incidence of the pretreatment step of the ZnO and MoO3 powders under different atmospheres (air, Ar or Ar/H2 flow) was analyzed. The huge photochromic effect discovered herein was interpreted as the creation of "self-closed Schottky barrier" at the solid/solid interfaces between the two oxides, associated with the full redox reaction which can be pictured by the equation ZnO1-ε + MoO3 → ZnO + MoO3-ε. Remarkable optical contrast between virgin and color states as well as self-bleaching in dark allowing the reversibility of the photochromism is emphasized. From this first discovery, deeper characterization of the self-bleaching process shows that the photochromic mechanism is complex with a bleaching efficiency (possibility to come back to the virgin material optical properties without any deterioration) and a bleaching kinetics, which are both dependent on the coloring irradiation time. This demonstrates that the oxygen exchange through the Schottky interface proceeds in at least two convoluted steps: an anionic surface exchange allowing a reversibility of the redox reaction followed by bulk diffusion of the exchanged anions which are then definitively trapped. An emergent "negative photochromism effect" (i.e., photochromism associated with a self-bleaching instead of a darkening under irradiation) is observed after a long irradiation time.

Influence of Quenching on the Opto-Electronic Properties of F:SnO2 Layers.

For many opto-electronic applications, F:SnO2 materials must benefit from high transparency, high conductivity, and high mechanical strength even after quenching. The purpose of this study was to investigate the influence of quenching on the opto-electronic properties of the F:SnO2 layers synthesized at high temperature on Si x C y O-coated soda-lime glass by atmospheric chemical vapor deposition. The morphology, structure, and composition of the layers were studied before and after quenching in air- and oxygen-rich atmospheres at 670 °C. The free carrier concentration was reduced by oxygen vacancy (VO) passivation, as well as by F and Na diffusion, with all effects scaling up with quenching time in air. The transmittance also decreased with quenching time as Na impurities acted as absorption and electron recombination centers. In an oxygen-rich atmosphere, the VO passivation was even more emphasized, with however a moderate contribution to conductivity loss. The F:SnO2 layer microstructure and composition were rather fringed through high-temperature deposition. The almost invariable free carrier concentration and transmittance of the F:SnO2 samples quenched in O2 versus air were related to a moderation in Na diffusion. For long quenching times (>20 min) in air, Na and F diffusion prevailed explaining the conductivity drop.

Synthesis of polyaniline nano-objects using poly(vinyl alcohol)-, poly(ethylene oxide)-, and poly[(N-vinyl pyrrolidone)-co-(vinyl alcohol)]-based reactive stabilizers.

Well-defined polyaniline (PANI) nano-objects (e.g., spheres, peanuts, rice grains, corals, and fibers) were prepared by aniline dispersion polymerization in aqueous media in the presence of various reactive polymer stabilizers (i.e., poly(ethylene oxide) (PEO), poly(vinyl alcohol) (PVA), and poly[(N-vinyl pyrrolidone)-co-(vinyl alcohol)] (PNVP-co-PVA)). It was found that the shape, size, and conductivity of resulting PANI nanostructures depended on the acidic conditions along with the nature, molecular weight, and functionality of the reactive stabilizer. PANI samples were analyzed by X-ray photoelectron spectroscopy (XPS), dynamic scanning calorimetry (DSC), thermogravimetric analysis (TGA), UV-visible and FTIR spectroscopy, transmission electron microscopy (TEM), atomic force microscopy (AFM), and conductivity measurements. PANI samples show conductivities between 5 x 10(-3) to 5 x 10(-1) S/cm depending upon the experimental conditions. The best conductivities were obtained when aniline was polymerized in a mixture of DMSO and water (2:3) in the presence of PEO- or PNVP-co-PVA-based reactive stabilizers.

Laser induced damage of fused silica polished optics due to a droplet forming organic contaminant.

