RESUMO
Recently, polysaccharide-based hydrogels crosslinked with the trivalent iron cation have attracted interest due to their remarkable properties that include high mechanical stability, stimuli-responsiveness, and enhanced absorptivity. In this study, a Fe3+ crosslinked hydrogel was prepared using the biocompatible extracellular polysaccharide (EPS) secreted by the marine bacterium Alteromonas macleodii Mo169. Hydrogels with mechanical strengths (G') ranging from 0.3 kPa to 44.5 kPa were obtained as a result of the combination of different Fe3+ (0.05-9.95 g L-1) and EPS (0.3-1.7 %) concentrations. All the hydrogels had a water content above 98 %. Three different hydrogels, named HA, HB, and HC, were chosen for further characterization. With strength values (G') of 3.2, 28.9, and 44.5 kPa, respectively, these hydrogels might meet the strength requirements for several specific applications. Their mechanical resistance increased as higher Fe3+ and polymer concentrations were used in their preparation (the compressive hardness increased from 8.7 to 192.1 kPa for hydrogel HA and HC, respectively). In addition, a tighter mesh was noticed for HC, which was correlated to its lower swelling ratio value compared to HA and HB. Overall, this preliminary study highlighted the potential of these hydrogels for tissue engineering, drug delivery, or wound healing applications.
Assuntos
Alteromonas , Hidrogéis , Ferro , Polissacarídeos Bacterianos , Hidrogéis/química , Alteromonas/química , Polissacarídeos Bacterianos/química , Ferro/química , Materiais Biocompatíveis/química , Reagentes de Ligações Cruzadas/química , Força CompressivaRESUMO
FucoPol, a fucose-rich polyanionic polysaccharide, was used for the first time for the preparation of hydrogel membranes (HMs) using Fe3+ as a crosslinking agent. This study evaluated the impact of Fe3+ and FucoPol concentrations on the HMs' strength. The results show that, above 1.5 g/L, Fe3+ concentration had a limited influence on the HMs' strength, and varying the FucoPol concentration had a more significant effect. Three different FucoPol concentrations (1.0, 1.75 and 2.5 wt.%) were combined with Fe3+ (1.5 g/L), resulting in HMs with a water content above 97 wt.% and an Fe3+ content up to 0.16 wt.%. HMs with lower FucoPol content exhibited a denser porous microstructure as the polymer concentration increased. Moreover, the low polymer content HM presented the highest swelling ratio (22.3 ± 1.8 g/g) and a lower hardness value (32.4 ± 5.8 kPa). However, improved mechanical properties (221.9 ± 10.2 kPa) along with a decrease in the swelling ratio (11.9 ± 1.6 g/g) were obtained for HMs with a higher polymer content. Furthermore, all HMs were non-cytotoxic and revealed anti-inflammatory activity. The incorporation of FucoPol as a structuring agent and bioactive ingredient in the development of HMs opens up new possibilities for its use in tissue engineering, drug delivery and wound care management.
RESUMO
The efficiency of natural olive pomace extracts for enhancing the quality of fresh-cut apples was compared with commercial ascorbic acid and two different packaging films (biodegradable polylactic acid (PLA) and oriented polypropylene (OPP)) were tested. The composition of atmosphere inside the packages, the physicochemical parameters (firmness, weight loss and color), the microbial load, total phenolic content and antioxidant activity of fresh-cut apples were evaluated throughout 12 days of storage at 4 °C. After 12 days of refrigerated storage, a significant decrease in O2 was promoted in PLA films, and the weight loss of the whole packaging was higher in PLA films (5.4%) than in OPP films (0.2%). Natural olive pomace extracts reduced the load of mesophilic bacteria (3.4 ± 0.1 log CFU/g and 2.4 ± 0.1 log CFU/g for OPP and PLA films, respectively) and filamentous fungi (3.3 ± 0.1 log CFU/g and 2.44 ± 0.05 log CFU/g for OPP and PLA films, respectively) growth in fresh-cut apples after five days of storage at 4 °C, and no detection of coliforms was verified throughout the 12 days of storage. In general, the olive pomace extract preserved or improved the total phenolic index and antioxidant potential of the fruit, without significant changes in their firmness. Moreover, this extract seemed to be more effective when combined with the biodegradable PLA film packaging. This work can contribute to the availability of effective natural food additives, the sustainability of the olive oil industries and the reduction of environmental impact. It can also be useful in meeting the food industries requirements to develop new functional food products.
