Cytotoxic effects of bioceramic materials on stem cells from human exfoliated deciduous teeth (SHED) / Efeitos citotóxicos de materiais biocerâmicos em células-tronco de dentes decíduos esfoliados humanos (SHED)

Objective: This study aimed to evaluate stem cell from human deciduous teeth (SHED) viability after exposure to different bioceramic materials. Material and Methods: Discs were constructed to obtain the material extracts according to the following groups: G1 - Bio-C Repair, G2 - MTA Repair HP, G3 - TheraCal LC, and G4 ­ Biodentine. Positive and negative control group were respectively maintained with αMEM + 10% FBS and αMEM + 1% FBS. SHED obtained through primary culture were in contact with material extracts for 24, 48, and 72h. MTT assay evaluated cell viability. Groups were plated in triplicate and the cell viability assay were repeated three times. Data were analyzed by two-way ANOVA followed by Tukey test (p<0.05). Results: The treatment and period comparisons showed statistically significant differences (p<0.000). G2 (MTA Repair HP) had greater cell viability values than the other experimental groups and negative control. MTA Repair HP and the control groups exhibited a similar behavior with cell viability values decreasing from 24h to 48h and increasing from 48h to 72h. Bio-C Repair, Biodentine, and Theracal LC did not show statistically significant differences among periods. Conclusions: SHED increased viability values after contact with MTA Repair HP in comparison with other bioceramic materials.(AU)

Objetivo: O objetivo desse estudo foi avaliar a viabilidade de células-tronco de dentes decíduos humanos (SHED) após o contato com diferentes materiais biocerâmicos. Material e Métodos: Foram confeccionados discos para obtenção dos extratos dos materiais de acordo com os seguintes grupos: G1 - Bio-C Repair, G2 - MTA Repair HP, G3 - TheraCal LC e G4 - Biodentine. Grupo de controle positivo e negativo foram mantidos respectivamente com αMEM + 10% FBS e αMEM + 1% FBS. SHED obtidas por cultura primária entraram em contato com os extratos de materiais por 24, 48 e 72h. O ensaio MTT avaliou a viabilidade celular. Os grupos foram semeados em triplicata e o ensaio de viabilidade celular foi repetido três vezes. Os dados foram analisados por ANOVA a dois critérios seguido pelo teste de Tukey (p<0,05). Resultados: As comparações de tratamentos e períodos mostraram diferenças estatisticamente significativas (p<0,000). O G2 (MTA Repair HP) apresentou maiores valores de viabilidade celular que os demais grupos experimentais e controle negativo. O MTA Repair HP e os grupos controle exibiram um comportamento semelhante com os valores de viabilidade celular diminuindo de 24h para 48h e aumentando de 48h para 72h. Bio-C Repair, Biodentine e Theracal LC não apresentaram diferenças estatisticamente significativas entre os períodos. Conclusões: SHED aumentou os valores de viabilidade após o contato com o MTA Repair HP em comparação com outros materiais biocerâmicos (AU)

Efeito de diferentes irrigantes finais na resistência união de um cimento de silicato de cálcio: estudo in vitro / Effect of different final irrigants on the bond strength of a calcium silicate cement : in vitro study

Objetivo: Este estudo teve como objetivo avaliar a resistência de união do cimento Biodentine® à dentina radicular após a utilização de diferentes irrigantes finais. Método: Vinte dentes humanos extraídos tiveram seu terço médio radicular cortado em fatias que foram submersas em hipoclorito de sódio 2,5% e posteriormente divididas aleatoriamente em 4 grupos experimentais (n=15) conforme o irrigante final utilizado (1) água destilada (controle), (2) QMixTM, (3) ácido cítrico 10%, (4) EDTA 17%. Após a imersão na substância teste as amostras foram preenchidas com o cimento Biodentine e imersas em solução salina tamponada com fosfato (PBS) por um período de 7 dias. O teste de push out foi realizado e os valores de resistência de união em Mpa foram obtidos. Os dados foram analisados pelos testes de Kruskal Wallis e Studend- Newman-Keuls. Resultados: Os piores valores de união foram obtidos após a utilização do EDTA enquanto a água destilada, o QMix e o ácido cítrico apresentaram resultados estatisticamente semelhantes entre si. Conclusão: A remoção da smear layer não resultou em melhora nos resultados de união do cimento Biodentine.(AU)

Objective: This study aimed to evaluate the bond strength of Biodentine® cement to root dentin after the use of different final irrigants. Method: Twenty extracted human teeth had their middle root third cut into slices that were submerged in 2.5% sodium hypochlorite and then randomly divided into 4 experimental groups (n=15) according to the final irrigant used (1) distilled water (control), (2) QMixTM, (3) 10% citric acid, (4) 17% EDTA. After immersion in the test substance the samples were filled with Biodentine cement and immersed in phosphate buffered saline (PBS) for a period of 7 days. The push out test was performed and the bond strength values in MPa were obtained. The data were analyzed by Kruskal Wallis and Studend- Newman-Keuls tests. Results: The worst bond values were obtained after using EDTA while distilled water, QMix and citric acid showed statistically similar results to each other. Conclusion: Removal of the smear layer did not result in improved bonding results of Biodentine cement.(AU)

Root filling quality and bond strength of endodontic sealers to human and bovine dentin / Qualidade da obturação e resistência de união de cimentos endodônticos à dentina humana e bovina

Objetivo: Este estudo teve como objetivo comparar a qualidade da obturação e a resistência de união de dois cimentos endodônticos, AH Plus e Bio-C Sealer, em dentes humanos e bovinos. Métodos: Os canais radiculares de 60 dentes unirradiculares [30 humanos (H) e 30 bovinos (B)] foram preparados e obturados por condensação lateral da guta-percha e AH Plus (grupos AP-H e AP-B) ou Bio-C Sealer (grupos BC-H e BC-B). Seis fatias de 1,5 mm de espessura foram obtidas de cada raiz. Os espécimes foram observados em estereomicroscópio para avaliar a qualidade da obturação, considerando possíveis espaços vazios no material obturador. Posteriormente, as fatias radiculares foram avaliadas em termos de resistência de união por push-out e modo de falha. Os dados foram analisados pelos testes de Mann-Whitney e coeficientes de correlação de Spearman (α=5%). Resultados: A qualidade de obturação fornecida por AP e BC foi semelhante em ambos os substratos de dentina. No entanto, ao comparar dentes humanos e bovinos, os escores de espaços vazios foram maiores nas amostras bovinas, para ambos os cimentos. AP teve maior resistência de união à dentina humana e bovina do que BC. No entanto, não houve diferença significativa na resistência de união entre os substratos dentinários, para ambos os cimentos testados. Além disso, houve uma correlação positiva e moderada entre os valores de resistência de união de dentes humanos e bovinos. O modo de falha misto foi o mais prevalente. Conclusão: AP e BC fornecem qualidade de obturação semelhante, mas o primeiro apresenta maiores valores de resistência de união à dentina humana e bovina. A utilização de dentes bovinos como substitutos de amostras humanas parece ser adequada em estudos relacionados à resistência de união, mas não naqueles que testam a qualidade da obturação endodôntica.(AU)

Objective: This study aimed to compare the filling quality and bond strength of two endodontic sealers, AH Plus and Bio-C Sealer, in human and bovine teeth. Methods: The root canals of 60 [30 human (H) and 30 bovine (B)] single-rooted teeth were prepared and filled by lateral condensation of gutta-percha and AH Plus (groups AP-H and AP-B) or Bio-C Sealer (groups BC-H and BC-B). Six 1.5-mm-thick slices were obtained from each root. The specimens were observed under a stereomicroscope to assess filling quality, considering possible voids within the filling material. Subsequently, root slices were evaluated in terms of push-out bond strength and failure mode. Data were analyzed by Mann-Whitney tests and Spearman correlation coefficients (α=5%). Results: The filling quality provided by AP and BC was similar in both dentin substrates. However, when comparing human and bovine teeth, void scores were greater in the bovine samples, for both sealers. AP had higher bond strength to human and bovine dentin than BC. However, there was no significant difference in bond strength between dentin substrates, for both sealers tested. Also, there was a positive and moderate correlation between the bond strength values of human and bovine teeth. The mixed failure mode was the most prevalent. Conclusion: AP and BC provide similar filling quality, but the first presents higher bond strength values to human and bovine dentin. The use of bovine teeth as substitutes for human samples seems adequate in studies related to bond strength, but not in those testing root canal filling quality.(AU)