We report on the effect of organic molecular contamination on single shot laser induced damage density at the wavelength of 351 nm, with a 3 ns pulse length. Specific contamination experiments were made with dioctylphthalate (DOP) in liquid or gaseous phase, on the surface of fused silica polished samples, bare or solgel coated. Systematic laser induced damage was observed only in the case of liquid phase contamination. Different chemical and morphological characterization methods were used to identify and understand the damage process. We demonstrate that the contaminant morphology, rather than its physicochemical nature, can be responsible for the decrease of laser induced damage threshold of optics.

Toward Simplified Electrochromic Devices Using Silver as Counter Electrode Material.

Novel design of electrochromic devices (ECDs) known for their ability to modify optical properties under an applied voltage, based on a minimization of the number of layers is reported. The use of a metallic electrode, playing the role of both the conductive layer and the counter electrode, allows us to simplify the assembly of a commonly five-layer battery-type device to four-layer ECD. Further minimization of the number of layers is achieved using a conductive and electrochromic material. The novelty of the device configuration is illustrated using poly(3,4-ethylenedioxythiophene) (PEDOT)-based materials as EC layer, lithium-based ionic liquid as electrolyte, and Ag as counter electrode. Such a four- or three-layer ECD deposited on paper substrate switches from light to deep blue in a narrow 0.7 V voltage window. Preliminary investigations of the mechanism indicate traces of Ag on the PEDOT layer upon cycling. Finally, the printed ECD is successfully activated using a mobile phone.

The effect of cyclo-DfKRG peptide immobilization on titanium on the adhesion and differentiation of human osteoprogenitor cells.

This study takes place in the field of development of a bioactive surface of titanium alloys. In this paper, titanium was functionalized with cyclo-DfKRG peptide by coating or grafting using different anchors (thiol or phosphonate) as spacers between the surface and the peptide. Cell adhesion, and differentiation of human osteoprogenitor (HOP) cells arising from human bone marrow were investigated. Our results seem to demonstrate that cyclo-DfKRG peptide coating with a phosphonate anchor and grafting procedure contributes to higher cell adhesion and a strong ALP and Cbfa1 mRNA expression, after 10 days of cell seeding. At the contrary, this peptide coated with a thiol anchor stimulates differentiation of HOP within 3 days of culture.

Core-level photoemission spectra of Mo0.3Cu0.7Sr2ErCu2Oy, a superconducting perovskite derivative. Unconventional structure-property relationships.

Detailed studies of the electronic states for Mo(0.3)Cu(0.7)Sr(2)ErCu(2)Oy samples with different oxygen contents are presented here. The influence of oxygenation on the electronic states for the Mo(0.3)Cu(0.7)Sr(2)ErCu(2)Oy system from the semiconducting to the superconducting state has been investigated by means of X-ray photoelectron spectroscopy (XPS). The XPS studies show that Mo is in a mixed Mo(V) and Mo(VI) oxidation state and Mo(V) is predominant over the Mo(VI) in the as-prepared (AP) sample. Yet annealing under an oxygen atmosphere enhances the Mo(VI) state. At the same time, a reduction in the copper species is observed. In the Cu 2p spectra, a larger energy separation between the satellite and main peaks (E(S)-E(M)) and a lower intensity ratio (I(S)/I(M)) are found to correlate with higher values of the superconducting transition temperature (T(C)). Analysis of these spectra within the Configuration Interaction (CI) model suggests that higher values of TC are related to lower values of the O 2p-Cu 3d charge transfer energy. The change in the Sr 3d and O 1s core level spectra correlates with the oxygen insertion in the (Mo/Cu)O(1+δ) chain site, after oxygenation. The hole concentration (Ph) in the copper plane has been obtained using the room temperature thermoelectric power (TEP) value; this shows an increasing tendency with increasing T(C), after oxygenation. From these experimental results, one observes that T(C)increases with decreasing charge transfer energy. This is, indeed, opposite to the accepted views and occurs in parallel with the shortening of the apical copper-oxygen distance (Cu(2)-O(2)) and the increasing of the CuO(2) plane buckling angle.