RESUMO
Food industry has been pressed to develop products with reduced sugar and low caloric value, while maintaining unchanged their rheological and physicochemical properties. The development of a strawberry preparation for the dairy industry, with prebiotic functionality, was herein investigated by in situ conversion of its intrinsic sucrose content into prebiotic fructo-oligosaccharides (FOS). Two commercial enzymatic complexes, Viscozyme® L and Pectinex® Ultra SP-L, were evaluated for the synthesis of FOS. Operational parameters such as temperature, pH, and enzyme:substrate ratio (E:S) were optimized to maximize FOS yield. The rheological and physicochemical properties of the obtained strawberry preparation were evaluated. For functional analysis, the resistance of FOS to the harsh conditions of the gastro-intestinal digestion was evaluated by applying the standardized INFOGEST static protocol. At optimal conditions (60 â, pH 5.0), Pectinex® produced 265 ± 3 g·L-1 FOS, yielding 0.57 ± 0.01 gFOS·ginitial sucrose-1 after 7 h reaction (E:S:1:40); and Viscozyme® produced 295 ± 1 g·L-1 FOS, yielding 0.66 ± 0.00 gFOS·ginitial sucrose-1 after 5 h (E:S:1:30). The obtained strawberry preparations contained more than 50 %(w/w) prebiotic FOS incorporated (DP 3-5), with 80 % reduction of its sucrose content. The caloric value was therefore reduced by 26-31 %. FOS showed resistance to gastrointestinal digestion being only slightly hydrolysed (<10 %). 1F-Fructofuranosylnystose was not digested at any phase of the digestion. Although the physicochemical properties of the prebiotic preparations were different from the original one, parameters such as the lower °Brix, water activity, consistency and viscosity, and its different color, may be easily adjusted. Results indicate that in situ synthesis strategies are efficient alternatives in the manufacture of reduced sugar and low-caloric food products with prebiotic potential.
Assuntos
Fragaria , Sacarose , Prebióticos , Oligossacarídeos/química , Carboidratos , AçúcaresRESUMO
Tomato pomace is a low-cost, renewable resource that has been studied for the extraction of the biopolyester cutin, which is mainly composed of long-chain hydroxy fatty acids. These are excellent building blocks to produce new hydrophobic biopolymers. In this work, the monomers of cutin were extracted and isolated from tomato pomace and utilized to produce cutin-based films. Several strategies for the depolymerization and isolation of monomeric cutin were explored. Strategies differed in the state of the raw material at the beginning of the extraction process, the existence of a tomato peel dewaxing step, the type of solvent used, the type of alkaline hydrolysis, and the isolation method of cutin monomers. These strategies enabled the production of extracts enriched in fatty acids (16-hydroxyhexadecanoic, hexadecanedioic, stearic, and linoleic, among others). Cutin and chitosan-based films were successfully cast from cutin extracts and commercial chitosan. Films were characterized regarding their thickness (0.103 ± 0.004 mm and 0.106 ± 0.005 mm), color, surface morphology, water contact angle (93.37 ± 0.31° and 95.15 ± 0.53°), and water vapor permeability ((3.84 ± 0.39) × 10-11 mol·m/m2·s·Pa and (4.91 ± 1.33) × 10-11 mol·m/m2·s·Pa). Cutin and chitosan-based films showed great potential to be used in food packaging and provide an application for tomato processing waste.