Profundidade de polimerização de uma resina bulk fill fluida após adição de xilitol / Depth of polymerization of a fluid bulk fill resin after addition of xylitol

Objetivo: Avaliar a profundidade de polimerização em diferentes espessuras da resina composta Tetric® N-Flow Bulk Fill com adição de xilitol em diferentes concentrações. Metodologia: A resina Tetric® N-Flow Bulk Fill foi misturada às concentrações do xilitol (0% [Controle], 2,5% e 5% g/g) por espatulação manual durante 1 min em uma câmara escura. Amostras cilíndricas foram confeccionadas em moldes de polimetilmetacrilato de 5 mm de diâmetro x 1 mm, 2 mm, 3 mm e 4 mm de espessura nas concentrações de xilitol propostas totalizando 12 grupos (n=3), fotoativadas por 10 s e armazenadas a 37º C por 24 h. Os espécimes foram submetidos ao teste de microdureza Vickers, sendo a profundidade de polimerização obtida por meio da razão base/topo. Foram utilizados testes não paramétricos de Kruskal Wallis para comparação das diferentes espessuras na mesma concentração e das diferentes concentrações na mesma espessura (p<0,05) através do software BioEstat 5.3. Resultados: Não houve diferença estatisticamente significativa entre as diferentes espessuras na mesma concentração, bem como entre as diferentes concentrações na mesma espessura (p=1,000). Todos os espécimes apresentaram profundidade de polimerização adequada (razão de dureza ≥80%), com exceção das amostras com 4 mm de espessura contendo 2,5 e 5% de xilitol, que apresentaram razão de dureza média de 79% e 74%, respectivamente. Conclusão: Nas condições deste estudo, pode-se concluir que a adição de xilitol a uma resina bulk fill fluida pode afetar a profundidade de polimerização em 4 mm (AU).

Objective: To evaluate the depth of cure at different thicknesses of the Tetric® NFlow Bulk Fill composite resin with the addition of xylitol at different concentrations. Materials and Methods: The Tetric™ N-Flow Bulk Fill resin was mixed with xylitol concentrations (0% [Control], 2.5%, and 5% g/g) by manual spatulation for 1 minute in a portable darkroom. Cylindrical samples were prepared in polymethyl methacrylate molds with diameters of 5 mm and thicknesses of 1 mm, 2 mm, 3 mm, and 4 mm at the proposed xylitol concentrations, totaling 12 groups (n=3), photoactivated for 10 seconds, and stored at 37°C for 24 hours. The specimens were subjected to Vickers microhardness testing, and the depth of cure was obtained by calculating the base/top ratio. Non-parametric Kruskal-Wallis tests were used to compare different thicknesses at the same concentration and different concentrations at the same thickness (p<0,05) using BioEstat 5.3 software. Results: There was no statistically significant difference between different thicknesses at the same concentration, as well as between different concentrations at the same thickness (p=1,000). All specimens exhibited adequate depth of cure (hardness ratio ≥80%), except for the samples with 4 mm thickness containing 2.5% and 5% xylitol, which showed average hardness ratios of 79% and 74%, respectively. Conclusion: Under the conditions of this study, it can be concluded that the addition of xylitol to a fluid bulk fill resin can affect the depth of cure at 4 mm (AU).

Avaliação do potencial de regeneração óssea guiada e biocompatibilidade de membrana polimétrica nano estruturada à base de quitosana / Evaluation of guided bone regeneration potential and biocompatibility of nano-structured polymeric membrane based on chitosan

A regeneração óssea guiada (ROG) é uma técnica muito utilizada na odontologia para reconstrução de defeitos alveolares para posterior instalação de implantes dentários. Para que a técnica seja efetiva, uma membrana que permita o isolamento de diferentes tipos teciduais é necessária. A quitosana nanoestruturada modificada por hidróxidos duplos lamelares (HDL) é um biopolímero sintético que busca unir as características promissoras da quitosana como material bioadesivo e com propriedades antimicrobianas com a hidrocalcita buscando aprimorar suas características estruturais. O objetivo deste estudo in vivo foi avaliar a biocompatibilidade e o potencial de regeneração óssea guiada de uma nova membrana produzida à base de quitosana nanoestrutada modificada por HDL. Ratos Wistar machos adultos (n=64) foram divididos randomicamente em 2 grupos de acordo com o tratamento: Colágeno (COL) e Quitosana (QTS). Os animais foram submetidos à cirurgia para instalação de uma membrana no subcutâneo da região dorsal e à realização de 2 defeitos críticos na calota craniana, respeitando cada lado do animal. O defeito do lado direito foi coberto por uma das membranas testadas (COL ou QTS) enquanto o outro permanecia descoberto (Controle). Oito animais de cada grupo foram sacrificados em 4 tempos de acompanhamento: 3, 7, 14 e 30 dias. Amostras de calota e subcutâneo foram coletadas e preservadas em paraformaldeído 4%. As amostras de calota foram escaneadas em viii microtomógrafico para análise da quantidade de osso neoformado. Em seguida, os espécimes de calota e subcutâneo foram processados laboratorialmente para exames histológicos em parafina: para avaliação histomorfológica das características do processo cicatricial e de degradação das membranas e histomorfométrica para quantificação do processo inflamatório e do nível de reação tecidual por meio do escore global de reação tecidual (EGRT). Análises descritivas e inferenciais foram realizadas para comparação entre os grupos com nível de significância de 5%. Os resultados não demonstraram diferenças entre os grupos COL e QTS quanto à intensidade do processo inflamatório e EGRT. Já em relação aos defeitos na calota, o grupo QTS apresentou maior neoformação óssea em relação ao grupo controle aos 30 dias (p=0,04). Com base nos resultados conclui-se que as membranas de quitosana nano particuladas modificadas por HDL apresentaram biocompatibilidade compatível com a membrana de colágeno e efetividade para uso como barreira em ROG. (AU)

Guided bone regeneration (GBR) is a technique widely used in dentistry to reconstruct alveolar defects for subsequent installation of dental implants. For the technique to be effective, a membrane that allows the isolation of different tissue types is necessary. Nanostructured chitosan modified by lamellar double hydroxides (HDL) is a synthetic biopolymer that seeks to combine the promising characteristics of chitosan as a bioadhesive material with antimicrobial properties with hydrocalcite seeking to improve its structural characteristics. The objective of this in vivo study was to evaluate the biocompatibility and guided bone regeneration potential of a new membrane produced based on nanostructured chitosan modified by HDL. Adult male Wistar rats (n=64) were randomly divided into 2 groups according to treatment: Collagen (COL) and Chitosan (QTS). The animals underwent surgery to install a membrane in the subcutaneous tissue of the dorsal region and to perform 2 critical defects in the cranial vault, respecting each side of the animal. The defect on the right side was covered by one of the tested membranes (COL or QTS) while the other remained uncovered (Control). Eight animals from each group were sacrificed at 4 follow-up times: 3, 7, 14 and 30 days. Calvary and subcutaneous samples were collected and preserved in 4% paraformaldehyde. The cap samples were scanned in a microtomograph to analyze the amount of newly formed bone. Then, the cap and subcutaneous specimens were processed in the laboratory for histological examinations in paraffin: for histomorphological evaluation of the characteristics of the scarring process and membrane degradation and histomorphometric for quantification of the inflammatory process and the level of tissue reaction through the global score of tissue reaction (EGRT). Descriptive and inferential analyzes were performed for comparison between groups with a significance level of 5%. The results showed no differences between the COL and QTS groups regarding the intensity of the inflammatory process and EGRT. In relation to the defects in the calvaria, x the QTS group presented greater new bone formation in relation to the control group at 30 days (p=0.04). Based on the results, it is concluded that the nanoparticulate chitosan membranes modified by HDL showed biocompatibility compatible with the collagen membrane and effectiveness for use as a barrier in GBR. (AU)

Análise da influência de solução de biovidro no procedimento endodôntico regenerativo / Analysis of the influence of bioglass solution on the regenerative endodontic procedure

Este estudo avaliou os efeitos de uma solução experimental de vidro bioativo F18 dopado com cobalto (F18Co) no reparo tecidual após procedimento endodôntico regenerativo (REP, do inglês regenerative endodontic procedure) em molares de ratos. A solução de F18Co foi preparada misturando o pó de F18Co com água destilada na proporção de 1:5. Os primeiros molares superiores direito ou esquerdo de 12 ratos Wistar foram utilizados, nos quais as polpas foram expostas, removidas e os canais irrigados com hipoclorito de sódio (NaOCl) 2,5%, seguido de ácido etilenodiaminotetraacético (EDTA) 17% (5 min cada). Em seguida, os molares foram divididos em dois grupos (n = 6): REP-SS e REP-F18Co, nos quais receberam irrigação final (5 min) com solução salina (SS) ou solução de F18Co, respectivamente. Em seguida, foi induzido sangramento intracanal e o dente foi selado. Molares não tratados foram usados como controles (n = 3). Após 21 dias, os ratos foram eutanasiados e as peças processadas para análise da formação de tecido mineralizado e tecido mole dentro do canal radicular, pela técnica de hematoxilinaeosina. A presença e maturação do colágeno foram avaliadas por coloração de tricrômio de Masson e picrosírius red. Análises da imunomarcação do antígeno nuclear de proliferação celular (PCNA) e osteocalcina (OCN) foram realizadas. Os dados foram submetidos ao teste de Mann-Whitney U (p < 0,05). Houve formação semelhante de tecido mineralizado em espessura e comprimento nos grupos REP-SS e REP-F18Co (p > 0,05). Em relação à presença de tecido neoformado no interior dos canais radiculares, a maioria dos espécimes de REP-F18Co apresentou formação de tecido até o terço cervical do canal radicular, enquanto do grupo REP-SS, até o terço médio (p < 0,05), e houve maior maturação colágena em REP-F18Co (p < 0,05). O número de células positivas para PCNA encontradas no terço apical do canal radicular foi significativamente maior em REP-F18Co, assim como a imunomarcação de OCN, que foi severa na maior parte dos espécimes do grupo REP-F18Co, e leve em REPSS. Conclui-se que a irrigação final com solução de biovidro F18Co em REP não influenciou a formação de tecido mineralizado, mas induziu a formação de tecido conjuntivo no interior dos canais radiculares, com maior maturação colágena, aumento no número de células positivas para PCNA e na imunomarcação de OCN.

This study evaluated the influence of an experimental solution of cobalt-doped F18 bioactive glass (F18Co) on tissue repair following regenerative endodontic procedure (REP) in rat molars. The F18Co solution was prepared at a ratio of 1:5 F18Co powder to distilled water. The right or left upper first molars of 12 Wistar rats were used, where the pulps were exposed, removed, and irrigated with 2.5% sodium hypochlorite (NaOCl), followed by 17% ethylenediaminetetraacetic acid (EDTA) (5 min each). Subsequently, the molars were divided into two groups (n = 6): REP-SS and REP F18Co, where they received a final irrigation (5 min) with saline solution (SS) or F18Co solution, respectively. Then, intracanal bleeding was induced, and the tooth was sealed. Untreated molars were used as controls (n = 3). At 21 days, the rats were euthanized, and the specimens were processed for analysis of mineralized tissue and soft tissue formation inside the root canal using haematoxylin-eosin. The presence and maturation of collagen was evaluated by Masson's trichrome and picrosirius red staining. Immunolabeling analyses of proliferating cell nuclear antigen (PCNA) and osteocalcin (OCN) were performed. The data were submitted to the Mann-Whitney U test (P < 0.05). There was similar formation of mineralized tissue in thickness and length in REP-SS and REP-F18Co groups (P > 0.05). Regarding the presence of newly formed soft tissue, most specimens of the REP-F18Co had tissue formation up to the cervical third of the canal, while the REP-SS specimens showed formation up to the middle third (P < 0.05), and there was higher maturation collagen in REP-F18Co (P < 0.05). The number of PCNA-positive cells found in the apical third of the root canal was significantly higher in the F18Co group, as well as the OCN immunolabeling, which was severe in most specimens of REP-F18Co, and low in most specimens of REP SS. In conclusion, the final irrigation with F18Co bioactive glass solution in REP did not influence mineralized tissue formation but induced soft tissue formation inside the root canals, with higher collagen maturation, and an increase in PCNA-positive cells and OCN immunolabeling

Influence of number and position of porcelain specimens in the furnace on flexural strength and translucency

The aim of this study was to investigate the influence of the quantity and positioning of feldspathic ceramic specimens inside the furnace on their flexural strength and translucency. The tested hypotheses were that the arrangement of specimens in the furnance would not influence 1) the translucency or 2) the biaxial strength of the porcelain. Methods: Ninety porcelain specimens were made (1.2 mm thickness and 13.5 mm diameter) and assigned into two main groups (n=15): G1 group - 15 firing cycles containing only one specimen each, always at the center of the refractory; and G5 group - 15 firing cycles containing five specimen each, where one specimen was at the center of the refractory and four specimens positioned equidistantly on the periphery. The translucency test was performed using a spectrophotometer, followed by the flexural strength test, according to ISO 6872:2015. T-student test was performed for both the mechanical and optical obtained data. Results: The flexural strength of the porcelain was not affected by the positioning (center x periphery) of the specimens inside the furnace (p =0.08), but the translucency was affected (periphery > center; p =0.009). Regarding to the number of feldspathic ceramic specimens, the biaxial flexural strength was affected (p =0.025), as well as the translucency (p <0.05). Conclusion: A higher quantity of feldspathic ceramic specimens for each firing cycle decreased its biaxial flexural strength and translucency. Also, specimens positioned at the center of the refractory became less translucent than those positioned at the periphery.

Light-curing of calcium hydroxide-based liners: pH analysis and calcium ion release / Fotoativação de forradores a base de hidróxido de cálcio: análise de pH e liberação de íons cálcio

Objective: Compare the pH values and calcium ion release of calcium hydroxide-based liner materials before and after light-curing. Material and Methods: The materials evaluated were: hydrox-cal white (HW), hydrox-cal dentin (HD), Biocal (BC) and UltraBlend Plus (UB). 120 samples of the liner materials were inserted into a PVC tube (n=15). The samples from HW+A, HD+A, BC+A and UB+A were subjected to photoactivation. The other groups HW+N, HD+N, BC+N and UB+N were only inserted in a glass tube with deionized water. The pH was measured 24 hours and 14 days after the inclusion of the samples with the aid of a pH meter. The calcium release was analyzed with the aid of an atomic absorption spectophotometer at 24h and 14 days. The results were submitted to the Shapiro-Wilk test, followed by ANOVA and Tukey test (p=0.05). Results: In 24h, the groups that were not light cured showed the highest pH values (p<0.05). In 14 days, BC+N and BC+A demonstrated the lowest pH values. The groups that were not light cured also showed higher calcium release values in 24h and 14 days (p<0.05). Conclusion: Photoactivation of calcium hydroxide-based liner materials negatively interferes with calcium ion release, as well as with pH.(AU)