RESUMO
Chitin-glucan complex (CGC) hydrogels were fabricated by coagulation of the biopolymer from an aqueous alkaline solution, and their morphology, swelling behavior, mechanical, rheological, and biological properties were studied. In addition, their in vitro drug loading/release ability and permeation through mimic-skin artificial membranes (Strat-M) were assessed. The CGC hydrogels prepared from 4 and 6 wt% CGC suspensions (Na51*4 and Na51*6 hydrogels, respectively) had polymer contents of 2.40 ± 0.15 and 3.09 ± 0.22 wt%, respectively, and displayed a highly porous microstructure, characterized by compressive moduli of 39.36 and 47.30 kPa and storage moduli of 523.20 and 7012.25 Pa, respectively. Both hydrogels had a spontaneous and almost immediate swelling in aqueous media, and a high-water retention capacity (>80%), after 30 min incubation at 37 °C. Nevertheless, the Na51*4 hydrogels had higher fatigue resistance and slightly higher-water retention capacity. These hydrogels were loaded with caffeine, ibuprofen, diclofenac, or salicylic acid, reaching entrapment efficiency values ranging between 13.11 ± 0.49% for caffeine, and 15.15 ± 1.54% for salicylic acid. Similar release profiles in PBS were observed for all tested APIs, comprising an initial fast release followed by a steady slower release. In vitro permeation experiments through Strat-M membranes using Franz diffusion cells showed considerably higher permeation fluxes for caffeine (33.09 µg/cm2/h) and salicylic acid (19.53 µg/cm2/h), compared to ibuprofen sodium and diclofenac sodium (4.26 and 0.44 µg/cm2/h, respectively). Analysis in normal human dermal fibroblasts revealed that CGC hydrogels have no major effects on the viability, migration ability, and morphology of the cells. Given their demonstrated features, CGC hydrogels are very promising structures, displaying tunable physical properties, which support their future development into novel transdermal drug delivery platforms.
RESUMO
Rheology modifiers are essential additives in numerous products in a variety of industries. Due to environmental awareness, consumer-oriented industries are interested in novel natural rheological agents that can replace synthetic chemicals. In this study, the chemical composition and rheological properties of a novel exopolysaccharide (EPS) produced by Alteromonas macleodii Mo 169 were investigated. It was mainly composed of uronic acids (50 mol%) and total carbohydrates were 17 % sulfated. The EPS viscosity increased with concentration, and a non-Newtonian shear thinning behavior was found for concentrations above 0.1 wt%. The elastic and viscous moduli indicated a weak gel-like structure above 0.4 wt%. It maintained its shear thinning behavior and viscoelastic properties in the presence of NaCl and CaCl2 for pH range 5-7 and temperatures up to 55 °C. Though the apparent viscosity decreased at pH 3 and 9 and temperatures above 65 °C, the shear thinning behavior was retained. The viscous and viscoelastic properties were recovered after heating (95 °C) and cooling (0 °C), indicating a good thermal stability and recoverability. After high shear force, the solution recovered original rheological properties within few seconds, demonstrating self-healing properties.