Objetivo: Comparar os valores de pH e liberação de íons cálcio de materiais forradores à base de hidróxido de cálcio antes e depois da fotopolimerização. Material e métodos: Os materiais avaliados foram: Hidrox-cal branco (HW), Hidrox-cal dentina (HD), Biocal (BC) e UltraBlend Plus (UB). 120 amostras dos materiais de revestimento foram inseridas em um tubo de PVC (n=15). As amostras de HW +A, HD+A, BC+A e UB+A foram submetidas à fotoativação. Os demais grupos HW +N, HD+N, BC+N e UB+N foram inseridos apenas em um tubo de vidro com água deionizada. O pH foi medido 24 horas e 14 dias após a inclusão das amostras com o auxílio de um medidor de pH. A liberação de cálcio foi analisada com o auxílio de um espectrofotômetro de absorção atômica em 24h e 14 dias. Os resultados foram submetidos ao teste de Shapiro-Wilk, seguido de ANOVA e teste de Tukey (p=0,05). Resultados: Em 24h, os grupos não fotopolimerizados apresentaram os maiores valores de pH (p<0,05). Em 14 dias, BC+N e BC+A apresentaram os menores valores de pH. Os grupos não fotopolimerizados também apresentaram maiores valores de liberação de cálcio em 24h e 14 dias (p<0,05). Conclusão: A fotoativação de materiais de revestimento à base de hidróxido de cálcio interfere negativamente na liberação de íons cálcio e no pH (AU)

Color and translucency stability of CAD/CAM restorative materials

Aim: This study assessed the color and translucency stability of a polymer infiltrated ceramic network (PICN) and compared it with a resin composite (RC) and a feldspathic ceramic (FEL). Methods: Disc-shaped samples of a PICN (Vita Enamic), a feldspathic ceramic (Vitablocks Mark II), and a resin composite (Brava block) were prepared from CAD/CAM blocks. PICN and RC surfaces were finished with a sequence of polishing discs and diamond paste. FEL samples received a glaze layer. The samples were subjected to 30-min immersions in red wine twice a day for 30 days. CIEL*a*b* coordinates were assessed with a spectrophotometer at baseline and after 15 and 30 days of immersion. Color alteration (ΔE00) and translucency parameter (TP00) were calculated with CIEDE2000. Average roughness was measured before the staining procedures. Color difference and translucency data were analyzed with repeated-measures ANOVA and Tukey's tests. Roughness was analyzed with the Kruskal-Wallis test. Results: Roughness was similar among the experimental groups. All materials had their color alteration significantly increased from 15 to 30 days of staining. PICN reached an intermediate ΔE00 between FEL and RC at 15 days. PICN revealed a color alteration as high as the composite after 30 days. No statistical difference was observed regarding translucency. Conclusion: PICN was not as color stable as the feldspathic ceramic at the end of the study. Its color alteration was comparable to the resin composite when exposed to red wine. However, the translucency of the tested materials was stable throughout the 30-day staining

Effect of frozen storage on preservation of a silicone-based test food material

Aim: This study aimed to evaluate the effect of frozen storage on the physical properties of a silicone-based test food material, highly used to evaluate the masticatory performance in research settings. Methods: A total of 1,666 silicone cubes of Optosil Comfort® with 5.6-mm edges were shaped and stored at -18°C. The cubes were subsequently tested for flexural strength (maximum force, displacement, stress, and strain) before breaking (n = 136), changes in weight and size (n = 170), and masticatory performance (n = 1360) at eight timepoints: immediately after cube preparation (baseline, no freezing), and 1, 2, 3 and 4 weeks, and 2, 4 and 6 months after frozen storage. The cubes were thawed 8 h before each assessment. Results: The maximum force, stress, maximum displacement, and deformation values for the cubes were not affected by freezing (P > 0.05). At all of the time points, the cubes exhibited similar weight (P = 0.366) and size (identical values). The masticatory performance for the cubes also showed no differences from baseline through 6 months (P = 0.061). Conclusion: Freezing Optosil Comfort® silicone cubes did not alter the physical and mechanical properties of the material, being suitable to optimize the assessment of masticatory parameters for research purposes

Analysis of the biocompatibility of a biocelulose and a poly L- lactic acid membrane

The use of selective barriers as resorbable membranes has become a routine clinical procedure for guided bone regeneration. Therefore, the production of membranes with a low inflammatory potential during their resorption process has become the goal of a considerable number of researches. Aim: The purpose of the present study was to evaluate the biocompatibility of poly (L- lactic acid) (PLLA) and biocelulose membranes (BC) inserted in the subcutaneous tissue on the dorsum of rats. Methods: Fifteen animals underwent surgical procedures for the insertion of 4 types of membranes: COL (Collagen membrane) ­ Control Group; BC (Biocellulose membrane); BCAg (Biocellulose membrane impregnated with Silver); PLLA (Poly (L-lactic acid) membrane). All membrane types were inserted into each animal. Animals were euthanized after 3, 7, and 15 days of the surgical procedure. Descriptive histological analyses were carried out to investigate host tissue reaction to membrane presence by assessing the anti-inflammatory process composition associated with the membrane resorption and the presence of foreign-body reaction or encapsulation. Results: The BC membranes showed a higher degree of inflammation and poor pattern of integration with the surrounding tissues than the PLLA and COL membranes. Conclusion: The PLLA and COL membranes present better biocompatibility than the BC membranes

Comparative of flexural strength, hardness, and fluoride release of two bioactive restorative materials with RMGI and composite resin

Aim: This study was fulfilled to evaluate the flexural strength, micro-hardness, and release of two fluoride ions of bioactive restorative materials (Cention N and Activa Bioactive), a resin modified glass ionomer (Fuji II LC), and a resin composite (Filtek z250). Methods: Forty samples from four restorative materials (Activa Bioactive, Fuji II LC, Cention N, and Filtek Z250) were provided according to the current standards of ISO 4049/2000 guide lines. Subsequently, the samples were stored for 24 hours and 6 months in artificial saliva, and successively, flexural strength and micro-hardness of the samples were measured. For each studied groups the pH was decreased from 6.8 to 4 in storage solution. The rate of changes in fluoride ion release was measured after three different storage periods of 24 hours, 48 hours, and 6 months in distilled water, according to the previous studies' method. Two-way ANOVA, One-way ANOVA, Tukey HSD Pair wise comparisons, and independent t-tests were used to analyze data (α= 0.05). Results: The highest flexural strength and surface micro-hardness after 24 hours and also after 6 month were observed for Cention N(p<0.001).Flexural strength of all samples stored for 6 months was significantly lower than the samples stored for 24 hours(p<0.001). The accumulative amount of the released fluoride ion in RMGI, after six-month storage period in distilled water was considerably higher (p<0.001) than 24 hours and 48 hours storage. The amount of fluoride ion release with increasing acidity of the environment (from pH 6.8 to 4) in Fuji II LC glass ionomer was higher than the bioactive materials (p<0.05). Conclusion: The flexural strength of RMGI was increased after storage against the Activa Bioactive,Cention N and Z250 composite. Storage of restorative materials in artificial saliva leads to a significant reduction in micro hardness. The behavior and amount of released fluoride ions in these restorative materials, which are stored in an acidic environment, were dependent on the type of restorative material

Dental staining after orthodontic debonding: effectiveness of two bleaching treatment protocols - in vitro study

Objective: The aim of this study was to compare the effectiveness of two bleaching treatment protocols to treat dental staining after orthodontic debonding. Materials and Methods: Twenty four bovine teeth were submitted to orthodontic bracket (Morelli, Edgewise Prescription, Slot 22) bonding (Transbond XT, 3M) and debonding, which were divided into three groups according to the bleaching protocol: hydrogen peroxide 10% (Whiteness, FGM) simulating home bleaching protocol (Home Bleaching Group), hydrogen peroxide 35% Whiteness, FGM) simulating dental office bleaching protocol (Office Bleaching Group) and Control Group, which was not exposed to any dental bleaching protocol, and stored in distilled water at 37°C. The specimens were submitted to the following processes: aging of resin remaining tegs by ultraviolet (UV), staining with coffee solution and tooth bleaching with 10% hydrogen peroxide (G1) and 35% hydrogen peroxide (G2). The color stability analysis (CIE color space L* a* b* was performed with Vita Easyshade Compact spectrophotometer before bonding (T0), after aging and staining processes (T1) and after bleaching treatment (T2). All teeth were stored in distilled water at 37°C between experimental times. The comparison between the groups and time effect evaluation were performed using ANOVA / Tukey ( =0.05) and ANOVA-MR with Bonferroni correction ( =0.016), respectively. Results: The color stability parameters L *, a * and b * indicated, with the exception of GC, a tendency of increase in T1 (G1 - L *: 76.72 ± 13.39; a *: 6.68 ± 3.71; b *: 43.14 ± 4.04 / G2: - L *: 75.78 ± 4.66; a *: 8.13 ± 2.75; b *: 43.42 ± 8.87), which reflected the tendency to decrease brightness in T1, followed by a tendency to return to T0 values (G1 - L *: 82.92 ± 12.16; a *: 4.25 ± 3.68; b *: 39.40 ± 9.49 / G2: - L *: 83.76 ± 8.02; a *: 8.76 ± 4.08; b *: 47.90 ± 5.88). Significant differences were observed in G2 in a * (T1: 8.13 ± 2.75, T2: 8.76 ± 4.08) and b * (T1: 43.42 ± 8.87; T2: 47.90 ± 5.88), indicating that this group did not return to the values presented in T0 (a *: 1.81 ± 1.70; b *: 35.40 ± 5.08) (p <0.05). Conclusion: Based on the results of this study, it can be concluded that home bleaching protocol presented better performance for dental surface whitening in an eventual staining after orthodontic debonding.

Objetivo: O objetivo deste estudo foi comparar a eficácia de dois protocolos de tratamento clareador para manchas dentárias causadas após a descolagem ortodôntica. Materiais e Métodos: Vinte e quatro dentes bovinos foram submetidos à colagem e descolagem de braquetes ortodônticos (Morelli, Prescrição Edgewise, Slot 22") (Transbond XT, 3M), que foram divididos em três grupos de acordo com o protocolo de clareamento: peróxido de hidrogênio 10% (Whiteness, FGM) simulando protocolo de clareamento caseiro (grupo clareamento caseiro), peróxido de hidrogênio 35% Whiteness, FGM) simulando protocolo de clareamento de consultório (grupo clareamento de consultório) e Grupo Controle, que não foi exposto a nenhum protocolo de clareamento dental, armazenado em água destilada a 37ºC. Os corpos de prova foram submetidos aos seguintes processos: envelhecimento das resinas remanescentes por ultravioleta (UV), manchamento em solução de café e clareamento dental com peróxido de hidrogênio 10% (G1) e peróxido de hidrogênio 35% (G2). A análise de estabilidade de cor (sistema CIE L* a* b*) foi realizada com espectrofotômetro Vita Easyshade Compact antes da colagem (T0), após os processos de envelhecimento e manchamento (T1) e após o tratamento clareador (T2). Todos os dentes foram armazenados em água destilada a 37 °C entre os tempos experimentais. A comparação entre os grupos e a avaliação do efeito do tempo foram realizadas utilizando ANOVA/Tukey ( =0,05) e ANOVA-MR com correção de Bonferroni ( =0,016), respectivamente. Resultados: Os parâmetros de estabilidade de cor L *, a* e b* indicaram, com exceção do GC, tendência de aumento em T1 (G1 - L*: 76,72 ± 13,39; a*: 6,68 ± 3,71; b*: 43,14 ± 4,04 / G2: - L* : 75,78 ± 4,66; a*: 8,13 ± 2,75; b*: 43,42 ± 8,87), o que refletiu a tendência de diminuição do brilho em T1, seguido de uma tendência de retorno aos valores de T0 (G1- L*: 82,92 ± 12,16 ; a*: 4,25 ± 3,68; b*: 39,40 ± 9,49 / G2: - L*: 83,76 ± 8,02; a*: 8,76 ± 4,08; b*: 47,90 ± 5,88). Foram observadas diferenças significativas no G2 em a* (T1: 8,13 ± 2,75, T2: 8,76 ± 4,08) e b* (T1: 43,42 ± 8,87; T2: 47,90 ± 5,88), indicando que esse grupo não retornou aos valores apresentados em T0 (a*: 1,81 ± 1,70; b*: 35,40 ± 5,08) (p<0,05). Conclusão: Com base nos resultados deste estudo, pode-se concluir que o protocolo de clareamento caseiro apresentou melhor desempenho para o clareamento da superfície dentária em um eventual manchamento após a descolagem ortodôntica.

Avaliação da sorção e solubilidade de água em cimentos de ionômero de vidro com e sem agente de proteção / Evaluation of water sorption and solubility in glass ionomer cements with and without protective agent

Objetivo: Avaliar o efeito de um protetor de superfície na sorção e solubilidade de cimentos de ionômero de vidro. Materiais e Métodos: Quatro materiais foram selecionados: ionômero modificado por resina encapsulado (Riva Light Cure); modificado por resina pó/líquido (Vitremer); convencional encapsulado (Equia Forte) e convencional pó/líquido (Fuji IX). Foram confeccionados 20 espécimes de cada, sendo metade com proteção superficial do Equia Forte Coat. As amostras foram mantidas em estufa a 37°C em repouso por 5 dias. Em seguida, esses foram pesados em intervalos de 24 horas. A espessura e o diâmetro foram medidos com um paquímetro digital para o cálculo do volume. Novas pesagens foram realizadas para a obtenção da massa intermediária. Em seguida, as amostras foram mantidas em repouso por 5 dias a 37°C e realizada nova pesagem. Resultados: Os dados obtidos de sorção e solubilidade foram submetidos à análise de variância (ANOVA dois fatores, material e protetor de superfície) e teste Tukey ( =0,05). Para sorção, houve diferença significativa apenas para o fator material (p<0,05), Vitremer > Equia Forte > Riva Light Cure > Fuji IX. O ionômero Fuji IX apresentou os menores valores de sorção, diferindo significativamente dos demais materiais, independentemente do uso do protetor superficial. Não houve diferença significativa para o fator proteção de superfície (p>0,05). Para solubilidade não houve diferença significativa no fator material, protetor de superfície ou interação material*protetor. Conclusão: O uso do protetor superficial não influenciou nos valores de sorção e solubilidade dos ionômeros avaliados e o ionômero convencional Fuji IX apresentou menores taxas de sorção.

Objective: evaluate the effect of a surface coating agents on the sorption and glass ionomer cements solubility. Materials and Methods: Four materials were selected: Encapsulated resin-modified ionomer (Riva Light Cure); Powder/liquid Encapsulated resin-modified (Vitremer); Encapsulated conventional (Equia Forte) and powder/ liquid conventional (Fuji IX). Twenty samples of each were made, half with surface protection of Equia Forte Coat. The samples were kept in an oven for 5 days. These were then weighed at 24-hour intervals. The thickness and diameter were measured using a digital caliper to calculate their volume. New weightings were performed to obtain the intermediate mass. Then, the samples were kept at rest for 5 days and weighed again. Results: The sorption and solubility data obtained were subjected to analysis of variance (two-way ANOVA, material and surface coating agents) and Tukey test ( =0.05). For sorption, there was a significant difference only for the material factor (p<0.05), Vitremer > Equia Forte > Riva Light Cure > Fuji IX. The Fuji IX ionomer showed the lowest sorption values, differing significantly from the other materials, regardless of the use of surface coating agents. There was no significant difference for the surface protection factor (p>0.05). For solubility there was no significant difference for the material factor, surface coating agents or material*surface coating agent interaction. Conclusion: The use of surface coating agents did not influence the sorption and solubility values of the evaluated ionomers and the conventional Fuji IX ionomer showed lower sorption rates.