Assuntos
Cloreto de Sódio , Temperatura , Reologia , ViscosidadeRESUMO
FucoPol is an acylated polysaccharide with demonstrated valuable functional properties that include a shear thinning fluid behaviour, a film-forming capacity, and an emulsion forming and stabilizing capacity. In this study, the different conditions (concentration, temperature, and time) for alkaline treatment were investigated to deacylate FucoPol. Complete deacetylation and desuccinylation was achieved with 0.02 M NaOH, at 60 °C for 15 min, with no significant impact on the biopolymer's sugar composition, pyruvate content, and molecular mass distribution. FucoPol depyruvylation by acid hydrolysis was attempted, but it resulted in a very low polymer recovery. The effect of the ionic strength, pH, and temperature on the deacetylated/desuccinylated polysaccharide, d-FucoPol, was evaluated, as well as its emulsion and film-forming capacity. d-FucoPol aqueous solutions maintained the shear thinning behaviour characteristic of FucoPol, but the apparent viscosity decreased significantly. Moreover, contrary to FucoPol, whose solutions were not affected by the media's ionic strength, the d-FucoPol solutions had a significantly higher apparent viscosity for a higher ionic strength. On the other hand, the d-FucoPol solutions were not affected by the pH in the range of 3.6-11.5, while FucoPol had a decreased viscosity for acidic pH values and for a pH above 10.5. Although d-FucoPol displayed an emulsification activity for olive oil similar to that of FucoPol (98 ± 0%) for an oil-to-water ratio of 2:3, the emulsions were less viscous. The d-FucoPol films were flexible, with a higher Young's modulus (798 ± 152 MPa), a stress at the break (22.5 ± 2.5 MPa), and an elongation at the break (9.3 ± 0.7%) than FucoPol (458 ± 32 MPa, 15.5 ± 0.3 MPa and 8.1 ± 1.0%, respectively). Given these findings, d-FucoPol arises as a promising novel biopolymer, with distinctive properties that may render it useful for utilization as a suspending or emulsifier agent, and as a barrier in coatings and packaging films.
Assuntos
Fucose , Polissacarídeos , Emulsões , Polissacarídeos/química , Viscosidade , Biopolímeros , ReologiaRESUMO
This work assessed the film-forming capacity of exopolysaccharides (EPS) produced by six Alteromonas strains recently isolated from different marine environments in French Polynesia atolls. The films were transparent and resulted in small colour alterations when applied over a coloured surface (ΔEab below 12.6 in the five different colours tested). Moreover, scanning electron microscopy showed that the EPS films were dense and compact, with a smooth surface. High water vapour permeabilities were observed (2.7-6.1 × 10-11 mol m-1 s-1 Pa-1), which are characteristic of hydrophilic polysaccharide films. The films were also characterised in terms of barrier properties to oxygen and carbon dioxide. Interestingly, different behaviours in terms of their mechanical properties under tensile tests were observed: three of the EPS films were ductile with high elongation at break (ε) (35.6-47.0%), low tensile strength at break (ê) (4.55-11.7 MPa) and low Young's modulus (εm) (10-93 MPa), whereas the other three were stiffer and more resistant with a higher ê (16.6-23.6 MPa), lower ε (2.80-5.58%), and higher εm (597-1100 MPa). These properties demonstrate the potential of Alteromonas sp. EPS films to be applied in different areas such as biomedicine, pharmaceuticals, or food packaging.
RESUMO
Mango peel is rich in nutritional and functional compounds, such as carbohydrates, dietary fibers, proteins, and phenolic compounds, with high potential to be applied in the food industry. Most of the investigation about recovery of bioactive compounds from fruit bioproducts involves extraction techniques and further separation of target compounds. There is still a lack of information about the potential of membrane processes to recover the nutritive/functional compounds present in aqueous extracts of those bioproducts. This research is addressed to study the performance of ultrafiltration (UF), followed by nanofiltration (NF) of UF permeates, to fractionate the compounds present in aqueous extracts of mango peel. Both UF and NF concentration processes were carried up to a volume concentration factor of 2.0. Membranes with molecular weight cut-offs of 25 kDa and 130 Da were used in the UF and NF steps, respectively. UF and NF concentrates showed antioxidant activity, attributed to the presence of phenolic compounds, with rejections of about 75% and 98.8%, respectively. UF membranes totally rejected the higher molecular weight compounds, and NF membranes almost totally concentrated the fermentable monosaccharides and disaccharides. Therefore, it is envisaged that NF concentrates can be utilized by the food industry or for bioenergy production.