Expansão rápida da maxila apoiada em mini-implantes (MARPE): efeitos da ancoragem bicortical (in vitro) e análise clínica da espessura óssea alveolar vestibular através de revisão sistemática e meta-análise / Mini-implant assisted rapid palatal expansion (MARPE): the effects of bicortical anchorage (in vitro) and buccal alveolar bone thickness clinical analysis through systematic review and meta-analysis

O objetivo desse estudo foi avaliar, in vitro, a influência mecânica do tipo de ancoragem (monocortical ou bicortical), utilizada na técnica de expansão rápida da maxila apoiada em mini-implantes (MARPE), na microarquitetura óssea trabecular onde o disjuntor é instalado, e, analisar, através de revisão sistemática e meta-análise, os efeitos desta técnica na espessura da tábua óssea vestibular dos dentes de suporte, comparando com a técnica de expansão convencional. Dezesseis mini-implantes do tipo auto-perfurantes foram distribuídos em dois grupos (dois dispositivos MARPE com 4 mini-implantes cada grupo) de acordo com o tipo de inserção óssea (monocortical e bicortical), instalados em osso de costela bovina, e, ativados em cinco tempos distintos onde a cada ativação, o corpo de prova era microtomografado. O espaçamento das trabéculas (Tb.Sp [mm]) foi o parâmetro utilizado para avaliar a microarquitetura óssea em cinco regiões de interesse (ROI) peri-implantar (osso ao redor do dispositivo, superior, inferior, anterior e posterior). O teste ANOVA two-way com análise post-hoc de Tukey (α = 0,05) foi usado para avaliar o efeito do tipo de inserção na microarquitetura óssea durante os ciclos de ativação. O efeito do tempo foi avaliado usando o teste ANOVA-MR com correção de Bonferroni (α = 0,003). Para responder à pergunta da revisão sistemática, as bases PubMed (MEDLINE), Scopus, Web of Science, The Cochrane Library, Virtual Health Library e OpenGrey foram utilizadas até março de 2019. Avaliações de risco de viés foram realizadas usando as ferramentas Cochrane Collaboration e ROBINS- I. No estudo in vitro, apenas o ROI superior (cervical) teve diferença significativa (p <0,003) após o quarto ciclo de ativação ao longo do tempo entre as ativações. Para o grupo monocortical, o espaçamento trabecular foi afetado quando todo o ROI foi analisado a partir do quarto ciclo de ativação, enquanto para o ROI superior, essa diferença tornou-se aparente a partir do terceiro ciclo de ativação (p <0,003). Em relação a revisão sistemática, as evidências limitadas indicaram que pacientes tratados com a técnica convencional tiveram uma perda maior da espessura óssea alveolar vestibular em comparação com pacientes usando MARPE (p=0,001). As análises de subgrupo mostraram que as diferenças foram significativas em ambas as regiões de pré-molares, direita (p = 0,004) e esquerda (p <0,0001). Baseado nos resultados encontrados pode-se concluir que a ancoragem monocortical é mais suscetível a danos ósseos ao redor dos mini- implantes, sendo a região superior (cervical) mais afetada. Assim como, evidências limitadas sugerem que o MARPE pode diminuir a perda do osso alveolar vestibular quando comparado a técnica de expansão convencional. (AU)

This study aimed to evaluate, in vitro, the mechanical influence of the type of anchorage (monocortical or bicortical), that is used in the mini-implant assisted rapid palatal expansion (MARPE) technique, on the trabecular bone microarchitecture where the appliance is installed, and to analyze, through systematic review and meta-analysis, the effects of this technique on the buccal palatal bone thickness of the supporting teeth, compared to the conventional technique. Sixteen self-drilling mini-implants were distributed into two groups (two MARPE devices with 4 mini-implants each group) according to the type of bone insertion (monocortical and bicortical), installed in bovine rib bone, and activated five different times where at each activation, the specimen was microtomographed. Trabecular spacing (Tb.Sp [mm]) was the parameter used to assess bone microarchitecture in five peri-implant regions of interest (ROI) (the whole area around the device, superior, inferior, anterior ,and posterior ). The two-way ANOVA test with post-hoc Tukey analysis (α = 0.05) was used to assess the effect of insertion type on bone microarchitecture during activation cycles.The effect of time was evaluated using the ANOVA-MR test with Bonferroni correction (α = 0.003). To answer the systematic review question, PubMed (MEDLINE), Scopus, Web of Science, The Cochrane Library, Virtual Health Library and OpenGrey databases were used for research until March 2019. Bias risk assessments were performed using the Cochrane Collaboration and ROBINS-I tools. In the in vitro study, only the superior (cervical) ROI had a significant difference (p<0.003) after the fourth activation cycle. For the monocortical group, trabecular spacing was affected when the whole area ROI was analyzed from the fourth activation cycle, on the other hand, when analyzing the superior ROI, this difference was significant from the third activation over time between the actvations (p<0.003). Regarding the systematic review, limited evidence indicated that patients treated with the conventional technique had a greater loss of buccal alveolar bone thickness compared to patients treated with the MARPE technique (p=0.001). Subgroup analyzes showed that differences were significant in both the right (p = 0.004) and left (p < 0.0001) premolar regions. Based on the results found, it can be concluded that monocortical anchorage is more susceptible to bone damage around the mini-implants, and the superior (cervical) region is more affected. As well, limited evidence suggests that MARPE technique may reduce the loss of buccal alveolar bone when compared to the conventional palatal expansion technique. (AU)

Cimentos biocerâmicos de silicato de cálcio: uma revisão de literatura / Calcium silicate cements: a literature review

Preservar a integridade da dentição natural é essencial para a manutenção da função e estética dental. Para alcançar este objetivo, a terapia endodôntica pode desempenhar um papel fundamental. Dentre os avanços aplicados à endodontia nas últimas décadas, o desenvolvimento dos materiais à base de silicato de cálcio proporcionou novas perspectivas de tratamento e resultados promissores em diversas aplicações clínicas. O objetivo deste trabalho é realizar uma revisão de literatura acerca desses materiais. Para isso, foi realizada uma pesquisa bibliográfica sobre o tema nas principais bases de dados e obtidos artigos científicos dos últimos 15 anos. A leitura crítica e minuciosa dos artigos permitiu a construção do texto que explorou o conceito, composição, mecanismos de ação e de reação de presa, vantagens, limitações e aplicações clínicas dos diversos biocerâmicos disponíveis em endodontia. O desenvolvimento dos materiais à base de silicato de cálcio possibilitou a execução de técnicas operatórias mais previsíveis e conservadoras. As modificações dos materiais mais recentes estão melhorando as suas propriedades e disponibilizando materiais cada vez mais inteligentes biologicamente e atraentes à prática clínica.

Preserving the integrity of the natural dentition is essential for maintaining dental function and esthetics. To achieve this goal, endodontic therapy can play a key role. Among the advances applied to endodontics in recent decades, the development of calcium silicate-based materials has provided new treatment perspectives and promising results in several clinical applications. The objective of this work is to carry out a literature review about these materials. For this, a bibliographic research was carried out on the subject in the main databases and scientific articles from the last 15 years were obtained. The critical and detailed reading of the articles allowed the construction of the text that explored the concept, properties, composition, mechanisms of action, advantages, limitations and clinical applications of the various bioceramics available in endodontics. With the study, we concluded that the development of calcium silicate-based materials allows the execution of more predictable and conservative operative techniques. Modifications to the latest materials are improving their properties and making materials increasingly biologically intelligent and attractive to clinical practice available.

Análise imunológica dos efeitos dos cimentos MTA, Bio-C Repair e Bio-C Repair Íon+ nas respostas de macrófagos inflamatórios de murino / Effects of cements MTA, Bio-C Repair and Bio-C Repair Ion+ on inflammatory murine macrophage responses, an immunological analysis

As melhorias alcançadas nas propriedades físico-químicas dos materiais endodônticos permitiram a utilização de materiais de reparo em situações clínicas que eram consideradas críticas. Os chamados biocerâmicos, derivados do MTA, apresentando boa biocompatibilidade e bioatividade, se tornaram uma solução eficaz. Estes materiais apresentam propriedades clínicas melhoradas, com excelente consistência e manuseabilidade, além de adequado tempo de trabalho e presa. Estes cimentos seguem em evolução e as empresas vêm investindo em melhorias em suas composições com o intuito de potencializar suas propriedades biotivas. Este trabalho teve como objetivo avaliar o cimento biocerâmico Bio-C Repair (Angelus, Londrina, Paraná, Brasil) e o seu potencial sucessor, o cimento Bio-C Repair Íon+ (Angelus, Londrina, Paraná, Brasil), bem como o MTA (Angelus, Londrina, Paraná, Brasil). Foi aprovado pelo Comitê de Ética no Uso de Animal (CEUA-UFMG 350/2019). Tais biocerâmicos foram avaliados quanto às respostas de macrófagos. Os experimentos foram realizados no laboratório de Gnotobiologia e Imunologia do Instituto de Ciências Biológicas (ICB) da Universidade Federal de Minas Gerais. Utilizou-se macrófagos murinos obtidos de camundongos C57BL/6 quando se avaliou a viabilidade celular (pelo método MTT), a aderência celular, a capacidade de fagocitose (na presença da levedura S. boulardii) e a detecção da produção de Espécies Reativas de Oxigênio (ROS), na ausência e na presença de Zymosan A (de Saccharomyces cerevisiae), bem como, na presença e na ausência dos cimentos. Os macrófagos inflamatórios foram obtidos do peritônio dos animais após a injeção de caldo Tioglicolato estéril a 3%. Após aspirados, os macrófagos foram centrifugados e a concentração celular final foi ajustada de acordo com cada ensaio proposto: viabilidade e aderência (1x106 cel/mL); ensaio de fagocitose e ROS (5x105 cel/mL). Fez-se a manipulação dos materiais sob fluxo laminar, quando foram inseridos em capilares estéreis. Os resultados de viabilidade celular demonstraram que houve diferença significativa na cultura de 24 horas, tratada com o Bio-C Repair Íon+, em relação ao grupo controle. Os ensaios de fagocitose e aderência celular não apresentaram diferença estatisticamente significante entre os grupos. As análises demonstraram expressivos níveis de ROS quando as células foram tratadas na presença de Zymozan A. Na presença desse estímulo, o Bio-C Repair Íon+ apresentou diferença significativa em relação a todos os demais biocerâmicos e ao grupo controle. Os resultados foram analisados pelo teste ANOVA (P<0,05), comparando-se os grupos experimentais entre si e o grupo controle. Conclui-se que o novo material reparador Bio-C Repair Íon+ apresenta ações de biocompatibilidade quase semelhantes ao Bio-C Repair e MTA. As diferenças observadas em relação ao Bio-C Repair Ion+ quanto à viabilidade celular e a produção de ROS podem estar relacionadas ao íon metálico presente em sua composição.

The improvements achieved in the physicochemical properties of endodontic materials allowed the use of repair materials in clinical situations considered critical. The so-called bioceramics, derived from MTA, showing good biocompatibility and bioactivity, have become an effective solution. These materials have improved clinical properties, exhibiting excellent consistency and handling, as well as good working and setting time. These types of cement are still evolving, and companies have been investing in improvements in their compositions to enhance their bioactive properties. This study aimed to evaluate the Bio-C Repair bioceramic cement (Angelus, Londrina, Paraná, Brazil) and its potential successor, the Bio-C Repair Íon+ (Angelus, Londrina, Paraná, Brazil), as well as the MTA (Angelus, Londrina, Paraná, Brazil). The Animal Use Ethics Committee (CEUA) of the Federal University of Minas Gerais (UFMG) approved the study (350/2019). Such bioceramics were evaluated in macrophage responses. The experiments were carried out in the Gnotobiology and Immunology laboratory of the Institute of Biological Sciences (ICB) of the UFMG. Murine macrophages obtained from C57BL/6 mice were used to evaluate cell viability (by the MTT method), cell adhesion, phagocytosis capacity (in the presence of the yeast S. boulardii), and in the detection of the production of Reactive Oxygen Species (ROS) in the absence and presence of Zymosan A (from Saccharomyces cerevisiae), as well as in the presence and absence of types of cement. Inflammatory macrophages were obtained by injecting sterile 3% thioglycolate broth into the animals' peritoneum. After aspirating, the macrophages were centrifuged, and the final cell concentration was adjusted according to each proposed assay: viability and adherence (1x106 cells/mL), phagocytosis, and ROS assay (5x105 cells/mL). The materials were manipulated under laminar flow when inserted into sterile capillaries. The cell viability results showed a significant difference in the 24-hour culture, treated with Bio-C Repair Ion+, to the control group. The phagocytosis and cell adhesion assays showed no statistically significant difference between the groups. The analyses showed expressive ROS levels when the cells were treated in the presence of Zymosan A. In the presence of this stimulus, the Bio-C Repair Ion+ showed a significant difference between all other bioceramics and the control group. The results were analyzed by the ANOVA test (P<0.05), comparing the experimental groups and the control group. It is concluded that the new repair material Bio-C Repair Ion+ has biocompatibility actions almost similar to Bio-C Repair and MTA. The differences observed with Bio-C Repair Ion+ regarding cell viability and ROS production may be related to the metallic ion's composition.

Comparison of the High Cycle Fatigue Behavior of the Orthodontic NiTi Wires: An in Vitro Study

Abstract Objective: To compare the high-cycle fatigue behavior of four commercially available NiTi orthodontic wires. Material and Methods: Twelve NiTi orthodontic wires, round, 0.016-in, three per brand, were selected and divided into four groups: G1 - Heat-activated NiTi, G2 - Superelastic NiTi, G3 - Therma-Ti, and G4 - CopperNiTi. The atomic absorption spectrometry method was used to determine the chemical composition of investigated NiTi wires. We also performed a fatigue test at three-point bending using a universal testing machine for 1000 cycles in a 35 °C water bath. For the first and thousandth cycle, the average plateau load and the plateau length were determined in the unloading area of the force versus displacement diagram. In addition, we calculated the difference between the average plateau load of the first and thousandth cycle (∆F), as well as the difference between the plateau length of both cases (∆L). Results: According to our results, there were no significant differences between the average plateau load of the first and thousandth cycles of each group (p>0.05) and in the plateau length of the first and thousandth cycles of the groups (p>0.05). Conclusion: There were no significant differences between the groups changing the superelasticity property after high-cycle fatigue.