RESUMO
Tomato pomace is rich in carotenoids (mainly lycopene), which are related to important bioactive properties. In general, carotenoids are known to react easily under environmental conditions, which may create a barrier in producing stable functional components for food. This work intended to evaluate the storage stability and in vitro release of lycopene from encapsulated tomato pomace extract, and its bioaccessibility when encapsulates were incorporated in yogurt. Microencapsulation assays were carried out with tomato pomace extract as the core material and arabic gum or inulin (10 and 20 wt%) as wall materials by spray drying (160 and 200 °C). The storage stability results indicate that lycopene degradation was highly influenced by the presence of oxygen and light, even when encapsulated. In vitro release studies revealed that 63% of encapsulated lycopene was released from the arabic gum particles in simulated gastric fluid, whereas for the inulin particles, the release was only around 13%. The feed composition with 20% inulin showed the best protective ability and the one that enabled releasing the bioactives preferentially in the intestine. The bioaccessibility of the microencapsulated lycopene added to yogurt increased during simulated gastrointestinal digestion as compared to the microencapsulated lycopene alone. We anticipate a high potential for the inulin microparticles containing lycopene to be used in functional food formulations.
RESUMO
The main objective of this study was to extend the shelf life of fresh red raspberry (Rubus idaeus. L. cv. 'Kweli') by using active film-pads inside commercial compostable packages. The pads were produced with chitosan (Ch) with the incorporation of green tea (GTE) and rosemary (RSME) ethanolic extracts as natural antifungal agents. Pads were placed on the bottom of commercial fruit trays underneath the fruits, and the trays were heat-sealed with a polyacid lactic (PLA) film. Preservation studies were carried out over 14 days of storage at refrigeration temperature (4 °C). Raspberry samples were periodically analyzed throughout storage, in terms of quality attributes (fungal decay, weight loss, firmness, surface color, pH, total soluble solids), total phenolic content and antioxidant activity. Gas composition inside the packages was also analyzed over time. From the packaging systems tested, the ones with active film-pads Ch + GTE and Ch + RSME were highly effective in reducing fungal growth and decay of raspberry during storage, showing only around 13% and 5% of spoiled fruits after 14 days, respectively, in contrast with the packages without pads (around 80% of spoiled fruits detected). In addition, fruits preserved using packages with Ch + RSME active film-pads showed lower mass loss (5.6%), decreased firmness (3.7%) and reduced antioxidant activity (around 9% and 15% for DPPH and FRAP methods, respectively). This sustainable packaging presents a potential strategy for the preservation of raspberries and other highly perishable small fruits.
RESUMO
Chitin-glucan complex (CGC) hydrogels were fabricated through a freeze-thaw procedure for biopolymer dissolution in NaOH 5 mol/L, followed by a dialysis step to promote gelation. Compared to a previously reported methodology that included four freeze-thaw cycles, reducing the number of cycles to one had no significant impact on the hydrogels' formation, as well as reducing the total freezing time from 48 to 18 h. The optimized CGC hydrogels exhibited a high and nearly spontaneous swelling ratio (2528 ± 68%) and a water retention capacity of 55 ± 3%, after 2 h incubation in water, at 37 °C. Upon loading with caffeine as a model drug, an enhancement of the mechanical and rheological properties of the hydrogels was achieved. In particular, the compressive modulus was improved from 23.0 ± 0.89 to 120.0 ± 61.64 kPa and the storage modulus increased from 149.9 ± 9.8 to 315.0 ± 76.7 kPa. Although the release profile of caffeine was similar in PBS and NaCl 0.9% solutions, the release rate was influenced by the solutions' pH and ionic strength, being faster in the NaCl solution. These results highlight the potential of CGC based hydrogels as promising structures to be used as drug delivery devices in biomedical applications.
RESUMO
Despite the fact that iongels are very attractive materials for gas separation membranes, they often show mechanical stability issues mainly due to the high ionic liquid (IL) content (≥60 wt%) needed to achieve high gas separation performances. This work investigates a strategy to improve the mechanical properties of iongel membranes, which consists in the incorporation of montmorillonite (MMT) nanoclay, from 0.2 to 7.5 wt%, into a cross-linked poly(ethylene glycol) diacrylate (PEGDA) network containing 60 wt% of the IL 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ([C2mim][TFSI]). The iongels were prepared by a simple one-pot method using ultraviolet (UV) initiated polymerization of poly(ethylene glycol) diacrylate (PEGDA) and characterized by several techniques to assess their physico-chemical properties. The thermal stability of the iongels was influenced by the addition of higher MMT contents (>5 wt%). It was possible to improve both puncture strength and elongation at break with MMT contents up to 1 wt%. Furthermore, the highest ideal gas selectivities were achieved for iongels containing 0.5 wt% MMT, while the highest CO2 permeability was observed at 7.5 wt% MMT content, due to an increase in diffusivity. Remarkably, this strategy allowed for the preparation and gas permeation of self-standing iongel containing 80 wt% IL, which had not been possible up until now.
RESUMO
Marine environments comprise almost three quarters of Earth's surface, representing the largest ecosystem of our planet. The vast ecological and metabolic diversity found in marine microorganisms suggest that these marine resources have a huge potential as sources of novel commercially appealing biomolecules, such as exopolysaccharides (EPS). Six Alteromonas strains from different marine environments in French Polynesia atolls were selected for EPS extraction. All the EPS were heteropolysaccharides composed of different monomers, including neutral monosaccharides (glucose, galactose, and mannose, rhamnose and fucose), and uronic acids (glucuronic acid and galacturonic acid), which accounted for up to 45.5 mol% of the EPS compositions. Non-carbohydrate substituents, such as acetyl (0.5-2.1 wt%), pyruvyl (0.2-4.9 wt%), succinyl (1-1.8 wt%), and sulfate (1.98-3.43 wt%); and few peptides (1.72-6.77 wt%) were also detected. Thermal analysis demonstrated that the EPS had a degradation temperature above 260 °C, and high char yields (32-53%). Studies on EPS functional properties revealed that they produce viscous aqueous solutions with a shear thinning behavior and could form strong gels in two distinct ways: by the addition of Fe2+, or in the presence of Mg2+, Cu2+, or Ca2+ under alkaline conditions. Thus, these EPS could be versatile materials for different applications.
Assuntos
Alteromonas , Polissacarídeos Bacterianos/química , Animais , Organismos Aquáticos , Biotecnologia , PolinésiaRESUMO
This study aimed to develop edible monolayer emulsion-based barriers with polysaccharides as film-forming components (chitosan and sodium alginate), soy lecithin as a surfactant and olive oil as a hydrophobic barrier. Monolayer barriers in the form of films were prepared by casting filmogenic emulsions composed of 2% w/v chitosan (dissolved in lactic acid 1% v/v) or 1% w/v sodium alginate, with different lipid contents (25, 50 and 100% w/w biopolymer basis) and different surfactant concentrations (5, 10 and 25% w/w, lipid basis). Glycerol was used as a plasticizer (25 % w/w, biopolymer basis). After the emulsion drying process, the obtained stand-alone films were sprayed with a crosslinking solution, achieving an optimized crosslinker content of 3.2 mgCa2+/cm2 alginate film and 4 mg tripolyphosphate/cm2 chitosan film. The effect of oil and lecithin contents, as well the presence of crosslinking agents, on the film's water vapour permeability (WVP), water vapour sorption capacity, mechanical properties and colour parameters, was evaluated. The results have shown that the lowest WVP values were obtained with formulations containing 25% lipid and 25% surfactant for chitosan films, and 100% lipid and 25% surfactant for alginate films. The application of the crosslinking agents decreased even further the WVP, especially for chitosan films (by 30%). Crosslinking also increased films' resistance to deformation under tensile tests. Overall, the films developed present a good potential as polysaccharide-based barriers with increased resistance to water, which envisages the use of the designed formulations to produce either edible/biodegradable films or edible coatings.