Novo sistema de retentor pré-fabricado perfurado e de iluminador em fibra óptica: estudo da resistência mecânica frente a variação dos cimentos resinosos / New system of hollow prefabricated post and optical fiber illuminator: study of the mechanical strength by varying resin cements

O presente estudo teve por objetivo avaliar a resistência à flexão de um pino experimental de fibra de vidro vazado, e a resistência adesiva entre este pino experimental à dentina radicular, associando a utilização de um dispositivo iluminador em fibra óptica, sob o processo de envelhecimento, além de determinar a distribuição de tensão pela Análise de Elementos Finitos (FEA). O pino experimental e o dispositivo iluminador de fibra óptica têm por finalidade aumentar a efetividade de fotoativação dos cimentos resinosos nos terços médios e apicais dos canais radiculares. Para o teste de flexão de 3 pontos, estritamente do pino de fibra de vidro, as amostras foram divididas em 4 grupos (n=10): pino convencional (pc), pino experimental sem preenchimento (pp), com preenchimento de cimento resinoso (ppc) e com preenchimento de fibra óptica (ppf). Para o teste de resistência adesiva Pull-out, 100 raízes de dentes bovinos foram restauradas com retentores intrarradiculares e coroas de resina composta, distribuídos em 10 grupos (n=10), tendo como variáveis: o tipo de pino de fibra de vidro [convencional (C) ou perfurado (P)], o sistema de fotoativação [com ou sem o iluminador de fibra óptica (O)], o tipo de cimento resinoso [fotoativado (F) ou polimerização dual (D)] e o envelhecimento das amostras [com e sem ciclagem mecânica (C)]. O processo de envelhecimento foi realizado através da ciclagem mecânica e as amostras foram submetidas ao teste de resistência adesiva Pull-out. A análise do modo de falha foi realizada em Estereomicroscópio. A Análise em Elementos Finitos avaliou a distribuição de tensão pela análise de von Mises, deformação total e tensão máxima principal no Software Ansys 19.3. A análise estatística foi constituída pelo teste de normalidade Shapiro-Wilk, análise de variância (ANOVA) 1, 2 e 3 fatores e teste Tukey 5%. As médias e desvios padrão de resistência à flexão foram (MPa): pc = 677 ± 81,1; ppc = 419 ± 23,2; ppf = 200 ± 32,5 e pp = 177 ± 32,8. As médias e desvios padrão de resistência adesiva foram (MPa): CD = 12,2 ± 1,21; PD = 11,1 ± 1,32; PF = 10,9 ± 1,29; POD = 13,7 ± 1,16; POF = 11,9 ± 1,48; CDC = 10,1 ± 1,33; PDC = 9,25 ± 1,11; PFC = 8,37 ± 1,25; PODC = 10,8 ± 0,95 e POFC = 9,82 ± 1,02. Os resultados do modo de falha foram: adesiva entre pino e cimento (56%), mista predominantemente adesiva entre cimento e dentina (22%), adesiva entre cimento e dentina (14%) e a mista predominantemente adesiva entre pino e cimento (8%). Concluiu-se que entre os pinos experimentais, o grupo do pino perfurado preenchido com cimento resinoso obteve o maior valor de resistência à flexão, a utilização do dispositivo iluminador aumentou os resultados de resistência adesiva nos grupos dos pinos perfurados e não houve diferença na distribuição de tensões entre os grupos. (AU)

The present study aimed to evaluate the flexural strength of an experimental hollow glass fiber post, and the bond strength between this experimental post and root dentin, associating the use of an optical fiber illuminating device, under the aging process, in addition to determine the stress distribution by Finite Element Analysis (FEA). The experimental post and optical fiber illuminating device are intended to increase the polymerization effectiveness of resin cements in the middle and apical regions of root canals. For the 3-point bending test, strictly of the fiber post, the samples were divided into 4 groups (n=10): conventional post (pc), experimental post without filling (pp), with resin cement filling (ppc) and with optical fiber filling (ppf). For the Pull-out test, 100 roots of bovine teeth were restored with intraradicular retainers and composite resin crowns, distributed into 10 groups (n=10), with the following variables: glass fiber post type [conventional (C) or hollow (P)], the photocuring system [with or without the optical fiber illuminating device (O)], the type of resin cement [light cured (F) or dual cured (D)] and aging of the samples [with and without mechanical cycling (C)]. The aging process was performed by mechanical cycling and the samples were submitted to the Pull-out bond strength test. Failure mode analysis was performed using a stereomicroscope. Finite Element Analysis evaluated the stress distribution by von Mises analysis, total strain and maximum principal stress in Ansys Software 19.3. Statistical analysis consisted of the Shapiro-Wilk normality test, 1-, 2- and 3-way analysis of variance (ANOVA) and Tukey test 5%. The means and standard deviations of flexural strength were (MPa): pc = 677 ± 81.1; ppc = 419 ± 23.2; ppf = 200 ± 32.5 and pp = 177 ± 32.8. The means and standard deviations of bond strength were (MPa): CD = 12.2 ± 1.21; PD = 11.1 ± 1.32; PF = 10.9 ± 1.29; POD = 13.7 ± 1.16; POF = 11.9 ± 1.48; CDC = 10.1 ± 1.33; PDC = 9.25 ± 1.11; PFC = 8.37 ± 1.25; PODC = 10.8 ± 0.95 and POFC = 9.82 ± 1.02. The failure mode results were: adhesive between post and cement (56%), mixed predominantly adhesive between cement and dentin (22%), adhesive between cement and dentin (14%) and mixed predominantly adhesive between post and cement (8 %). It was concluded that among the experimental posts, the hollow post group filled with resin cement obtained the highest flexural strength value, the use of the illuminating device increased the results of bond strength in the hollow post groups and there was no difference in the stress distribution among the groups (AU)

Force degradation of elastomeric chains after storage time and mechanical brushing

Abstract The purpose of this in vitro study was to evaluate the force decrease of different elastomeric chains after different times: initial, 10 minutes, 1 day, 28 days and after mechanical brushing. Twenty orthodontic elastomeric chains segments were utilized for each commercial brand. Initially, the elastomeric chain of 15mm long were immediate stretched up to 20 mm in an Instron and the force was measured in gf. After all specimens were placed stretched on rectangular acrylic jigs with distance of 20 mm, immersed in deionized water at 37oC for 10 minutes and the force (gf) was measured again. Five test measurements of remaining force were made at the following time intervals: initial, 10 minutes, 1 day, 28 days and mechanical brushing. After 28 days, the acrylic plates with the specimens were adapted in the mechanical brushing machines (MSCT 3) and the elastomeric chains were submitted to mechanical brushing and the force (gf) measure again. The force (gf) was submitted to mixed-model ANOVA and Sidak post-hoc test (α=0.05). A statistically significant reduction in the force was found for all orthodontic elastomeric chain types after 1 day, 28 days and mechanical brushing (p<0.05). Morelli and 3M Unitek elastomeric chains showed significantly higher force than Abzil and GAC (p<0.05) after 1 day, 28 days and mechanical brushing. In conclusion, the force delivered by all elastomeric chains decayed rapidly over time. Morelli and 3M Unitek elastomeric chains consistently had a significantly greater force after mechanic brushing, while GAC the lowest.

Resumo O objetivo deste estudo in vitro foi avaliar a redução da força de diferentes cadeias elastoméricas após diferentes tempos: inicial, 10 minutos, 1 dia, 28 dias e após escovação mecânica. Vinte segmentos de cadeias elastoméricas ortodônticas foram utilizadas para cada marca comercial. Inicialmente, a cadeia elastomérica de 15 mm de comprimento foi esticada imediatamente até 20 mm na Instron e a força foi medida em (gf). Após, todas as amostras foram adaptadas esticadas em placas retangulares de acrílico na distância de 20 mm, imersas em água deionizada a 37o C por 10 minutos e a força (gf) foi medida novamente. Cinco medidas de força foram feitas nos seguintes intervalos de tempo: inicial, 10 minutos, 1 dia, 28 dias e após a escovação mecânica. Após 28 dias, as placas de acrílico com as amostras foram adaptadas na máquina de escovação (MSCT 3) e as cadeias elastoméricas foram submetidas a escovação mecânica e a medida de força (gf) novamente. Os dados da força (gf) foram submetidos a ANOVA modelo misto e teste post-hoc de Sidak (α = 0,05). Uma redução estatisticamente significativa na força foi encontrada para todos os tipos de cadeia elastomérica ortodôntica após 1 dia, 28 dias e escovação mecânica (p<0,05). As cadeias elastoméricas Morelli e 3M Unitek apresentaram força significativamente superior em relação a Abzil e GAC (p<0,05) após 1 dia, 28 dias e escovação mecânica. Em conclusão, a força distribuída por todas as cadeias elastoméricas decaiu rapidamente com o tempo. As cadeias elastoméricas Morelli e 3M Unitek consistentemente tiveram uma força significativamente maior após a escovação mecânica, enquanto GAC a mais baixa.