RESUMO
Pineapple peel still contains an important amount of phenolic compounds and vitamins with valuable antioxidant activity. In this way, the aim of this study was the recovery of the bioactive compounds from pineapple peel using environmentally friendly and low-cost techniques, envisaging their application in food products. From the solid-liquid extraction conditions tested, the one delivering an extract with higher total phenolic content and antioxidant capacity was a single extraction step with a solvent-pineapple peel ratio of 1:1 (w/w) for 25 min at ambient temperature, using ethanol-water (80-20%) as a solvent. The resulting extract revealed a total phenolic content value of 11.10 ± 0.01 mg gallic acid equivalent (GAE)/g dry extract, antioxidant activity of 91.79 ± 1.98 µmol Trolox/g dry extract by the DPPH method, and 174.50 ± 9.98 µmol Trolox/g dry extract by the FRAP method. The antioxidant rich extract was subjected to stabilization by the spray drying process at 150 °C of inlet air temperature using maltodextrin (5% w/w) as an encapsulating agent. The results showed that the antioxidant capacity of the encapsulated compounds was maintained after encapsulation. The loaded microparticles obtained, which consist of a bioactive powder, present a great potential to be incorporated in food products or to produce bioactive packaging systems.
RESUMO
This study seeks to render residues from banana plants into a useful byproduct with possible applications in wound dressings and food packaging. Films based on cellulose extracted from banana plant pseudostem and doped with phenolic compounds extracted from banana plant leaves were developed. The phenolic compounds were extracted using batch solid-liquid and Soxhlet methods, with different drying temperatures and periods of time. The total phenolic content and antioxidant activity were quantified. The optimum values were obtained using a three-day period batch-solid extraction at 40 °C (791.74 ± 43.75 mg/L). SEM analysis indicates that the pseudostem (PS) films have a porous structure, as opposed to hydroxyethyl cellulose (HEC) films which presented a homogeneous and dense surface. Mechanical properties confirmed the poor robustness of PS films. By contrast HEC films manifested improved tensile strength at low levels of water activity. FTIR spectroscopy reinforced the need to improve the cellulose extraction process, the success of lignin and hemicellulose removal, and the presence of phenolic compounds. XRD, TGA and contact angle analysis showed similar results for both films, with an amorphous structure, thermal stability and hydrophilic behavior.
RESUMO
Corn fiber from the corn starch industry is a by-product produced in large quantity that is mainly used in animal feed formulations, though it is still rich in valuable components, such as arabinoxylans, with proven film-forming ability. During arabinoxylans' recovery under alkaline extraction, a dark-colored biopolymer fraction is obtained. In this work, a purified arabinoxylan extract from corn fiber with an intense brownish color was decolorized using hydrogen peroxide as the decolorizing agent. Biodegradable films prepared by casting the decolorized extract exhibited a light-yellow color, considered more appealing, envisaging their application in food packaging. Films were prepared with glycerol as plasticizer and citric acid as cross-linker. Although the cross-linking reaction was not effective, films presented antioxidant activity, a water vapor permeability similar to that of non-decolorized films, and other polysaccharides' and mechanical properties that enable their application as packaging materials of low-water-content food products.
RESUMO
Fresh figs are very appreciated and have been associated with health benefits. However, these fruits are highly perishable. In this study, edible coatings were studied envisaging their positive effect in enhancing figs' shelf-life. Fig fruits cv. 'Pingo de mel' were harvested at commercial ripening stage and single emulsion-based coatings, composed of chitosan + olive oil and alginate + olive oil, were applied. After coatings application by dipping each fruit in the emulsion-based solutions at 4 °C and drying, the coated fruits were sprayed with crosslinking solutions (6% tripolyphosphate and 1% calcium chloride for chitosan and alginate-based coatings, respectively). Then, were maintained at 4 °C and analyzed after 1, 7, 14 and 19 days of storage. After each time interval, fruits were further maintained at 25 °C for 2 days. The results have shown that coatings were effective on delaying fungal decay and postharvest ripening indicators (respiration rate, mass loss, softening and total soluble solids/titratable acidity ratio). The results foresee a fruits' shelf life between 14 and 19 days under refrigeration at 4 °C that may be followed up to 2 days at ambient temperature, higher than that estimated for uncoated fruits (less than 14 days at 4 °C plus to 2 days at ambient temperature).